CN205654039U - Antiskid polyurethane terrace - Google Patents
Antiskid polyurethane terrace Download PDFInfo
- Publication number
- CN205654039U CN205654039U CN201620519975.XU CN201620519975U CN205654039U CN 205654039 U CN205654039 U CN 205654039U CN 201620519975 U CN201620519975 U CN 201620519975U CN 205654039 U CN205654039 U CN 205654039U
- Authority
- CN
- China
- Prior art keywords
- aqueous polyurethane
- polyurethane
- colored paint
- layer
- paint layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model provides an antiskid polyurethane terrace, include: the basic unit, the complex is in waterborne polyurethane priming paint layer in the basic unit, the complex is in waterborne polyurethane paint layer on the waterborne polyurethane priming paint layer, the complex is in the last waterborne polyurethane non -slip cover finish paint layer of waterborne polyurethane paint layer, the frosted surface texture of waterborne polyurethane non -slip cover finish paint layer type of having. The utility model provides an antiskid waterborne polyurethane terrace surface type of having dull polish structure to have excellent anti -skidding effect, effectual to have solved current polyurethane terrace surfac ratio more smooth, is having water to have greasy dirt ground easy slipping's problem, and color gloss is good, and is easy to be clean, resistant greasy dirt.
Description
Technical field
This utility model relates to terrace technical field, relates to a kind of antiskid polyurethane terrace, especially
Relate to a kind of anti-skidding aqueous polyurethane floor.
Background technology
Widely used in tradition terrace is concrete floor, and the floor material of use is by water
Mud, sand and a small amount of additive are stirred, mix composition, and its defect is easy cracking, rises
Dirt, dusting, lack flexibility, and is difficult to meet the terraces such as Factory Building, laboratory, office, room
Use requirement.And existing terrace former thus results in because of not enough etc. with the adhesive force on basic unit ground
In use, it also occur that the enamelled coating on surface and basic unit ground occur relative displacement to produce
The situations such as fold.
Polyurethane floor refer to polyurethane floor coatings combine a kind of Novel solvent-free or aqueous,
Free of contamination ground surface function construction technology, is constructed to meet some specific class ground using requirement
Level ground, as high-grade meeting or recreation center focus on comfort requirement；Industrial and mining establishment focus on anticorrosion and wear-resisting
Requirement；Food service industry focuses on high-low temperature resistant, logistic industry requires quickly to come into operation.Gu Te
It is not applicable to various industrial and mining establishment workshop, parking lot, sports ground etc. and has anti-skidding, anticorrosion, wear-resisting
The terrace application required.And polyurethane floor more wearability, pliability, construction are convenient,
Quickly can reach use requirement after floor construction, change what enterprise's terrace renovation was worried completely
Matter of time.
The polyurethane floor coatings of literal sense refer to in molecular backbone structure containing repeating
The macromolecular compound of carbamate (-NHCOO-) feature unit is a class ground of film forming matter
Level ground coating.Its mechanism is by binary or multicomponent isocyanate prepolymer (such as MDI, TDI, HDI)
With binary or the macromolecular compound of multi-hydroxy compound effects.Such as polyurethanes
Being the macromolecular compound containing-NHCOO-unit in molecular structure, this unit is by isocyanate group
Forming with hydroxyl reaction, reaction equation is as follows:
-N=C=O+HOˉ→-NH-COOˉ。
The film forming matter of existing broad sense polyurethane floor coatings has been not limited to polyurethane, also wraps
Including polyureas and polyurethane/polyurea heterozygote, so-called polyureas refers in molecular backbone structure containing weight
One family macromolecule chemical combination of the allophanate (-NHCONH-) constitutional repeating unit appearing again existing
Thing.
Along with fast development and the extensive application of every profession and trade of polyurethane floor, to polyurethane floor
Performance requirement the most increasingly improve, but the non-skid property of existing polyurethane floor is still that it
The defect existed.
Therefore, how to provide a kind of antiskid polyurethane terrace, have become as the most each research and development type enterprise
One of focus of industry extensive concern.
Utility model content
In view of this, the technical problems to be solved in the utility model is to provide a kind of anti-skidding poly-ammonia
Ester terrace, a kind of anti-skidding aqueous polyurethane floor, the Anti-slippery water that this utility model provides
Property polyurethane floor has a preferable skidproof effect, and color good luster, easy to clean, oil resistant
Dirty.
