CN208896737U - A kind of oil pressure and the firmly golden combination process product of electroforming - Google Patents
A kind of oil pressure and the firmly golden combination process product of electroforming Download PDFInfo
- Publication number
- CN208896737U CN208896737U CN201821561653.7U CN201821561653U CN208896737U CN 208896737 U CN208896737 U CN 208896737U CN 201821561653 U CN201821561653 U CN 201821561653U CN 208896737 U CN208896737 U CN 208896737U
- Authority
- CN
- China
- Prior art keywords
- product
- halves
- electroforming
- oil pressure
- combination process
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model provides the firmly golden combination process product of a kind of oil pressure and electroforming, comprising: the two halves product suppressed；Solder layer, together by the two halves Product jointing；And noble metal hard gold layer, it is attached to two halves product surface, the thickness range of two halves product is 0.01mm-0.5mm or 0.1mm-0.15mm, die pressing used in two halves product includes the rectangular of unilateral 10mm-30mm bigger than product or with the equidistant sheet material of type, two halves product surface decorative pattern includes impression level, bright sand effect, fantasy coloured effect or coining micro text, noble metal hard gold layer are the hard gold layer of gold or silver.The fineness of the handicraft product decorative pattern is high, and the hardness of product, wearability and oxidation resistance are strong, and processing cost is controlled, and antenatal consumption is reduced.
Description
[technical field]
The utility model relates to a kind of combination process products, the in particular to work of the firmly golden combination process production of oil pressure and electroforming
Art products.
[background technique]
Noble metal refers to gold, silver, platinum family element, and the more noble metal that circulates in the market is Jin Heyin.Noble metal is more
For manufacturing collectibles, jewellery etc., with the fast development of social economy and culture, demand of the people to craftwork also increasingly increases
More, it has unique texture with the craftwork made of certain substrate cooperation noble metal, has been favored by people, can apply
In daily life, such as: the covers such as stamp, postal card, mail cover, stamp folder, bankbook, memorial money, test paper money, process gift book, picture,
And the thickness of noble metal can become thin, reduce grammes per square metre not only to reduce purchase cost, and can make more
Beauty, current technique are usually the hard gold ornaments for individually carrying out oil pressure technique or electroforming formation, pass through the hard gold production of electroforming
Product decorative pattern fineness it is not high, hard gold class product also needs to punch green body when removing production on surface, destroys entire decorations
The integrality and aesthetic measure of product, and the product of oil pressure technique is individually used, hardness and wear resistance be not high, the antioxygen of product
Change indifferent, and the higher cost of two kinds of techniques production product, antenatal consumption are bigger.
[summary of the invention]
The purpose of the utility model is to overcome the deficiencies in the prior art, a kind of oil pressure and the firmly golden combination process of electroforming are provided
Product, the fineness of the handicraft decorative pattern is high, and the hardness of product, wearability and oxidation resistance are strong, without conventional hard
Golden class product surface punching, product is completely beautiful, improves the quality of compound hard golden product, and simultaneous processing cost is controlled, dropped
Low antenatal consumption.
The technical solution of the utility model is achieved in that a kind of oil pressure of the utility model and the hard compound work of gold of electroforming
Art products, the handicraft include:
The two halves product or physical product suppressed；And
Noble metal hard gold layer is attached to the two halves product surface or the physical product surface.
Preferably, further include: welding layer, together by two halves Product jointing.
Preferably, the thickness range of the two halves product is 0.01mm-0.5mm.
Preferably, die pressing used in the two halves product include the rectangular of unilateral 10mm-30mm bigger than product or
With the equidistant sheet material of type.
Preferably, the two halves product surface decorative pattern includes impression level, bright sand effect, fantasy coloured effect or coining are micro-
Contracting text.
Preferably, the noble metal hard gold layer is the hard gold layer of gold or silver.
The utility model has the beneficial effects that:
Product decorative pattern has been effectively ensured in the firmly golden combination process product of a kind of oil pressure and electroforming that the utility model provides
Fineness enhances the hardness, wearability and oxidation resistance of product, without in conventional hard golden class product surface punching, produces
Product are completely beautiful, improve the quality of compound hard golden product, and simultaneous processing cost is controlled, and reduce antenatal consumption.
[Detailed description of the invention]
The attached default appearance and modeling figure for locking job contract art products Fig. 1 shows according to the utility model embodiment 1；
Attached drawing 2 indicates the floral designs of the lock job contract art products two halves product formation according to the utility model embodiment 1；
Attached drawing 3 indicates the positive rear surface pattern of art products of undertaking to perform work within a time limit and according to specifications according to the lock of the utility model embodiment 1.
[specific embodiment]
Referring to attached drawing 1, a kind of embodiment 1-3 of oil pressure and the firmly golden combination process product manufacture craft of electroforming, the embodiment
1-3 is illustrated for locking packet production process.
