CN207059372U - A kind of two-sided Composite lint of polar fleece and Shu Mianrong - Google Patents
A kind of two-sided Composite lint of polar fleece and Shu Mianrong Download PDFInfo
- Publication number
- CN207059372U CN207059372U CN201720819319.6U CN201720819319U CN207059372U CN 207059372 U CN207059372 U CN 207059372U CN 201720819319 U CN201720819319 U CN 201720819319U CN 207059372 U CN207059372 U CN 207059372U
- Authority
- CN
- China
- Prior art keywords
- layer
- styrene butadiene
- polar fleece
- butadiene latex
- carboxylic styrene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
It the utility model is related to polar fleece and the two-sided Composite lints of Shu Mianrong, top surface and bottom surface are respectively, there is the first carboxylic styrene butadiene latex layer, PU glue layers, the second carboxylic styrene butadiene latex layer successively between the polar fleece layer of cloth and Shu Mianrong layer of cloths from side to opposite side, the thickness of the first carboxylic styrene butadiene latex layer is 0.06 0.08mm, the thickness of PU glue layers is 0.1 0.2mm, and the thickness of the second carboxylic styrene butadiene latex layer is 0.1 0.12mm.The two-sided Composite lint of polar fleece and Shu Mianrong of the present utility model, first carboxylic styrene butadiene latex is coated on polar fleece layer of cloth and Shu Mianrong layer of cloths, dry carboxylic styrene butadiene latex and form the first carboxylic styrene butadiene latex layer and the second carboxylic styrene butadiene latex layer, then PU glue is coated on the first carboxylic styrene butadiene latex layer or the second carboxylic styrene butadiene latex layer again, two-sided Composite lint is formed in bonding polar fleece and Shu Mianrong, the two-sided Composite lint of polar fleece and Shu Mianrong of above-described embodiment improves the firmness of PU glue by coating carboxylic styrene butadiene latex, improves the tear resistance of flannelette.
Description
Technical field
A kind of two-sided Composite lint of polar fleece and Shu Mianrong is the utility model is related to, belongs to textile technology field.
Background technology
Beaver is the fabric of the equal villous shape in two sides, and flannelette upper surface has more fine hair, and third dimension is strong, glossiness
Height, it is soft abundant.The one side of polar fleece and the two-sided Composite lints of Shu Mianrong is polar fleece, another side Shu Mianrong, is made interior
Outer both sides have different feels.Polar fleece and the two-sided Composite lints of Shu Mianrong are typically that two pieces of flannelettes are used into PU in the prior art
Glue bond forms, but directly relatively low by PU glue bond bonding strengths, and two pieces of flannelettes easily occur in use for some time
The phenomenon of separation.
Utility model content
The technical problems to be solved in the utility model is：To overcome polar fleece in the prior art and the two-sided combination fine hairs of Shu Mianrong
The low technical problem of cloth bonding strength, there is provided a kind of high polar fleece of bond strength and the two-sided Composite lints of Shu Mianrong.
Technical scheme is used by the utility model solves its technical problem：
The utility model provides a kind of polar fleece and the two-sided Composite lints of Shu Mianrong, and top surface and bottom surface are respectively, described to shake
There is the first carboxylic styrene butadiene latex layer, PU glue layers, the successively between grain flannelette napped fabric layer and Shu Mianrong layer of cloths from side to opposite side
Dicarboxyl styrene-butadiene latex layer, the thickness of the first carboxylic styrene butadiene latex layer is 0.06-0.08mm, and the thickness of PU glue layers is
0.1-0.2mm, the thickness of the second carboxylic styrene butadiene latex layer is 0.1-0.12mm.
Preferably, the two-sided Composite lint of polar fleece and Shu Mianrong of the present utility model, the first carboxylic styrene butadiene latex layer
The viscosity of carboxylic styrene butadiene latex used is 200-210/mPaS, total solid content 45-48%.
