CN209522800U - A kind of glass-film with infrared ray barriers function - Google Patents
A kind of glass-film with infrared ray barriers function Download PDFInfo
- Publication number
- CN209522800U CN209522800U CN201822164703.4U CN201822164703U CN209522800U CN 209522800 U CN209522800 U CN 209522800U CN 201822164703 U CN201822164703 U CN 201822164703U CN 209522800 U CN209522800 U CN 209522800U
- Authority
- CN
- China
- Prior art keywords
- layer
- film
- infrared ray
- glass
- metal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model discloses a kind of glass-films with infrared ray barriers function, including release film layer, installation glue-line, transparent substrate layer, the first metal oxide layer, metal layer, the second metal oxide layer, flame-retardant layer and anti-scratch layer, the lower surface of the transparent substrate layer is fixed with installation glue-line, the lower surface of the installation glue-line is fixed with release film layer, the upper surface of the transparent substrate layer is fixed with the first metal oxide layer, and the upper surface of first metal oxide layer is provided with metal layer.The utility model passes through setting metal layer; and the material silver of metal layer; silver free electron density with higher passes through the first metal oxide layer of setting and the second metal oxide layer so higher reflectivity can be played to infrared ray; preferable protective effect can be played to metal layer; and infrared ray can be reflected, by the way that flame-retardant layer is arranged, preferable flame retardant effect can be played; by the way that anti-scratch layer is arranged, preferable anti-scratch effect can be played.
Description
Technical field
The utility model relates to glass technical field of membrane, specially a kind of glass-film with infrared ray barriers function.
Background technique
Glass-film, that uses in daily life is relatively broad, such as all can on vehicle glass vehicle window and on glass housing
Apply to glass-film, the type of glass-film is also very much, have an implosion guard film, half mirror film, ultraviolet ray intercepting glass film and
Infrared-proof glass film etc..
But the anti-infrared effect of current infrared-proof glass film, flame retardant effect and anti-scratch effect are all poor,
Therefore we have proposed a kind of glass-films with infrared ray barriers function to solve the above problems.
Utility model content
(1) the technical issues of solving
In view of the deficiencies of the prior art, the utility model provides a kind of glass-film with infrared ray barriers function, solution
It has determined all poor problem of anti-infrared effect, flame retardant effect and anti-scratch effect of existing infrared-proof glass film.
(2) technical solution
To achieve the above object, the utility model provides the following technical solutions: a kind of glass with infrared ray barriers function
Glass film, including release film layer, installation glue-line, transparent substrate layer, the first metal oxide layer, metal layer, the second metal oxide
Layer, flame-retardant layer and anti-scratch layer, the lower surface of the transparent substrate layer are fixed with installation glue-line, the lower surface of the installation glue-line
It is fixed with release film layer, the upper surface of the transparent substrate layer is fixed with the first metal oxide layer, the first metal oxidation
The upper surface of nitride layer is provided with metal layer, and the upper surface of the metal layer is fixed with the second metal oxide layer, second gold medal
The upper surface for belonging to oxide skin(coating) is fixed with flame-retardant layer, and the upper surface of the flame-retardant layer is fixed with anti-scratch layer.
The technical program is advanced optimized, the release film layer is polytetrafluoroethylene (PTFE) release film.
The technical program is advanced optimized, the installation glue-line is the pressure of organic siliconresin and organic silicon rubber mixing composition
Sensitive adhesive, and wherein it is added with ultraviolet absorbing agent.
The technical program is advanced optimized, the transparent substrate layer is polycarbonate film.
The technical program is advanced optimized, the material of first metal oxide layer is zinc oxide.
The technical program is advanced optimized, the material of the metal layer is silver.
The technical program is advanced optimized, the material of second metal oxide layer is indium tin composite oxides.
The technical program is advanced optimized, the material of the flame-retardant layer is polyvinyl chloride.
The technical program is advanced optimized, the anti-scratch layer is quasi cobalt carbon diaphragm.
(3) beneficial effect
Compared with prior art, the utility model provides a kind of glass-film with infrared ray barriers function, have with
It is lower the utility model has the advantages that
1, the glass-film with infrared ray barriers function, by the way that metal layer is arranged, and the material silver of metal layer, silver have
Higher free electron density, so higher reflectivity can be played to infrared ray, by the way that the first metal oxide layer is arranged
With the second metal oxide layer, and the material of the first metal oxide layer and the second metal oxide layer is respectively zinc oxide and indium
Tin composite oxides so not only possessing higher transmissivity to visible light, but also can preferably reflect infrared ray, and the first metal oxygen
Compound layer and the second metal oxide layer are separately positioned on the two sides of metal layer, and preferable protection can be played to metal layer and is made
With being able to suppress the deterioration of metal layer, so the barriers function of the glass-film infrared ray is preferable, and service life is longer.
