CN208437657U - A kind of kiln road formula foamed aluminium tinuous production - Google Patents
A kind of kiln road formula foamed aluminium tinuous production Download PDFInfo
- Publication number
- CN208437657U CN208437657U CN201821181054.2U CN201821181054U CN208437657U CN 208437657 U CN208437657 U CN 208437657U CN 201821181054 U CN201821181054 U CN 201821181054U CN 208437657 U CN208437657 U CN 208437657U
- Authority
- CN
- China
- Prior art keywords
- furnace
- kiln road
- foamed aluminium
- aluminum water
- external
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model discloses a kind of kiln road formula foamed aluminium tinuous productions, belong to foamed aluminium production equipment technology, including aluminium melting furnace, multipurpose furnace, kiln road die preheating furnace, reaction foaming furnace, cooling bay, trolley, foamed aluminium production mould, trolley circular flow track returns to kiln road die preheating furnace after sequentially passing through kiln road die preheating furnace, reaction foaming furnace and cooling bay;There are two multipurpose furnaces, two multipurpose furnaces are connect with aluminium melting furnace respectively, the outlet upper end of kiln road die preheating furnace is equipped with aluminum water sprue gate, the mobile casting ladle that aluminum water in two multipurpose furnaces can be poured into aluminum water sprue gate respectively is installed, mobile casting ladle is equipped with weighing device above kiln road die preheating furnace.Utility model can successively supply aluminum water and preheated mold, and aluminum water transhipment Distance Shortened reduces the temperature leak in aluminum water transport process to 3 meters, and then can reduce aluminum water temperature in aluminium melting furnace, reduce consumption;Production capacity is improved simultaneously, is reduced costs.
Description
Technical field
The utility model belongs to foamed aluminium production equipment technology, and in particular to a kind of kiln road formula foamed aluminium continuous production
Line.
Background technique
Foamed aluminium be after adding additives to pure aluminum or aluminum alloys, to be formed by foam process, at the same have concurrently metal and
Bubble feature.Its density is small, high-selenium corn impact capacity is strong, high temperature resistant, fire protecting performance are strong, anticorrosive, sound insulation and noise reduction, thermal conductivity
It is low, electromagnetic wave shielding is high, weatherability is strong, have filter capacity, easy processing, easy to install, forming accuracy is high, can carry out external coating.
Aluminum foam product has applied to military products component and protection, aviation tooling, core weary material transhipment protection, motor-car, bridge protect,
Gobo, decorative engineering etc..
However the super large-scale size bubbles aluminium of existing foam aluminium manufacturer production is the casting solution foaming czochralski method used
It is interrupted production technology, which has the disadvantage that
1. each mold will be preheated independently, 2.5 hours time-consuming, it is unable to continuous production.
2. aluminum water transhipment distance reaches 15 meters, therefore aluminum water transports to the temperature that foaming furnace can be lost 120 DEG C or so, causes to melt
Aluminum water, which will burn 850 DEG C or more, in aluminium furnace just can guarantee technique requirement, and aluminum water temperature losses are big, cause energy consumption height.
3. productive temp wants that a billet (billet goes out 52 squares of foamed aluminium boards) could be produced within 3.5 hours, therefore
A production line can only also produce 7 billets, that is, 360 squares or so of foamed aluminium board within 24 hours, and production capacity is low, is produced into
This height.
Utility model content
In order to solve the above problems existing in the present technology, the utility model aim is to provide a kind of kiln road formula foamed aluminium
Tinuous production.
The technology employed by the present utility model is
A kind of kiln road formula foamed aluminium tinuous production, including aluminium melting furnace, multipurpose furnace, kiln road die preheating furnace, reaction foaming
Furnace, cooling bay, trolley, foamed aluminium production mould and trolley circular flow track, the trolley circular flow track sequentially pass through
Kiln road die preheating furnace is returned to by cyclic track after kiln road die preheating furnace, reaction foaming furnace and cooling bay;The multipurpose furnace
There are two, two multipurpose furnaces are connect with aluminium melting furnace respectively, and the outlet upper end of kiln road die preheating furnace is equipped with aluminum water sprue gate,
The movable type that aluminum water in two multipurpose furnaces can be poured into aluminum water sprue gate respectively is installed above kiln road die preheating furnace
Casting ladle, the movable type casting ladle are equipped with weighing device;The trolley has more, and more trolleys are successively in trolley circular flow track
Operation, every trolley place a set of foamed aluminium production mould.
