CN205871399U - Multi -functional decoration note paper of soft environmental protection - Google Patents
Multi -functional decoration note paper of soft environmental protection Download PDFInfo
- Publication number
- CN205871399U CN205871399U CN201620609236.XU CN201620609236U CN205871399U CN 205871399 U CN205871399 U CN 205871399U CN 201620609236 U CN201620609236 U CN 201620609236U CN 205871399 U CN205871399 U CN 205871399U
- Authority
- CN
- China
- Prior art keywords
- composite bed
- hot composite
- hot
- sheet material
- material layers
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model discloses a multi -functional decoration note paper of soft environmental protection decorates the note paper and has the lamellar structure, includes heat recombination layer A (2), foam sheet layer (3), heat recombination layer B (4), substrate layer (5) from top to bottom in proper order. There is pattern layer (1) in printing of heat recombination layer A's (2) surface and/or suppression. The utility model discloses a decorate the note paper and have fire -retardant, mould proof, performance such as antibiotic, syllable -dividings, thermal -insulated, dampproofing, waterproof, decorate the note paper simultaneously and have better compliance, improve the security of decoration note paper application.
Description
Technical field
This utility model relates to a kind of soft environment protection multifunctional decoration paper.
Background technology
Expanded material has good shock-absorbing capacity and is widely used, current PVC foam material be Application comparison widely
Decoration paper, but the decoration paper kind of employing PVC foam processing and manufacturing is more single, and the CBA used exists
Foaming process decomposes not exclusively, leaves residue in the substrate, not only affect the performance of decoration paper product, and easily
Cause the pollution of environment.The diversified demand of people, when being used for example as interior material or packaging material, Ren Menyao can not be met
Ask decoration paper in addition to attractive in appearance, environmental protection, also to have fire-retardant, mildew-resistant, antibacterial, sound insulation, the function such as heat insulation, moistureproof, waterproof, simultaneously
Having pliability, improve the safety of application, this complex function decoration paper is rarely found.
Summary of the invention
In order to solve the problems referred to above, this utility model provides soft environment protection multifunctional decoration paper, and this decoration paper has
There are fire-retardant, mildew-resistant, antibacterial, sound insulation, the performance such as heat insulation, moistureproof, waterproof, there is preferable shock-absorbing capacity, and environmental protection, one-tenth simultaneously
This is low.
This utility model be the technical scheme is that
A kind of soft environment protection multifunctional decoration paper, described decoration paper has layer structure, includes the most successively
Hot composite bed A, foamed sheet sheet material layers, hot composite bed B and substrate layer.
Described heat is combined the upper surface of A layer and also prints and/or be suppressed with pattern layer.
Described substrate layer is flexible parent metal, and material is the one in paper, paper tinsel, non-woven fabrics, woven cloth, thickness be 0.1～
0.7mm, all comprises vistanex in described hot composite bed A and hot composite bed B, described foamed sheet sheet material layers is by foamed plastic or sends out
Bubble rubber is made, and the apparent density of described foamed sheet sheet material layers is 0.02～0.60g/cm3, average pore size is 50～300 μm, 50%
Compression stress during compression is 50～230kPa, and thickness is 0.5～4mm.
Described hot composite bed A, foamed sheet sheet material layers and hot composite bed B are at least added with in the material of a layer fire retardant,
One or more in antibacterial, antifungus agent.
Described printed patterns decorative pattern is intaglio printing, letterpress, flexographic printing, silk screen printing, laser offset printing, heat
One in transfer.
Described substrate layer, preferably flexible parent metal, material is the one in paper, paper tinsel, non-woven fabrics, woven cloth, and thickness is
0.1～0.7mm.In the case of the thickness of substrate layer is less than 0.1mm, during there is construction or using, produce decoration paper
Split the worry of equivalent damage, in the case of more than 0.7mm, make decoration paper become weight, produce crack and crimp, cause difficulty
With construction.
The apparent density of described foamed sheet sheet material layers is preferably 0.02～0.60g/cm3.If apparent density is less than 0.02g/cm3
Time, then come into question in terms of intensity, it is impossible to obtain good processability, if apparent density is more than 0.60g/cm3Time, then soft
Property reduce, impact absorbency is poor, shock-absorbing capacity reduction.