This utility model provides a kind of antiskid polyurethane terrace, including:
Basic unit；
The aqueous polyurethane prime coat being compounded in described basic unit；
The aqueous polyurethane colored paint layer being compounded on described aqueous polyurethane prime coat；
It is compounded in the aqueous polyurethane anti-skid cover top coat layer on described aqueous polyurethane colored paint layer；
Described aqueous polyurethane anti-skid cover top coat layer has the surface texture of class frosted.
Preferably, described aqueous polyurethane anti-skid cover top coat layer is that waterborne polyurethane glass microballon is prevented
Sliding cover enamelled coating；
Described waterborne polyurethane glass microballon anti-skid cover top coat layer comprises glass microballoon.
Preferably, described glass microballoon granule is at the described anti-skidding cover of waterborne polyurethane glass microballon
Enamelled coating surface is entirely prominent or part is prominent.
Preferably, it is characterised in that the particle diameter of described glass microballoon is 220～320 mesh.
Preferably, the thickness of described aqueous polyurethane prime coat is 0.1～0.3mm；
The thickness of described aqueous polyurethane colored paint layer is 0.1～0.3mm；
The thickness of described aqueous polyurethane anti-skid cover top coat layer is 0.1～0.3mm.
Preferably, described aqueous polyurethane colored paint layer includes the first aqueous polyurethane colored paint layer and
Two aqueous polyurethane colored paint layers；
Described first aqueous polyurethane colored paint layer is compounded on described aqueous polyurethane prime coat；
Described second aqueous polyurethane colored paint layer is compounded in described first aqueous polyurethane colored paint layer
On；
Described aqueous polyurethane anti-skid cover top coat layer is compounded in described second aqueous polyurethane colored paint
On layer.
Preferably, the thickness of described first aqueous polyurethane colored paint layer is 0.05～0.15mm；
The thickness of described second aqueous polyurethane colored paint layer is 0.05～0.15mm.
Preferably, described aqueous polyurethane prime coat is by NPU aqueous polyurethane priming paint roller coating or spray
Formed after being coated in described substrate surface；
Described aqueous polyurethane prime coat is NPU aqueous polyurethane prime coat.
Preferably, described aqueous polyurethane colored paint layer is by NPU aqueous polyurethane colored paint roller coating or spray
Formed after being coated in described aqueous polyurethane primer coat surface；
Described aqueous polyurethane colored paint layer is NPU aqueous polyurethane colored paint layer.
Preferably, described waterborne polyurethane glass microballon anti-skid cover top coat layer is by the poly-ammonia of TPU aqueous
After ester finish mixes with glass microballoon, then roller coating is behind described aqueous polyurethane colored paint layer surface
Formed；
Described waterborne polyurethane glass microballon anti-skid cover top coat layer is TPU waterborne polyurethane glass
Microballon anti-skid cover top coat layer.
This utility model provides a kind of antiskid polyurethane terrace, including: basic unit；It is compounded in institute
State the aqueous polyurethane prime coat in basic unit；It is compounded in the water on described aqueous polyurethane prime coat
Property polyurethane colored paint layer；The aqueous polyurethane being compounded on described aqueous polyurethane colored paint layer is anti-skidding
Cover enamelled coating；Described aqueous polyurethane anti-skid cover top coat layer has the surface texture of class frosted.With
Prior art is compared, and the antiskid polyurethane terrace surface that this utility model provides has class frosted knot
Structure, thus there is the skidproof effect of excellence, effectively solve existing polyurethane floor surface ratio
More smooth, have, there being water, the problem easily skidded in greasy dirt ground；And color good luster, it is easy to clean,
Resistance to greasy dirt.
Accompanying drawing explanation
The structure diagram of the anti-skidding aqueous polyurethane floor that Fig. 1 provides for this utility model.
Detailed description of the invention
In order to further appreciate that this utility model, below in conjunction with embodiment to of the present utility model excellent
Embodiment is selected to be described, but it is to be understood that these describe simply for further illustrating this
The feature and advantage of utility model rather than the restriction to this utility model patent requirements.
The all raw materials of this utility model, are not particularly limited its source, commercially buy
Or prepare according to conventional method well known to those skilled in the art.
The all raw materials of this utility model, are not particularly limited its purity, and this utility model is preferred
Use analytical pure or the purity requirement of polyurethane floor preparation field routine.
The all raw materials of this utility model, its trade mark and abbreviation belong to this area routine trade mark and letter
Claiming, each trade mark and abbreviation are all explicit in the field of its associated uses, this area
Technical staff is according to the trade mark, abbreviation and corresponding purposes, it is possible to be commercially available from city's mid-sales or
Conventional method prepares.