Multipurpose furnace can not only make aluminum water holding furnace, can also complete aluminum water alloying.
Preferably, agitating paddle lifting movable stand, the agitating paddle lifting movement are installed at the top of the reaction foaming furnace
It is equipped on frame and is equipped with motor connection agitating paddle and the lifting rotatable T-shaped hook of internal model.
Preferably, the top of the foaming furnace is equipped with the slidingtype roof door protruded into for agitating paddle;The preheating of kiln road mold
The inlet and outlet of furnace and the inlet and outlet for reacting foaming furnace are separately installed with overhead door.
Further, there are three the cooling bays, three cooling bays pass through transfer car(buggy) and trolley circular flow track respectively
Connection;Three cooling bays are interconnected.
Further, the bottom of the cooling bay is equipped with cooling water dish, and cooling bay is equipped with for going up and down foamed aluminium production
The lifting device of mold.
Preferably, the foamed aluminium production mould includes bottom plate, internal model and external mould frame;The internal model is upper and lower side perforation
Tubular, the internal model seal groove being adapted to internal model lower end is offered in the middle part of the plate upper surface, and the internal model is close by internal model
Sealing groove is detachably connected with bottom plate;Under connection status, the aluminum water mixing chamber of upper end opening is collectively formed with bottom plate for internal model;It is described outer
Framed includes at least two blocks of exterior sheathings, and the exterior sheathing is vertically arranged, is assembled into upper and lower side by connector between exterior sheathing and passes through
Logical external mould frame;The edge of the plate upper surface has the external mold seal groove being adapted to the lower end of external mould frame, the external mold
Frame is detachably connected by external mold seal groove with bottom plate;Under connection status, the aluminium of upper end opening is collectively formed with bottom plate for external mould frame
Water sizing chamber.
Preferably, the left and right ends of the exterior sheathing are respectively equipped with lateral keyhole, the connector include lock plunger and
Inclined-plane locking pin, the rear end of the lock plunger connect limited block, the front of lock plunger offer be adapted to inclined-plane locking pin it is oblique
Face;Under connection status, the front of the lock plunger passes through the keyhole of two neighboring exterior sheathing, and the inclined-plane locking pin insertion is oblique
In face, thus two exterior sheathings of locking.
Preferably, the exterior sheathing includes external mold long slab and external mold short slab, and the external mold long slab and external mold short slab have respectively
Two pieces, two pieces of external mold long slabs and the assembled rectangular external mould frame of two pieces of external mold short slabs;The left and right ends of the external mold short slab point
She You be vertical it is convex stupefied, the medial surface of the external mold long slab is equipped with and the convex stupefied sealing card slot being adapted to.
Further, suspending hook is respectively equipped at the top of the external mold long slab and external mold short slab.
Further, the edge of the bottom plate has suspending hook hole, and the suspending hook hole is located at external mold seal groove
Outside.
Preferably, the outer wall top of the internal model is equipped with Lift hook.
Preferably, the upper end of the internal model, which is equipped with, promotes hangers.
Further, the lower end of the internal model is equipped with the tenon being adapted to internal model seal groove;The lower end of the external mould frame is set
There is the tenon being adapted to external mold seal groove.
The utility model has the following beneficial effects:
The utility model can successively supply aluminum water and preheated mold, and aluminum water is transported Distance Shortened to 3 meters, reduced
Temperature leak in aluminum water transport process, and then can reduce aluminum water temperature in aluminium melting furnace, reduce consumption.
The utility model can be realized continous way production, and productive temp 40 divides a billet, is able to produce 36 within every 24 hours
A billet, that is, 1872 squares of foamed aluminium board, improve production capacity, reduce costs.
Detailed description of the invention
Fig. 1 is the structural schematic diagram of the utility model kiln road formula foamed aluminium tinuous production.
Fig. 2 is the structural schematic diagram of foamed aluminium production mould.
Fig. 3 is the explosive view of Fig. 2.
Fig. 4 is the structural schematic diagram of connector.
Fig. 5 is the structural schematic diagram that lifting rotates T-shaped hook.
