CN207594459U - Synthetic leather production release film - Google Patents
Synthetic leather production release film Download PDFInfo
- Publication number
- CN207594459U CN207594459U CN201721363625.XU CN201721363625U CN207594459U CN 207594459 U CN207594459 U CN 207594459U CN 201721363625 U CN201721363625 U CN 201721363625U CN 207594459 U CN207594459 U CN 207594459U
- Authority
- CN
- China
- Prior art keywords
- synthetic leather
- release film
- leather production
- layer
- production release
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model is related to a kind of synthetic leather production release film, which includes the PET film layer being cascading and embossed layer.The production of above-mentioned synthetic leather is good with release film heat resistance, is resistant to 140 155 DEG C in synthetic leather production process of high temperature, will not roll set, it is less brittle, be not easy to tear, color inhibition, 80 100 reuses can be born.
Description
Technical field
The utility model is related to synthetic leather production field, more particularly to a kind of synthetic leather production release film.
Background technology
Synthetic leather is because its beautiful changeable lines design is liked by consumers in general, the lines on existing synthetic leather surface
Formation need using release paper, the base material of usual release paper uses long fine base stock.The production of synthetic leather is because of its process costs side
The considerations of face, reuses release paper requirement 20-40 times, but includes being difficult to take off the defects of paper substrates, brittle, easily tears
It splits, not solvent resistant, poor flatness, easy xanthochromia etc., it is difficult to obtain technology solution.
Have currently on the market and prepare release film, but in synthetic leather production using PET film to be bonded CPP or PE, in order to
Reduce cost, speed of production substantially achieves 15-25m/min, even up to 35m/min generally than very fast.In order to coordinate synthesis
Remove from office surface rapid curing, between oven temperature can reach 140-155 DEG C, if using CPP or PE fitting PET come do release paper (because
The difference of its temperature tolerance and tension), surface band textured CPP or PE will necessarily be caused to be heat-shrinked, and then lines is caused to deform,
Increase the defect ware rate in synthetic leather technique.If the reduction of baking oven oven temperature is produced, it is made to cater to PET and CPP or PE
Temperature and tension, then can only greatly influence production efficiency speed control in 5-8m/min.
Therefore, the prior art could be improved.
Utility model content
Based on this, the purpose of this utility model is to provide a kind of synthetic leather production release film.
Specific technical solution is as follows:
A kind of synthetic leather production release film, including the PET film layer being cascading and embossed layer.
In wherein some embodiments, adhesive layer is additionally provided between the PET film layer and the embossed layer.
In wherein some embodiments, the embossed layer is UV cured layers.
In wherein some embodiments, the embossed layer has figure lines.
In wherein some embodiments, the thickness of the PET film layer is 100-200 μm.
In wherein some embodiments, the thickness of the embossed layer is 40-80 μm.
In wherein some embodiments, the thickness of the adhesive layer is 10-15 μm.
Above-mentioned synthetic leather production creatively uses PET film by the use of release film as ground, after UV resin solidifications
Form embossed layer.Above-mentioned synthetic leather production is good with release film heat resistance, is resistant in synthetic leather production process 140-155 DEG C
High temperature, will not roll set, it is less brittle, be not easy to tear, color inhibition, can bear 80-100 times reuse.Further, it is described
Adhesive layer (adhesion promoter cures) is also provided between PET film layer and the embossed layer, further enhances PET film
Bonding force between layer and embossed layer improves the peeling force of release film entirety.
Description of the drawings
Fig. 1 is the structure diagram of 1 synthetic leather production release film of embodiment;
Fig. 2 is the structure diagram of 2 synthetic leather production release film of embodiment.
Specific embodiment
For the ease of understanding the utility model, the utility model will be described more fully below.But this practicality
It is novel to realize in many different forms, however it is not limited to embodiment described herein.On the contrary, provide these implementations
The purpose of example is to make the more thorough and comprehensive of the understanding to the disclosure of the utility model.
Unless otherwise defined, all of technologies and scientific terms used here by the article is led with belonging to the technology of the utility model
The normally understood meaning of technical staff in domain is identical.It is only in the term used in the description of the utility model herein
The purpose of description specific embodiment, it is not intended that in limitation the utility model.Term as used herein "and/or" includes
The arbitrary and all combination of one or more relevant Listed Items.