Embodiment 1:
The technique the following steps are included:
Step 1, sawing sheet and mold manufacture: by silver-colored green body pressure rolling it is preset thickness by pressure rolling process, and cuts into
The sheet material of required moulding, moulding tailor size principal security product grammes per square metre and control reduce production capacity waste, needle depending on product
To the present embodiment, preset thickness range is the strip sheet material of 0.01mm, and die pressing is to be cut into sheet material unilateral to compare product
Big 10mm's is rectangular, and the product is wherein indicated in Fig. 1 and presets appearance and modeling, light-colored part is reserved processing part waste material
Position, waste part is too small, deviation is put in production process sets and be easy to weigh wounded product, and excessive to be easy to cause waste, selection is suitably given up
Material position is it is anticipated that control cost；
In addition, oil pressure mold and blanking die needed for synchronous production, the mold data root of oil pressure mold and blanking die
According to preset product appearance, grammes per square metre, size, structure determination, production method comprising steps of
(1-1) passes through computer graphics Software on Drawing embossment model；
The model data of drafting is carved coppersmith by CNC engraving machine by (1-2)；
(1-3) is discharged using coppersmith by Cremation Machine and corrodes die steel, the embossment needed for the production of die steel surface
Pattern；
(1-4) handles die surface effect according to the default of product；
(1-5) assembling；
The surface effect of step (1-4) includes carving pattern level, bright sand effect, fantasy coloured effect or coining micro text.
Step 2, oil pressure: the silver strip material cut being put into the oil pressure cavity body of mould prepared and be cold-pressed drum, pressure
Product surface decorative pattern processed, 20 tons of pressure, to ensure that product pattern precision, compacted products surface detail includes relief flower lamina
It is secondary, bright sand effect, fantasy coloured effect or coining micro text, as shown in Figure 2.
Step 3, blanking process cut extra waste material, leave compacting by the semi-finished product suppressed by blanking die
Good two halves product, as shown in Figure 3；
The two halves product suppressed is welded, holds mould and/or sandblasting press polish processing by step 4；
Step 5, electroforming process: the product that will be welded adheres to one in product surface by the firmly golden electroforming process of no cyanogen
The hard gold layer of layer gold, electroforming is with a thickness of 0.005mm；
Step 6, postprocessing working procedures: obtaining finished product after post treatment, postprocessing working procedures include according to product design drawing into
Row, carries out surface effect product defective to hold mould and/or sandblasting calendered surface effect process, and carry out quality inspection.
Embodiment 2:
The technique the following steps are included:
Step 1, sawing sheet and mold manufacture: by golden green body pressure rolling it is preset thickness by pressure rolling process, and cuts into
The sheet material of required moulding, moulding tailor size principal security product grammes per square metre and control reduce production capacity waste, needle depending on product
To the present embodiment, preset thickness range is the strip sheet material of 0.5mm, and die pressing is unilateral bigger than product for sheet material to be cut into
30mm's is rectangular；
In addition, oil pressure mold and blanking die needed for synchronous production, the mold data root of oil pressure mold and blanking die
According to preset product appearance, grammes per square metre, size, structure determination, production method comprising steps of
(2-1) passes through computer graphics Software on Drawing embossment model；
The model data of drafting is passed through CNC engraving machine engraved die steel by (2-2), needed for the production of die steel surface
Embossing pattern；
(2-3) is heat-treated die steel, promotes the hardness of die steel, so that die steel hardness reaches certain
59 degree of Rockwell hardness；
(2-4) handles the surface effect of mold according to the default of product；
(2-5) assembling.
The surface effect of step (2-4) includes carving pattern level, bright sand effect, fantasy coloured effect or coining micro text.
Step 2, oil pressure: the gold plaque material cut being put into the oil pressure cavity body of mould prepared and be cold-pressed drum, pressure
Product surface decorative pattern processed, 4000 tons of pressure, to ensure that product pattern precision, compacted products surface detail includes impression
Level, bright sand effect, fantasy coloured effect or coining micro text.
Step 3, blanking process cut extra waste material, leave compacting by the semi-finished product suppressed by blanking die
Good two halves product；
The two halves product suppressed is welded, holds mould and/or sandblasting press polish processing by step 4；
Step 5, electroforming process: the product that will be welded adheres to one in product surface by the firmly golden electroforming process of no cyanogen
The hard gold layer of layer gold, electroformed layer is with a thickness of 0.3mm；
Step 6, postprocessing working procedures: obtaining finished product after post treatment, postprocessing working procedures include according to product design drawing into
Row, carries out surface effect product defective to hold mould and/or sandblasting calendered surface effect process, and carry out quality inspection.