In figure: 1- aluminium melting furnace;2- multipurpose furnace;3- kiln road die preheating furnace;4- reacts foaming furnace;5- cooling bay;6- trolley;
7- foamed aluminium production mould;8- trolley circular flow track;9- movable type casting ladle;10- overhead door;31- aluminum water sprue gate;41-
Agitating paddle lifts movable stand;42- agitating paddle;43- slidingtype roof door;44- lifting rotates T-shaped hook;51- cools down water dish;
52- lifting device;100- bottom plate;101- internal model seal groove;102- external mold seal groove;103- suspending hook hole;200- internal model;
201- Lift hook;202- promotes hangers;300- external mould frame;310- exterior sheathing;311- keyhole;312- external mold long slab;313- external mold
Short slab;314- is convex stupefied;315- seals card slot;316- suspending hook;320- connector;321- lock plunger;The inclined-plane 322- locking pin;
323- limited block;324- beveled aperture.
Specific embodiment
With reference to the accompanying drawing and specific embodiment is further elaborated the utility model.
As shown in Figure 1, a kind of kiln road formula foamed aluminium tinuous production of the present embodiment, including aluminium melting furnace 1, multipurpose furnace 2, kiln
Road die preheating furnace 3, reaction foaming furnace 4, cooling bay 5, trolley 6, foamed aluminium production mould 7 and trolley circular flow track 8, platform
Vehicle circular flow track 8 returns to the preheating of kiln road mold after sequentially passing through kiln road die preheating furnace 3, reaction foaming furnace 4 and cooling bay 5
Furnace 3;There are two multipurpose furnaces 2, and two multipurpose furnaces 2 are connect with aluminium melting furnace 1 by aluminum water transfer slide respectively, kiln road die preheating furnace
3 outlet upper end is equipped with aluminum water sprue gate 31, and the top of kiln road die preheating furnace 3 is equipped with can be respectively by two multipurpose furnaces 2
Interior aluminum water pours into the mobile casting ladle 9 at aluminum water sprue gate 31, and mobile casting ladle 9 is equipped with weighing device, and mobile casting ladle 9 passes through
Aluminum water is poured into aluminum water sprue gate 31 by aluminum water chute, and aluminum water transfer slide is no more than 4 meters plus the total length of aluminum water chute;Trolley
6 have more, and more trolleys 6 are successively run in trolley circular flow track 8, and every trolley 6 places a set of foamed aluminium production mould
7。
This production line include an aluminium melting furnace 1 and two multipurpose furnaces 2 (aluminum water holding furnace can also be made according to process requirements), two
A multipurpose furnace 2 is in turn using can guarantee continual offer aluminum water.5 foamed aluminiums can be once put into kiln road die preheating furnace 3
Production mould 7 preheats simultaneously, it is ensured that the continual preheating foamed aluminium production mould 7 for providing up requirement.Trolley circulation fortune
Row track 8, which forms circulation loop, can uninterruptedly produce foamed aluminium.
Process flow prepares: aluminium melting furnace 1 melts aluminum water to the foamed aluminium production in 800 DEG C or so, kiln road die preheating furnace 3
Mold 7 is preheating to 670 DEG C or so simultaneously.Aluminum water melt it is good after put aluminum water to two multipurpose furnaces 2, aluminium melting furnace 1 be supplemented aluminium ingot after
Continuous fusing is stand-by.Multipurpose furnace 2 plus alloying component and additive make aluminum water viscosity reach technique requirement, and two multipurpose furnace 2 one make
Spare with one, two multipurpose furnaces 2 are used alternatingly certifiable production line thickening aluminum water (or aluminum water) and can successively supply.
Start process: mobile casting ladle 9 connects aluminum water Weighing from multipurpose furnace 2, and the mobile rotation of casting ladle 9 passes through chute
It pours into aluminum water sprue gate 31 and introduces foamed aluminium production mould 7 preheated in kiln road die preheating furnace 3, connect aluminum water and be loaded with foam
The trolley 6 of aluminium production mould 7 is run in reaction foaming furnace 4.When the trolley 6 of front is run in reaction foaming furnace 4, kiln road mould
Remaining 4 trolleys 6 for being loaded with foamed aluminium production mould 7 while mobile cover in tool preheating furnace 3, and kiln road die preheating furnace
Trolley 6 outside 3 starts to preheat into kiln road die preheating furnace 3, and the foamed aluminium production mould 7 on second trolley 6 starts to connect aluminium
Water.Foams held for some time terminates to foam in reaction foaming furnace 4, and the trolley 6 for being loaded with foaming body runs to cooling bay 5, and one
It fixes time mold removal, before trolley 6 returns to kiln road die preheating furnace 3, first process terminates, and is recycled with this and reaches continuous life
It produces.