Preferably, the two-sided Composite lint of polar fleece and Shu Mianrong of the present utility model, the second carboxylic styrene butadiene latex layer
The viscosity of carboxylic styrene butadiene latex used is 220-240/mPaS, total solid content 48-50%.
Preferably, the two-sided Composite lint of polar fleece and Shu Mianrong of the present utility model, the polar fleece layer of cloth and Shu Mianrong
Also there is stamp on layer of cloth.
Preferably, the two-sided Composite lint of polar fleece and Shu Mianrong of the present utility model, the polar fleece layer of cloth and Shu Mianrong
Layer of cloth has different colors.
Preferably, the two-sided Composite lint of polar fleece and Shu Mianrong of the present utility model, the fine hair on the polar fleece layer of cloth
Measure as 5000000-6000000 roots every square centimeter.
Preferably, the two-sided Composite lint of polar fleece and Shu Mianrong of the present utility model, the fine hair on the Shu Mianrong layer of cloths
Measure as 6000000-8000000 roots every square centimeter.
The beneficial effects of the utility model are：The two-sided Composite lint of polar fleece and Shu Mianrong of the present utility model, first shaking
Carboxylic styrene butadiene latex is coated on grain flannelette napped fabric layer and Shu Mianrong layer of cloths, drying carboxylic styrene butadiene latex forms the first carboxylic styrene butadiene latex layer
With the second carboxylic styrene butadiene latex layer, then PU is coated on the first carboxylic styrene butadiene latex layer or the second carboxylic styrene butadiene latex layer again
Glue, two-sided Composite lint, the two-sided combination fine hair of polar fleece and Shu Mianrong of above-described embodiment are formed in bonding polar fleece and Shu Mianrong
Cloth improves the firmness of PU glue by coating carboxylic styrene butadiene latex, improves the tear resistance of flannelette.
Brief description of the drawings
The utility model is further illustrated with reference to the accompanying drawings and examples.
Fig. 1 is the sectional view of the utility model polar fleece and the two-sided Composite lints of Shu Mianrong；
Reference in figure is：
1- polar fleece layer of cloths；2- the first carboxylic styrene butadiene latex layers；3-PU glue layers；4- the second carboxylic styrene butadiene latex layers；5-
Shu Mianrong layer of cloths.
Embodiment
The utility model is described in further detail presently in connection with accompanying drawing.These accompanying drawings are simplified schematic diagram,
Only illustrate basic structure of the present utility model in a schematic way, therefore it only shows the composition relevant with the utility model.
Embodiment
The present embodiment provides a kind of polar fleece and the two-sided Composite lints of Shu Mianrong, as shown in figure 1, top surface and bottom surface difference
For, between the polar fleece layer of cloth 1 and Shu Mianrong layer of cloths 5 from side to opposite side successively have the first carboxylic styrene butadiene latex layer 2,
PU glue layers 3, the second carboxylic styrene butadiene latex layer 4, the thickness of the first carboxylic styrene butadiene latex layer 2 is 0.06-0.08mm, such as
0.06mm, 0.07mm, 0.08mm etc., the thickness of PU glue layers 3 are 0.1-0.2mm, such as 0.1mm, 0.15mm, 0.2mm, second
The thickness of carboxylic styrene butadiene latex layer 4 is 0.1-0.12mm, such as 0.1mm, 0.11mm, 0.12mm.
The two-sided Composite lint of polar fleece and Shu Mianrong of above-described embodiment, first on polar fleece layer of cloth 1 and Shu Mianrong layer of cloths 5
Carboxylic styrene butadiene latex is coated, the coated weight of carboxylic styrene butadiene latex is done according to the difference of polar fleece layer of cloth 1 and the property of Shu Mianrong layer of cloths 5
Selection is gone out, drying carboxylic styrene butadiene latex forms the first carboxylic styrene butadiene latex layer 2 and the second carboxylic styrene butadiene latex layer 4, Ran Houzai
PU glue is coated on the first carboxylic styrene butadiene latex layer 2 or the second carboxylic styrene butadiene latex layer 4, polar fleece is adhered by and Shu Mianrong is formed
Two-sided Composite lint, the two-sided Composite lint of polar fleece and Shu Mianrong of above-described embodiment are improved by coating carboxylic styrene butadiene latex
The firmness of PU glue, improve the tear resistance energy of flannelette.
