CN206477190U - A kind of pulp grinder mill with the Ni-based diamondite sprayed coating of nanometer - Google Patents
A kind of pulp grinder mill with the Ni-based diamondite sprayed coating of nanometer Download PDFInfo
- Publication number
- CN206477190U CN206477190U CN201720081716.8U CN201720081716U CN206477190U CN 206477190 U CN206477190 U CN 206477190U CN 201720081716 U CN201720081716 U CN 201720081716U CN 206477190 U CN206477190 U CN 206477190U
- Authority
- CN
- China
- Prior art keywords
- nanometer
- mill
- sprayed coating
- diamondite
- based diamondite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model provides a kind of pulp grinder mill with the Ni-based diamondite sprayed coating of nanometer, the mill is cirque structure, provided with Liang Ge concentric circles area, it is Nei Mo areas close to the center of circle, multiple first racks are provided with, is Wai Mo areas away from the center of circle, is provided with multiple second racks, the mill card is provided with the Ni-based diamondite sprayed coating of nanometer, and the Ni-based diamondite sprayed coating of nanometer is made up of nanometer tungsten carbide and Ni60 alloy powders.The utility model in disc surface by setting the Ni-based diamondite sprayed coating of nanometer, using nanometer tungsten carbide and the mixture of nickel-base alloy, hardness is up to HV 1,200 1300, make coating that there is very high hardness and wearability, the collision of the impurity such as sandstone in waste paper, cullet, peg can be born and extruded without coming off, and then extend the service life of mill.
Description
Technical field
The utility model is related to paper pulp manufacture field, more particularly to a kind of with the Ni-based diamondite spraying of nanometer
The pulp grinder mill of layer.
Background technology
Traditional pulp grinder generally uses burr grinder, and two mills are not contacted face-to-face, and gap only has
0.10-0.30mm;One of mill transfixion, another mill rotates at a high speed, and paper pulp enters two from the centre of mill
In gap between individual mill.The rack for high rigidity of being gathered on mill, cuts off paper pulp fiber, rubs disconnected.The rack of mill by
Paper fiber and the abrasion of the high intensity of various impurity, mill is scrapped after tooth height is ground off 5 mm.
Traditional mill is cast using high Ni-Cr stainless steel, heat treatment hardness HRC 50-60, with relatively good wear-resisting
Property, toughness and corrosion resistance.The paper pulp raw material of separate sources is processed, but the service life of the mill typically only has 1-6 months,
It is difficult to the requirement for meeting paper pulp processing.
Therefore, prior art has yet to be improved and developed.
Utility model content
The purpose of this utility model is to provide a kind of pulp grinder with the Ni-based diamondite sprayed coating of nanometer
Mill, it is intended to which it is poor to solve existing pulp grinder mill wearability, the problem of service life is short.
The technical solution of the utility model is as follows:
A kind of pulp grinder mill with the Ni-based diamondite sprayed coating of nanometer, the mill is annular knot
Structure, provided with Liang Ge concentric circles area, what it is close to the center of circle is Nei Mo areas, is provided with multiple first racks, away from the center of circle for Wai Mo areas,
Multiple second racks are provided with, the mill card is provided with the Ni-based diamondite sprayed coating of nanometer, the Ni-based carbon of nanometer
Change tungsten alloy sprayed coating to be made up of nanometer tungsten carbide and Ni60 alloy powders.
The described pulp grinder mill with the Ni-based diamondite sprayed coating of nanometer, wherein, first rack
Sparse is distributed in Nei Moqu, and the flank of tooth forms acute rake angle with the mill face.
The described pulp grinder mill with the Ni-based diamondite sprayed coating of nanometer, wherein, second rack
Area is ground in intensive distribution outside, and the second rack being divided into several regions, the same area is parallel to each other.
The described pulp grinder mill with the Ni-based diamondite sprayed coating of nanometer, wherein, the nanometer is Ni-based
The thickness of diamondite sprayed coating is 0.3-0.8mm.