Lifting stirring is carried out for convenience, and the top of reaction foaming furnace 4 is equipped with agitating paddle lifting movable stand 41, agitating paddle
The agitating paddle 42 for being equipped with motor and lifting rotation T-shaped hook 44 are installed on lifting movable stand 41.Foamed aluminium equipped with aluminum water
Production mould 7 enters, and after reacting foaming furnace 4, agitating paddle lifting movable stand 41, which is moved at furnace roof, falls agitating paddle 42, and hair is added
Infusion stirs 4-6 minutes, then removes agitating paddle 42.
In order to reduce scattering and disappearing for temperature, the top of foaming furnace 4 is equipped with the slidingtype roof door 43 protruded into for agitating paddle 42;Kiln road
The inlet and outlet of die preheating furnace 3 and the inlet and outlet for reacting foaming furnace 4 are separately installed with overhead door 10, can be effective
Reduce the loss of heat.
In order to improve the production efficiency, there are three cooling bays 5, three cooling bays 5 are transported by transfer car(buggy) and trolley circulation respectively
Row track 8 connects;Three cooling bays 5 are interconnected.Three cooling positions can orderly be staggered cooling by productive temp, the company of can be improved
The cooling efficiency of continuous production.There are two broken rails above trolley or so transfer car(buggy), transfer car(buggy) makes of being mainly: 1, having foamed
Foamed aluminium is transferred to each cooling zone.2, the trolley 6 withdrawn is transported to the right and passes through broken rail and the trolley to go back circulation fortune
Row track 8 is connected, and so that trolley 6 is returned to initial position and is achieved the purpose that recycling.
Specifically, the bottom of cooling bay 5 is equipped with cooling water dish 51, cooling bay 5 is equipped with for going up and down foamed aluminium production mould
The lifting device 52 of tool 7.Lifting mold withdraws convenient for trolley 6 and returns to initial bit by trolley circular flow track 8 and reach platform
The purpose that vehicle is recycled.
As shown in Figures 2 and 3, in order to improve the service life of mold, foamed aluminium production mould 7 includes bottom plate 100, internal model
200 and external mould frame 300;Internal model 200 is the tubular of upper and lower side perforation, offer in the middle part of 100 upper surface of bottom plate under internal model 200
The internal model seal groove 101 of adaptation is held, internal model 200 is detachably connected by internal model seal groove 101 with bottom plate 100;Under connection status,
The aluminum water mixing chamber of upper end opening is collectively formed in internal model 200 and bottom plate 100;External mould frame 300 includes at least two blocks of exterior sheathings 310,
Exterior sheathing 310 is vertically arranged, is assembled into the external mould frame 300 of upper and lower side perforation between exterior sheathing 310 by connector 320;Bottom plate
The edge of 100 upper surfaces has the external mold seal groove 102 being adapted to the lower end of external mould frame 300, and external mould frame 300 is close by external mold
Sealing groove 102 is detachably connected with bottom plate 100;Under connection status, the aluminium of upper end opening is collectively formed with bottom plate 100 for external mould frame 300
Water sizing chamber.
The assemble sequence of foamed aluminium production mould 7: 1, first, in accordance with the position of external mold seal groove 102 exterior sheathing 310 is set
It, then will be each using connector 320 in the upper surface (lower end of exterior sheathing 310 will be caught in external mold seal groove 102) of bottom plate 100
The connection of a exterior sheathing 310 forms external mould frame 300, and it is spare that external mould frame 300 then hung bottom plate 100 again;2, on bottom plate 100
The sealing material for having viscosity mixed up is spread in internal model seal groove 101 and external mold seal groove 102, layer overlay high temperature cotton is then covered with
And then one layer of sealing material for having viscosity is first placed on the alignment of internal model 200 on internal model seal groove 101;3, then again external mould frame
It 300 slings and is put on external mold seal groove 102 (interior external mold sealing material and operation be the same);4, hammer strikes 200 and of internal model downwards
External mould frame 300 makes itself and 100 compression seal of bottom plate, and mold is completed.