This utility model provides a kind of antiskid polyurethane terrace, it is characterised in that including:
Basic unit；
The aqueous polyurethane prime coat being compounded in described basic unit；
The aqueous polyurethane colored paint layer being compounded on described aqueous polyurethane prime coat；
It is compounded in the aqueous polyurethane anti-skid cover top coat layer on described aqueous polyurethane colored paint layer；
Described aqueous polyurethane anti-skid cover top coat layer has the surface texture of class frosted.
Described being combined is not particularly limited, with well known to those skilled in the art by this utility model
Complex method, those skilled in the art can according to practical service environment, product requirement or
Requirement for anticorrosion is adjusted and selects, and compound concrete mode described in the utility model is preferably and is coated with
Cloth, smear, spray, be wound around, bond and one or more in roller coating, more preferably spraying
Or roller coating.
Described basic unit is not particularly limited by this utility model, with well known to those skilled in the art
The basic unit for composite non-slip polyurethane floor, those skilled in the art can be according to reality
Border applicable cases, combining case and properties of product select and adjust, and can be concrete floor
Face or rock land face etc..
Aqueous polyurethane prime coat described in the utility model, i.e. direct combination paint in basic unit
Layer, the lower surface of described aqueous polyurethane prime coat is directly bonded on substrate surface；This practicality is new
The material of described aqueous polyurethane prime coat is not particularly limited, with those skilled in the art by type
Known to the material for polyurethane floor, those skilled in the art can according to reality should
Selecting with situation, combining case and properties of product and adjust, this utility model is for improving
The performance of overall aqueous polyurethane terrace and layer by layer between composite performance, the poly-ammonia of described aqueous
Ester prime coat is preferably NPU aqueous polyurethane prime coat, is particularly preferred as Shanghai and herds Fructus Citri tangerinae novel-section
It is new that the MOOJU-NPU aqueous polyurethane prime coat of material company limited, more preferably Shanghai herd Fructus Citri tangerinae
The transparent MOOJU-NPU aqueous polyurethane prime coat of shaped material company limited；The most described aqueous
Polyurethane primer layer is preferably by NPU aqueous polyurethane priming paint roller coating or be sprayed on described basic unit table
Formed behind face, the most preferably by transparent MOOJU-NPU aqueous polyurethane priming paint roller coating or
Formed after being sprayed on described substrate surface.
The thickness of described aqueous polyurethane prime coat is not particularly limited by this utility model, with this
The thickness for polyurethane floor known to skilled person, those skilled in the art can
To select according to practical situations, combining case and properties of product and to adjust, this reality
It is preferably 0.1～0.3mm, more preferably with the thickness of novel described aqueous polyurethane prime coat
0.15～0.25mm, most preferably 0.2mm.
Aqueous polyurethane colored paint layer described in the utility model, i.e. direct combination is at the poly-ammonia of described aqueous
Enamelled coating on ester prime coat, the lower surface of described aqueous polyurethane colored paint layer is directly bonded on described
Aqueous polyurethane prime coat upper surface；This utility model material to described aqueous polyurethane colored paint layer
Matter is not particularly limited, with the material for polyurethane floor well known to those skilled in the art i.e.
Can, those skilled in the art can be according to practical situations, combining case and properties of product
Select and adjust, this utility model be improve overall aqueous polyurethane terrace performance and
Composite performance between layer by layer, described aqueous polyurethane colored paint layer is preferably NPU aqueous polyurethane
Colored paint layer, the most preferably the MOOJU-NPU water of Shanghai Mu Ju new material company limited
Property polyurethane colored paint layer；The most described aqueous polyurethane colored paint layer is preferably by NPU aqueous polyurethane color
Paint roller coating or formed after being sprayed on described aqueous polyurethane primer coat surface, the most preferably by
MOOJU-NPU aqueous polyurethane colored paint roller coating or be sprayed on described aqueous polyurethane prime coat table
Formed behind face.
The thickness of described aqueous polyurethane colored paint layer is not particularly limited by this utility model, with this
The thickness for polyurethane floor known to skilled person, those skilled in the art can
To select according to practical situations, combining case and properties of product and to adjust, this reality
It is preferably 0.1～0.3mm, more preferably with the thickness of novel described aqueous polyurethane colored paint layer
0.15～0.25mm, most preferably 0.2mm.
