CN206267486U

CN206267486U - Connected decorative board

Info

Publication number: CN206267486U
Application number: CN201621318014.9U
Authority: CN
Inventors: 梁知荣
Original assignee: Chongqing Wancai Technology World Industrial Co Ltd
Current assignee: Chongqing Wancai Technology World Industrial Co Ltd
Priority date: 2016-12-04
Filing date: 2016-12-04
Publication date: 2017-06-20
Anticipated expiration: 2026-12-04

Abstract

This patent discloses a kind of connected decorative board, including base plate, panel and connection both row's latex layers are provided between wire netting between the two, the base plate and panel；The base plate is concatenated by metal wire by row's shive and formed, and the base plate is domed；The wire netting runs through the latex layer, and the length direction of latex layer is orthogonal with the length direction of the base plate, and the backplate surface is coated with aqueous polyurethane coating.The connected decorative board that this patent is provided can resist ground influence of moisture, but also with the characteristics of amount of smoke is few when burning.

Description

Connected decorative board

Technical field

The utility model is related to a kind of plate for being layed in ground, is a kind of connected decorative board specifically.

Background technology

With the improvement of people ' s living standards, in the compound upper decoration plate block in ground, it is employed to be in more and more On the decoration in front yard.As a kind of technical scheme of splicing composite plates that Chinese patent CN205572634U is provided, including polylith are flat The bamboo chip or wood chip of sleeping splicing, the bamboo chip or wood chip lower surface paste a plurality of viscose top, the viscose top and bamboo chip Or wood chip is into 90 degree, the lower surface of the bamboo chip or wood chip and viscose top is provided with adhered layer, the following table of the adhered layer Face is provided with base layer.

But also there is following technological deficiency in above-mentioned patented technology：

Decorative panel is on ground, and ground moisture in itself is heavier, and moisture enters in decorative panel and in the adhesive linkage Or aqueous water is formed at viscose top, this directly results in two unfavorable results：1st, the active ingredient of adhesive linkage or viscose top is due to liquid The attachment of state water, viscosity declines, and influences the structural stability of whole decorative panel；2nd, the decorative panel is internally formed dark and damp ring Border, makes bacterial virus quickly grow, and healthy hidden danger is caused to people.

Utility model content

Technical problem to be solved in the utility model is to provide a kind of spliced dress that can resist ground influence of moisture Plaque.

In order to solve the above technical problems, the utility model provides following technical scheme：

Connected decorative board, including base plate, panel and between wire netting between the two, the base plate and panel It is provided with row's latex layer of both connections；The base plate is concatenated by metal wire by row's shive and formed, and the base plate is in arch Shape；The wire netting runs through the latex layer, and the length direction of latex layer is orthogonal with the length direction of the base plate, described Backplate surface is coated with aqueous polyurethane coating.

When connected decorative board is installed, it is necessary to be preset on mattess for accommodating the recessed of the arch floor Groove, aqueous polyurethane coating is coated in backplate surface；Then the design size according to latex layer is glued with position on the base plate Rubberized fabric, it is desirable to which adhesive plaster keeps level concordant with ground, it is impossible to allows adhesive plaster to be arched upward with arch floor, then re-lays metal Net, latex is added in the adhesive plaster position（Such as natural emulsion）, after after latex desiccation, adhesive plaster is clamped through wire netting with tweezers, And the adhesive plaster is torn take away；Then panel is installed on wire netting.

Using the technical solution of the utility model, have the following technical effect that：

1st, base plate of the present utility model does not use sealing to set, but can by moisture using the shive of metal wire concatenation Concentrate and enter in decorative panel, certain space is stored for the moisture is provided by base plate is domed；The wire netting is used to absorb The moisture, the effect of wire netting is not used to support the panel, and the gravity of panel transmission downwards is mainly by the groove It is supported；

2nd, the aqueous polyurethane coating can start to soften after absorbing the moisture, and the aqueous polyurethane for having part to soften is applied Material is influenceed to be attached on the wire netting by air movement, and the intensity of the wire netting can be increased after solidifying again By force；So it is to prevent the wire netting of excessive rustization from dropping on base plate, it is ensured that the structural stability of decorative panel；Due to aqueous The softening of polyurethane coating and aerial non-directional spread, and play the effect of bacteria growing inhibiting.

Further, also including polyvinylidene chloride layer, polyvinylidene chloride layer is filled between the base plate and panel.

It is before panel is installed, polyvinylidene chloride filler to be passed through into wire netting net when filling polyvinylidene chloride layer Eye is injected at base plate, because polyvinylidene chloride filler mobility is poor, so the space immediately below latex layer cannot be complete Fill up, so moisture is still able to be entered into decorative panel in the base plate gap below by latex layer.The utility model is not It is to reach the purpose of protection decorative panel by preventing moisture into decorative panel, but is limited by controlling the free air space of moisture System, the influence for reducing moisture.

On the one hand the polyvinylidene chloride layer can provide certain mechanical support effect, make energy between panel and base plate Enough undertakings for directly carrying out power；Still further aspect is in high temperature environments（Catch fire）, polyvinylidene chloride layer can only soften, no Volatile, the polyvinylidene chloride layer can comprehensively cover the aqueous polyurethane coating on the base plate well, prevent water Property polyurethane coating be heated after volatilization and form toxic smoke, pollute environment.

Further, the wire netting is copper mesh.

Copper mesh is easily prepared, and copper is easily oxidized, and meets the utility model and is used as wire netting to be oxidized material It is required that；And copper mesh low manufacture cost is, it is necessary to when changing, cost is relatively low.