After mold is preheating to the temperature of requirement, access aluminum water is moved in foaming furnace, corresponding foaming agent is added to interior
In the aluminum water mixing chamber for the upper end opening that mould 200 and bottom plate 100 are collectively formed, agitating device is protruded into, is mixed in aluminum water mixing chamber
It closes.Since the cross section of internal model 200 is relatively small, the liquid level of aluminum water is relatively higher, is conducive to mixing dispersion.Mix aluminum water
Afterwards, internal model 200 is taken out from top, aluminum water flows into the aluminum water foam chamber for the upper end opening that external mould frame 300 and bottom plate 100 are collectively formed
It is interior, it is kept the temperature and is foamed.
After to be foamed, unitary mould is moved to cooling zone, carries out water-spraying control, cooling knot from 100 lower surface of bottom plate
Shu Houyi to demoulding area.Then exterior sheathing 310 is removed, it is stand-by finally to clear up mold.
As shown in figure 4, connector 320 wraps specifically, the left and right ends of exterior sheathing 310 are respectively equipped with lateral keyhole 311
Lock plunger 321 and inclined-plane locking pin 322 are included, the rear end of lock plunger 321 connects limited block 323, and the front of lock plunger 321 offers
The beveled aperture 324 being adapted to inclined-plane locking pin 322;Under connection status, the front of lock plunger 321 passes through two neighboring exterior sheathing
310 keyhole 311, inclined-plane locking pin 322 is inserted into beveled aperture 324, to lock two adjacent exterior sheathings 310.Connector
320 use the form of lock plunger 321 and inclined-plane locking pin 322, can not only effectively lock two adjacent exterior sheathings 310
Tightly, and it is easy to operate, only need one hammer can be completed the operation locked and dismantled.
In order to improve leakproofness, exterior sheathing 310 includes external mold long slab 312 and external mold short slab 313, external mold long slab 312 and outer
Mould short slab 313 has two pieces respectively, two pieces of external mold long slabs 312 and the assembled rectangular external mould frame 300 of two pieces of external mold short slabs 313;Outside
The left and right ends of mould short slab 313 is respectively equipped with vertical convex stupefied 314, and the medial surface of external mold long slab 312 is equipped with fits with convex stupefied 314
The sealing card slot 315 matched, after assembled, convex stupefied 314 are caught in sealing card slot 315, can be guaranteed the leakproofness of aluminum water sizing chamber, be kept away
Exempt from aluminum water leakage.
In order to facilitate assembled operation, the top of external mold long slab 312 and external mold short slab 313 is respectively equipped with suspending hook 316.
In order to facilitate movement, the edge of bottom plate 100 has suspending hook hole 103, and it is close that suspending hook hole 103 is located at external mold
The outside of sealing groove 102.
In order to facilitate the assembly and removal of internal model 200, the outer wall top of internal model 200 is equipped with Lift hook 201.
As shown in figure 5, lifting internal model 200 after stirring for convenience, the upper end of internal model 200 is equipped with lifting hangers 202,
The T-shaped hook 44 of rotary pulling rotation tangles lifting hangers 202 after stirring, can guarantee agitating device and internal model 200 1
It rises and is lifted off bottom plate 100, (the T-shaped hook 44 of lifting rotation and agitating device synchronization lifting).
In order to further increase leakproofness, the lower end of internal model 200 is equipped with the tenon being adapted to internal model seal groove 101;External mold
The lower end of frame 300 is equipped with the tenon being adapted to external mold seal groove 102.
The utility model is not limited to above-mentioned optional embodiment, anyone can obtain under the enlightenment of the utility model
Other various forms of products, however, making any variation in its shape or structure, all the utility model rights that falls into are wanted
The technical solution in confining spectrum is sought, is all fallen within the protection scope of the utility model.
Claims (9)
1. a kind of kiln road formula foamed aluminium tinuous production, it is characterised in that: including aluminium melting furnace (1), multipurpose furnace (2), kiln road mold
Preheating furnace (3), reaction foaming furnace (4), cooling bay (5), trolley (6), foamed aluminium production mould (7) and trolley circular flow track
(8), the trolley circular flow track (8) sequentially passes through kiln road die preheating furnace (3), reaction foaming furnace (4) and cooling bay (5)
After return to kiln road die preheating furnace (3);There are two the multipurpose furnaces (2), and two multipurpose furnaces (2) connect with aluminium melting furnace (1) respectively,
The outlet upper end of kiln road die preheating furnace (3) is equipped with aluminum water sprue gate (31), and the top of kiln road die preheating furnace (3) is installed
There are the mobile casting ladle (9) that the aluminum water in two multipurpose furnaces (2) can be poured into aluminum water sprue gate (31) respectively, the movable type
Casting ladle (9) is equipped with weighing device;The trolley (6) has more, and more trolleys (6) are successively transported in trolley circular flow track (8)
Row, every trolley (6) place a set of foamed aluminium production mould (7).
