CN206899893U - Rub resistance transfer membrane - Google Patents
Rub resistance transfer membrane Download PDFInfo
- Publication number
- CN206899893U CN206899893U CN201720463091.1U CN201720463091U CN206899893U CN 206899893 U CN206899893 U CN 206899893U CN 201720463091 U CN201720463091 U CN 201720463091U CN 206899893 U CN206899893 U CN 206899893U
- Authority
- CN
- China
- Prior art keywords
- layer
- rub resistance
- transfer membrane
- imaging layer
- utility
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model discloses a kind of rub resistance transfer membrane, wherein, the rub resistance transfer membrane includes film layer, imaging layer and the reflector layer being cascading, and particularly, transfer membrane also includes the transparent rub resistance peel ply being stacked between the film layer and the imaging layer.Technical solutions of the utility model are avoided that transfer membrane imaging layer is impaired by external world's friction, to ensure the image quality of transfer membrane.
Description
Technical field
Transfer technical field of membrane is the utility model is related to, more particularly to a kind of rub resistance transfer membrane.
Background technology
Transfer membrane is widely used to packaging field, and relative to traditional printing technology, transfer membrane is lucuriant in design and great
Innervation, and there is certain anti-counterfeiting power.The reflector layer at the transfer membrane back side is handled with after adhering object fixation, peeling off by gum
The positive PET film layer of transfer membrane, you can expose imaging layer.The imaging layer of existing transfer membrane directly contacts with external environment, can
It can be collided with, be hit by the external world, and it is impaired to rub, and then influence the image quality of transfer membrane.
Utility model content
Main purpose of the present utility model is to propose a kind of rub resistance transfer membrane, it is intended to solves transfer membrane in the prior art
Imaging layer directly contacts with external environment, may be collided with, hit by the external world, and the impaired technical problem that rubs.
To achieve the above object, the utility model proposes rub resistance transfer membrane, including be cascading film layer,
Imaging layer and reflector layer, the transfer membrane are also transparent between the film layer and the imaging layer including being stacked
Rub resistance peel ply.
Preferably, the material of the rub resistance peel ply is mixed by acrylic lacquer and wax.
Preferably, the dry measure scope of acrylic lacquer is 0.2g/ ㎡~0.5g/ ㎡ in the rub resistance peel ply.
Preferably, the rub resistance peel ply has nano metal layer back to magnetron sputtering in the aspect of the imaging layer.
Preferably, the thickness of the nano metal layer is in and is uniformly arranged.
Preferably, the imaging layer is made or is molded by resin material UV solidifications and is made.
Preferably, the aspect of the imaging layer back to the rub resistance peel ply is provided with laser anti-counterfeit pattern.
Preferably, the reflector layer is aluminium coated and/or zinc sulfide phosphor layer.
The technical solution of the utility model is peeled off by using setting transparent rub resistance between imaging layer and film layer
Layer, and rub resistance peel ply is adhesively fixed on imaging layer in the aspect of the film layer, so as to be shelled by the rub resistance
Absciss layer realizes protection to imaging layer, and when avoiding transfer membrane and being collided with, hit by the external world, imaging layer friction is damaged, so that into
As the pattern of layer is scratched, the display effect of transfer membrane ensure that;Simultaneously as the rub resistance transfer membrane is in use, finally need
Film layer is removed, rub resistance peel ply is also beneficial to the disengaging of film layer and imaging layer.
Brief description of the drawings
, below will be to embodiment in order to illustrate more clearly of the utility model embodiment or technical scheme of the prior art
Or the required accompanying drawing used is briefly described in description of the prior art, it should be apparent that, drawings in the following description are only
It is some embodiments of the utility model, for those of ordinary skill in the art, is not paying the premise of creative work
Under, other accompanying drawings can also be obtained according to the structure shown in these accompanying drawings.
Fig. 1 is the structural representation of the embodiment of the utility model rub resistance transfer membrane one;
Fig. 2 is the structural representation of another embodiment of the utility model rub resistance transfer membrane.
