CN206752245U - A kind of environment-friendly type haydite concrete melting ice and snow road surface - Google Patents
A kind of environment-friendly type haydite concrete melting ice and snow road surface Download PDFInfo
- Publication number
- CN206752245U CN206752245U CN201720586471.4U CN201720586471U CN206752245U CN 206752245 U CN206752245 U CN 206752245U CN 201720586471 U CN201720586471 U CN 201720586471U CN 206752245 U CN206752245 U CN 206752245U
- Authority
- CN
- China
- Prior art keywords
- cement
- environment
- antiseepage
- polymer
- tack coat
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model is a kind of environment-friendly type haydite concrete melting ice and snow road surface, and its structure is：Polymer-modified cement mortar antiseepage tack coat is provided with above Portland cement concrete pavement structure sheaf, is ceramicite cement concrete surface feature layer above polymer-modified cement mortar antiseepage tack coat；Described polymer-modified cement mortar antiseepage tack coat is mixed by cement, styrene-butadiene latex polymer, water according to mass ratio；Described ceramicite cement concrete surface feature layer forms to be manufactured by haydite as the cement concrete material of aggregates.Once there is snowfall icing terrible weather disaster, can actively, in time, effectively melting ice and snow, without suspending traffic, ensure vehicle pass-through safety, avoid manually dispensing Nacl and endangered to caused by environment, and saved the expense of road maintenance.
Description
Technical field
The utility model belongs to highway engineering field in Communication and Transportation Engineering, and specifically a kind of environment-friendly type haydite concrete melts
Ice snow melting road surface.
Background technology
The terrible weather disaster such as accumulated snow icing causes pavement skid resistance condition to decline in highway engineering, so as to trigger various friendships
Interpreter's event, great casualties and economic damage, and serious negative social is caused to influence.And traditional means are on road
Face surface dispenses Snow Agent, and this method has certain hysteresis quality, it is necessary to suspend traffic, it is impossible to timely and effectively prevents and treats road surface product
Avenge the phenomenon to freeze, and conventional Snow Agent causes serious influence to environment for Nacl, and environment-friendly snowmelt agent price
Costliness, operation is carried out by the way of manually dispensing, can cause greatly to waste.In view of this, using environment-friendly type haydite coagulation
Soil surface can not only accomplish timely and effectively melting ice and snow, be made without suspending traffic, and using environment-friendly snowmelt agent, right
Environmental nonpollution, and waste caused by artificial spreading mode is avoided, saving maintenance costs.
The content of the invention
The purpose of this utility model is that solve at this stage using artificial the drawbacks of dispensing Snow Agent, there is provided a kind of environment-friendly type pottery
Grain concrete melting ice and snow road surface.Reach in time, melting ice and snow on one's own initiative, without suspending traffic, reduce chloride salt material
Use, protect the environment around road, and save maintenance costs.
The technical solution of the utility model is：A kind of environment-friendly type haydite concrete melting ice and snow pavement structure is：Light water
Polymer-modified cement mortar antiseepage tack coat, polymer-modified cement mortar antiseepage are provided with above cement concrete road surface structare layer
It is ceramicite cement concrete surface feature layer above tack coat；Described polymer-modified cement mortar antiseepage tack coat is by water
Mud, styrene-butadiene latex polymer（Solid masses）, water mixes in proportion；Described ceramicite cement concrete surface feature layer is
Manufactured and formed as the cement concrete material of aggregates by haydite.
The thickness of described polymer-modified cement mortar antiseepage tack coat is 1cm.
The thickness of described ceramicite cement concrete surface feature layer is 4cm.
The beneficial effect that the utility model is brought is that environment-friendly snowmelt agent and haydite are made by mixing into special aggregate,
The cement-concrete paving of the haydite containing Snow Agent is shaped to surface feature layer, integrally dropped equivalent to by the freezing point of road surface
It is low, once there is snowfall icing terrible weather disaster, can actively, in time, effectively melting ice and snow, without suspending traffic, ensure
Vehicle pass-through safety, avoids manually dispensing Nacl and is endangered to caused by environment, while use prefabricated haydite containing Snow Agent in advance,
The service efficiency of environment-friendly snowmelt agent can be effectively improved, saves road maintenance expense.
Brief description of the drawings
Fig. 1 is environment-friendly type ceramicite cement concrete melting ice and snow pavement structure schematic diagram of the present utility model.
Fig. 2 is template paving location structural representation of the present utility model.
Fig. 3 is polymer-modified cement mortar antiseepage tack coat making schematic diagram of the present utility model.
Fig. 4 is ceramicite cement concrete surface feature layer making schematic diagram of the present utility model.
In figure, 1 is Portland cement concrete pavement structure sheaf, and 2 polymer-modified cement mortar antiseepage tack coats, 3 be pottery
Grain cement concrete pavement functional layer, 4 be haydite containing Snow Agent, and 5,6 be template, and 7 be roller bearing.
Embodiment
It will be understood to those of skill in the art that the following example is merely to illustrate the utility model, and should not be regarded as limiting
The scope of the utility model.In the examples where no specific technique or condition is specified, according to document in the art described by skill
Art or condition are carried out according to product description.Agents useful for same or the unreceipted production firm person of instrument, are that can pass through purchase
Buy the conventional products of acquisition.