The average pore size of described foamed sheet sheet material layers is preferably 50～300 μm.In this pore diameter range, on the one hand owing to sending out
The loose structure of bubble sheet layer, when decoration paper receives the energy of vibration source, owing to material internal has the biggest in-fighting,
Energetic solution transmission come absorbs, and buffering effect is best.On the other hand, owing to having individual blisters structure, air in hole
Heat conductivity is the least, interconnects between abscess and abscess, makes acoustic wave energy be attenuated, and has the most heat insulation, sound insulation value.
From flexibility and the impact absorbency of raising decoration paper, for ensureing the intensity of decoration paper, described simultaneously
Compression stress when the 50% of bubble sheet layer compresses is preferably 50～230kPa.
To foam sheet layer thickness of the present utility model, there is no particular limitation, from obtaining the resiliency of decoration paper, preventing
Mould, antibacterial, sound insulation, heat insulation, moistureproof, waterproof etc. functional, from the point of view of ensureing the aesthetic property of decoration paper, thickness is preferably simultaneously
0.5～4mm.
For as foamed sheet sheet material layers of the present utility model, it is preferred to use the one in foamed plastic, bipeltate is made.
For the raw material of foamed plastic, there is no particular limitation, the most preferably list Low Density Polyethylene, in
Density polyethylene, high density polyethylene (HDPE), wire Low Density Polyethylene, polypropylene, ethylene and the copolymer of propylene, ethylene or propylene
Copolymer, ethylene and other olefinics with other alpha-olefins (such as butene-1, amylene-1, hexene-1,4-methylpentene-1 etc.)
Unsaturated monomer (such as vinyl acetate, acrylic acid, acrylate, methacrylic acid, methacrylate, vinyl alcohol etc.)
The polyolefin resins such as copolymer；The phenylethylene trees such as polystyrene, acrylonitrile-butadiene-styrene copolymer (ABS resin)
Fat；The polyamide-based resins such as 6-nylon, 66-nylon, 12-nylon；Polyamidoimide；Polyurethane；Polyimides；Polyetherimide
Amine；The acrylic resins such as polymethyl methacrylate；Polrvinyl chloride；Polyvinyl fluoride；Alkenylaromatic hydroxy-aromatic resin；Poly-to benzene two
The polyester resins such as formic acid glycol ester, polybutylene terephthalate (PBT)；The Merlon such as Bisphenol-A based polycarbonate；Bunching
Aldehyde；Polyphenylene sulfides etc., it should be noted that foamed plastic layer can be used alone or is used in combination of two or more.
For the raw material of bipeltate, there is no particular limitation, the most preferably lists natural rubber, poly-isobutyl
Natural rubber or the synthetic rubber such as alkene, polyisoprene, neoprene, ethylene propylene diene rubber, butyl rubber, nitrile rubber, this
A little rubber constituents can be used alone or are used in combination of two or more.
For composite bed A hot in this utility model and the raw material of hot composite bed B, there is no particular limitation, from improving and sending out
From the point of view of the compatibility of bubble sheet layer, preferred polyolefm resin, the most preferably list polyethylene, polypropylene, polybutene, poly-fourth
Diene, polyisoprene, ethylene-methyl acrylate copolymer, ethylene-ethyl acrylate copolymer, ethylene-(methyl) acrylic acid
Copolymer, vinyl-vinyl acetate copolymer, vinyl-vinyl acetate copolymer saponified, ionomer in one or several
Kind.
Preferably, in order to strengthen fire-retardant, the mildew-resistant of decoration paper, antibacterial, sound insulation, the performance such as heat insulation, moistureproof, waterproof, institute
State in hot composite bed A, foamed sheet sheet material layers or hot composite bed B and be further added with the auxiliary agents such as fire retardant, antibacterial, antifungus agent.Make
For auxiliary agent, it is not particularly limited, such as, can enumerate 8-hydroxyquinoline ketone, organosilicon quaternary ammonium salt, nanometer silver, aluminium hydroxide, swollen
Swollen property graphite, magnesium hydroxide, antimony trioxide, zinc oxide, copper oxide, ammonium dihydrogen phosphate, lithium carbonate, Kazon etc..These auxiliary agents were both
Can be used alone a kind, it is also possible to combine several used above.