2. a kind of kiln road formula foamed aluminium tinuous production according to claim 1, it is characterised in that: the reaction foaming furnace
(4) agitating paddle lifting movable stand (41) is installed at the top of, outfit motor is installed on agitating paddle lifting movable stand (41)
Agitating paddle (42) and lifting rotate T-shaped hook (44).
3. a kind of kiln road formula foamed aluminium tinuous production according to claim 2, it is characterised in that: the foaming furnace (4)
Top be equipped with the slidingtype roof door (43) that protrudes into for agitating paddle (42);The inlet and outlet of kiln road die preheating furnace (3)
And the inlet and outlet of reaction foaming furnace (4) is separately installed with overhead door (10).
4. a kind of kiln road formula foamed aluminium tinuous production according to claim 1, it is characterised in that: the cooling bay (5)
There are three, three cooling bays (5) are connect by transfer car(buggy) with trolley circular flow track (8) respectively;Three cooling bays (5) are mutual
Connection.
5. a kind of kiln road formula foamed aluminium tinuous production according to claim 4, it is characterised in that: the cooling bay (5)
Bottom be equipped with cooling water dish (51), cooling bay (5) is equipped with the lifting device for going up and down foamed aluminium production mould (7)
(52)。
6. a kind of kiln road formula foamed aluminium tinuous production described in -5 any one according to claim 1, it is characterised in that: described
Foamed aluminium production mould (7) includes bottom plate (100), internal model (200) and external mould frame (300);
The internal model (200) is the tubular of upper and lower side perforation, is offered in the middle part of bottom plate (100) upper surface and internal model
(200) the internal model seal groove (101) of lower end adaptation, the internal model (200) can by internal model seal groove (101) and bottom plate (100)
Dismantling connection;Under connection status, the aluminum water mixing chamber of upper end opening is collectively formed with bottom plate (100) for internal model (200);
The external mould frame (300) includes at least two pieces of exterior sheathings (310), and the exterior sheathing (310) is vertically arranged, exterior sheathing
(310) external mould frame (300) of upper and lower side perforation is assembled between by connector (320);The side of bottom plate (100) upper surface
Edge offers the external mold seal groove (102) being adapted to the lower end of external mould frame (300), and the external mould frame (300) is sealed by external mold
Slot (102) is detachably connected with bottom plate (100);Under connection status, external mould frame (300) is collectively formed upper end with bottom plate (100) and opens
The aluminum water sizing chamber of mouth.
7. a kind of kiln road formula foamed aluminium tinuous production according to claim 6, it is characterised in that: the exterior sheathing
(310) left and right ends are respectively equipped with lateral keyhole (311), and the connector (320) includes lock plunger (321) and bevel lock
The rear end of tight pin (322), the lock plunger (321) connects limited block (323), and the front of lock plunger (321) offers and inclined-plane
The beveled aperture (324) of locking pin (322) adaptation;Under connection status, the front of the lock plunger (321) passes through two neighboring external mold
The keyhole (311) of plate (310), the inclined-plane locking pin (322) are inserted into beveled aperture (324), thus two external molds of locking
Plate (310).
8. a kind of kiln road formula foamed aluminium tinuous production according to claim 7, it is characterised in that: the exterior sheathing
It (310) include external mold long slab (312) and external mold short slab (313), the external mold long slab (312) and external mold short slab (313) have respectively
Two pieces, two pieces of external mold long slabs (312) and the assembled rectangular external mould frame (300) of two pieces of external mold short slabs (313);The external mold short slab
(313) left and right ends is respectively equipped with vertical convex stupefied (314), the medial surface of the external mold long slab (312) be equipped with it is convex stupefied
(314) the sealing card slot (315) being adapted to.
9. a kind of kiln road formula foamed aluminium tinuous production according to claim 8, it is characterised in that: the internal model (200)
Lower end be equipped with the tenon that is adapted to internal model seal groove (101);The lower end of the external mould frame (300) is equipped with and external mold seal groove
(102) tenon being adapted to.