CN205853479U - A kind of anti-fouling glass - Google Patents
A kind of anti-fouling glass Download PDFInfo
- Publication number
- CN205853479U CN205853479U CN201620844975.7U CN201620844975U CN205853479U CN 205853479 U CN205853479 U CN 205853479U CN 201620844975 U CN201620844975 U CN 201620844975U CN 205853479 U CN205853479 U CN 205853479U
- Authority
- CN
- China
- Prior art keywords
- glass
- layer
- film
- fouling
- thickness
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
This utility model relates to glass technology field, is specifically related to a kind of anti-fouling glass.Including glass-base, glass-base is used PVB film bonding to form by the float glass of 3 layers, it is respectively glass inner layer, glass middle level and glass outer layer, glass inner layer or glass outer layer is provided with amorphous state magnesium fluoride film, amorphous state magnesium fluoride film is provided with optically catalytic TiO 2 film.The light transmission of this glass is good, and light transmittance is more than 90%, and self-cleaning property is good, is difficult to adhesion dust, and bonding dust on the glass surface or spot can be come off by sharp separation after being rushed by water.
Description
Technical field
This utility model relates to glass technology field, is specifically related to a kind of anti-fouling glass.
Background technology
Along with the development of low-carbon economy, energy-saving and cost-reducing type building, it has also become pursued by society especially builder
Cause.Transparent glass is used to be generally used as the way of constructure screen wall and door and window.This way effectively achieves room
Interior daylighting, keep out the wind and block conduction of heat and the heat radiation of outdoor air, improve and ensured indoor environment.But, existing curtain
Wall and glass door and window under irradiation by sunlight, and under the influence of outdoor cold and heat air, it will directly affect the temperature of indoor,
Heat insulation effect is undesirable.Furthermore precisely due to long-term practical glass outer surface is easily adhered dust, have a strong impact on the printing opacity of glass
Rate.And this glass is commonly used on the building that floor is higher, the scouring of glass is the most difficult.
Summary of the invention
The purpose of this utility model is to solve the problem that current glass is weak to cleaning, it is provided that a kind of anti-fouling glass.
In order to reach above-mentioned utility model purpose, this utility model by the following technical solutions:
A kind of anti-fouling glass, including glass-base, glass-base is used PVB film bonding to form by the float glass of 3 layers,
It is respectively glass inner layer, glass middle level and glass outer layer, glass inner layer or glass outer layer is provided with amorphous state Afluon (Asta) thin
Film, is provided with optically catalytic TiO 2 film on amorphous state magnesium fluoride film.
Preferably, described glass inner layer, be partly or entirely provided with poly-carbonic acid between glass middle level and glass outer layer
Ester layer.
Preferably, the thickness of described amorphous state magnesium fluoride film is 150-200nm.
Preferably, the thickness of described optically catalytic TiO 2 film is 80-130nm.
Preferably, the thickness of described glass inner layer, glass middle level and glass outer layer is 2-5mm.
Preferably, the thickness of Polycarbonate Layer is 1-3mm.
Preferably, glass-base is soda-lime glass, crystal glass or borosilicate glass.
This utility model compared with prior art, provides the benefit that: light transmission is good, and light transmittance is more than 90%, self-cleaning property
Good, it is difficult to adhesion dust, bonding dust on the glass surface or spot can be come off by sharp separation after being rushed by water.
Accompanying drawing explanation
Fig. 1 is structural representation of the present utility model.
In figure: 1 glass-base, 2 glass inner layer, 3 glass middle levels, 4 glass outer layer, 5 amorphous state magnesium fluoride films, 6 dioxies
Change titanium photocatalysis film, 7 Polycarbonate Layer.
Detailed description of the invention
Below by specific embodiment, the technical solution of the utility model is further described explanation.
Embodiment 1:
A kind of anti-fouling glass, as it is shown in figure 1, include glass-base 1, inner surface or outer surface at glass-base 1 are provided with
Functional layer, functional layer includes two-layer, and ground floor is amorphous state magnesium fluoride film 5, and amorphous state magnesium fluoride film 5 passes through vacuum evaporation
Or the method for sputtering deposit prepares, the second layer is the optically catalytic TiO 2 film 6 arranged on amorphous state magnesium fluoride film 5.
Glass-base 1 is used PVB film bonding to form by the float glass of 3 layers, respectively glass inner layer 2, glass middle level 3
With glass outer layer 4, functional layer is arranged on the surface of glass inner layer 2 or glass outer layer 4, at glass inner layer 2, glass middle level 3 and
Polycarbonate Layer 7 partly or entirely it is provided with between glass outer layer 4.
