CN206139459U - Storage tank tank container anticorrosive repair structure - Google Patents
Storage tank tank container anticorrosive repair structure Download PDFInfo
- Publication number
- CN206139459U CN206139459U CN201621103488.1U CN201621103488U CN206139459U CN 206139459 U CN206139459 U CN 206139459U CN 201621103488 U CN201621103488 U CN 201621103488U CN 206139459 U CN206139459 U CN 206139459U
- Authority
- CN
- China
- Prior art keywords
- storage tank
- corrosion
- container
- anticorrosive
- thickness
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model discloses a storage tank tank container anticorrosive repair structure, it includes storage tank tank container, storage tank tank container waits that it is the mat surface to restore the surface, for the mat surface wait restore that the surface is provided with thickness is 0.5 1mm's anticorrosive end agent layer, has anticorrosive end agent layer surface set gradually thickness is 0.3 0.4mm first anticorrosive coating, is thickness 0.5 0.6mm the second anticorrosive coating, it is the anticorrosive surface course of 0.02mm that second anticorrosive coating surface is provided with thickness. The utility model provides a storage tank tank container anticorrosive repair structure not only can prolong storage tank tank container's life, can also reduce cost of maintenance, and whole repair structure's anticorrosive life can reach more than 15 years, can reduce the maintenance cost of user to the storage tank tank container later stage.
Description
Technical field
This utility model is related to storage tank can container, and more particularly, to a kind of storage tank can container anti-corrosion structure is repaired.
Background technology
At present the domestic industrial civilian serious corrosion of storage tank can container generally existing, obscission, to normal band is run
Carry out very big hidden danger, the anti-corrosion that the long-term corrosion-resistant, nothing of urgent need comes off repairs structure to solve.
Utility model content
The purpose of this utility model is to provide a kind of storage tank can container anti-corrosion to repair structure, and it can extend storage tank tank appearance
Device service life, reduces maintenance cost.
To solve above-mentioned technical problem, embodiment of the present utility model is tied there is provided a kind of storage tank can container anti-corrosion reparation
Structure, it includes storage tank can container, and the complex surface to be repaired of storage tank can container is matsurface, is that the complex surface to be repaired of matsurface is provided with
Thickness is the anti-corrosion priming agent layer of 0.5-1mm, and anti-corrosion priming agent layer surface is disposed with the first anti-corrosion that thickness is 0.3-0.4mm
Layer, thickness are second anticorrosive coat of 0.5-0.6mm, and the second anti-corrosion layer surface is provided with thickness for 0.02mm anti-corrosion surface layers.
Compared with prior art, the storage tank can container anti-corrosion that this utility model is provided repairs structure can not only extend storage tank
The service life of can container, moreover it is possible to reduce maintenance cost, the whole anti-corrosion service life for repairing structure, can up to more than 15 years
User is reduced for the maintenance cost in storage tank can container later stage.
Further, surface cleanness to be repaired is sa2.5 levels, and roughness is more than 75 μm.
Further, depression in the surface position to be repaired is provided with metal mending oxidant layer.
Further, metal repairing agent is the super healant 44143 of happy Thailand's metal.
Further, complex surface to be repaired is provided with rust conversion agent layer.
Further, rust conversion agent layer is using happy Thailand's rust conversion agent 754.
Further, anti-corrosion priming agent is CERA-5X (CERA#5X) or 42076,44178.
Further, the first anticorrosive coat, the second anticorrosive coat adopt CERA-5-5 (CERA#5-5) material.
Further, depressed area is provided with the embedded metal mending oxidant layer in one end, the other end and is fixed on depressed area surface
Some carbon fiber wires.
Further, metal repairing agent layer surface is provided with wave structure.
As previously described CERA#5X, CERA#5-5 material is Japanese anti-corrosion material brand system code.
As previously described 42076,44178 is Henkel, happy Thailand's anti-corrosion material brand type code.
Description of the drawings
Fig. 1 is that storage tank can container anti-corrosion repairs structural representation.
Specific embodiment
In order that technological means, creation characteristic, reached purpose and effect that this utility model is realized are easy to understand, under
Face in conjunction with specific embodiments, is expanded on further this utility model.
Embodiment of the present utility model provides a kind of storage tank can container anti-corrosion and repairs structure, and it includes storage tank can container
E, referring to Fig. 1, the figure is the partial structurtes of storage tank can container, and the complex surface to be repaired of storage tank can container is matsurface, is matsurface
Complex surface to be repaired be provided with the anti-corrosion priming agent layer 1 that thickness is 0.5-1mm, anti-corrosion priming agent layer surface is disposed with thickness and is
First anticorrosive coat 2, thickness of 0.3-0.4mm is second anticorrosive coat 3 of 0.5-0.6mm, and the second anti-corrosion layer surface is provided with thickness
For 0.02mm anti-corrosions surface layer 4, while can making up storage tank tank corrosion defect by above-mentioned reparation structure, additionally it is possible to extend storage
The service life of groove tank.Used as anti-corrosion priming agent layer, its surface can be arranged can arrange in ripple struction, and the ripple struction carbon fibre
Dimension.