The described pulp grinder mill with the Ni-based diamondite sprayed coating of nanometer, wherein, the nanometer is Ni-based
Layer of sand is additionally provided between diamondite sprayed coating and the mill.
The described pulp grinder mill with the Ni-based diamondite sprayed coating of nanometer, wherein, if the mill by
Dry fan-shaped grinding is spliced, and is fixed on a size and the mill identical by the fixing hole being arranged in grinding
On second mill.
The beneficial effects of the utility model are:The utility model provides a kind of with the Ni-based diamondite spraying of nanometer
The pulp grinder mill of layer, by setting the Ni-based diamondite sprayed coating of nanometer in disc surface, using nanometer tungsten carbide
With the mixture of nickel-base alloy, hardness is up to HV 1200-1300, coating is had very high hardness and wearability, can bear to give up
The collision of the impurity such as sandstone, cullet, peg and extruded in paper without coming off, and then extend the service life of mill,
Installed in addition, mill is divided into several sector grindings, be easy to the local replacing of mill.
Brief description of the drawings
Fig. 1 is a kind of pulp grinder mill with the Ni-based diamondite sprayed coating of nanometer that the utility model is provided
Structural representation.
Fig. 2 is a kind of pulp grinder mill with the Ni-based diamondite sprayed coating of nanometer that the utility model is provided
Partial sectional view.
Accompanying drawing marks explanation:1st, Nei Moqu;2nd, Wai Moqu;3rd, the first rack;4th, the second rack;5th, fixing hole;6th, nanometer
Tungsten carbide of nickel-base alloy spraying coating.
Embodiment
To make the purpose of this utility model, technical scheme and advantage clearer, clear and definite, develop simultaneously implementation referring to the drawings
The utility model is further described example.
Referring to Fig. 1 to Fig. 2, a kind of paper pulp with the Ni-based diamondite sprayed coating of nanometer provided for the utility model
Millstone, the mill is cirque structure, provided with Liang Ge concentric circles area, and what it is close to the center of circle is Nei Mo areas 1, is provided with the
One rack 3, is Wai Mo areas 2 away from the center of circle, is provided with the second rack 4.In actual production process, paper pulp is through in the mill
The heart enters, and flows from inside to outside, sequentially passes through the attrition process in Nei Mo areas 1 and Wai Mo areas 2.Nei Mo areas are first carried out to the paper pulp
Corase grind, then circulate to the progress of Wai Mo areas 2 fine gtinding.
As shown in Fig. 2 the mill card is provided with the Ni-based diamondite sprayed coating 6 of nanometer, nanometer tungsten carbide of nickel-base
The thickness of alloy spraying coating 6 is 0.3-0.8mm.Preferably, the Ni-based diamondite sprayed coating 6 of nanometer by nanometer tungsten carbide and
Ni60 alloy powders are made, and can bear the collision of the impurity such as sandstone in waste paper, cullet, peg and extrude without coming off.
In actual applications, the Ni-based diamondite sprayed coating 6 of nanometer can be made by following process:The nanometer tungsten carbide and Ni60
Alloy powder, in the disc surface, forms the preliminary Ni-based diamondite sprayed coating 6 of nanometer, then use by supersonic spray coating
Oxy-acetylene flame is sintered the Ni-based diamondite sprayed coating 6 of nanometer, 1000 DEG C of sintering temperature, makes the Ni-based carbonization of nanometer
Tungsten alloy sprayed coating 6 reaches more than 200MPA with mill formation metallurgical binding, bond strength;While nanometer tungsten carbide of nickel-base
Nanometer tungsten carbide and nickel-base alloy combine together in alloy spraying coating 6, make in the Ni-based diamondite sprayed coating 6 of nanometer WC and
The hard phases such as CrC, CrB and Ni formation high intensity metallurgical binding, when being worn away Hard Inclusion do not allow it is easy to fall off, therefore coating have
There is very high hardness and wearability, hardness is up to HV 1200-1300.Simultaneously as the Ni-based diamondite sprayed coating 6 of nanometer
The presence of middle tungsten carbide nanometer phase so that the Ni-based diamondite sprayed coating 6 of nanometer has higher toughness, is touched by impurity
Coating is difficult to collapse de- when hitting.Further, since the nanometer after the Ni-based very high density of diamondite sprayed coating 6 of nanometer, sintering is Ni-based
Diamondite sprayed coating 6 has smooth initial surface, can be used without processing, saves substantial amounts of machining expense.