Described decoration paper has shock-absorbing capacity, when stress is 2～1000kPa, minimum static buffering coefficient be 3.2～
6.Cushioning coefficient is the least, represents that the energy that padded coaming unit volume absorbs is the most, thus buffering efficiency is the highest, minimum buffer system
Number typicallys represent the optimal use state of padded coaming.Minimum static buffering coefficient of the present utility model is surveyed by static experiment method
, described decoration paper, when stress is 2～1000kPa, can play good cushioning effect, it is achieved buffering energy-absorbing, carry
The safety of high decoration paper application.
Preferably, the preparation method of described soft environment protection multifunctional decoration paper is: hot composite bed A and foam sheet
Layer, foamed sheet sheet material layers and hot composite bed B, hot composite bed B and substrate layer be all be combined good bond by heat together with, answer in heat
Close layer A surface printing and/or be suppressed with pattern layer, post processing, packaging, obtain soft environment protection multifunctional decoration paper.
Described hot complex method can include the compression process of hot-rolling, flame recombination laser treatment with irradiation, heated
The one of the contact melt process on roller.From improving decoration paper each interlaminar bonding fastness, ensure the basis of foamed sheet sheet material layers simultaneously
From the point of view of body structure and performance, it is preferred to use flame assembly machine carries out hot Combined Processing, and hot combined temp is 110～280 DEG C, heat is multiple
The speed of related movement closed between layer and flame assembly machine flame is 20～35m/min.
Fire row device on flame assembly machine is set to 4-8 row, flame hole by rows on fire row device, adjacent two
Flame hole spacing is 20-40mm, and adjacent two flame holes of adjacent rows are dislocation arrangement.So ensure hot combined temp
Precision, avoids hot combined temp uneven simultaneously, causes respective material retraction in flame recombination process to change, fall
Low to substrate layer fibre morphology and the requirement of foamed sheet sheet material layers apparent condition.
In this utility model, hot composite bed A upper print pattern layer give the multiple decorative pattern of decoration paper and/or
Color, such that it is able to more improve aesthetic.Now, the method for printing is not particularly limited, it is, for example possible to use intaglio plate
The known printing process such as printing, letterpress, flexographic printing, silk screen printing, laser offset printing, thermal transfer.
Soft environment protection multifunctional decoration paper described in the utility model is used as ornament materials, including interior material and packaging
Material.As interior material, it is used for example as interior trim wallpaper, especially in amusement of children garden, unavoidably deposits in active procedure
Falling, unexpected, the phenomenon touched, particularly when the child in chasing is run along wall, the least meeting bumps against wall, and causes wound
Evil, therefore, the wall fitting of special occasions such for amusement of children garden needs to particularly contemplate the softness of wall fitting paper using
And shock-absorbing capacity, soft environment protection multifunctional decoration paper described in the utility model is permissible because of its excellent softness and shock-absorbing capacity
Improve the safety coefficient of application, give fire-retardant, mildew-resistant, antibacterial, sound insulation, the performance such as heat insulation, moistureproof, waterproof simultaneously.Simultaneously as
Packaging material, are giving outside attractive in appearance, environmental protection, are also giving identical multifunctionality.
Beneficial effect: soft environment protection multifunctional decoration paper that this utility model provides and preparation method thereof and prior art
In conventional decoration paper compare and have the advantage that
1, decoration paper uses many layer structures, by the hot complex technique of flame, it is achieved that the directly heat of each interlayer is compound,
Avoid High Temperature High Pressure structure to foamed sheet sheet material layers own and the damage of performance, eliminate coating technique, eliminate tradition glue
The solvent contamination of method, reduces substrate layer fibre morphology and the requirement of foamed sheet sheet material layers apparent condition, and plastic performance is good.Can
To select different foamed sheet sheet material layers according to demand, it is ensured that decoration paper, when stress is 2～1000kPa, can play
Well cushioning effect, it is achieved buffering energy-absorbing, minimum cushioning coefficient is 3.2～6.
2, during hot composition process can meet foamed sheet sheet material layers, apparent density, aperture, expansion ratio, compression stress are wanted
Ask, it is also possible in the material of hot composite bed A, foamed sheet sheet material layers or hot composite bed B, add fire retardant, antibacterial further, prevent
Mould dose, it is achieved that decoration paper is had fire-retardant, mildew-resistant, antibacterial, sound insulation, the multi-functional demand such as heat insulation, moistureproof, waterproof.
