CN205885190U - Enamel cast iron bowl - Google Patents

Abstract

The utility model discloses an enamel cast iron bowl, including the fashioned base member of integrative manufacturing, the base member is followed including bowl wall, the bowl end and bowl, the base member is by an interior cover glaze layer, the first ground coat, cast iron layer, the second ground coat, insulating layer and the 2nd cover glaze layer of including in proper order outside to, bowl wall upper portion is provided with the convex part, and the convex part is 45~120 with the bowl angle that the wall became. The utility model discloses a setting up enamel cast iron bowl's structure into a cover glaze layer, the first ground coat, cast iron layer, the second ground coat, insulating layer and the 2nd cover glaze layer, simultaneously setting up the convex part on bowl wall upper portion, the convex part is 45~120 with bowl angle that the wall became for not only the outward appearance is good, hardness is high, the excellent wearability for enamel cast iron bowl, and the thermal insulation is high, and the staff can direct contact holds the enamel cast iron bowl of high temperature material.

Description

A kind of enamelled cast iron bowl

Technical field

This utility model is related to table ware field, more particularly, to a kind of enamelled cast iron bowl.

Background technology

Bowl, as the daily necessary foods utensil of people, is often used in holding liquid or semi-fluid object, due to enamel casting Ferrum bowl is made of cast iron, and its heat conductivility is high relative to for china bowl.When by filling the liquid of boiling or semi-fluid object, ward off The temperature of porcelain cast iron bowl is higher, and staff cannot directly contact.

Utility model content

In view of this, the enamelled cast iron bowl that this utility model provides, the current enamelled cast iron bowl temperature of solution is higher, and staff is no The technical problem of method directly contact.

The technical solution of the utility model is achieved in that

A kind of enamelled cast iron bowl, including the matrix of integrally manufactured molding；Described matrix includes bowl wall, bowl bottom and bowl edge；

Described matrix includes the first cover coat, the first ground glaze layer, cast iron layer, the second ground glaze layer, heat-insulated from inside to outside successively Layer and the second cover coat；

Described bowl wall top is provided with protuberance, and described protuberance is 45～120 ° with described bowl wall angulation.

Preferably, described first ground glaze layer and described second ground glaze layer are unorganic glass matter ground glaze layer；Described first face Glaze layer and described second cover coat are unorganic glass matter cover coat；Described thermal insulation layer is silica gel.

Preferably, the thickness of described non-sticking lining is 0.1～0.3mm；The thickness of described first ground glaze layer be 0.05～ 0.2mm；The thickness of described cast iron layer is 1～2mm；The thickness of described second ground glaze layer is 0.1～0.2mm；Described thermal insulation layer Thickness is 1～2mm；The thickness of described second cover coat is 0.15～0.3mm.

The beneficial effects of the utility model are:

This utility model pass through by the structure setting of enamelled cast iron bowl be the first cover coat, the first ground glaze layer, cast iron layer, the Two ground glaze layers, thermal insulation layer and the second cover coat, are arranging protuberance on bowl wall top, protuberance and bowl wall angulation are 45 simultaneously ～120 ° so that enamelled cast iron bowl not only outward appearance is good, hardness is high, wearability good, and thermal insulation is high, and staff can be with directly contact It is contained with the enamelled cast iron bowl of high temperature material.

Brief description

In order to be illustrated more clearly that this utility model embodiment or technical scheme of the prior art, below will be to embodiment Or in description of the prior art the accompanying drawing of required use be briefly described it should be apparent that, drawings in the following description are only It is some embodiments of the present utility model, for those of ordinary skill in the art, in the premise not paying creative work Under, other accompanying drawings can also be obtained according to these accompanying drawings.

Fig. 1 is the structural representation of this utility model enamelled cast iron bowl；

Fig. 2 is the structural representation of matrix in Fig. 1.

In figure:

1st, matrix；101st, the first cover coat；102nd, the first ground glaze layer；103rd, cast iron layer；104th, the second ground glaze layer；105th, every Thermosphere；106th, the second cover coat；2nd, bowl wall；3rd, bowl bottom；4th, bowl edge；5th, protuberance.

Specific embodiment

Below in conjunction with the accompanying drawing in this utility model embodiment, the technical scheme in this utility model embodiment is carried out Clearly and completely description is it is clear that described embodiment is only a part of embodiment of this utility model rather than whole Embodiment.Based on the embodiment in this utility model, those of ordinary skill in the art are not under the premise of making creative work The every other embodiment being obtained, broadly falls into the scope of this utility model protection.