2, the glass-film with infrared ray barriers function, by the way that flame-retardant layer is arranged, and the material of flame-retardant layer is polychlorostyrene second
Alkene can play preferable flame retardant effect, when fire occurs, can play the role of stopping fire spreading, anti-by being arranged
Layer is scratched, and the material of anti-scratch layer is quasi cobalt carbon diaphragm, quasi cobalt carbon diaphragm has hardness high, and corrosion-resistant, coefficient of friction is small, Ke Yiqi
To preferable anti-scratch, corrosion-resistant, wear-resisting effect, so as to improve the service life of glass.
Detailed description of the invention
Fig. 1 is the utility model overall structure diagram.
In figure: 1, release film layer;2, glue-line is installed;3, transparent substrate layer;4, the first metal oxide layer;5, metal layer;
6, the second metal oxide layer;7, flame-retardant layer;8, anti-scratch layer.
Specific embodiment
The following will be combined with the drawings in the embodiments of the present invention, carries out the technical scheme in the embodiment of the utility model
Clearly and completely describe, it is clear that the described embodiments are only a part of the embodiments of the utility model, rather than whole
Embodiment.Based on the embodiments of the present invention, those of ordinary skill in the art are without making creative work
Every other embodiment obtained, fall within the protection scope of the utility model.
Referring to Fig. 1, the utility model provides a kind of technical solution: a kind of glass-film with infrared ray barriers function,
Including release film layer 1, installation glue-line 2, transparent substrate layer 3, the first metal oxide layer 4, metal layer 5, the second metal oxide
Layer 6, flame-retardant layer 7 and anti-scratch layer 8, the lower surface of transparent substrate layer 3 are fixed with installation glue-line 2, and the lower surface of installation glue-line 2 is solid
Surely there is release film layer 1, the upper surface of transparent substrate layer 3 is fixed with the first metal oxide layer 4, the first metal oxide layer 4
Upper surface is provided with metal layer 5, and the upper surface of metal layer 5 is fixed with the second metal oxide layer 6, the second metal oxide layer 6
Upper surface be fixed with flame-retardant layer 7, the upper surface of flame-retardant layer 7 is fixed with anti-scratch layer 8, by the way that metal layer 5, and metal layer is arranged
5 material silver, silver free electron density with higher pass through setting so higher reflectivity can be played to infrared ray
First metal oxide layer 4 and the second metal oxide layer 6, and the first metal oxide layer 4 and the second metal oxide layer 6
Material is respectively zinc oxide and indium tin composite oxides, so not only possessing higher transmissivity to visible light, but also can be preferably anti-
Infrared ray is penetrated, and the first metal oxide layer 4 and the second metal oxide layer 6 are separately positioned on the two sides of metal layer 5, it can be right
Metal layer 5 plays preferable protective effect, is able to suppress the deterioration of metal layer 5, so the barriers function of the glass-film infrared ray
Preferably, and service life is longer, and by the way that flame-retardant layer 7 is arranged, and the material of flame-retardant layer 7 is polyvinyl chloride, can play preferable
Flame retardant effect can play the role of stopping fire spreading when fire occurs, by the way that anti-scratch layer 8, and anti-scratch layer is arranged
8 material is quasi cobalt carbon diaphragm, and quasi cobalt carbon diaphragm has hardness high, and corrosion-resistant, coefficient of friction is small, can play it is preferable it is anti-scratch,
Corrosion-resistant, wear-resisting effect, so as to improve the service life of glass.
Specifically, release film layer 1 is polytetrafluoroethylene (PTFE) release film, convenient for removing, and against weather is stronger and acidproof resistance to
Alkaline better performances.
Specifically, installation glue-line 2 is the pressure-sensitive adhesive of organic siliconresin and organic silicon rubber mixing composition, and wherein add
Added with ultraviolet absorbing agent, there is high temperature resistant and ageing-resistant performance, and convenient for absorbing the ultraviolet light in light.
Specifically, transparent substrate layer 3 is polycarbonate film, light transmittance is higher, and impact resistance is preferable.
Specifically, the material of the first metal oxide layer 4 is zinc oxide, the high transmittance to visible light can be played,
Simultaneously but also with the high reflectance to infrared ray.
Specifically, the material of metal layer 5 is silver, higher reflectivity can be played to the infrared ray in light.
Specifically, the material of the second metal oxide layer 6 is indium tin composite oxides, can play to the higher of visible light
Transmissivity, while but also with the high reflectance to infrared ray.
Specifically, the material of flame-retardant layer 7 is polyvinyl chloride, convenient for playing preferable flame retardant effect.
Specifically, anti-scratch layer 8 is quasi cobalt carbon diaphragm, convenient for playing anti-scratch effect, and the corrosion resistance of quasi cobalt carbon diaphragm
Can preferably, coefficient of friction is also preferable.
When in use, release film layer 1 to be thrown off, is affixed directly on glass, the material of metal layer 5 is silver, because
Silver free electron density with higher, so possessing higher reflectivity to infrared ray, the two sides of metal layer 5 are respectively arranged with
First metal oxide layer 4 and the second metal oxide layer 6, and the first metal oxide layer 4 and the second metal oxide layer 6
Material is respectively zinc oxide and indium tin composite oxides, and zinc oxide and indium tin composite oxides possess visible light higher
Rate is penetrated, and higher reflectivity is possessed to infrared ray, so the barriering effect to infrared ray can be reinforced, and can preferably be protected
Metal layer 5, the anti-deterioration for inhibiting metal layer 5 of energy are protected, the material of flame-retardant layer 7 is that polyvinyl chloride can play when a fire
Stop the effect of fire spreading, the material of anti-scratch layer 8 is quasi cobalt carbon diaphragm, and quasi cobalt carbon diaphragm has hardness height, corrosion-resistant, friction system
Number is small, can play preferable anti-scratch, corrosion-resistant, wear-resisting effect.