Method of testing:
Apparent density measures
The apparent density of foamed sheet sheet material layers is to measure based on the method described in GB/T6343-2009.Along laterally side
To the parallel sample taking 5 10000 × 10000mm, measure its average thickness and quality.
ρaApparent density, unit is kilogram every cubic metre of (kg/m3)
The quality of m sample, unit is gram (g)
maThe quality of air-out, unit is gram (g)
The volume of V sample, unit is cubic millimeter (mm3)
Average pore size
Read the enlarged drawing picture in foamed sheet sheet material layers aperture by digit microscope, measure the certain area at section
(1mm2The area of the whole abscesses manifested in), after carrying out equivalent circle diameter conversion, is averaged with abscess number, thus obtains flat
All apertures.
Thickness measurement
Substrate layer described in the utility model is based on the method described in GB/T6672-2001 with the thickness of foamed sheet sheet material layers
Measure.At sample longitudinal end about 1m, the most whole width intercepts sample, sample width 100mm, long 1000mm,
Using thickness measurement equipment that 20 positions of sample are carried out thickness measurement, average thickness is the arithmetic mean of instantaneous value of all measured values.
Compression stress during 50% compression measures
Compression stress when foamed sheet sheet material layers 50% is compressed is to measure based on the method described in GB/T18942.1-2003
's.
Minimum static buffering coefficient determination
The minimum static buffering coefficient of soft environment protection multifunctional decoration paper described in the utility model is based on GBT 8168-
Method described in 2008 measures.
Accompanying drawing illustrates:
Fig. 1 is the vertical section structure schematic diagram of decoration paper described in the utility model.
In figure: 1, pattern layer；2, hot composite bed A；3, foamed sheet sheet material layers；4, hot composite bed B；5, substrate layer.
Detailed description of the invention:
With embodiment, content of the present utility model is described further below in conjunction with the accompanying drawings.
Embodiment one:
Substrate layer 5 selects the non-woven fabrics that the slurry of 70%, the polyester of 30% are formed, and thickness is 0.1mm.
Hot composite bed A2 is polyvinyl resin (Central Plains petrochemical industry, model: 7050).
Foamed sheet sheet material layers 3 uses commercially available polyolefin (polyethylene) foam sheet (Changzhou three and plastic cement, model L-4500),
The apparent density of foamed sheet sheet material layers 3 is 0.02g/cm3, average pore size be 180 μm, 50% compression time compression stress be 50kPa,
Thickness is 0.5mm.
Hot composite bed B4 is acrylic resin (raising sub-petrochemical industry, model: F401).
Hot composite bed B4, foamed sheet sheet material layers 3 are used hot melt compounding machine to carry out heat with substrate layer 5 and be combined, hot combined temp
110 DEG C, selecting flame assembly machine to be combined with hot composite bed A2 foamed sheet sheet material layers 3, wherein fire row device is set to 4 row,
Flame hole is by rows on fire row device, and adjacent two flame hole spacing are 20mm, and adjacent two flames of adjacent rows
Mouth is dislocation arrangement, and hot combined temp is 110 DEG C, and the speed of related movement between hot composite bed A2 and flame assembly machine flame is
For 20m/min, then, the outer surface to hot composite bed A2, i.e. in Fig. 1, the upper surface of hot composite bed A2 carries out sided corona treatment, makes
Formed on hot composite bed A2 surface with the coating of pigment with intaglio printing, be dried, again through upper at hot composite bed A2 of embossing
The embossing aspect of raised or sunken structure is made on surface, thus constitutes pattern flower-pattern layer 1, cooling, obtains soft environment protection multifunctional
Decoration paper.When stress is 140kPa, minimum static buffering coefficient is 4.5.
Described pattern layer 1 can be hot composite bed A2 upper surface by made by printing process with pigment
Coating, it is also possible to be by the rat made by embossing procedure or the embossing of sunk structure at hot composite bed A2 upper surface
Aspect, it is also possible to be as set forth in the present embodiment by printing and the coating with pigment made by embossing and described embossed layer
The structure that face is overlapping.
Embodiment two:
Substrate layer 5 selects pure paper, and thickness is 0.5mm.
Hot composite bed A2 is ethylene vinyl acetate copolymer (Atofina of France, model: 2805).
