CN205711510U - Ultra-fine cationic polyester brocade easily contaminates fiber - Google Patents
Ultra-fine cationic polyester brocade easily contaminates fiber Download PDFInfo
- Publication number
- CN205711510U CN205711510U CN201620629936.5U CN201620629936U CN205711510U CN 205711510 U CN205711510 U CN 205711510U CN 201620629936 U CN201620629936 U CN 201620629936U CN 205711510 U CN205711510 U CN 205711510U
- Authority
- CN
- China
- Prior art keywords
- ultra
- fiber
- cationic polyester
- filling part
- fine cationic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
This application discloses a kind of ultra-fine cationic polyester brocade and easily contaminate fiber, formed by a plurality of fibre single thread boundling, every described fibre single thread includes M shape skeleton respectively and is filled in the filling part in M shape skeleton surrounding gap, described M shape skeleton component is chinlon, described filling part component is terylene, is formed with antistatic coating between described M shape skeleton and filling part.Fabric prepared by this tencel has the effect of antistatic accumulation.
Description
Technical field
The application belongs to spining technology field, particularly relates to a kind of ultra-fine cationic polyester brocade and easily contaminates fiber.
Background technology
Along with society progress, people to dress require more and more higher, except to wear comfortable in addition to, also to look for novelty and ask
Different, and the release of fabric lining, the most well meeting the requirement of masses, but common fiber pull resistance is poor, quality is the most not
Stable.
The fiber of prior art is because diameter of section is relatively big, and contact surface area is less, so cooling down in cooling procedure
Amount is difficult to quickly enter fibrous inside, so production efficiency is relatively low;And the fiber of prior art is all solid, so warming
Effect is poor;And the fiber of prior art does not the most possess the functions such as deodorization, sterilization, anticorrosion.
It addition, the thinnest fiber is more difficult to coloring, and dyeing cost is the highest.And, traditional fiber does not the most possess moisture absorption and resists
Antistatic property.
Utility model content
The purpose of this utility model is to provide a kind of ultra-fine cationic polyester brocade easily to contaminate fiber, of the prior art to overcome
Not enough.
For achieving the above object, the following technical scheme of this utility model offer:
The embodiment of the present application discloses a kind of ultra-fine cationic polyester brocade and easily contaminates fiber, a plurality of fibre single thread boundling form, often
Fibre single thread described in bar includes M shape skeleton respectively and is filled in the filling part in M shape skeleton surrounding gap, described
M shape skeleton component is chinlon, and described filling part component is terylene, is formed anti-between described M shape skeleton and filling part
Electrostatic coating.
Preferably, in above-mentioned ultra-fine cationic polyester brocade easily dye fiber, described antistatic coating is polyester/graphite nano
Conducing composite material.
Preferably, in above-mentioned ultra-fine cationic polyester brocade easily dye fiber, on described M shape skeleton, multiple gas is distributed
Hole.
Preferably, in above-mentioned ultra-fine cationic polyester brocade easily dye fiber, described chinlon and/or terylene are coloured filament.
Preferably, in above-mentioned ultra-fine cationic polyester brocade easily dye fiber, described chinlon is undyed filament, described in wash
Synthetic fibre is the filament of dyeing.
Preferably, in above-mentioned ultra-fine cationic polyester brocade easily dye fiber, described filling part surface is additionally provided with one layer of light and touches
Catalytic material.
Preferably, in above-mentioned ultra-fine cationic polyester brocade easily dye fiber, in described filling part, it is dispersed with silver ion for sterilization
Agent.
Compared with prior art, the utility model has the advantage of:
1, fabric prepared by this tencel has the effect of antistatic accumulation;
2, be conducive to absorbing hydrone and locking hydrone by multiple pores, reach the effect of moisture absorption.
Accompanying drawing explanation
In order to be illustrated more clearly that the embodiment of the present application or technical scheme of the prior art, below will be to embodiment or existing
In having technology to describe, the required accompanying drawing used is briefly described, it should be apparent that, the accompanying drawing in describing below is only this
Some embodiments described in application, for those of ordinary skill in the art, on the premise of not paying creative work,
Other accompanying drawing can also be obtained according to these accompanying drawings.
Fig. 1 show the cross section structure signal of ultra-fine cationic polyester brocade easily dye fiber in this utility model specific embodiment
Figure.
Detailed description of the invention
Below in conjunction with the accompanying drawing in this utility model embodiment, the technical scheme in this utility model embodiment is carried out
Detailed description, it is clear that described embodiment is only a part of embodiment of this utility model rather than whole enforcement
Example.Based on the embodiment in this utility model, those of ordinary skill in the art are institute on the premise of not making creative work
The every other embodiment obtained, broadly falls into the scope of this utility model protection.