Drawing reference numeral explanation:
Label | Title | Label | Title |
100 | Rub resistance transfer membrane | 110 | Film layer |
120 | Rub resistance peel ply | 130 | Nano metal layer |
140 | Imaging layer | 150 | Reflector layer |
160 | Laser anti-counterfeit pattern |
Realization, functional characteristics and the advantage of the utility model purpose will be described further referring to the drawings in conjunction with the embodiments.
Embodiment
Below in conjunction with the accompanying drawing in the utility model embodiment, the technical scheme in the embodiment of the utility model is carried out
Clearly and completely describing, it is clear that described embodiment is only part of the embodiment of the present utility model, rather than all
Embodiment.Based on the embodiment in the utility model, those of ordinary skill in the art are not making creative work premise
Lower obtained every other embodiment, belong to the scope of the utility model protection.
If it is to be appreciated that related in the utility model embodiment directionality instruction (such as upper and lower, left and right, it is preceding,
Afterwards ...), then directionality instruction be only used for explain it is relative between each part under a certain particular pose (as shown in drawings)
Position relationship, motion conditions etc., if the particular pose changes, directionality instruction also correspondingly changes therewith.
If, should " first ", " the in addition, relate to the description of " first ", " second " etc. in the utility model embodiment
Two " etc. description is only used for describing purpose, and it is not intended that instruction or implying its relative importance or implicit indicating meaning
The quantity of the technical characteristic shown.Thus, " first " is defined, the feature of " second " can express or implicitly include at least one
Individual this feature.In addition, the technical scheme between each embodiment can be combined with each other, but must be with ordinary skill
Personnel can be implemented as basis, and this technical side is will be understood that when the combination appearance of technical scheme is conflicting or can not realize
The combination of case is not present, also not within the protection domain of the requires of the utility model.
The utility model proposes a kind of rub resistance transfer membrane.
In the utility model embodiment, reference picture 1, the rub resistance transfer membrane 100 includes the film being cascading
Layer 110, imaging layer 140 and reflector layer 150, transfer membrane also include being stacked between film layer 110 and imaging layer 140
Transparent rub resistance peel ply 120.
Specifically, film layer 110 is PET film, and PET film is using polyethylene terephthalate as raw material, is used
Sheet is made in extrusion molding, then through thin-film material made of biaxial tension, it has the good transparency and air-tightness, needed herein
Illustrate, in film layer 110 thin definition refer to that the thickness of film layer 110 is smaller, the pattern of imaging layer 140 can be allowed without hindrance
Show with hindering;Pattern is provided with imaging layer 140, the pattern can be for decorative pattern or for false proof anti-counterfeiting mark;It is reflective
Layer 150 is used to carry out light to reflex to imaging layer 140 so that the color of imaging layer 140 is more gorgeous;It is common, the antifriction
Before wiping transfer membrane 100 comes into operation, also need to make special gum processing away from the surface of imaging layer 140 to reflector layer 150, with
Transfer membrane is set to be adhered to the surface of product to be printed.
The technical solution of the utility model between imaging layer 140 and film layer 110 by using setting transparent antifriction
Peel ply 120 is wiped, and rub resistance peel ply 120 is adhesively fixed on imaging layer 140 in the aspect of film layer 110, so as to
Protection to imaging layer 140 is realized by the rub resistance peel ply 120, when avoiding transfer membrane and being collided with, hit by the external world, into
It is damaged as layer 140 rubs, so that the pattern of imaging layer 140 is scratched, ensure that the display effect of transfer membrane;Simultaneously as turn
Film is moved in use, finally needing to remove film layer 110, rub resistance peel ply 120 is also beneficial to film layer 110 and imaging layer
140 disengaging.
Further, the material of rub resistance peel ply 120 is mixed by acrylic lacquer and wax.Wherein, acrylic acid is clear
The main component of paint is acrylic resin, extender pigment, auxiliary agent and organic solvent etc., acrylic lacquer can air drying, have
Good rub resistance and adhesive force.Herein it should be noted that acrylic lacquer layer not only have good rub resistance and
Adhesive force, also with good temperature tolerance, can effectively avoid causing because of the change of environment temperature imaging layer 130 occur aging and
Fade.In the present embodiment, the wax in rub resistance peel ply 120 is OP waxes, and OP waxes are cheap, easy to use, nontoxic, demoulding effect
Fruit is good, and certainly, in other embodiment, the wax in rub resistance peel ply 120 is alternatively one kind or more in OPE waxes or montanin wax
Kind.