Further, it is inlaid with Florfenicol particle in the polyvinylidene chloride layer.

Florfenicol particle is inlayed, when exactly injecting above-mentioned polyvinylidene chloride filler, Florfenicol is added in filler Particle；The effect of Florfenicol particle is added in order in high temperature environments, Florfenicol powder mixes with polyvinylidene chloride, carries The softening point of polyvinylidene chloride high, it is to avoid polyvinylidene chloride softens too early.If high temperature is only because summer air is obstructed Caused by additional boiling water wine falls, after that described polyvinylidene chloride slightly softens, the active ingredient of the Florfenicol particle with As the polyvinylidene chloride for softening is moved, the softening point at movement can be raised, if temperature is not too high, polyvinylidene chloride Can solidify immediately.

Further, the Florfenicol particle includes the Florfenicol powder in housing and housing, the housing be by The hollow spheres that chlorinated rubber is made.

It is lower than polyvinylidene chloride because the chlorinated rubber softening point only has 60 degree, polyvinylidene chloride can be allowed soft Before change, Florfenicol powder is discharged in advance.

Brief description of the drawings

Fig. 1 is the structural representation of the utility model connected decorative board.

Specific embodiment

The utility model is described in further detail below by specific embodiment：

Embodiment one

As shown in figure 1, the present embodiment connected decorative board, including base plate 1, panel 4 and in metal between the two Net 3, the wire netting is copper mesh.Also include polyvinylidene chloride layer, polyvinylidene chloride layer is filled in the base plate and face Between plate.The wire netting is completely covered panel lower surface, and the latex layer is in bar shaped, is distributed between being waited between each latex layer.

Row's latex layer 2 of both connections is provided between the base plate and panel（Using styrene-butadiene latex）；The base plate by One row's shive is concatenated by metal wire and formed, and the base plate is domed；The wire netting runs through the latex layer, latex layer Length direction is orthogonal with the length direction of the base plate.

The backplate surface is coated with aqueous polyurethane coating.Florfenicol is inlaid with the polyvinylidene chloride layer Grain, Florfenicol particle includes the Florfenicol powder in housing and housing, and the housing is the sky being made up of chlorinated rubber Heart spherosome.

Embodiment two

The present embodiment is differed only in embodiment one, and the present embodiment is without Florfenicol particle.

Comparative example one

This comparative example is that the present embodiment is without aqueous polyurethane coating with the difference of embodiment one.

Experiment：High temperature is tested

1st, 100 ~ 200 degree of experiments

The sample decorative panel of 50*50cm is respectively prepared according to embodiment one, two and comparative example one, then by three kinds of decorations Plate is respectively put into 160 degree of controlled temperature cabinet, and three kinds of smoke situations of sample are observed respectively.In preceding 10 minutes embodiments one and contrast The equal non smoke of example one is produced, and at 6-7 minutes, is implemented two and is started smog occur；At 14-17 minutes, the embodiment one with Comparative example one produces black smog, and both of which is produced without other smog.

2nd, 400 ~ 500 degree of experiments

The sample decorative panel of 50*50cm is respectively prepared according to embodiment one, two and comparative example one, then respectively by three kinds Decorative panel is respectively put into 480 degree of controlled temperature cabinet, and three kinds of smoke situations of sample are observed respectively.3-5 minutes, embodiment First, comparative example one starts black smog occur with implementing two, and base plate starts to burn, but the flare of the base plate in embodiment one Less, extinguish after flare occurs 20 seconds, the base plate sustained combustion of comparative example one and implementation two, until base plate burns down completely；It is real Test example one and only have black smog with comparative example one, there is green smog in embodiment two.

From the foregoing, the scheme of embodiment one is not only not likely to produce toxic smog, and there is stronger anti-flammability.

Above-described is only embodiment of the present utility model, and the general knowledge such as known concrete structure and characteristic is herein in scheme Excessive description is not made.It should be pointed out that for a person skilled in the art, not departing from the premise of the utility model structure Under, some deformations and improvement can also be made, these should also be considered as protection domain of the present utility model, and these are all without influence Effect and practical applicability that the utility model is implemented.This application claims protection domain should be with the content of its claim It is defined, specific embodiment in specification etc. records the content that can be used for explaining claim.

Claims

1. connected decorative board, including base plate, panel and in wire netting between the two, it is characterised in that the base plate It is provided between panel and is connected both row's latex layers；The base plate is concatenated by metal wire by row's shive and formed, institute State base plate domed；The wire netting runs through the latex layer, and the length direction of latex layer is mutual with the length direction of the base plate Perpendicular, the backplate surface is coated with aqueous polyurethane coating.

2. connected decorative board as claimed in claim 1, it is characterised in that also including polyvinylidene chloride layer, gather inclined dichloro Pvdf layer is filled between the base plate and panel.

3. connected decorative board as claimed in claim 2, it is characterised in that the wire netting is copper mesh.

4. connected decorative board as claimed in claim 2, it is characterised in that be inlaid with fluorobenzene in the polyvinylidene chloride layer Buddhist nun examines particle.

5. connected decorative board as claimed in claim 4, it is characterised in that the Florfenicol particle includes housing and shell Internal Florfenicol powder, the housing is the hollow spheres being made up of chlorinated rubber.

6. connected decorative board as claimed in claim 5, it is characterised in that the wire netting is completely covered panel lower surface, The latex layer is in bar shaped, is distributed between being waited between each latex layer.