Preferably, the described pulp grinder mill with the Ni-based diamondite sprayed coating of nanometer, wherein, the first tooth
Bar 3 it is sparse be distributed in Nei Mo areas 1, the flank of tooth forms acute rake angle with the mill face.When so making slurry into mill, together
When acted on by centrifugal force and axial thrust, be press against by inclined teeth inclined-plane after slurry is ground and carry out essence into Wai Mo areas 2 quickly
Fine lapping.
In actual applications, area 1 is ground in the intensive distribution of the second rack 4 outside, and fine gtinding, Wai Mo areas 1 are carried out to slurry
The second rack 4 being divided into several regions, the same area is parallel to each other, and is conducive to making slurry enter the second rack 4 unobstructedly
Between slot in.
In actual applications, p sandblastings layer is additionally provided between the Ni-based diamondite sprayed coating 6 of nanometer and the mill,
The sandblasting layer can play a part of cleaning mill face, while also contributing to the Ni-based diamondite sprayed coating 6 of nanometer preferably
It is attached on the mill.
As shown in figure 1, in actual applications, the mill can be spliced by several sector grindings, and by setting
Put the fixing hole 5 in grinding and be fixed on a size with the mill of mill identical second, the mill is split into
Several sector grindings, facilitate the processing and replacing of mill, after the rack abrasion in some region, need to only change region mill
Piece, further saves cost.
It should be appreciated that application of the present utility model is not limited to above-mentioned citing, those of ordinary skill in the art are come
Say, can according to the above description be improved or converted, all these modifications and variations should all belong to the appended power of the utility model
The protection domain that profit is required.
Claims (6)
1. a kind of pulp grinder mill with the Ni-based diamondite sprayed coating of nanometer, it is characterised in that the mill is
Cirque structure, provided with Liang Ge concentric circles area, is Nei Mo areas close to the center of circle, is provided with multiple first racks, away from the center of circle
For Wai Mo areas, multiple second racks are provided with, the mill card is provided with the Ni-based diamondite sprayed coating of nanometer.
2. the pulp grinder mill according to claim 1 with the Ni-based diamondite sprayed coating of nanometer, its feature
Be, first rack it is sparse be distributed in Nei Moqu, the flank of tooth forms acute rake angle with the mill face.
3. the pulp grinder mill according to claim 1 with the Ni-based diamondite sprayed coating of nanometer, its feature
It is, area is ground in the intensive distribution of second rack outside, the second rack being divided into several regions, the same area is mutually put down
OK.
4. the pulp grinder mill according to claim 1 with the Ni-based diamondite sprayed coating of nanometer, its feature
It is, the thickness of the Ni-based diamondite sprayed coating of nanometer is 0.3-0.8mm.
5. the pulp grinder mill according to claim 4 with the Ni-based diamondite sprayed coating of nanometer, its feature
It is, sandblasting layer is additionally provided between the Ni-based diamondite sprayed coating of nanometer and the mill.
6. the pulp grinder mill according to claim 1 with the Ni-based diamondite sprayed coating of nanometer, its feature
It is, the mill is spliced by several sector grindings, and is fixed on one greatly by the fixing hole being arranged in grinding
On the small and mill of mill identical second.