CN205981956U - Grind and disperse inside hardness testing arrangement of attrition medium for carbon nanotube paste - Google Patents
Grind and disperse inside hardness testing arrangement of attrition medium for carbon nanotube paste Download PDFInfo
- Publication number
- CN205981956U CN205981956U CN201620987800.1U CN201620987800U CN205981956U CN 205981956 U CN205981956 U CN 205981956U CN 201620987800 U CN201620987800 U CN 201620987800U CN 205981956 U CN205981956 U CN 205981956U
- Authority
- CN
- China
- Prior art keywords
- hardness test
- rotating disk
- rotating shaft
- cross bar
- vertical columns
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model discloses a grind and disperse inside hardness testing arrangement of attrition medium for carbon nanotube paste, including the carousel, the bottom center of carousel is equipped with hollow hollow rotating shaft, and the hollow rotating shaft suit just rotates with stationary mast and is connected in stationary mast's bottom, the carousel evenly is provided with a plurality of fixed block along the circumferencial direction, and every fixed block center sets up an arc recess, every arc recessed wall face arc sucking disc that has all bonded, stationary mast's top is provided with two slide rails, and two equal vertical settings of slide rail just are parallel to each other, and sliding connection has first horizontal horizontal pole in the slide rail, and sliding connection has the horizontal horizontal pole of second in another slide rail, the hardness test needle is through hanging the fixed bottom that sets up at first horizontal horizontal pole of pole, grinding disk is connected bottom the horizontal horizontal pole of pivot and second, and grinding disk can rotate under the drive of pivot. This application can be tested zirconia bead's surface and inside hardness, prevents that the unqualified zirconia bead of hardness from flowing in the product line.
Description
Technical field
The application is related to one of carbon nano tube paste production process assistance test instrument, particularly a kind of grinding distribution
Carbon nano tube paste abrasive media inner hardness test device.
Background technology
CNT is as monodimension nanometer material, lightweight, and hexagonal structure connects perfection, has the power of many exceptions
, electricity and chemical property.
CNT has good mechanical property, and CNTs tensile strength reaches 50~200GPa, is 100 times of steel, close
Degree but only have steel 1/6, at least higher an order of magnitude than ordinary graphite fiber;Its elastic modelling quantity up to 1TPa, with diamond
Elastic modelling quantity quite, about the 5 of steel times.For the CNT of the solid wall with ideal structure, its tensile strength is about
800GPa.Although the structure of CNT is similar to the structure of macromolecular material, its structure is stablized than macromolecular material
Many.CNT is the material with highest specific strength that can prepare at present.If will be with Other Engineering material as matrix and carbon
Nanotube makes composite, and composite material exhibits can be made to go out good intensity, elasticity, fatigue resistance and isotropism, to multiple
The performance of condensation material brings great improvement.
The hardness of CNT is suitable with diamond, but has good pliability, can stretch.In October, 2000, beautiful
The research worker of Pennsylvania State University of state claims, and the intensity of the strength ratio same volume steel of CNT is high 100 times, after weight but only has
1/6 to the 1/7 of person.CNT thus claimed " super fiber ".CNT was once placed in by the research worker of Moscow State University
Under the hydraulic pressure of 1011 MPa(Be equivalent to the deep pressure of ten thousand metres under water), due to huge pressure, CNT is crushed.Remove
After removing pressure, CNT has recovered shape as spring immediately, shows good toughness.This enlightenment people can utilize
CNT manufactures frivolous spring, as damping device on automobile, train, can significantly mitigate weight.
CNT has good electric conductivity, because the structure of CNT and the lamellar structure of graphite are identical, institute
To have good electric property, electrical conductivity is generally up to 10,000 times of copper.
CNT has good heat transfer property, and CNT can synthesize the heat conducting material of high anisotropy.Separately
Outward, CNT has higher thermal conductivity, as long as adulterating micro CNT in the composite, the heat of this composite
Conductance will be likely to be obtained very big improvement.