Foamed sheet sheet material layers 3 uses commercially available polyurethane foam sheet (chain of mountains gluing, model LM), foamed sheet sheet material layers apparent
Density is 0.20g/cm3, average pore size be 50 μm, 50% compression time compression stress be 230kPa, thickness be 2mm.
Hot composite bed B4 is ethylene vinyl acetate copolymer (Atofina of France, model: 2805).
Hot composite bed B4, foamed sheet sheet material layers 3 are used hot melt compounding machine to carry out heat with substrate layer 5 and be combined, hot combined temp
150 DEG C, selecting flame assembly machine to be combined with hot composite bed A2 foamed sheet sheet material layers 3, thermal composite machine selects flame assembly machine,
Wherein fire row device is set to 8 row, and flame hole is by rows on fire row device, and adjacent two flame hole spacing are 30mm, and
Adjacent two flame holes of adjacent rows are dislocation arrangement, and hot combined temp is 280 DEG C, hot composite bed A2 and flame assembly machine fire
Speed of related movement between flame is 25m/min, then, the upper surface of hot composite bed A2 is carried out sided corona treatment, uses flexibility
Version is printed on hot composite bed A2 surface and forms pattern layer 1, through being dried, cooling down, obtains soft environment protection multifunctional decoration and uses
Paper.When stress is 10kPa, minimum static buffering coefficient is 3.2.
Embodiment three:
Substrate layer 5 selects aluminium foil, and thickness is 0.2mm.
Hot composite bed A is acrylic resin (Maoming Petrochemical, model T36F).
Foamed sheet sheet material layers uses commercially available Duprene rubber foamed sheet material (the most precious macromolecule, model YB-3025), foam sheet
The apparent density of layer is 0.15g/cm3, average pore size be 300 μm, 50% compression time compression stress be 200kPa, thickness be
3mm。
Hot composite bed B is acrylic resin (Maoming Petrochemical, model T36F).
Hot composite bed B4, foamed sheet sheet material layers 3 are used hot melt compounding machine to carry out heat with substrate layer 5 and be combined, hot combined temp
230 DEG C, selecting flame assembly machine to be combined with hot composite bed A2 foamed sheet sheet material layers 3, wherein fire row device is set to 6 row,
Flame hole is by rows on fire row device, and adjacent two flame hole spacing are 30mm, and adjacent two flames of adjacent rows
Mouth is dislocation arrangement, and hot combined temp is 220 DEG C, and the speed of related movement between hot composite bed and flame assembly machine flame is
22m/min, then, carries out sided corona treatment to hot composite bed A2 upper surface, uses letterpress at the upper surface of hot composite bed A2
Form pattern bonding layer, through dry, then embossing, prepare pattern layer 1, cooling on hot composite bed A2 surface, to obtain final product
To soft environment protection multifunctional decoration paper.When stress is 20kPa, minimum static buffering coefficient is 6.
Embodiment four:
Substrate layer 5 selects woven cloth, and thickness is 0.7mm.
Hot composite bed A2 is polyvinyl resin (Central Plains petrochemical industry, model: 7050).
Foamed sheet sheet material layers 3 uses commercially available nitrile rubber foam sheet (wide abundant rubber and plastic, model NKX-55), foamed sheet sheet material layers
Apparent density be 0.06g/cm3, average pore size be 70 μm, 50% compression time compression stress be 150kPa, thickness be 4mm.
Hot composite bed B4 is polyvinyl resin (Central Plains petrochemical industry, model: 7050).
Hot composite bed B4, foamed sheet sheet material layers 3 are used hot melt compounding machine to carry out heat with substrate layer 5 and be combined, hot combined temp
230 DEG C, selecting flame assembly machine to be combined with hot composite bed A2 foamed sheet sheet material layers 3, wherein fire row device is set to 4 row,
Flame hole is by rows on fire row device, and adjacent two flame hole spacing are 30mm, and adjacent two flames of adjacent rows
Mouth is dislocation arrangement, and hot combined temp is 200 DEG C, the speed of related movement between hot composite bed A2 and flame assembly machine flame
25m/min, then, carries out sided corona treatment to the upper surface of hot composite bed A2, uses and be screen printed onto the formation of hot composite bed A surface
Pattern bonding layer, through dry, then embossing, forms pattern layer 1, cooling, obtains soft ring on hot composite bed A surface
Protect multifunction decorative paper using.When stress is 1000kPa, minimum static buffering coefficient is 3.6.