As shown in Figure 1 and Figure 2, the enamelled cast iron bowl of offer of the present utility model, including the matrix 1 of integrally manufactured molding；Base Body 1 includes bowl wall 2, bowl bottom 3 and bowl along 4；Matrix 1 includes the first cover coat 101, the first ground glaze layer 102, casting from inside to outside successively Iron layer 103, the second ground glaze layer 104, thermal insulation layer 105 and the second cover coat 106；Bowl wall 2 top is provided with protuberance 5, protuberance 5 and bowl Wall 2 angulation is 45～120 °.

In technique scheme, matrix 1 is shaped by die casting, then through careful polishing setting, the method manufacture obtains Matrix 1 there is very high shock strength；Bowl wall 2, bowl bottom 3 and bowl, along 4 regions defining a upper end open, are easy to hold Liquid or semi-fluid object；By the structure setting of matrix 1 is the first cover coat 101, the first ground glaze layer 102, cast iron layer 103rd, the second ground glaze layer 104, thermal insulation layer 105 and the second cover coat 106 so that enamelled cast iron bowl not only outward appearance is good, hardness is high, resistance to Mill property is good, and thermal insulation is high；In order to directly contact is contained with the enamelled cast iron bowl of high temperature material, arrange convex on bowl wall 2 top Portion 5, protuberance 5 is 45～120 ° with bowl wall 2 angulation；By using the technical scheme of above-mentioned matrix 1 and the technology of protuberance 5 Scheme so that enamelled cast iron bowl not only outward appearance is good, hardness is high, wearability good, and thermal insulation is high, and staff can be contained with directly contact It is placed with the enamelled cast iron bowl of high temperature material.

It should be noted that in order to improve the adhesion strength between each layer of enamelled cast iron, the first ground glaze layer 102 and the second bottom Glaze layer 104 is unorganic glass matter ground glaze layer, and the first cover coat 104 and the second cover coat 106 are unorganic glass matter cover coat, every Thermosphere 105 be silica gel, the enamelled cast iron bowl of this structure while making, between each layer, there is high bond strength, enamelled cast iron bowl Outward appearance good.

It should be noted that when the thickness of the first cover coat 101 is 0.1～0.3mm；The thickness of the first ground glaze layer 102 is 0.05～0.2mm；The thickness of cast iron layer 103 is 1～2mm；The thickness of the second ground glaze layer 104 is 0.1～0.2mm；Thermal insulation layer 105 Thickness be 1～2cm；When the thickness of the second cover coat 106 is 0.15～0.3mm, the thermal insulation of enamelled cast iron bowl is good.

The foregoing is only preferred embodiment of the present utility model, not in order to limit this utility model, all this Within the spirit of utility model and principle, any modification, equivalent substitution and improvement made etc., should be included in this utility model Protection domain within.

Claims (3)

1. a kind of enamelled cast iron bowl is it is characterised in that include the matrix (1) of integrally manufactured molding；Described matrix (1) includes bowl wall (2), bowl bottom (3) and bowl edge (4)；

Described matrix (1) include successively from inside to outside the first cover coat (101), the first ground glaze layer (102), cast iron layer (103), Two ground glaze layers (104), thermal insulation layer (105) and the second cover coat (106)；

Described bowl wall (2) top is provided with protuberance (5), and described protuberance (5) and described bowl wall (2) angulation be 45～ 120°.

2. enamelled cast iron bowl as claimed in claim 1 is it is characterised in that described first ground glaze layer (102) and described second bottom Glaze layer (104) is unorganic glass matter ground glaze layer；Described first cover coat (101) and described second cover coat (106) are inorganic Nature of glass cover coat；Described thermal insulation layer (105) is silica gel.

3. enamelled cast iron bowl as claimed in claim 1 it is characterised in that described first cover coat (101) thickness be 0.1～ 0.3mm；The thickness of described first ground glaze layer (102) is 0.05～0.2mm；The thickness of described cast iron layer (103) is 1～2mm；Institute The thickness stating the second ground glaze layer (104) is 0.1～0.2mm；The thickness of described thermal insulation layer (105) is 1～2mm；Described second face The thickness of glaze layer (106) is 0.15～0.3mm.