Because CNT has above-mentioned many excellent specific properties, therefore the research of CNT and nano material in recent years
More and more deep, the wide application prospect of CNT also constantly shows.
The Chinese invention patent application of Application No. 201510950204.6 disclosed in 4 days Mays in 2016, its innovation and creation
Entitled " a kind of lithium battery carbon nano tube paste and preparation method thereof ", the composition in carbon nano tube paste be carbon nanometer
Pipe, carbon black, surfactant, thickening agent, solvent.Its proportioning is, CNT:Carbon black:Surfactant:Thickening agent:Solvent=
(3~10wt%):(0~8wt%):(0.1~1.3wt%):(0~1wt%):(80~96wt%), using this proportioning according to mix and blend work
Skill prepares dispersed uniform carbon nano tube paste.In the presence of surface activity, thickening agent, using high speed machine stirring and
The mode that ultrasonic agitation combines, makes conductive agent degree of scatter greatly improve.Carry out to being difficult to scattered carbon nanotube conducting agent
The pre-prepared of slurry reduces stirring in cell size for the next step and requires so as to reach preferable dispersion effect, up to
To preferable mixed effect.
The Chinese invention patent application of Application No. 201410114650.9 disclosed in 25 days June in 2014, its invention wound
Entitled " the carbon nanotube conducting slurry and its production and use " made, carbon nanotube conducting slurry by conductive functional filler,
Conductive functional filler pressed by dispersant, solvent:Dispersant:Solvent=2~10:0.2~5:85~97.8 mass ratio is formulated.Lead
Electricity Functional body is spherical CNT group, spherical CNT aggregate or its with carbon black, acetylene black, carbon fiber, conductive stone
The combination of one or more of ink, Graphene.Preparation method is to add described conductive functional filler and dispersant in described ratio
Enter stirring in solvent, obtain premix material, by premix material in grinding machine for grinding, formed and include multiple particle diameters for 0.1~3 micron
Spherical CNT group electrocondution slurry.This carbon nanotube conducting slurry can be used as the conduction of lithium battery positive and negative pole material
Agent.
The mode that above-mentioned patent application, the stirring of the first high speed machine and ultrasonic agitation combine, is mainly suitable for small lot
Produce or the low aqueous dispersion of viscosity uses, produce in enormous quantities and substantially all disperseed using second sand mill.
And zirconium oxide bead is made up of raw material with micron order and Subnano-class zirconium oxide with yittrium oxide, for requiring
" no pollution " and high viscosity, the extra-fine grinding of high rigidity material and a kind of scattered grinding bead, just suitable performances requirement is higher
Carbon nano tube paste preparation.
Zirconium oxide bead, wear-resistant, long service life, therefore cost are also very high.However, some manufacturers, high for pursuing
Volume profit, employs cheap zirconium oxide bead inferior, or because molding key technology parameter is not controlled so that hardness number
Not up to standard, so that the rate of wear of zirconium oxide bead is fast, service life greatly shortens, and frequent replacing oxidation is informed by production line,
Cost is led to increase, for the sand milling tinuous production using zirconium oxide bead in a large number, after the zirconium oxide bead of Fast Wearing will enter
Procedure, leads to stopping production of production etc..However, the little zirconium oxide bead of the ball shape of zirconium oxide bead, especially diameter, internal hard
Degree is difficult to test again, therefore, so that chromium plating zirconium oxide bead is existed in a large number.
Content of the invention
The application technical problem to be solved is for above-mentioned the deficiencies in the prior art, and provides a kind of grinding distribution carbon to receive
Mitron slurry abrasive media inner hardness test device, this grinding distribution carbon nano tube paste is surveyed with abrasive media inner hardness
Trial assembly is put and the surface of zirconium oxide bead and inner hardness can be tested, and prevents the underproof zirconium oxide bead of hardness from flowing into producing line.
For solving above-mentioned technical problem, the application employed technical scheme comprise that:
A kind of grinding distribution carbon nano tube paste abrasive media inner hardness test device, including rotating disk, vertical columns,
Hardness test pin, abrasive disc and operation display panel.