Further, the viscosity of carboxylic styrene butadiene latex is 200-210/mPa used in the first carboxylic styrene butadiene latex layer 2
S, total solid content 45-48%.The viscosity of carboxylic styrene butadiene latex is 220-240/ used in the second carboxylic styrene butadiene latex layer 4
MPaS, total solid content 48-50%.
It can be coordinated well with polar fleece and Shu Mianrong respectively using above-mentioned carboxylic styrene butadiene latex, above-mentioned viscosity
With the carboxylic styrene butadiene latex of solid content is very convenient is commercially available, for example just there is symbol in Zhejiang Tianchen Rubber Co., Ltd.
Close the carboxylic styrene butadiene latex sale for stating performance.
Further, also there is stamp on the polar fleece layer of cloth 1 and Shu Mianrong layer of cloths 5.The polar fleece layer of cloth 1 and relax
Velveteen layer of cloth 5 has different colors.Pass through stamp and dyeing so that flannelette is more attractive in appearance.
Further, the fine hair amount on the polar fleece layer of cloth 1 is 5000000-6000000 roots every square centimeter.
Further, the fine hair amount on the Shu Mianrong layer of cloths 5 is 6000000-8000000 roots every square centimeter.
Using it is above-mentioned according to desirable embodiment of the present utility model as enlightenment, pass through above-mentioned description, related work people
Member can carry out various changes and amendments in the range of without departing from this item utility model technological thought completely.This item is real
The content being not limited to new technical scope on specification, it is necessary to which its technology is determined according to right
Property scope.
Claims (7)
1. a kind of polar fleece and the two-sided Composite lints of Shu Mianrong, it is characterised in that top surface and bottom surface are respectively polar fleece layer of cloth (1)
With Shu Mianrong layer of cloths (5), have the between the polar fleece layer of cloth (1) and Shu Mianrong layer of cloths (5) successively from side to opposite side
One carboxylic styrene butadiene latex layer (2), PU glue layers (3), the second carboxylic styrene butadiene latex layer (4), the first carboxylic styrene butadiene latex layer
(2) thickness is 0.06-0.08mm, and the thickness of PU glue layers (3) is 0.1-0.2mm, the thickness of the second carboxylic styrene butadiene latex layer (4)
Spend for 0.1-0.12mm.
2. polar fleece according to claim 1 and the two-sided Composite lints of Shu Mianrong, it is characterised in that the first carboxyl fourth
The viscosity of carboxylic styrene butadiene latex used in benzene latex layer (2) is 200-210/mPaS, total solid content 45-48%.
3. polar fleece according to claim 2 and the two-sided Composite lints of Shu Mianrong, it is characterised in that the second carboxyl fourth
The viscosity of carboxylic styrene butadiene latex used in benzene latex layer (4) is 220-240/mPaS, total solid content 48-50%.
4. polar fleece according to claim 1 and the two-sided Composite lints of Shu Mianrong, it is characterised in that the polar fleece layer of cloth
(1) and on Shu Mianrong layer of cloths (5) also there is stamp.
5. polar fleece according to claim 1 and the two-sided Composite lints of Shu Mianrong, it is characterised in that the polar fleece layer of cloth
(1) and Shu Mianrong layer of cloths (5) have different colors.
6. polar fleece and the two-sided Composite lints of Shu Mianrong according to claim any one of 1-5, it is characterised in that described to shake
Fine hair amount on grain flannelette napped fabric layer (1) is 5000000-6000000 roots every square centimeter.
7. polar fleece and the two-sided Composite lints of Shu Mianrong according to claim any one of 1-5, it is characterised in that described to relax
Fine hair amount on velveteen layer of cloth (5) is 6000000-8000000 roots every square centimeter.