CN205915857U - Tectorial membrane for colored steel strippable from UV rendition decorating film - Google Patents
Tectorial membrane for colored steel strippable from UV rendition decorating film Download PDFInfo
- Publication number
- CN205915857U CN205915857U CN201620521184.0U CN201620521184U CN205915857U CN 205915857 U CN205915857 U CN 205915857U CN 201620521184 U CN201620521184 U CN 201620521184U CN 205915857 U CN205915857 U CN 205915857U
- Authority
- CN
- China
- Prior art keywords
- layer
- thickness
- film
- texture
- peel ply
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model belongs to the technical field of the decorating film, concretely relates to tectorial membrane for colored steel strippable from UV rendition decorating film, the decorating film including set up peel ply on base film layer, set up texture layer on the peel ply, set up the layer of aluminizing on the texture layer, layer after that on setting up the layer of aluminizing, base film layer's material is selected from a kind or several kinds among polydiethylene terephthalate, polyvinyl chloride, polyethylene, polypropylene, polyamide and the polyvinyl alcohol. The utility model discloses a phenomenon of base film layer and texture layer peeling off can not appear among the prior art in the mode on peel ply protection texture layer.
Description
Technical field
This utility model belongs to decoration technical field of membrane and in particular to a kind of peelable uv transfer decorative of film-coated color plate
Film.
Background technology
Decorating film is that have various textures on thin film, and has the material of decorative effect.Because decorating film is not only provided that
Simulant grain, has the visual effect the same with real-texture, and has superior properties of product, has gradually been applied to daily
The every field of life.The film-coated color plate fitted with sheet metal with decorating film, has excellent processability, incrustation
Property, the excellent properties such as corrosion resistance, scoring resistance, heat-resisting quantity, be mainly used in household electrical appliances and industrial products incrustation, also
It is applied to building decoration facestock, the field such as elevator manufacture, it has become all kinds of expensive goods and decorated requisite materials, had both exempted from
Except painting process, simplify production technology, turn avoid environmental pollution simultaneously, enjoy manufacturer and consumer to like, application
Field and market prospect are very wide.
Existing film-coated color plate decorating film is to be transferred or polished by uv glue on organic polymer basement membrane surface to grab
The mode carved forms texture layer, through the imitative metal effect of formation of aluminizing, also can form chromatograph by printing, so that decorating film is had fresh
Gorgeous color.The film-coated color plate that this decorating film is fitted with sheet metal, due to containing organic polymer base membrane layer, for
Uv glue transfers the decorating film of processing mode formation it is easy to there is the phenomenon that base membrane layer is peeled off with texture layer, and for polishing
Grab the decorating film that quarter mode formed it is easy to the phenomenon that occurs aluminium coated to peel off with texture layer, cause properties of product can not expire
Foot requires, and application is restricted.
Utility model content
This utility model mainly provides a kind of peelable uv transfer decorative film of film-coated color plate, protects stricture of vagina using peel ply
Reason layer, is not in the phenomenon that in prior art, base membrane layer is peeled off with texture layer.Its technical scheme is as follows: described decorating film includes
The peel ply being arranged on base membrane layer, the texture layer being arranged on peel ply, the aluminium coated being arranged on texture layer, it is arranged on plating
Following layer on aluminium lamination, the material of base membrane layer is selected from polyethylene terephthalate, polrvinyl chloride, polyethylene, polypropylene, gathers
One or more of amide and polyvinyl alcohol.
Preferably, the material of described peel ply is selected from one of organosilicon, polyurethane, epoxy resin and acrylic resin
Or it is several.Peel ply has good glossiness, hardness, wearability and ageing resistance, and texture layer is played a protective role.
Preferably, described texture layer is uv solidification glue water layer.
Preferably, the material of described following layer is selected from one or more of vinylacetate, polyurethane and acrylate.
Preferably, the thickness of described base membrane layer is 10-100 μm, and the thickness of peel ply is 0.1-5 μm, the thickness of texture layer
For 2-50 μm, the thickness of aluminium coated is 5-30 μm, and the thickness of following layer is 0.1-5 μm.
Preferably, the thickness of described base membrane layer is 20-50 μm, and the thickness of peel ply is 0.2-2 μm, and the thickness of texture layer is
5-20 μm, the thickness of aluminium coated is 10-20 μm, and the thickness of following layer is 0.2-2 μm.
Preferably, under room temperature or heating condition, base membrane layer is separable with peel ply.