In addition, when the complex surface to be repaired of storage tank can container has depressed area, depression in the surface position to be repaired is arranged
Have a metal mending oxidant layer 5, and if the cleannes of complex surface to be repaired cannot it is up to standard in the case of, complex surface to be repaired is provided with corrosion
Conversion oxidant layer, for example with happy Thailand's rust conversion agent 754 corrosion conversion processing is carried out.
Used as a kind of selection, surface cleanness to be repaired is sa2.5 levels, and roughness is more than 75 μm.
Used as a kind of improvement, depressed area is provided with the embedded metal mending oxidant layer in one end, the other end and fixes (such as binding agent
With reference to) in some carbon fiber wires on depressed area surface, in the case of it is larger-size for depressed area, can be to greatest extent
Raising metal mending oxidant layer firmness, and be the globality for increasing metal mending oxidant layer and other structures layer, metal mending
Oxidant layer surface is provided with wave structure.
Mending course for storage tank can container is described below in detail：
The first step, the storage tank can container to repairing, first have to carry out high pressure water washing, relief grinding cleaning, guarantee cleared table
All dirts such as rust deposite, the greasy dirt in face；
Second step, sandblasting operation is carried out again, reach surface cleanness sa2.5 level, more than 75 μm of roughness；
Under 3rd step, specific condition, if sandblasting has local not thoroughly, not up to cleannes sa2.5 level when, with happy safe rust
Erosion transforming agent 754 is brushed, and converts corrosion layer, it is ensured that the antiseptic property of apparatus body；
If the 4th step, surface there are the defects such as defect, crack, few meat, repaiied with the super healant 44143 of happy Thailand's metal
Mend, molding of polishing after dry solidification；
5th step, surface wettability bottoming, brushing special anticorrosive priming agent CERA#5X or 42076,44178 thickness 0.5-1mm,
Dry solidification.
6th step, clean surface, drying with happy safe cleaning grease removal agent 755 and 82253；
7th step, with CERA#5-5 material surfaces spray 2 times, thickness is 0.3-0.4mm and 0.5-0.6mm, is solidified respectively
It is dried；
8th step, with CERA#5 material spraying finish paints, thickness is that 0.02mm solidifies drying；
The paint of the 9th step, storage tank tank appearance brushing sign；
Tenth step, complete after above-mentioned operation, storage tank tank just can come into operation.
It should be noted that be category closing occasion in storage tank, need to be by the safety work guidelines of regulation during construction.
It will be understood by those skilled in the art that the respective embodiments described above are to realize of the present utility model being embodied as
Example, and in actual applications, can in the form and details to it, various changes can be made, without departing from spirit of the present utility model
And scope.
Claims (10)
1. a kind of storage tank can container anti-corrosion repairs structure, and it includes storage tank can container, it is characterised in that the storage tank can container
Complex surface to be repaired is matsurface, is that the complex surface to be repaired of matsurface is provided with the anti-corrosion priming agent layer that thickness is 0.5-1mm, described anti-
Rotten priming agent layer surface is disposed with the second anti-corrosion that thickness is first anticorrosive coat of 0.3-0.4mm, thickness is 0.5-0.6mm
Layer, the second anti-corrosion layer surface is provided with thickness for 0.02mm anti-corrosion surface layers.
2. storage tank can container anti-corrosion according to claim 1 repairs structure, it is characterised in that the surface cleaning to be repaired
Spend for sa2.5 levels, roughness is more than 75 μm.
3. storage tank can container anti-corrosion according to claim 1 repairs structure, it is characterised in that the complex surface to be repaired it is recessed
Sunken position is provided with metal mending oxidant layer.
4. storage tank can container anti-corrosion according to claim 3 repairs structure, it is characterised in that the metal repairing agent is pleasure
The super healant 44143 of safe metal.
5. storage tank can container anti-corrosion according to claim 1 repairs structure, it is characterised in that the complex surface to be repaired is arranged
There is rust conversion agent layer.
6. storage tank can container anti-corrosion according to claim 5 repairs structure, it is characterised in that the rust conversion agent layer is adopted
With happy Thailand's rust conversion agent 754.
7. storage tank can container anti-corrosion according to claim 1 repairs structure, it is characterised in that the anti-corrosion priming agent is
CERA-5X or 42076,44178.
8. storage tank can container anti-corrosion according to claim 1 repairs structure, it is characterised in that first anticorrosive coat, the
Two anticorrosive coats adopt CERA-5-5 materials.
9. storage tank can container anti-corrosion according to claim 3 repairs structure, it is characterised in that the depressed area is provided with
The embedded metal mending oxidant layer in one end, the other end are fixed on some carbon fiber wires on depressed area surface.
10. storage tank can container anti-corrosion according to claim 3 repairs structure, it is characterised in that the metal mending oxidant layer
Surface is provided with wave structure.