CN208515117U - A kind of BOPP cigarette film structure for taking into account glossiness performance and anti-blocking properties - Google Patents
A kind of BOPP cigarette film structure for taking into account glossiness performance and anti-blocking properties Download PDFInfo
- Publication number
- CN208515117U CN208515117U CN201820369138.2U CN201820369138U CN208515117U CN 208515117 U CN208515117 U CN 208515117U CN 201820369138 U CN201820369138 U CN 201820369138U CN 208515117 U CN208515117 U CN 208515117U
- Authority
- CN
- China
- Prior art keywords
- layer
- blocking
- account
- taking
- film structure
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model provides a kind of BOPP cigarette film structure for taking into account glossiness performance and anti-blocking properties, including upper resist blocking and that layer, upper photic zone, lustre adding layer, upper hot sealing layer, middle layer, lower antistatic layer, lower hot sealing layer and lower resist blocking and that layer, each layer is set gradually from top to bottom, upper resist blocking and that layer surface is attached with antifoggant, the upper photic zone is polyethylene terephthalate layer, the lustre adding layer is nano zine oxide, and the upper resist blocking and that layer and lower resist blocking and that layer are polymethacrylates layer.In the utility model, resist blocking and that layer, the material of photic zone and lustre adding layer, size cooperate, and make glossiness, mist degree close to traditional structure, and resistance to blocking can be improved, and be a kind of new thin film structure for taking into account two kinds of performances.
Description
Technical field
The utility model belongs to BOPP cigarette film structure technical field of improvement, especially one kind and takes into account glossiness performance and anti-sticking
The even BOPP cigarette film structure of performance.
Background technique
A kind of important application of BOPP film is the packaging for cigarette, i.e. BOPP cigarette film, is widely used in small
In the packaging of packet and item packet.Traditional BOPP cigarette film passes through three-layer co-extruded technique and biaxial tension system by a variety of polypropylene functional materials
At having certain barriers function to smell and moisture, the cigarette film performance of the type includes resistance to blocking energy, antistatic property and light
Learn performance, wherein resistance to blocking can and optical property mutually restrict, i.e., resistance to blocking energy difference be because BOPP cigarette film surface excessively
Smooth, BOPP cigarette film surface is formed caused by vacuum, and be added after anti-adhesive substances the optical property of BOPP cigarette film can be caused compared with
Big negative effect, and traditional BOPP cigarette film has preferable optical property, but resistance to blocking can be poor, so tradition BOPP
Cigarette film can no longer meet higher and higher performance requirement, be badly in need of the novel B OPP of a kind of firm resistance to blocking energy and optical property
Cigarette film.
Utility model content
The purpose of the utility model is to overcome the deficiencies in the prior art, provide it is structurally reasonable, by resist blocking and that layer, light transmission
The common cooperation of layer and lustre adding layer to improve simultaneously resistance to blocking can and one kind of optical property take into account glossiness performance and anti-sticking
The even BOPP cigarette film structure of performance.
The technical scheme adopted by the utility model is that:
A kind of BOPP cigarette film structure for taking into account glossiness performance and anti-blocking properties, it is characterised in that: including upper resist blocking and that
Layer, upper photic zone, lustre adding layer, upper hot sealing layer, middle layer, lower antistatic layer, lower hot sealing layer and lower resist blocking and that layer, each layer from up to
Under set gradually, upper resist blocking and that layer surface is attached with antifoggant, and the upper photic zone is polyethylene terephthalate layer, institute
Stating lustre adding layer is nano zine oxide, and the upper resist blocking and that layer and lower resist blocking and that layer are polymethacrylates layer.
Further, the upper hot sealing layer is linear low density polyethylene layer, and the lower hot sealing layer is total for polypropylene random
Polymers layer, the middle layer are homopolypropylene layer, and the antistatic layer is polyether ester amides layer.
Further, the upper photic zone and lustre adding layer with a thickness of 1~1.5 micron.
Further, the upper resist blocking and that layer and lower resist blocking and that layer with a thickness of 0.05~0.08 micron.
Further, the upper hot sealing layer and lower hot sealing layer with a thickness of 1.2~1.5 microns.
Further, the base with a thickness of 10~15 microns.
Further, the antistatic layer with a thickness of 0.3~0.6 micron.
The advantages and positive effects of the utility model are as follows:
In the utility model, upper hot sealing layer is linear low density polyethylene layer, and lower hot sealing layer is polypropylene random copolymer
Layer, middle layer are homopolypropylene layer, and antistatic layer is polyether ester amides layer, four-layer structure are formed through coextrusion process, in upper heat
Sealing surface coats lustre adding layer, in the layer surface coating upper photic zone that adds lustre to, distinguishes on upper photic zone surface and lower heat-sealing layer surface
Painting is covered with resist blocking and that layer and lower resist blocking and that layer, and resist blocking and that layer, the material of photic zone and lustre adding layer, size cooperate, and makes gloss
Degree, mist degree are close to traditional structure, and resistance to blocking can be improved, and be a kind of novel thin film knot for taking into account two kinds of performances
Structure.
