CN207093578U - A kind of spherical joint bearing inner race of surface with hard coat - Google Patents
A kind of spherical joint bearing inner race of surface with hard coat Download PDFInfo
- Publication number
- CN207093578U CN207093578U CN201720218088.3U CN201720218088U CN207093578U CN 207093578 U CN207093578 U CN 207093578U CN 201720218088 U CN201720218088 U CN 201720218088U CN 207093578 U CN207093578 U CN 207093578U
- Authority
- CN
- China
- Prior art keywords
- inner ring
- service life
- hard coat
- spherical joint
- bearing inner
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
A kind of spherical joint bearing inner race of surface with hard coat, including inner ring body, there is WC-Co chrome coating by HVAF at the working region of the inner ring body surface.The utility model is as a result of the structure for having WC-Co chrome coating by HVAF at the working region of oscillating bearing inner peripheral surface, make the working face of inner ring there is compact structure, hardness is high, the advantages such as surface roughness is low, not only effectively increase the wearability of inner ring, extend the service life of inner ring, so as to have great role to the friction life-span improved with PTFE washer, and its salt spray resistance antiseptic property is excellent, salt fog resistance corrodes >=192 hours, so as to greatly improve its security reliability and service life in harshness marine environment, also significantly improve the endurance service life of the part under heavy loads simultaneously, dead load is worn >=1600 hours, service life relatively electroplates hard chrome and improves more than 2 times.
Description
Technical field
The oscillating bearing inner ring technical field in mechanical industry is the utility model is related to, a kind of surface band is specifically related to and surpasses
The spherical joint bearing inner race of velocity of sound flame-spraying WC-Co chrome coating.
Background technology
Oscillating bearing is the crucial important component of national economy and national defense construction.As General Mechanical Parts, weight can be met
Load, long life requirement, and with rotate flexibly, it is few safeguard, it is compact-sized, be easy to assemble and disassemble, in the course of the work can be in order to avoid dimension
Repair and the excellent specific properties such as lubricant need not be added, be widely used in Aero-Space, engineering machinery, truck, water conservancy projects, work
Industry robot and military project machinery etc..
Inner ring and outer ring of the core component of oscillating bearing for spherical arc.Outer ring is bearing steel, and slidingsurface is one layer
Polytetrafluoroethylene (PTFE) fabric.Inner ring is hardened bearing steel, needs that the constant load in direction can be born, while when bearing radial load,
Need that the less axial load of either direction can be born.The condition of work of space flight, aviation and oscillating bearing peculiar to vessel is very severe, holds
Can be occurred quickly by Service Environment, inner-ring bearing working surfaces such as high temperature, high rotating speed, vibration, high load capacity, chemical mediator corrosion
The damages such as abrasion, heating, spot corrosion and peeling cause bearing failure.Swinging, under high pulling torque effect, inner-ring bearing working face easily goes out
Several failure modes such as existing adhesive wear, abrasive wear, corrosive wear, fatigue wear and erosive wear, while outer ring poly- four
PVF substrate is easily galled by inner peripheral surface and damaged, and causes the increase of Internal and external cycle mating surface gap and coefficient of friction to increase, or even go out
Phenomena such as existing stuck.
The content of the invention
The purpose of this utility model is problem and shortage be present for above-mentioned, there is provided a kind of to improve the wear-resisting of inner ring
Decay resistance, so as to lift it in the security reliability of harshness marine environment and the surface of service life with hard coat
Spherical joint bearing inner race.
What the technical solution of the utility model was realized in:
Spherical joint bearing inner race of the surface described in the utility model with hard coat, including inner ring body, its feature
It is:There is WC-Co chrome coating by HVAF at the working region of the inner ring body surface.
Wherein, the thickness of the WC-Co chrome coating is 0.1~0.2mm, porosity≤0.5%, roughness Ra≤0.04
μm, hardness >=1200HV.
The edge of the WC-Co chrome coating is connected with inner ring bulk transition, and the width of transitional region be 0.5~
1mm。
The material of the inner ring body is G102Cr18Mo bearing steels.
The utility model compared with prior art, has advantages below:
The utility model passes through HVAF as a result of at the working region of oscillating bearing inner peripheral surface
There is the structure of WC-Co chrome coating, make the working face of inner ring there is the advantages such as compact structure, hardness are high, surface roughness is low,
The wearability of inner ring is not only effectively increased, extends the service life of inner ring, so as to improving the friction longevity with PTFE washer
Life has great role, and its salt spray resistance antiseptic property is excellent, and salt fog resistance corrodes >=192 hours, so as to greatly improve
It while also significantly improves the part under heavy loads resistance to tired in the security reliability and service life of harshness marine environment
Labor service life, dead load are worn >=1600 hours, and service life relatively electroplates hard chrome and improves 2~6 times.Moreover, tungsten carbide cobalt chrome
The edge of coating is connected with inner ring transition, so as to ensure that the bond strength of WC-Co chrome coating and inner ring, is effectively prevented
Coating is in the phenomenon that edge is cracking or peels off.
The utility model is further described below in conjunction with the accompanying drawings.
Brief description of the drawings
Fig. 1 is cross section structure diagram of the present utility model.
Fig. 2 is side structure schematic diagram of the present utility model.
Embodiment
As Figure 1-Figure 2, spherical joint bearing inner race of the surface described in the utility model with hard coat, including it is interior
Body 1 is enclosed, the material of the inner ring body 1 is G102Cr18Mo bearing steels, is passed through at the working region on the surface of inner ring body 1
HVAF has WC-Co chrome coating 2, and the thickness of the WC-Co chrome coating 2 is 0.1~0.2mm, and porosity≤
0.5%, roughness Ra≤0.04 μm, hardness >=1200HV.In order to ensure the bond strength of WC-Co chrome coating 2 and inner ring, have
Effect prevents coating from connecting in the phenomenon that edge is cracking or peels off, edge and the transition of inner ring body 1 of WC-Co chrome coating 2
Connect, and the width of transitional region 3 is 0.5~1mm.As a result of at the working region of oscillating bearing inner peripheral surface by super
Velocity of sound flame-spraying has the structure of WC-Co chrome coating 2, makes the working face of inner ring have compact structure, hardness height, surface thick
The advantages such as rugosity is low, the wearability of inner ring is not only effectively increased, extend the service life of inner ring, so as to improving and PTFE
The friction life-span of pad has great role, and its salt spray resistance antiseptic property is excellent, and salt fog resistance corrodes >=192 hours, so as to
Its security reliability and service life in harshness marine environment is greatly improved, while also significantly improves the part and exists
Endurance service life under heavy duty, dead load are worn >=1600 hours, and service life relatively electroplates hard chrome and improves more than 2 times.
The utility model is described by embodiment, but the utility model is not construed as limiting, with reference to this practicality
New description, other changes of the disclosed embodiments, is such as readily apparent that for the professional person of this area, such
Change should belong within the scope of the utility model claims restriction.
Claims (2)
1. a kind of spherical joint bearing inner race of surface with hard coat, including inner ring body(1), it is characterised in that:In described
Enclose body(1)There is WC-Co chrome coating by HVAF at the working region on surface(2), the tungsten carbide cobalt chrome
Coating(2)Thickness be 0.1~0.2mm, and the WC-Co chrome coating(2)Edge and inner ring body(1)Transition connects,
Transitional region(3)Width be 0.5~1mm.
2. spherical joint bearing inner race of the surface according to claim 1 with hard coat, it is characterised in that:The inner ring
Body(1)Material be G102Cr18Mo bearing steels.