The thickness of glass inner layer 2 is 2mm, and the thickness 3 in glass middle level is 4mm, and the thickness of glass outer layer 4 is 5mm, poly-carbon
The thickness of acid esters layer 7 is 1mm, and the thickness of amorphous state magnesium fluoride film 5 is 160nm, and the thickness of optically catalytic TiO 2 film 6 is
130nm。
Glass-base 1 is soda-lime glass, crystal glass or borosilicate glass.
Embodiment 2:
A kind of anti-fouling glass, as it is shown in figure 1, include glass-base 1, inner surface or outer surface at glass-base 1 are provided with
Functional layer, functional layer includes two-layer, and ground floor is amorphous state magnesium fluoride film 5, and amorphous state magnesium fluoride film 5 passes through vacuum evaporation
Or the method for sputtering deposit prepares, the second layer is the optically catalytic TiO 2 film 6 arranged on amorphous state magnesium fluoride film 5.
Glass-base 1 is used PVB film bonding to form by the float glass of 3 layers, respectively glass inner layer 2, glass middle level 3
With glass outer layer 4, functional layer is arranged on the surface of glass inner layer 2 or glass outer layer 4, at glass inner layer 2, glass middle level 3 and
Polycarbonate Layer 7 partly or entirely it is provided with between glass outer layer 4.
The thickness of glass inner layer 2 is 3mm, and the thickness 3 in glass middle level is 5mm, and the thickness of glass outer layer 4 is 2mm, poly-carbon
The thickness of acid esters layer 7 is 2mm, and the thickness of amorphous state magnesium fluoride film 5 is 200nm, and the thickness of optically catalytic TiO 2 film 6 is
80nm。
Glass-base 1 is soda-lime glass, crystal glass or borosilicate glass.
Embodiment 3:
A kind of anti-fouling glass, as it is shown in figure 1, include glass-base 1, inner surface or outer surface at glass-base 1 are provided with
Functional layer, functional layer includes two-layer, and ground floor is amorphous state magnesium fluoride film 5, and amorphous state magnesium fluoride film 5 passes through vacuum evaporation
Or the method for sputtering deposit prepares, the second layer is the optically catalytic TiO 2 film 6 arranged on amorphous state magnesium fluoride film 5.
Glass-base 1 is used PVB film bonding to form by the float glass of 3 layers, respectively glass inner layer 2, glass middle level 3
With glass outer layer 4, functional layer is arranged on the surface of glass inner layer 2 or glass outer layer 4, at glass inner layer 2, glass middle level 3 and
Polycarbonate Layer 7 partly or entirely it is provided with between glass outer layer 4.
The thickness of glass inner layer 2 is 5mm, and the thickness 3 in glass middle level is 2mm, and the thickness of glass outer layer 4 is 4mm, poly-carbon
The thickness of acid esters layer 7 is 3mm, and the thickness of amorphous state magnesium fluoride film 5 is 150nm, the thickness of optically catalytic TiO 2 film 6
For 120nm.
Glass-base 1 is soda-lime glass, crystal glass or borosilicate glass.
Claims (7)
1. an anti-fouling glass, it is characterised in that include glass-base (1), glass-base (1) is used by the float glass of 3 layers
PVB film bonding forms, and respectively glass inner layer (2), glass middle level (3) and glass outer layer (4), at glass inner layer (2) or glass
It is provided with amorphous state magnesium fluoride film (5) on glass outer layer (4), amorphous state magnesium fluoride film (5) is provided with titanium-dioxide photo and urges
Change thin film (6).
A kind of anti-fouling glass the most according to claim 1, it is characterised in that described glass inner layer (2), glass middle level (3)
And between glass outer layer (4), partly or entirely it is provided with Polycarbonate Layer (7).
A kind of anti-fouling glass the most according to claim 1, it is characterised in that the thickness of described amorphous state magnesium fluoride film (5)
Degree is 150-200nm.
A kind of anti-fouling glass the most according to claim 1, it is characterised in that described optically catalytic TiO 2 film (6)
Thickness is 80-130nm.
A kind of anti-fouling glass the most according to claim 1, it is characterised in that described glass inner layer (2), glass middle level (3)
It is 2-5mm with the thickness of glass outer layer (4).
A kind of anti-fouling glass the most according to claim 2, it is characterised in that the thickness of Polycarbonate Layer (7) is 1-3mm.
A kind of anti-fouling glass the most according to claim 1, it is characterised in that glass-base (1) is soda-lime glass, crystal glass
Or borosilicate glass.