Preferably, the texture of described texture layer is wire drawing texture, frosted texture, fiber pattern or geometric error modeling.
Using above-mentioned film-coated color plate with peelable uv transfer decorative film, this utility model has the advantage that
This utility model formed peelable uv transfer decorative film when fitting into film-coated color plate with sheet metal, in room temperature
Or under heating condition, the base membrane layer of bottom can be torn off, peel ply and texture layer are transferred on sheet metal, peel ply is to stricture of vagina
Reason layer plays a protective role.The basement membrane on decorating film being formed compared to traditional film-coated color plate decorating film, this utility model
Layer is peelable, protects texture layer using peel ply, therefore there is not the base membrane layer phenomenon peeling-off with texture layer.In addition, basement membrane
Layer can also recycle, and reduce material cost, make product more environmentally-friendly.The overlay film being formed using this utility model decorating film is color
Plate is more prominent on test performance, such as bending, impact resistance, cupping performance etc.;Simultaneously because peel ply is very thin, texture can be made
Effect becomes apparent from, and simulated effect is more preferable.
Brief description
Fig. 1 is the peelable uv transfer decorative membrane structure figure of film-coated color plate of the present utility model.
Wherein: 1, base membrane layer, 2, peel ply, 3, texture layer, 4, aluminium coated, 5, following layer.
Specific embodiment
As shown in figure 1, being the peelable uv transfer decorative film of film-coated color plate of the present utility model, described decorating film includes setting
The texture layer 3 put in the peel ply 2 on base membrane layer 1, being arranged on peel ply 2, the aluminium coated 4 being arranged on texture layer 3, setting
Following layer 5 on aluminium coated 4.
The material of base membrane layer 1 be selected from polyethylene terephthalate, polrvinyl chloride, polyethylene, polypropylene, polyamide and
One or more of polyvinyl alcohol.The material of peel ply 2 is selected from organosilicon, polyurethane, epoxy resin and acrylic resin
One or more.Texture layer 3 is uv solidification glue water layer.The material of following layer 5 is selected from vinylacetate, polyurethane and acrylic acid
One or more of ester.
The thickness of base membrane layer 1 is 10-100 μm, and the thickness of peel ply 2 is 0.1-5 μm, and the thickness of texture layer 3 is 2-50 μm,
The thickness of aluminium coated 4 is 5-30nm, and the thickness of following layer 5 is 0.1-5 μm.
Embodiment 1
50 μ m thick pet (polyethylene terephthalate) base membrane layer 1 surface processing in surface corona, using nick
Version coating method forms the organosilicon peel ply 2 that thickness is 1 μm, then uv transfer modes is used above in peel ply 2 and forms thickness
Spend the wire drawing texture layer 3 for 10 μm, then evaporation thickness forms aluminium coated 4 for the aluminum of 10nm on wire drawing texture layer 3, then
Again the vinylacetate following layer 5 that thickness is 1 μm is formed using micro- plate gravure coating method, obtain peelable uv transfer wire drawing texture
Decorating film.
Embodiment 2
On the surface of untreated 30 μ m thick pvc (polrvinyl chloride) base membrane layers 1 in surface, using the extrusion coated mode of slit
Form the polyurethane peel ply 2 that thickness is 0.5 μm, then uv transfer modes are used above forming thickness in peel ply 2 is 2 μm
Frosted texture layer 3, then on frosted texture layer 3, sputter thickness forms aluminium coated 4 for the aluminum of 5nm, then adopts nick again
Version coating method forms the acrylate following layer 5 that thickness is 0.5 μm, obtains peelable uv transfer frosted grain decorating film.
Embodiment 3
On 45 μ m thick pp (polypropylene) base membrane layer 1 surface of chemical surface treatment, thickness is formed using spraying coating mode
Spend for 1.5 μm of acrylic resin peel plies 2, then uv transfer modes are used above in peel ply 2 and form the fibre that thickness is 50 μm
Dimension texture layer 3, then on fiber pattern layer 3, sputter thickness forms aluminium coated 4 for the aluminum of 12nm, then adopts slit to squeeze again
Go out coating method and form the polyurethane following layer 5 that thickness is 2 μm, obtain peelable uv transfer fiber pattern decorating film.
