CN205933716U - There is not steamed fireproof membrane - Google Patents
There is not steamed fireproof membrane Download PDFInfo
- Publication number
- CN205933716U CN205933716U CN201620086301.5U CN201620086301U CN205933716U CN 205933716 U CN205933716 U CN 205933716U CN 201620086301 U CN201620086301 U CN 201620086301U CN 205933716 U CN205933716 U CN 205933716U
- Authority
- CN
- China
- Prior art keywords
- layer
- fire
- film
- biaxially oriented
- oriented polypropylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model relates to a there is not steamed fireproof membrane, in proper order including being used for strengthening fire -retardant enhancement layer, biaxially oriented polypropylene rete, having cold mounting or heat recombination's viscose layer, the coating of fire -retardant enhancement layer is in the one side of biaxially oriented polypropylene rete, the coating of viscose layer is in the another side of biaxially oriented polypropylene rete. The utility model discloses a there is not steamed fireproof membrane, the fire prevention particle that adds in the production of BOPP film is few, does not influence the shaping and the physical properties of film, has certain fire line simultaneously. Can processing through the fire prevention enhancement layer make the BOPP film reach VTM completely 0 the level reaches the high fire behavior who requires. But prevent fires PET, PI relatively at the field greatly reduced cost of packing and label more than 30%. Realize halogen free completely, environment friendly.
Description
Technical field
The utility model is related to a kind of halogen-free flameproof film, and more particularly, to a kind of Biaxially oriented polypropylene of halogen-free flameproof is thin
Film.
Background technology
At present packaging and the market halogen-free flameproof of label material mainly based on the materials such as pet, pi, manufacturing cost
Height is it is impossible to meet the demand of mass market, and usage amount big BOPP (bidirectional stretching polypropylene film) market, in fireproof neck
Domain cannot substantial amounts of be promoted because technique is immature, fine ratio of product is low.It is low that fire prevention BOPP film is less than fire prevention PET on cost
More than 30%, lower by more than 50% than PI, but the volume production that will be directly realized by fire prevention BOPP at present is immature in formula and process aspect,
Also rest on research and development, test manufacture stage, and the coating layer thickness directly passing through to carry out the fire prevention coating of bopp at present outside line is big, cost
High, low production efficiency.
Utility model content
The utility model solve technical problem be:Build a kind of halogen-free flameproof film, overcome existing biaxial stretching polypropylene
The coating layer thickness of alkene membrane fireproofing coating is big, high cost, the technical problem of low production efficiency.
The technical solution of the utility model is:Build a kind of halogen-free flameproof film, include successively for strengthening fire-retardant resistance
Combustion enhancement layer, biaxially oriented polypropylene film layer, have cold mount or adhesive-layer that heat is compound, described fire-retardant enhancement layer is coated in described
The one side of biaxially oriented polypropylene film layer, described adhesive-layer is coated in the another side of described biaxially oriented polypropylene film layer.
Further technical scheme of the present utility model is:Also include release layer, described release layer is fitted in described adhesive-layer
On.
Further technical scheme of the present utility model is:The thickness range of described fire-retardant enhancement layer is 5 μm to 15 μm.
Further technical scheme of the present utility model is:The thickness range of described biaxially oriented polypropylene film layer is for 10 μm extremely
50μm.
Further technical scheme of the present utility model is:The thickness range of described adhesive-layer is 5 μm to 50 μm.
Further technical scheme of the present utility model is:The thickness range of described release layer is 5 μm to 200 μm.
Of the present utility model have the technical effect that:Build a kind of halogen-free flameproof film, include successively for strengthening fire-retardant resistance
Combustion enhancement layer, biaxially oriented polypropylene film layer, have cold mount or adhesive-layer that heat is compound, described fire-retardant enhancement layer is coated in described
The one side of biaxially oriented polypropylene film layer, described adhesive-layer is coated in the another side of described biaxially oriented polypropylene film layer.This reality
With new halogen-free flameproof film, the fire prevention particle that BOPP film is added in producing is few, does not affect the shaping of film and physical
Can, there is certain fire line simultaneously.By the process of enhancement layer of preventing fires, BOPP film can be made to be fully achieved VTM-0 level, reach
The fire protecting performance of high request.Cost more than 30% can be substantially reduced in the field of packaging and label for fire prevention PET, PI relatively.
Fully achieve halogen-free, environmental friendliness.
Brief description
Fig. 1 is structural representation of the present utility model.
Specific embodiment
With reference to specific embodiment, technical solutions of the utility model are further illustrated.
As shown in figure 1, specific embodiment of the present utility model is:Build a kind of halogen-free flameproof film, include successively using
In strengthen fire-retardant fire-retardant enhancement layer 1, biaxially oriented polypropylene film layer 2, have cold mount or adhesive-layer 3 that heat is compound, described resistance
Combustion enhancement layer 1 is coated in the one side of described biaxially oriented polypropylene film layer 2, and described adhesive-layer 3 is coated in described biaxial tension and gathers
The another side of propylene film layer 2.