Environment-friendly type haydite concrete melting ice and snow pavement structure of the present utility model is：Portland cement concrete pavement structure
Be provided with polymer-modified cement mortar antiseepage tack coat 2 above layer 1, polymer-modified cement mortar antiseepage tack coat 2 it is upper
Face is ceramicite cement concrete surface feature layer 3；Described polymer-modified cement mortar antiseepage tack coat is by cement, butadiene-styrene rubber
Newborn polymer（Solid masses）, water according to mass ratio be 3：0.5~1：1 mixes；Described ceramicite cement concrete road surface work(
Ergosphere is manufactured as the cement concrete material of aggregates by haydite and formed.Polymer-modified cement mortar antiseepage tack coat 2
Thickness be 1cm, the thickness of ceramicite cement concrete surface feature layer 3 is 4cm.
Preparation method：
1）Ceramicite cement concrete aggregate processing：
（1）According to mass ratio it is 20-50 first by Snow Agent and water：100 prepare mixed solution, the chlorination that Snow Agent uses
Calcium；
（2）By the mixed solution to complete and haydite powder according to mass ratio 10-30：100 prepare haydite compound；
（3）Haydite compound is prepared into 10 ~ 20mm spherical particle；
（4）Spherical particle is air-dried 48 hours under field conditions (factors), or dried 12 hours under the conditions of 105 DEG C；
（5）Spherical haydite is put into high temperature furnace, temperature setting is 400 DEG C, and 400 DEG C are slowly risen to by low temperature to high temperature
Afterwards, 20 ~ 30 minutes are continued；
（6）Then it is 1000 ~ 1200 DEG C by temperature setting to be calcined, roasting time was controlled at 20 ~ 30 minutes, obtained haydite
Cement concrete aggregate；
2）The preparation on melting ice and snow road surface：
（1）Portland cement concrete pavement structure sheaf 1 is carried out, keeps its clean surface no-sundries；
（2）Template 5 is laid on Portland cement concrete pavement structure sheaf, template should be higher by Portland cement concrete pavement
Structure sheaf 1cm, width of the template inner vertical in runway direction is consistent with Portland cement concrete pavement featured layer width, mould
Plate fixation；
（3）After fixing template, in template, the 1cm polymer injected above of Portland cement concrete pavement structure sheaf 1
Modified cement mortar antiseepage tack coat 2, polymer-modified cement mortar antiseepage tack coat 2 is flattened using roller bearing 7；
（4）Template 6 is and then laid in template 5, template 6 is alignd with template 5, and the height that template 6 is higher by template 5 is
4cm, described template are made up of the material that wooden or iron grade has certain rigidity and intensity, surfacing, ensure constructing
During do not deform；
（5）Snow Agent haydite 4 will be contained with pavement stone according to mass ratio 20-50：100 ratio mixes, as system
The mixing aggregate of standby cement concrete material is stand-by；
（6）Aggregate will be mixed with cement, water, sand according to 2 ~ 3：1：0.3~0.4：1.5 ~ 2 ratios are mixed into ceramicite cement and mixed
Solidifying soil, ceramicite cement concrete is injected into template 6, on polymer-modified cement mortar antiseepage tack coat 2, and uses roller bearing
7 flatten ceramicite cement concrete, form ceramicite cement concrete surface feature layer 3, described roller bearing is cylinder, using steel
Iron is made, the smooth no pit in surface；
（7）Road concrete retarder is sprayed according to 200 ~ 300g/ ㎡ on ceramicite cement concrete surface feature floor 3,
The materials such as generally use citric acid, sodium gluconate, treat that the surface temperature of ceramicite cement concrete surface feature layer 3 is completed with making
The product of time is 160 ~ 260 afterwards（℃*h）When, gently remove the table of ceramicite cement concrete surface feature layer 3 for spraying retarder
The cement slurry in face so that mixing aggregate is exposed, and form removal 6 and template 5；
（8）Plastic sheeting is covered on ceramicite cement concrete surface feature layer 3 and carries out health, preserving period is 28 days, it
Open to traffic afterwards.
The advantages of general principle of the present utility model, principal character and the utility model has been shown and described above.One's own profession
The technical staff of industry is it should be appreciated that the utility model is not restricted to the described embodiments, described in above-described embodiment and specification
Simply illustrate principle of the present utility model, on the premise of the spirit and scope of the utility model is not departed from, the utility model is also
Various changes and modifications are had, these changes and improvements are both fallen within claimed the scope of the utility model.The utility model
Claimed scope is by appended claims and its equivalent thereof.
Claims (3)
- A kind of 1. environment-friendly type haydite concrete melting ice and snow road surface, it is characterised in that：Environment-friendly type haydite concrete melting ice and snow road The structure in face is：Polymer-modified cement mortar antiseepage tack coat is provided with above Portland cement concrete pavement structure sheaf, is polymerize It is ceramicite cement concrete surface feature layer above thing modified cement mortar antiseepage tack coat；Described polymer-modified cement sand Slurry antiseepage tack coat is mixed in proportion by cement, styrene-butadiene latex polymer, water；Described ceramicite cement concrete road surface work( Ergosphere forms to be manufactured by haydite containing Snow Agent as the cement concrete material of aggregates.
- 2. environment-friendly type haydite concrete melting ice and snow road surface according to claim 1, it is characterised in that：Polymer modification water The thickness 1cm of cement mortar antiseepage tack coat.
- 3. environment-friendly type haydite concrete melting ice and snow road surface according to claim 1, it is characterised in that：Ceramicite cement coagulation The thickness of soil surface functional layer is 4cm.