Embodiment five:
Hot composite bed A2 is based on ethylene and ethylene-methyl acrylate copolymer, and sheet thickness is 0.1mm.
The foamed sheet sheet material layers 3 foaming body with polyurethane as main constituent, the apparent density of foamed sheet sheet material layers is 0.08g/cm3、
Average pore size be 180 μm, 50% compression time compression stress be 110kPa, thickness be 1.5mm.
Hot composite bed B4 is the sheet material based on polyurethane, and sheet thickness is 0.05mm.
On substrate layer 5, heat is combined hot composite bed B4, foamed sheet sheet material layers 3 and hot composite bed A2, thermal composite machine successively
Select flame assembly machine, wherein fire row device is set to 4 row, flame hole by rows on fire row device, adjacent two flames
Mouth spacing is 20mm, and adjacent two flame holes of adjacent rows are dislocation arrangement, and hot combined temp is 110 DEG C, and heat is combined
Relative between each aspect i.e. substrate layer 5, hot composite bed B4, foamed sheet sheet material layers 3 and hot composite bed A2 and flame assembly machine flame
Movement velocity is 20m/min, after heat has been combined, the upper surface of hot composite bed A2 is carried out sided corona treatment, uses intaglio process
Brush and form pattern layer 1 at hot composite bed A2 surface printing, through being dried, cooling down, obtain soft environment protection multifunctional decoration and use
Paper.When stress is 140kPa, minimum static buffering coefficient is 4.5.
Embodiment six:
Substrate layer 5 selects pure paper, and thickness is 0.5mm.
Hot composite bed A2 is the sheet material based on polybutadiene, and sheet thickness is 0.2mm.
The foamed sheet sheet material layers 3 foaming body with polyurethane as main constituent, the apparent density of foamed sheet sheet material layers 3 is 0.60g/cm3、
Average pore size be 300 μm, 50% compression time compression stress be 230kPa, thickness be 2mm.
Hot composite bed B4 is the sheet material based on polyethylene, and sheet thickness is 0.1mm.
On foamed sheet sheet material layers 3, heat is combined hot composite bed A2 successively, on foamed sheet sheet material layers 3 heat in turn below is compound
Hot composite bed B4, hot composite base sheet material layers 5 below hot composite bed B4, thermal composite machine selects flame assembly machine, wherein fire row device
Being set to 8 row, flame hole is by rows on fire row device, and adjacent two flame hole spacing are 30mm, and the phase of adjacent rows
Adjacent two flame holes are dislocation arrangement, and hot combined temp is 180 DEG C, the compound each aspect such as substrate layer 5 of heat, hot composite bed B4,
Speed of related movement between foamed sheet sheet material layers 3 and hot composite bed A2 and flame assembly machine flame is 25m/min, through overdrying
Dry, cooling, obtains the soft environment protection multifunctional decoration paper of hot composite bed A2 surface pattern-free flower-pattern layer 1.It is 10kPa at stress
Time, minimum static buffering coefficient is 3.2.
Embodiment seven:
Step is with embodiment six, and difference is: heat be combined after, first pass through dry, again be embossed heat answer
Close layer A2 surface and form pattern layer 1, then cool down, obtain soft environment protection multifunctional decoration paper.
Embodiment eight:
Substrate layer 5 selects aluminium foil, and thickness is 0.2mm.
Hot composite bed A2 is based on ethylene-ethyl acrylate copolymer, the sheet of ethylene-(methyl) acrylic copolymer
Material, thickness is 0.2mm.
Foamed sheet sheet material layers 3 is the foaming body made with natural rubber and butyl rubber, and the apparent density of foamed sheet sheet material layers 3 is
0.45g/cm3, average pore size be 300 μm, 50% compression time compression stress be 200kPa, thickness be 3mm.
Hot composite bed B4 be material be the sheet material of polrvinyl chloride, thickness is 0.3mm.
Hot composite bed A2 and hot composite bed B4 the auxiliary agents such as fire retardant, antibacterial, antifungus agent have been also added with.Such as fire retardant phosphorus
Acid dihydride ammonium, antibacterial copper oxide, antifungus agent nanometer silver.