Raw material is as follows used in the utility model embodiment:
PET film, UV resins, photosensitizer, levelling agent, adhesion promoter are commercially available to be bought.
Embodiment 1
With reference to figure 1, a kind of synthetic leather production release film of the present embodiment the, including (thickness of PET film 101 being cascading
Spend is 150 μm) and embossed layer 102 (thickness is 60 μm).
The raw material that the embossed layer includes following mass percent is prepared:
UV resins 70%
Levelling agent 20%
Photosensitizer 10%.
The preparation method of above-mentioned synthetic leather production release film, includes the following steps:
(1) PET film is obtained;
(2) embossing coating is prepared:By UV resins (UV epoxy acrylates), levelling agent (UV levelling agent SC-333/ levellings
Agent, Siloxane-Oxyalkylene Copolymers levelling agent) and photosensitizer be mixed, control viscosity be 500-800cps;In the adhesive layer
The upper coating embossing coating, it is in semi-cured state that the embossing coating is dried at 85-95 DEG C;
(3) composite material for obtaining step (2) carries out embossing operation (forming figure lines in embossed layer), control technique
Parameter is:Embossing pressure is 2.54g/cm2, rolling speed 15m/min, ultraviolet irradiation energy is 1200MT/m2To get described
Synthetic leather production release film.
Embodiment 2
With reference to figure 2, a kind of synthetic leather production release film of the present embodiment, including the PET film layer 101 being cascading
(thickness is 150 μm), adhesive layer 103 and embossed layer 102 (thickness is 80 μm).
The raw material that the embossed layer includes following mass percent is prepared:
UV resins 73%
Levelling agent 17%
Photosensitizer 10%.
The preparation method of above-mentioned synthetic leather production release film, includes the following steps:
(1) PET film is obtained;
(2) in coating adhesion promoter (titanate coupling agent) on the PET film, drying forms adhesive layer;
(3) embossing coating is prepared:By UV resins (UV urethane acrylates), levelling agent, (UV levelling agents SC-333/ flows
Flat agent) and photosensitizer be mixed, control viscosity be 500-800cps;In coating the embossing coating on the adhesive layer,
It is in semi-cured state that the embossing coating is dried at 85-95 DEG C;
(4) composite material for obtaining step (3) carries out embossing operation (forming figure lines in embossed layer), control technique
Parameter is:Embossing pressure is 2-3g/cm2, rolling speed 12-18m/min, ultraviolet irradiation energy is 1000-1400MT/m2, i.e.,
Obtain the synthetic leather production release film.
Performance test
Peeling force | Heat-resisting quantity | Reuse number | |
Embodiment 1 | 3kgf/25mm | 140℃ | 40 |
Embodiment 2 | 8kgf/25mm | 165℃ | 80 |
PET and PE meets release film | 2kgf/25mm | 120℃ | 25 |
Each technical characteristic of embodiment described above can be combined arbitrarily, to make description succinct, not to above-mentioned reality
It applies all possible combination of each technical characteristic in example to be all described, as long as however, the combination of these technical characteristics is not deposited
In contradiction, it is all considered to be the range of this specification record.
Embodiment described above only expresses the several embodiments of the utility model, and description is more specific and detailed,
But therefore it can not be interpreted as the limitation to utility model patent range.It should be pointed out that the common skill for this field
For art personnel, without departing from the concept of the premise utility, various modifications and improvements can be made, these are belonged to
The scope of protection of the utility model.Therefore, the protection domain of the utility model patent should be determined by the appended claims.
Claims (4)
1. a kind of synthetic leather production release film, which is characterized in that including the PET film layer being cascading and embossed layer;Institute
It states and is additionally provided with adhesive layer between PET film layer and the embossed layer;The embossed layer is UV cured layers;The embossed layer has figure
Lines.
2. synthetic leather production release film according to claim 1, which is characterized in that the thickness of the PET film layer is
100-200μm。
3. synthetic leather production release film according to claim 1, which is characterized in that the thickness of the embossed layer is 40-
80μm。
4. synthetic leather production release film according to claim 1, which is characterized in that the thickness of the adhesive layer is 10-
15μm。