Rotating disk can rotate, and the bottom centre of rotating disk is provided with the hollow rotating shaft of hollow, and hollow rotating shaft is sleeved on fixing vertical
The bottom of post, and be connected with vertical columns rotation.
Rotating disk is along the circumferential direction evenly arranged with several fixed blocks, the centrally disposed arc groove of each fixed block,
Each arc groove internal face is all bonded with arc sucker.
The top of vertical columns is provided with two slide rails, and two slide rails are all vertically arranged and are parallel to each other, in a slide rail
Slidably connect first level cross bar, in another slide rail, slidably connect the second horizontal cross bar.
Hardness test pin is fixedly installed on the bottom of first level cross bar by hanger bar.
Abrasive disc is connected with the second horizontal cross bar bottom by rotating shaft, and abrasive disc can rotate under the drive of rotating shaft.
Operation display panel is arranged on vertical columns, and is connected with hardness test pin.
Described hollow rotating shaft is passed through linear bearing and is connected with vertical columns rotation.
The rotation of described rotating disk is driven by interval motor.
Six fixed blocks are provided with described rotating disk, rotating disk is connected with six indexing indexers.
It is provided with displacement transducer on described first level cross bar and the second horizontal cross bar.
After the application adopts said structure, have the advantages that:
1. the bottom of zirconium oxide bead can be inhaled by the setting of the arc sucker in above-mentioned arc groove and arc groove
Attached fixation.
2. the setting of above-mentioned rotating disk and multiple fixed block, can place multiple zirconium oxide beads, also can one-time continuous carry out many
The case depth of individual zirconium oxide bead grinds or inner hardness test, also can once test multiple Duplicate Samples, it is to avoid test error,
Make test accuracy higher.
3. above-mentioned turntable rotation, can make abrasive disc be located at the surface of arc groove, axis of rotation, drive abrasive disc to turn
Dynamic, elevating lever highly declines simultaneously, and zirconium oxide bead surface can be ground.The setting of upper displacement sensors, by right
The control of lifter rod lifting displacement, and then the grinding depth of zirconium oxide bead is controlled, the grinding depth of zirconium oxide bead is general
Half less than zirconium oxide bead diameter.
4. above-mentioned hardness test pin can be under the drive of elevating lever, and height declines, to the oxidation being fixed in arc groove
Zirconium bead surface or inner hardness are tested, and hardness display instrument then can automatically show and record hardness data.
Brief description
Fig. 1 is that a kind of structure of the application grinding distribution carbon nano tube paste abrasive media inner hardness test device is shown
It is intended to.
Specific embodiment
With concrete better embodiment, the application is described in further detail below in conjunction with the accompanying drawings.
As shown in figure 1, a kind of grinding distribution carbon nano tube paste abrasive media inner hardness test device, wherein have and turn
Disk 1, hollow rotating shaft 11, fixed block 12, arc groove 13, arc sucker 14, vertical columns 2, hardness test pin 3, first level
The technical characteristics such as cross bar 31, hanger bar 32, abrasive disc 4, the second horizontal cross bar 41, rotating shaft 42, guidance panel 5.
A kind of grinding distribution carbon nano tube paste abrasive media inner hardness test device, including rotating disk, vertical columns,
Hardness test pin, abrasive disc and operation display panel.
Rotating disk can rotate, and the bottom centre of rotating disk is provided with the hollow rotating shaft of hollow, and hollow rotating shaft is sleeved on fixing vertical
The bottom of post, and be connected with vertical columns rotation.
Rotating disk is along the circumferential direction evenly arranged with several fixed blocks, the centrally disposed arc groove of each fixed block,
Each arc groove internal face is all bonded with arc sucker.
The top of vertical columns is provided with two slide rails, and two slide rails are all vertically arranged and are parallel to each other, in a slide rail
Slidably connect first level cross bar, in another slide rail, slidably connect the second horizontal cross bar.