On substrate layer 5, heat is combined hot composite bed B4, foamed sheet sheet material layers 3 and hot composite bed A2, thermal composite machine successively
Select flame assembly machine, wherein fire row device is set to 6 row, flame hole by rows on fire row device, adjacent two flames
Mouth spacing is 30mm, and adjacent two flame holes of adjacent rows are dislocation arrangement, and hot combined temp is 220 DEG C, and heat is combined
Speed of related movement between each aspect and flame assembly machine flame is 22m/min, after heat has been combined, to hot composite bed A2's
Upper surface carries out sided corona treatment, uses letterpress to form pattern bonding layer at hot composite bed A2 surface printing, through being dried,
It is embossed formation pattern layer 1 again, then cools down, obtain soft environment protection multifunctional decoration paper.It is 20kPa at stress
Time, minimum static buffering coefficient is 6.
Embodiment nine:
Substrate layer 5 selects the woven cloth made with polypropylene, the third polyethylene, and thickness is 0.7mm.
Hot composite bed A2 be material be polyacrylic sheet material, thickness is 0.5mm.
The foamed sheet sheet material layers 3 foaming body with polystyrene as main constituent, the apparent density of foamed sheet sheet material layers 3 is 0.03g/
cm3, average pore size be 70 μm, 50% compression time compression stress be 150kPa, thickness be 4mm.
Hot composite bed B4 be material be vinyl-vinyl acetate copolymer or polyacrylic sheet material, thickness is 0.3mm.
Described foamed sheet sheet material layers 3 and/or hot composite bed B4 the auxiliary agents such as fire retardant, antibacterial, antifungus agent have been also added with.As
8-hydroxyquinoline ketone, organosilicon quaternary ammonium salt, nanometer silver, aluminium hydroxide, expansile graphite, magnesium hydroxide, antimony trioxide, oxidation
Zinc, copper oxide, ammonium dihydrogen phosphate, lithium carbonate, Kazon etc..These auxiliary agents both can be used alone a kind, it is also possible to combine several with
Upper use, its consumption is conventional amount used, in the present embodiment, has been also added with fire retardant antimony trioxide, antibacterial organosilicone quaternary ammonium
Salt, Fungicides Casson.
On substrate layer 5, heat is combined hot composite bed B4, foamed sheet sheet material layers 3 and hot composite bed A2, thermal composite machine successively
Select flame assembly machine, wherein fire row device is set to 4 row, flame hole by rows on fire row device, adjacent two flames
Mouth spacing is 30mm, and adjacent two flame holes of adjacent rows are dislocation arrangement, and hot combined temp is 260 DEG C, and heat is combined
Speed of related movement 30m/min between each aspect and flame assembly machine flame, after heat has been combined, upper to hot composite bed A2
Surface carries out sided corona treatment, uses and is screen printed onto hot compound A layer surface formation pattern layer 1, through being dried, cooling down,
To soft environment protection multifunctional decoration paper.When stress is 1000kPa, minimum static buffering coefficient is 3.6.
Embodiment ten:
Substrate layer 5 selects the woven cloth made with polypropylene, the third polyethylene, and thickness is 0.7mm.
Hot composite bed A2 be material be the sheet material of Merlon, thickness is 0.5mm.
Foamed sheet sheet material layers 3 is the foam sheet that Merlon is made, and the apparent density of foamed sheet sheet material layers 3 is 0.30g/cm3、
Average pore size be 70 μm, 50% compression time compression stress be 150kPa, thickness be 4mm.
Hot composite bed B4 be material be the sheet material of vinyl-vinyl acetate copolymer or Merlon, thickness is 1mm.
Described hot composite bed A2, foamed sheet sheet material layers 3 and hot composite bed B4 have been also added with fire retardant magnesium hydroxide.
On substrate layer 5, heat is combined hot composite bed B4, foamed sheet sheet material layers 3 and hot composite bed A2, thermal composite machine successively
Select flame assembly machine, wherein fire row device is set to 4 row, flame hole by rows on fire row device, adjacent two flames
Mouth spacing is 30mm, and adjacent two flame holes of adjacent rows are dislocation arrangement, and hot combined temp is 280 DEG C, and heat is combined
Speed of related movement 35m/min between each aspect and flame assembly machine flame, after heat has been combined, upper to hot composite bed A2
Surface carries out sided corona treatment, uses the existing printing processes such as flexographic printing, silk screen printing, laser offset printing or thermal transfer in heat
Composite bed A2 surface forms pattern layer 1, through being dried, cooling down, obtains soft environment protection multifunctional decoration paper.At stress it is
During 1000kPa, minimum static buffering coefficient is 4.5.