As shown in figure 1, specific implementation process of the present utility model is:Fire-retardant enhancement layer 1 has certain thickness and adds
Plus the resin bed of powder flame-proof agent, the flame retardant rating due to increasing the biaxially oriented polypropylene film of 10%-20% does not reach will
Ask it is necessary to be further added by one layer of fire-retardant enhancement layer to reach flame retardant rating come the anti-flammability to lift biaxially oriented polypropylene film.By polyester
One or more of resin, polyurethane resin, acrylic resin, organic siliconresin mixed with resin powder flame-proof dosage form becomes mixing
Thing, is coated in the one side of biaxially oriented polypropylene film layer 2.Using fire retardant be:Generally phosphorus system or with the resistance of other powder
Combustion agent, the thickness range of fire-retardant enhancement layer 1 is 5 μm to 15 μm.Biaxially oriented polypropylene film is to pass through film using plastic pellet
Two-way the drawing high of production equipment completes, and adds a certain proportion of fire retardant, the powder flame-proof agent of interpolation in pp plastic pellet simultaneously
Add generally phosphorus system or the mixing composition with other powder flame-proof agent, the 10%-20% of adding proportion opposed plastic particle.
Add the certain fire resistance of lifting of fire retardant, current technology can not directly the ratio by increasing fire retardant realize fire-retardant,
If adding excessive, being difficult to plastic pellet and being difficult to film forming, and reducing the physics tensile property of film, therefore can be by again
Fire-retardant reinforcement is realizing anti-flammability.The thickness range of described biaxially oriented polypropylene film layer is 10 μm to 50 μm.Adhesive-layer 3 has
Cold mount or performance that heat is compound, by one of resin of acrylic resin, polyester resin, polyurethane resin or rubber series or many
Plant and form with the resin with pressure-sensitive or thermal viscosity, the thickness 5u-50u of resin bed.The thickness range of described adhesive-layer is 5
μm to 50 μm.
As shown in figure 1, specific embodiment of the present utility model is:Also include release layer 4, the Ge Laxin of different grammes per square metres or
Any one of resin mould release membrance of single copper release liners or different-thickness.Described release layer 4 is arranged on described adhesive-layer 3, uses
In the described adhesive-layer 3 of protection.It is compound to the layer upper surface of described release layer 4 through dried described adhesive-layer 3 by compounding machine,
Complete the production of release layer 4.The thickness range of described release layer 4 is 5 μm to 200 μm.
Of the present utility model have the technical effect that:Build a kind of halogen-free flameproof film, include successively for strengthening fire-retardant resistance
Combustion enhancement layer 1, biaxially oriented polypropylene film layer 2, have cold mount or adhesive-layer 3 that heat is compound, described fire-retardant enhancement layer 1 is coated in
The one side of described biaxially oriented polypropylene film layer 2, described adhesive-layer 3 is coated in the another of described biaxially oriented polypropylene film layer 2
Face.Halogen-free flameproof film of the present utility model, BOPP film produce in add fire prevention particle few, do not affect film shaping and
Physical property, has certain fire line simultaneously.By the process of enhancement layer of preventing fires, BOPP film can be made to be fully achieved VTM-0
Level, reaches the fire protecting performance of high request.Cost can be substantially reduced in the field of packaging and label for fire prevention PET, PI relatively
More than 30%.Fully achieve halogen-free, environmental friendliness.
Above content be with reference to specific preferred embodiment further detailed description of the utility model it is impossible to
Identification is of the present utility model to be embodied as being confined to these explanations.Ordinary skill for the utility model art
For personnel, without departing from the concept of the premise utility, some simple deduction or replace can also be made, all should regard
For belonging to protection domain of the present utility model.
Claims (6)
1. a kind of halogen-free flameproof film is it is characterised in that include for strengthening fire-retardant fire-retardant enhancement layer successively, biaxial tension gathers
Propylene film layer, have cold mount or adhesive-layer that heat is compound, described fire-retardant enhancement layer is coated in described biaxially oriented polypropylene film layer
One side, described adhesive-layer is coated in the another side of described biaxially oriented polypropylene film layer.
2. according to claim 1 halogen-free flameproof film it is characterised in that also including release layer, described release layer is fitted in
On described adhesive-layer.
3. according to claim 1 halogen-free flameproof film it is characterised in that the thickness range of described fire-retardant enhancement layer is 5 micro-
Rice is to 15 microns.
4. according to claim 1 halogen-free flameproof film it is characterised in that the thickness model of described biaxially oriented polypropylene film layer
Enclose for 10 microns to 50 microns.
5. according to claim 1 halogen-free flameproof film it is characterised in that described adhesive-layer thickness range be 5 microns extremely
50 microns.
6. according to claim 2 halogen-free flameproof film it is characterised in that described release layer thickness range be 5 microns extremely
200 microns.