In conclusion this has the glass-film of infrared ray barriers function, by the way that metal layer 5, and the material of metal layer 5 is arranged
Silver, silver free electron density with higher, so higher reflectivity can be played to infrared ray, by the way that the first metal is arranged
Oxide skin(coating) 4 and the second metal oxide layer 6, and the material of the first metal oxide layer 4 and the second metal oxide layer 6 is distinguished
For zinc oxide and indium tin composite oxides, so not only possessing higher transmissivity to visible light, but also infrared ray can be preferably reflected,
And first metal oxide layer 4 and the second metal oxide layer 6 be separately positioned on the two sides of metal layer 5, metal layer 5 can be risen
To preferable protective effect, it is able to suppress the deterioration of metal layer 5, so the barriers function of the glass-film infrared ray is preferable, and is made
With lasting a long time, by the way that flame-retardant layer 7 is arranged, and the material of flame-retardant layer 7 is polyvinyl chloride, can play preferable flame retardant effect,
When fire occurs, can play the role of stopping fire spreading, by the way that anti-scratch layer 8 is arranged, and the material of anti-scratch layer 8 is
Quasi cobalt carbon diaphragm, quasi cobalt carbon diaphragm have hardness high, and corrosion-resistant, coefficient of friction is small, can play preferable anti-scratch, corrosion-resistant, resistance to
The effect of mill, so as to improve the service life of glass.
It should be noted that, in this document, relational terms such as first and second and the like are used merely to a reality
Body or operation are distinguished with another entity or operation, are deposited without necessarily requiring or implying between these entities or operation
In any actual relationship or order or sequence.Moreover, the terms "include", "comprise" or its any other variant are intended to
Non-exclusive inclusion, so that the process, method, article or equipment including a series of elements is not only wanted including those
Element, but also including other elements that are not explicitly listed, or further include for this process, method, article or equipment
Intrinsic element.In the absence of more restrictions, the element limited by sentence "including a ...", it is not excluded that
There is also other identical elements in process, method, article or equipment including the element.
While there has been shown and described that the embodiments of the present invention, for the ordinary skill in the art,
It is understood that these embodiments can be carried out with a variety of variations in the case where not departing from the principles of the present invention and spirit, repaired
Change, replacement and variant, the scope of the utility model is defined by the appended claims and the equivalents thereof.
Claims (9)
1. a kind of glass-film with infrared ray barriers function, including release film layer (1), installation glue-line (2), transparent substrate layer
(3), the first metal oxide layer (4), metal layer (5), the second metal oxide layer (6), flame-retardant layer (7) and anti-scratch layer (8),
It is characterized by: the lower surface of the transparent substrate layer (3) is fixed with installation glue-line (2), the lower surface of installation glue-line (2)
It being fixed with release film layer (1), the upper surface of the transparent substrate layer (3) is fixed with the first metal oxide layer (4), and described first
The upper surface of metal oxide layer (4) is provided with metal layer (5), and the upper surface of the metal layer (5) is fixed with the second metal oxygen
The upper surface of compound layer (6), second metal oxide layer (6) is fixed with flame-retardant layer (7), the upper table of the flame-retardant layer (7)
Face is fixed with anti-scratch layer (8).
2. a kind of glass-film with infrared ray barriers function according to claim 1, it is characterised in that: the release film
Layer (1) is polytetrafluoroethylene (PTFE) release film.
3. a kind of glass-film with infrared ray barriers function according to claim 1, it is characterised in that: the installation glue
Layer (2) is the pressure-sensitive adhesive of organic siliconresin and organic silicon rubber mixing composition, and is wherein added with ultraviolet absorbing agent.
4. a kind of glass-film with infrared ray barriers function according to claim 1, it is characterised in that: the transparent base
Material layer (3) is polycarbonate film.
5. a kind of glass-film with infrared ray barriers function according to claim 1, it is characterised in that: first gold medal
The material for belonging to oxide skin(coating) (4) is zinc oxide.
6. a kind of glass-film with infrared ray barriers function according to claim 1, it is characterised in that: the metal layer
(5) material is silver.
7. a kind of glass-film with infrared ray barriers function according to claim 1, it is characterised in that: second gold medal
The material for belonging to oxide skin(coating) (6) is indium tin composite oxides.
8. a kind of glass-film with infrared ray barriers function according to claim 1, it is characterised in that: the flame-retardant layer
(7) material is polyvinyl chloride.
9. a kind of glass-film with infrared ray barriers function according to claim 1, it is characterised in that: described anti-scratch
Layer (8) is quasi cobalt carbon diaphragm.