It is well known that the dry measure of acrylic lacquer and the ability of rub resistance are directly proportional in rub resistance peel ply 120, however,
The dry measure of acrylic lacquer is bigger, and the cost of transfer membrane is higher, display effect is poorer, and therefore, the utility model is considering
After the rub resistance effect and display effect of transfer membrane, the dry measure control of acrylic lacquer in rub resistance peel ply 120 is existed
In the range of 0.2g/ ㎡~0.5g/ ㎡, in this way, can meet the preferable rub resistance effect of transfer membrane, and can ensures that transfer membrane is clear
The pattern of imaging layer 140 is shown clearly.
Further, in order to improve the display effect of rub resistance transfer membrane 100, it is avoided to be scratched, rub resistance peel ply
120 have nano metal layer 130 back to magnetron sputtering in the aspect of imaging layer 140.Nano metal layer 130 has higher hardness,
The abrasive resistance on the surface of imaging layer 140 can be greatly improved, avoids imaging layer 140 from being scratched.The design of right this patent is not limited to
This, in other embodiment, can also set polymer resin layer to improve transfer membrane table on the surface of rub resistance peel ply 120
The abrasive resistance in face.
For the fixing intensity between Enhanced Imaging layer 140 and reflector layer 150, in the utility model above-described embodiment into
It is made as layer 140 is made or is molded by resin material UV solidifications.So-called UV solidifications refer to ultraviolet photo-curing technique, mould pressing process
Refer to by the fixed imaging layer 140 that heats, pressurizes.Wherein, imaging layer 140 can be adhesively fixed on by ultraviolet photo-curing technique
On reflector layer 150, mould pressing process can further reduce the gap between imaging layer 140 and reflector layer 150, and then improve imaging layer
140 fixing intensity.
Refer to Fig. 2, in order that the utility model proposes rub resistance transfer membrane 100 possess anti-counterfeit capability, in this reality
With in new another embodiment, the aspect of imaging layer 140 back to rub resistance peel ply 120 is provided with laser anti-counterfeit pattern 160, should
Laser anti-counterfeit pattern 160 enables to the display effect of imaging layer 140 complicated and changeable, and then improves the false proof effect of imaging layer 140
Fruit.
Preferred embodiment of the present utility model is the foregoing is only, not thereby limits the scope of the claims of the present utility model,
Every equivalent structure change under inventive concept of the present utility model, made using the utility model specification and accompanying drawing content
Change, or directly/be used in other related technical areas indirectly and be included in scope of patent protection of the present utility model.
Claims (6)
- A kind of 1. rub resistance transfer membrane, it is characterised in that including film layer, imaging layer and the reflector layer being cascading, The transfer membrane also includes the transparent rub resistance peel ply being stacked between the film layer and the imaging layer.
- 2. rub resistance transfer membrane as claimed in claim 1, it is characterised in that the rub resistance peel ply is back to the imaging layer Aspect on magnetron sputtering have nano metal layer.
- 3. rub resistance transfer membrane as claimed in claim 2, it is characterised in that the thickness of the nano metal layer is in uniformly to set Put.
- 4. rub resistance transfer membrane as claimed in claim 1, it is characterised in that the imaging layer is made up of resin material UV solidifications In on the reflector layer;Or the imaging layer is made on the reflector layer by being molded.
- 5. rub resistance transfer membrane as claimed in claim 1, it is characterised in that the imaging layer is back to the rub resistance peel ply Aspect be provided with laser anti-counterfeit pattern.
- 6. the rub resistance transfer membrane as described in claim 1 to 5 any one, it is characterised in that the reflector layer is aluminium coated And/or zinc sulfide phosphor layer.