CN206317483U - A kind of high-performance slit abatvoix and foam aluminum plate composite plate - Google Patents
A kind of high-performance slit abatvoix and foam aluminum plate composite plate Download PDFInfo
- Publication number
- CN206317483U CN206317483U CN201621309735.3U CN201621309735U CN206317483U CN 206317483 U CN206317483 U CN 206317483U CN 201621309735 U CN201621309735 U CN 201621309735U CN 206317483 U CN206317483 U CN 206317483U
- Authority
- CN
- China
- Prior art keywords
- plate
- upper cover
- substrate
- cover plate
- slit
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model discloses the composite plate of a kind of high-performance slit abatvoix and foamed aluminium board, is mainly used as sound-absorbing material.Including upper cover plate, substrate, adhesive layer, angle steel and fixed nail, the upper cover plate surface sets slit, the substrate is the foam aluminium plate being placed in upper cover plate, two angle steel are set in the substrate bottom surface, adhesive layer is set between the angle steel and the substrate, the fixation is followed closely through the upper cover plate, substrate, adhesive layer angle steel is fixed composite plate and pressed in cold press, and pressure is 2MPa~3MPa;The slit length of the upper cover plate is 1mm~4mm, and width is 30 μm~60 μm.This composite plate has can be while take into account fire prevention, and corrosion-resistant, intensity is high, the multiple performance such as lightweight, because two kinds of materials belong to sound-absorbing material in terms of sound-absorbing, sound-absorbing effect is made after being combined more preferably, better than other porous composite sound-absorbing sheet materials.
Description
Technical field
The utility model is related to composite sound-absorbing sheet material technical field, more particularly to a kind of slit abatvoix and foamed aluminium board
Composite plate.
Background technology
Due to society's constantly development and progress, noise turns into a kind of important public harm of today's society, influence
Scope constantly expands, and people just interfere to normal life and work, it is therefore desirable to reduced or eliminated and made an uproar using sound-absorbing material
The harm of sound.
From sound-absorbing material, it is necessary first to consider sound absorption properties, at the same also to consider the preventing fires of sound-absorbing material, it is corrosion-resistant, strong
The performances such as degree, it is also contemplated that outward appearance and whether being easily installed.The sound-absorbing material used at present mainly includes fiber abatvoix, aluminium
Perforated sound-absorbing plate processed, wooden perforated sound-absorbing plate etc., although have respective advantage, but there is also can not take into account two or more simultaneously
The deficiency of performance.
Utility model content
It is high that the utility model pin technical problem to be solved is to provide a kind of sound-absorption coefficient, and with fire prevention, high intensity, resistance to
The compoiste sound-absorbing board of the performances such as corrosion.
The technical scheme that the utility model is used is as follows:A kind of high-performance slit abatvoix and foamed aluminium board it is compound
Plate, including upper cover plate, substrate, adhesive layer, angle steel and fixed nail, the upper cover plate surface set slit, and the substrate is to be placed in
Foam aluminium plate in upper cover plate, sets two angle steel, between the angle steel and the substrate in the substrate bottom surface
Adhesive layer is set, and the fixed nail is through the upper cover plate, substrate, and adhesive layer angle steel is fixed.
Further, the composite plate is pressed in cold press, and pressure is 2MPa~3MPa;The slit length of the upper cover plate
For 1mm~4mm, width is 30 μm~60 μm.
The beneficial effects of the utility model are:Slit abatvoix and foam aluminum plate composite plate have can while take into account fire prevention,
Corrosion-resistant, intensity is high, the multiple performance such as lightweight, because two kinds of materials belong to sound-absorbing material in terms of sound-absorbing, makes suction after being combined
Audio fruit is more preferable, better than other porous composite sound-absorbing sheet materials.
Brief description of the drawings
Accompanying drawing 1 is slit compound foamed aluminum plate cross-sectional view;
Cross-sectional view when accompanying drawing 2 does not install upper cover plate for slit compound foamed aluminum plate;
Accompanying drawing 3 is slit compound foamed aluminum plate upper cover plate cross-sectional view
Label is represented in accompanying drawing:1st, substrate, 2, upper cover plate, 3, angle steel, 4, adhesive layer, 5, fixed nail.