Embodiment 4
On untreated 20 μ m thick pva (polyvinyl alcohol) base membrane layer 1 surface, forming thickness using net roller coat mode for cloth is
2 μm of acrylic resin peel ply 2, is then used above uv transfer modes in peel ply 2 and forms the geometric error modeling that thickness is 5 μm
Layer 3, then on geometric error modeling layer 3, evaporation thickness forms aluminium coated 4 for the aluminum of 20nm, then adopts slit extrusion coated again
Mode forms the vinylacetate following layer 5 that thickness is 1 μm, obtains peelable uv transfer geometric error modeling decorating film.
Embodiment 5
On 100 μ m thick pa (polyamide) base membrane layer 1 surface of chemical surface treatment, thickness is formed using spraying coating mode
Spend the epoxy resin peel ply 2 for 5 μm, then uv transfer modes are used above in peel ply 2 and form the geometry that thickness is 20 μm
Texture layer 3, then on geometric error modeling layer 3, evaporation thickness forms aluminium coated 4 for the aluminum of 30nm, then adopts slit to extrude again
Coating method forms the polyurethane following layer 5 that thickness is 0.2 μm, obtains peelable uv transfer geometric error modeling decorating film.
Comparative example 1
Do cure process in chemically treated 30 μ m thick pet base membrane layer 1 one side, another side is formed using uv transfer modes
Thickness is 10 μm of wire drawing texture layer 3, then on wire drawing texture layer 3, evaporation thickness forms aluminium coated 4 for the aluminum of 10nm, connects
And again the polyurethane following layer 5 that thickness is 1 μm is formed using the extrusion coated mode of slit, obtain peelable uv transfer wire drawing texture
Decorating film.
Comparative example 2
Do cure process in untreated 30 μ m thick pet base membrane layer 1 surface one side, another side grabs quarter mode using polishing
Form wire drawing texture layer 3, forming thickness using micro- plate gravure coating method is 1 μm of priming coat, then evaporation thickness on priming coat
Form aluminium coated 4 for the aluminum of 10nm, then again the polyurethane following layer that thickness is 1 μm is formed using the extrusion coated mode of slit
5, obtain peelable uv transfer wire drawing texture decorating film.
Performance test
Example 1-5 and comparative example 1-2 prepare the decorating film surface treated heat with 0.5mm thickness respectively completing
Galvanized steel plain sheet polyurethane hot melt carries out laminating and becomes film-coated color plate (in embodiment tearing off base membrane layer 1), then according to gbt
The performances such as the bending of 12754-1991, gbt1732-93, gbt 4156-2007 test film-coated color plate, impact resistance, cupping, respectively
It is compared, the textures simulation effect of embodiment and comparative example is compared, result is as shown in table 1 simultaneously.
Table 1 the performance test results
It will be apparent to those skilled in the art that can technical scheme as described above and design, make other various
Corresponding change and deformation, and all these change and deformation all should belong to the protection of this utility model claim
Within the scope of.
Claims (6)
1. a kind of film-coated color plate with peelable uv transfer decorative film it is characterised in that: described decorating film includes being arranged on base membrane layer
(1) peel ply (2) on, the texture layer (3) being arranged on peel ply (2), the aluminium coated (4) being arranged on texture layer (3), set
Put the following layer (5) on aluminium coated (4).
2. film-coated color plate according to claim 1 with peelable uv transfer decorative film it is characterised in that: texture layer (3) is
Uv solidification glue water layer.
3. film-coated color plate according to claim 1 with peelable uv transfer decorative film it is characterised in that: base membrane layer (1)
Thickness is 10-100 μm, and the thickness of peel ply (2) is 0.1-5 μm, and the thickness of texture layer (3) is 2-50 μm, the thickness of aluminium coated (4)
Spend for 5-30nm, the thickness of following layer (5) is 0.1-5 μm.
4. film-coated color plate according to claim 3 with peelable uv transfer decorative film it is characterised in that: base membrane layer (1)
Thickness is 20-50 μm, and the thickness of peel ply (2) is 0.2-2 μm, and the thickness of texture layer (3) is 5-20 μm, the thickness of aluminium coated (4)
Spend for 10-20nm, the thickness of following layer (5) is 0.2-2 μm.
5. film-coated color plate according to claim 1 with peelable uv transfer decorative film it is characterised in that: room temperature or fire-bar
Under part, base membrane layer (1) is separable with peel ply (2).
6. film-coated color plate according to claim 1 with peelable uv transfer decorative film it is characterised in that: texture layer (3)
Texture is wire drawing texture, frosted texture, fiber pattern or geometric error modeling.