Shown in Fig. 1, ultra-fine cationic polyester brocade easily contaminates fiber, a plurality of fibre single thread boundling form, every fiber list
Silk includes M shape skeleton 1 respectively and is filled in the filling part 2 in M shape skeleton surrounding gap, M shape skeleton 1 component
For chinlon, filling part component is terylene, is formed with antistatic coating 3 between M shape skeleton 1 and filling part 2.
Preferably, antistatic coating 3 is Nanomter conducting composite polyester/graphite material.
In this technical scheme, by the antistatic coating of Nanomter conducting composite polyester/graphite material material so that sun from
Sub-monofilament has micro conductive, and the fabric that therefore prepared by this monofilament has the function of antistatic accumulation.
Further, multiple pore 4 is distributed on M shape skeleton 1.
In this technical scheme, be conducive to absorbing hydrone and locking hydrone by multiple pores, reach the effect of moisture absorption.
Further, chinlon and/or terylene are coloured filament.
Preferably, chinlon is undyed filament, and terylene is the filament of dyeing.
In other embodiments, chinlon and terylene can have different colors.
In one embodiment, filling part surface is additionally provided with one layer of photocatalyst material.
In this technical scheme, outside fiber bodies, it is additionally provided with one layer of photocatalyst material, and photocatalyst material tool itself
The functions such as standby deodorization, sterilization, anticorrosion.
In another embodiment, it is dispersed with silver ion disinfectant in filling part.
In this technical scheme, silver ion disinfectant is embedded in filling part, has permanent and does not damage fibrous raw material
Bactericidal effect.
The preparation method of superfine polyamide fiber, including: note color after chinlon 6 filament raw material drying, wash monofilament raw material drying;Spinning;
Winding;Add bullet;Inspection;Finished product.
The parameter of preparation technology meets:
Chinlon 6 filament raw material and the baking temperature washing monofilament raw material are 120~140 DEG C;
Wash the spinning temperature of monofilament: 285~295 DEG C;
The spinning temperature of chinlon 6 filament: 245~255 DEG C;
The speed of winding: 3100~3300 meter per seconds;
Adding bullet: draw ratio: 1.6~1.8 times, heating-up temperature: 160~180 DEG C, D/Y compares: 1.5~1.8, process velocity:
600~700 meter per seconds.
By this technological means, Final finishing need not dyeing, saves a large amount of water, electricity, gas and artificial, and has environmental protection and energy saving
Important meaning.
It should be noted that in this article, the relational terms of such as first and second or the like is used merely to a reality
Body or operation separate with another entity or operating space, and deposit between not necessarily requiring or imply these entities or operating
Relation or order in any this reality.And, term " includes ", " comprising " or its any other variant are intended to
Comprising of nonexcludability, so that include that the process of a series of key element, method, article or equipment not only include that those are wanted
Element, but also include other key elements being not expressly set out, or also include for this process, method, article or equipment
Intrinsic key element.In the case of there is no more restriction, statement " including ... " key element limited, it is not excluded that
Including process, method, article or the equipment of described key element there is also other identical element.
The above is only the detailed description of the invention of the application, it is noted that for the ordinary skill people of the art
For Yuan, on the premise of without departing from the application principle, it is also possible to make some improvements and modifications, these improvements and modifications also should
It is considered as the protection domain of the application.
Claims (7)
1. a ultra-fine cationic polyester brocade easily contaminates fiber, it is characterised in that formed by a plurality of fibre single thread boundling, every described fibre
Dimension monofilament includes M shape skeleton respectively and is filled in the filling part in M shape skeleton surrounding gap, described M shape bone
Frame component is chinlon, and described filling part component is terylene, is formed with antistatic coating between described M shape skeleton and filling part.
Ultra-fine cationic polyester brocade the most according to claim 1 easily contaminates fiber, it is characterised in that: described antistatic coating is poly-
Ester/graphite conductive nano composites.
Ultra-fine cationic polyester brocade the most according to claim 1 easily contaminates fiber, it is characterised in that: divide on described M shape skeleton
It is furnished with multiple pore.
Ultra-fine cationic polyester brocade the most according to claim 1 easily contaminates fiber, it is characterised in that: described chinlon and/or terylene
For coloured filament.
Ultra-fine cationic polyester brocade the most according to claim 4 easily contaminates fiber, it is characterised in that: described chinlon is undyed
Filament, described terylene is the filament of dyeing.
Ultra-fine cationic polyester brocade the most according to claim 1 easily contaminates fiber, it is characterised in that: described filling part surface also sets
There is one layer of photocatalyst material.
Ultra-fine cationic polyester brocade the most according to claim 1 easily contaminates fiber, it is characterised in that: it is dispersed with in described filling part
Silver ion disinfectant.