Embodiment 3:
The technique the following steps are included:
Step 1, mold manufacture and sawing sheet:
The production of oil pressure mold and blanking die: the mold data of oil pressure mold and blanking die is according to outside preset product
Sight, grammes per square metre, size, structure determination, production method comprising steps of
(2-1) passes through computer graphics Software on Drawing embossment model；
The model data of drafting is passed through CNC engraving machine engraved die steel by (2-2), needed for the production of die steel surface
Embossing pattern；
(2-3) is heat-treated die steel, promotes the hardness of die steel, so that die steel hardness reaches certain
60 degree of Rockwell hardness；
(2-4) handles the surface effect of mold according to the default of product；
(2-5) assembling.
The surface effect of step (2-4) includes carving pattern level, bright sand effect, fantasy coloured effect or coining micro text.
By silver-colored green body pressure rolling be preset thickness by pressure rolling process, and cut into the sheet material of required moulding, moulding according to
Depending on product, tailors size principal security product grammes per square metre and control reduces production capacity waste, for the present embodiment, preset thickness range
For the strip sheet material of 0.15mm, die pressing is that sheet material is cut into the equidistant sheet material of type；
Step 2, oil pressure: the silver strip material cut being put into the oil pressure cavity body of mould prepared and be cold-pressed drum, pressure
Product surface decorative pattern processed, 3000 tons of pressure, to ensure that product pattern precision, compacted products surface detail includes that coining is miniature
Text.
The two halves product suppressed is welded, holds mould and/or sandblasting press polish processing by step 3；
Step 4, electroforming process: the product that will be welded adheres to one in product surface by the firmly golden electroforming process of no cyanogen
The hard gold layer of layer silver, electroformed layer is with a thickness of 0.1mm；
Step 5, postprocessing working procedures: obtaining finished product after post treatment, postprocessing working procedures include according to product design drawing into
Row, carries out surface effect product defective to hold mould and/or sandblasting calendered surface effect process, and carry out quality inspection.
Lock job contract art products made of the firmly golden compound manufacture process of the oil pressure of three above embodiment and electroforming include:
The two halves product suppressed, the thickness range of two halves product are 0.01mm-0.5mm, used in two halves product
Die pressing includes the rectangular of unilateral 10mm-30mm bigger than product or with the equidistant sheet material of type, and two halves product surface decorative pattern includes floating
Carve pattern level, bright sand effect, fantasy coloured effect or coining micro text；
Welding layer, together by two halves Product jointing；And
Noble metal hard gold layer, is attached to the two halves product surface, and noble metal hard gold layer is the hard gold layer of gold or silver.
Three above embodiment is hollow products, related technique be after being welded after product point half oil pressure again
Electroforming is firmly golden, and certainly, those skilled in the art can also need to make solid product according to the ornaments of actual design, in this way, institute
The process being related to directly carries out electroforming processing after the completion of punching press, the technique such as welds without carrying out.
The fineness of the handicraft decorative pattern is high, and the hardness of product, wearability and oxidation resistance are strong, without in routine
Hard gold class product surface punching, product is completely beautiful, improves the quality of compound hard golden product, and simultaneous processing cost is controlled,
Antenatal consumption is reduced, is reduced costs while improving yield, the more conducively market of the compound ornaments of noble metal and craftwork pushes away
Extensively.
Described above is only the preferred embodiment of the utility model, and above-mentioned specific embodiment is not to the utility model
Limitation.In the technical idea scope of the utility model, various modifications and modification, the ordinary skill of all this fields can occur
Retouching, modification or the equivalent replacement that personnel are made as described above belong to the range that the utility model is protected.
Claims (6)
1. the firmly golden combination process product of a kind of oil pressure and electroforming, it is characterised in that the handicraft includes:
The two halves product or physical product suppressed；And
Noble metal hard gold layer is attached to the two halves product surface or the physical product surface.
2. the firmly golden combination process product of a kind of oil pressure according to claim 1 and electroforming, it is characterised in that further include: welding
Layer, together by the two halves Product jointing.
3. the firmly golden combination process product of a kind of oil pressure according to claim 1 and electroforming, it is characterised in that: the two halves produce
The thickness range of product is 0.01mm-0.5mm.
4. the firmly golden combination process product of a kind of oil pressure according to claim 1 and electroforming, it is characterised in that: the two halves produce
Die pressing used in product includes the rectangular of unilateral 10mm-30mm bigger than product or with the equidistant sheet material of type.
5. the firmly golden combination process product of a kind of oil pressure according to claim 1 and electroforming, it is characterised in that: the two halves produce
Product surface detail includes impression level, bright sand effect, fantasy coloured effect or coining micro text.
6. the firmly golden combination process product of a kind of oil pressure according to claim 1 and electroforming, it is characterised in that: the noble metal
Hard gold layer is the hard gold layer of gold or silver.