Hardness test pin is fixedly installed on the bottom of first level cross bar by hanger bar.
Abrasive disc is connected with the second horizontal cross bar bottom by rotating shaft, and abrasive disc can rotate under the drive of rotating shaft.
Operation display panel is arranged on vertical columns, and is connected with hardness test pin.
Described hollow rotating shaft is passed through linear bearing and is connected with vertical columns rotation.
The rotation of described rotating disk is driven by interval motor.
Six fixed blocks are provided with described rotating disk, rotating disk is connected with six indexing indexers.
It is provided with displacement transducer on described first level cross bar and the second horizontal cross bar.
After the application adopts said structure, have the advantages that:
1. the bottom of zirconium oxide bead can be inhaled by the setting of the arc sucker in above-mentioned arc groove and arc groove
Attached fixation.
2. the setting of above-mentioned rotating disk and multiple fixed block, can place multiple zirconium oxide beads, also can one-time continuous carry out many
The case depth of individual zirconium oxide bead grinds or inner hardness test, also can once test multiple Duplicate Samples, it is to avoid test error,
Make test accuracy higher.
3. above-mentioned turntable rotation, can make abrasive disc be located at the surface of arc groove, axis of rotation, drive abrasive disc to turn
Dynamic, elevating lever highly declines simultaneously, and zirconium oxide bead surface can be ground.The setting of upper displacement sensors, by right
The control of lifter rod lifting displacement, and then the grinding depth of zirconium oxide bead is controlled, the grinding depth of zirconium oxide bead is general
Half less than zirconium oxide bead diameter.
4. above-mentioned hardness test pin can be under the drive of elevating lever, and height declines, to the oxidation being fixed in arc groove
Zirconium bead surface or inner hardness are tested, and hardness display instrument then can automatically show and record hardness data.
The preferred implementation of the application described in detail above, but, the application is not limited in above-mentioned embodiment
Detail, in the range of the technology design of the application, multiple equivalents can be carried out to the technical scheme of the application, this
A little equivalents belong to the protection domain of the application.
Claims (5)
1. a kind of grinding distribution carbon nano tube paste with abrasive media inner hardness test device it is characterised in that:Including rotating disk,
Vertical columns, hardness test pin, abrasive disc and operation display panel;
Rotating disk can rotate, and the bottom centre of rotating disk is provided with the hollow rotating shaft of hollow, and hollow rotating shaft is sleeved on vertical columns
Bottom, and be connected with vertical columns rotation;
Rotating disk is along the circumferential direction evenly arranged with several fixed blocks, the centrally disposed arc groove of each fixed block, each
Arc groove internal face is all bonded with arc sucker;
The top of vertical columns is provided with two slide rails, and two slide rails are all vertically arranged and are parallel to each other, and slide in a slide rail
It is connected with first level cross bar, in another slide rail, slidably connect the second horizontal cross bar;
Hardness test pin is fixedly installed on the bottom of first level cross bar by hanger bar;
Abrasive disc is connected with the second horizontal cross bar bottom by rotating shaft, and abrasive disc can rotate under the drive of rotating shaft;
Operation display panel is arranged on vertical columns, and is connected with hardness test pin.
2. grinding distribution carbon nano tube paste according to claim 1 abrasive media inner hardness test device, it is special
Levy and be:Described hollow rotating shaft is passed through linear bearing and is connected with vertical columns rotation.
3. grinding distribution carbon nano tube paste according to claim 1 abrasive media inner hardness test device, it is special
Levy and be:The rotation of described rotating disk is driven by interval motor.
4. grinding distribution carbon nano tube paste according to claim 1 abrasive media inner hardness test device, it is special
Levy and be:Six fixed blocks are provided with described rotating disk, rotating disk is connected with six indexing indexers.
5. grinding distribution carbon nano tube paste according to claim 1 abrasive media inner hardness test device, it is special
Levy and be:It is provided with displacement transducer on described first level cross bar and the second horizontal cross bar.