Detailed description of the invention
Fig. 1 is the structure chart of the utility model.
Specific embodiment
Below with reference to embodiment, the present invention will be further described, and it is not limited that following embodiments, which are illustrative,
, the protection scope of the utility model cannot be limited with following embodiments.
A kind of BOPP cigarette film structure for taking into account glossiness performance and anti-blocking properties, as shown in Figure 1, the wound of the utility model
Newly it is: including upper resist blocking and that layer 1, upper photic zone 2, lustre adding layer 3, upper hot sealing layer 4, middle layer 5, lower antistatic layer 8, lower heat-sealing
Layer 7 and lower resist blocking and that layer 6, each layer is set gradually from top to bottom, and upper resist blocking and that layer surface is attached with antifoggant, the upper photic zone
For polyethylene terephthalate layer, the lustre adding layer is nano zine oxide, and the upper resist blocking and that layer and lower resist blocking and that layer are equal
For polymethacrylates layer.
In the present embodiment, upper hot sealing layer is linear low density polyethylene layer, and lower hot sealing layer is polypropylene random copolymer layer,
Middle layer is homopolypropylene layer, and antistatic layer is polyether ester amides layer.
Preferred scheme is: upper photic zone and lustre adding layer with a thickness of 1~1.5 micron.Upper resist blocking and that layer is anti-stick under
Even layer with a thickness of 0.05~0.08 micron.Upper hot sealing layer and lower hot sealing layer with a thickness of 1.2~1.5 microns.The thickness of base
It is 10~15 microns.Antistatic layer with a thickness of 0.3~0.6 micron.
Performance test results are as follows:
Tensile strength: longitudinal 130 megapascal, lateral 240 megapascal
Percent thermal shrinkage: longitudinal 4%, lateral 3%
Friction factor (dynamic): 0.3
Mist degree: 1.1%
Glossiness: 91%
In the utility model, upper hot sealing layer is linear low density polyethylene layer, and lower hot sealing layer is polypropylene random copolymer
Layer, middle layer are homopolypropylene layer, and antistatic layer is polyether ester amides layer, four-layer structure are formed through coextrusion process, in upper heat
Sealing surface coats lustre adding layer, in the layer surface coating upper photic zone that adds lustre to, distinguishes on upper photic zone surface and lower heat-sealing layer surface
Painting is covered with resist blocking and that layer and lower resist blocking and that layer, and resist blocking and that layer, the material of photic zone and lustre adding layer, size cooperate, and makes gloss
Degree, mist degree are close to traditional structure, and resistance to blocking can be improved, and be a kind of novel thin film knot for taking into account two kinds of performances
Structure.
Claims (7)
1. a kind of BOPP cigarette film structure for taking into account glossiness performance and anti-blocking properties, it is characterised in that: including upper resist blocking and that layer,
Upper photic zone, lustre adding layer, upper hot sealing layer, middle layer, lower antistatic layer, lower hot sealing layer and lower resist blocking and that layer, each layer is from top to bottom
It sets gradually, upper resist blocking and that layer surface is attached with antifoggant, and the upper photic zone is polyethylene terephthalate layer, described
Lustre adding layer is nano zine oxide, and the upper resist blocking and that layer and lower resist blocking and that layer are polymethacrylates layer.
2. a kind of BOPP cigarette film structure for taking into account glossiness performance and anti-blocking properties according to claim 1, feature
Be: the upper hot sealing layer be linear low density polyethylene layer, the lower hot sealing layer be polypropylene random copolymer layer, it is described in
Interbed is homopolypropylene layer, and the antistatic layer is polyether ester amides layer.
3. a kind of BOPP cigarette film structure for taking into account glossiness performance and anti-blocking properties according to claim 1, feature
Be: the upper photic zone and lustre adding layer with a thickness of 1~1.5 micron.
4. a kind of BOPP cigarette film structure for taking into account glossiness performance and anti-blocking properties according to claim 1 or 2 or 3,
It is characterized by: the upper resist blocking and that layer and lower resist blocking and that layer with a thickness of 0.05~0.08 micron.
5. a kind of BOPP cigarette film structure for taking into account glossiness performance and anti-blocking properties according to claim 4, feature
Be: the upper hot sealing layer and lower hot sealing layer with a thickness of 1.2~1.5 microns.
6. a kind of BOPP cigarette film structure for taking into account glossiness performance and anti-blocking properties according to claim 5, feature
Be: the middle layer with a thickness of 10~15 microns.
7. a kind of BOPP cigarette film structure for taking into account glossiness performance and anti-blocking properties according to claim 6, feature
Be: the antistatic layer with a thickness of 0.3~0.6 micron.