Embodiment
The utility model is described in detail below in conjunction with the accompanying drawings:
As shown in Figure 1-Figure 3, the composite plate of a kind of high-performance slit abatvoix of the utility model and foamed aluminium board, including upper
Cover plate 2, substrate 1, adhesive layer 4, angle steel 3 and fixed nail 5, the upper cover plate 2 is the Microfracture plate that surface sets slit, passes through punching press
It is made, slit length is 1mm~4mm, width is 30 μm~60 μm.The substrate 1 is the foamed aluminium board being placed in upper cover plate 2
Material, foamed aluminium board is formed by flux foaming.Two angle steel 3 are set in the bottom surface of substrate 1 as angle is enclosed, in the angle steel 3
Adhesive layer 4 is set between the substrate 1.Composite plate is pressed in cold press, and pressure is 2MPa~3MPa.Passed through with fixed nail 5
The upper cover plate 2, substrate 1, adhesive layer 4, angle steel 3 are fixed, fixed nail 5 generally nailing.
Above-mentioned utility model concrete technology flow process is as follows:
A) first right angle in 90 ° will be rolled over two sides of plate bending machine as the Microfracture plate of upper cover plate;
B) gluing fixation will be carried out with two angle steel as the two of the foamed aluminium board of substrate sides, glue uses epoxy resin
AB glue, temperature is useful in -50 DEG C~± 150 DEG C;
C) foamed aluminium board and the Microfracture plate rolled well are overlayed and pressed on cold pressing machine platform, pressure parameter is 2MPa
~3MPa;
D) the finished product sheet material both sides pressed are fastened with nailing.
Example 1
Making 600*600*20 slits compound foamed aluminum plate, (Microfracture plate material selection steel plate, foamed aluminium elects through-hole foam as
Aluminium), concrete technology flow process is as follows:
1st, 600*600*20 slit steel plate both sides 90 ° of right angle of plate bending machine folding;
2nd, the through-hole foam plate that the specification prepared is 598*600*22, both sides are carried out with 20*20*3 angle steel
Gluing fixation, 1 hour set time, temperature is room temperature;
3rd, slit steel plate and foamed aluminium are overlayed and pressed on cold pressing machine platform, pressure parameter is set as 2MPa;
4th, the composite plate after pressing is fastened with nailing.
Obtain 600*600*20 slit compound foamed aluminum plates.
Example 2
(Microfracture plate material selection aluminium sheet, foamed aluminium is logical to the slit compound foamed aluminum plate of making 1000*1000*30 specifications
Hole foamed aluminium), concrete technology flow process is as follows:
1st, 1000*1000*30 slit aluminium sheet both sides 90 ° of right angle of plate bending machine folding;
2nd, the through-hole foam plate that the specification prepared is 998*1000*32, both sides are carried out with 30*30*3 angle steel
Gluing fixation, 1 hour set time, temperature is room temperature;
3rd, slit aluminium sheet and foamed aluminium are stacked and pressed on cold pressing machine platform, pressure parameter is set as 3MPa;
4th, the composite plate after pressing is fastened with nailing.
Obtain the slit compound foamed aluminum plate of 1000*1000*30 specifications.
Claims (3)
1. the composite plate of a kind of high-performance slit abatvoix and foamed aluminium board, including upper cover plate, substrate, adhesive layer, angle steel and solid
Fixed nail, it is characterised in that the upper cover plate surface sets slit, and the substrate is the foam aluminium plate being placed in upper cover plate,
The substrate bottom surface sets two angle steel, and adhesive layer is set between the angle steel and the substrate, and the fixed nail is worn
The upper cover plate, substrate are crossed, adhesive layer, angle steel are fixed.
2. composite plate according to claim 1, it is characterised in that the composite plate is pressed in cold press, and pressure is 2MPa
~3MPa.
3. composite plate according to claim 1, it is characterised in that the slit length of the upper cover plate is 1mm~4mm, wide
Spend for 30 μm~60 μm.