Embodiment 11:
Substrate layer 5 selects the woven cloth made with polypropylene, the third polyethylene, and thickness is 0.7mm.
Hot composite bed A2 be material be polyacrylic sheet material, thickness is 0.5mm.
Foamed sheet sheet material layers 3 be material be the foaming body of polystyrene, the apparent density of foamed sheet sheet material layers 3 is 0.10g/cm3、
Average pore size be 70 μm, 50% compression time compression stress be 150kPa, thickness be 4mm.
Hot composite bed B4 be material be vinyl-vinyl acetate copolymer or polyacrylic sheet material, thickness is 0.3mm.
Described foamed sheet sheet material layers 3 and/or hot composite bed B4 the auxiliary agents such as fire retardant, antibacterial, antifungus agent have been also added with.As
8-hydroxyquinoline ketone, organosilicon quaternary ammonium salt, nanometer silver, aluminium hydroxide, expansile graphite, magnesium hydroxide, antimony trioxide, oxidation
Zinc, copper oxide, ammonium dihydrogen phosphate, lithium carbonate, Kazon etc..These auxiliary agents both can be used alone a kind, it is also possible to combine several with
Upper use, its consumption is conventional amount used, in the present embodiment, has been also added with fire retardant magnesium hydroxide, antibacterial 8-hydroxyquinoline
Ketone.
On substrate layer 5, heat is combined hot composite bed B4, foamed sheet sheet material layers 3 and hot composite bed A2, thermal composite machine successively
Select flame assembly machine, wherein fire row device, be set to 4 row, flame hole by rows on fire row device, adjacent two flames
Mouth spacing is 30mm, and adjacent two flame holes of adjacent rows are dislocation arrangement, and hot combined temp is 260 DEG C, and heat is combined
Speed of related movement 30m/min between each aspect and flame assembly machine flame, after heat has been combined, upper to hot composite bed A2
Surface carries out sided corona treatment, uses laser offset printing to become pattern layer 1 at hot composite bed A surface printing, through being dried, cooling down,
Obtain soft environment protection multifunctional decoration paper.When stress is 1000kPa, minimum static buffering coefficient is 4.3.
Embodiment 12:
Step is with embodiment 11, and difference is: in hot recombination process, uses thermal transfer on hot composite bed A surface
Be printed as pattern bonding layer, in last handling process, first pass through dry, again be embossed formation pattern layer 1, the coldest
But, soft environment protection multifunctional decoration paper is obtained.
The above, be only preferred embodiment of the present utility model, not this utility model is made any in form
Restriction, although this utility model is disclosed above with preferred embodiment, but is not limited to this utility model, any ripe
Know professional and technical personnel, in the range of without departing from technical solutions of the utility model, when in the technology of available the disclosure above
Hold and make a little change or be modified to the Equivalent embodiments of equivalent variations, as long as without departing from technical solutions of the utility model
Hold, any simple modification, equivalent variations and modification above example made according to technical spirit of the present utility model, the most still
Belong in the range of technical solutions of the utility model.
Claims (4)
1. a soft environment protection multifunctional decoration paper, it is characterised in that: decoration paper has layer structure, the most successively
Including hot composite bed A, foamed sheet sheet material layers, hot composite bed B and substrate layer.
Soft environment protection multifunctional decoration paper the most according to claim 1, it is characterised in that: described heat is combined the upper of A layer
Surface is also printed and/or is suppressed with pattern layer.
Soft environment protection multifunctional decoration paper the most according to claim 1, it is characterised in that: described substrate layer thickness is
0.1～0.7mm, the apparent density of described foamed sheet sheet material layers is 0.02～0.60g/cm3, average pore size is 50～300 μm, 50%
Compression stress during compression is 50～230kPa, and thickness is 0.5～4mm.
Soft environment protection multifunctional decoration paper the most according to claim 1 and 2, it is characterised in that: described hot composite bed A,
Foamed sheet sheet material layers and hot composite bed B are at least added with in the material of a layer one in fire retardant, antibacterial, antifungus agent or
Several.