This utility model improve overall aqueous polyurethane terrace performance and layer by layer between answer
Closing performance, described aqueous polyurethane colored paint layer includes the first aqueous polyurethane colored paint layer and the second water
Property polyurethane colored paint layer；Described first aqueous polyurethane colored paint layer is compounded in described aqueous polyurethane
Prime coat upper surface；Described second aqueous polyurethane colored paint layer is compounded in the described first poly-ammonia of aqueous
Ester colored paint layer upper surface；Described aqueous polyurethane anti-skid cover top coat layer is compounded in described second aqueous
Polyurethane colored paint layer upper surface.
The thickness of described first aqueous polyurethane colored paint layer is not particularly limited by this utility model,
With the thickness for polyurethane floor well known to those skilled in the art, people in the art
Member can select according to practical situations, combining case and properties of product and adjust,
The thickness of the first aqueous polyurethane colored paint layer described in the utility model is preferably 0.05～0.15mm,
More preferably 0.08～0.12mm, most preferably 0.1mm.
The thickness of described second aqueous polyurethane colored paint layer is not particularly limited by this utility model,
With the thickness for polyurethane floor well known to those skilled in the art, people in the art
Member can select according to practical situations, combining case and properties of product and adjust,
The thickness of the second aqueous polyurethane colored paint layer described in the utility model is preferably 0.05～0.15mm,
More preferably 0.08～0.12mm, most preferably 0.1mm.
It is anti-skidding that this utility model uses two-layer aqueous polyurethane colored paint layer can not only realize aqueous
The outward appearance multiformity of polyurethane floor, it is ensured that appearance luster is lasting, additionally aid realization layer by layer it
Between bonding force, it is ensured that between prime coat and top coat layer firm persistently, increase mechanical strength.
Aqueous polyurethane anti-skid cover top coat layer described in the utility model, i.e. direct combination is at described water
Enamelled coating on property polyurethane colored paint layer, the lower surface of described aqueous polyurethane anti-skid cover top coat layer is straight
Connect and be bonded in described aqueous polyurethane colored paint layer upper surface.This utility model is for strengthening surface anti-skidding
Performance, described aqueous polyurethane anti-skid cover top coat layer has the surface texture of class frosted.
The material of described aqueous polyurethane anti-skid cover top coat layer is limited by this utility model the most especially
System, this utility model be improve aqueous polyurethane terrace surface non-skid property and layer by layer between
Composite performance, it is micro-that described aqueous polyurethane anti-skid cover top coat layer is preferably waterborne polyurethane glass
Pearl anti-skid cover top coat layer；Described waterborne polyurethane glass microballon anti-skid cover top coat layer preferably comprises
Glass microballoon, described glass microballoon granule is more preferably anti-skidding at described waterborne polyurethane glass microballon
Cover enamelled coating (aqueous polyurethane anti-skid cover top coat layer) surface is entirely prominent or part is prominent.
Described glass microballoon is not particularly limited by this utility model, ripe with those skilled in the art
The glass microballoon known, those skilled in the art can be according to practical situations, compound feelings
Condition and properties of product select and adjust, and this utility model is preferably oleophyllie hydrophobic type glass
Microballon.The granularity of described glass microballoon is not particularly limited by this utility model, art technology
Personnel can select according to practical situations, combining case and properties of product and adjust,
This utility model is preferably 220～320 mesh, more preferably 240～300 mesh, is most preferably
260～280 mesh, most preferably 320 mesh.
This utility model does not has spy to the paint vehicle material of described aqueous polyurethane anti-skid cover top coat layer
Do not limit, with the material for polyurethane floor well known to those skilled in the art, ability
Field technique personnel can select according to practical situations, combining case and properties of product
And adjustment, this utility model be improve aqueous polyurethane terrace non-skid property and layer by layer between
Composite performance, described aqueous polyurethane anti-skid cover top coat layer, the most described waterborne polyurethane glass
Microballon anti-skid cover top coat layer is preferably TPU waterborne polyurethane glass microballon anti-skid cover top coat layer, more
It is particularly preferred as the MOOJU-TPU aqueous polyurethane glass of Shanghai Mu Ju new material company limited
Glass microballon anti-skid cover top coat layer；The most described waterborne polyurethane glass microballon anti-skid cover top coat layer is preferred
By TPU waterborne polyurethane glass microballon anti-skid cover finish paint roller coating or be sprayed on the poly-ammonia of described aqueous
Formed behind ester colored paint layer surface, the most preferably rolled by MOOJU-TPU aqueous polyurethane colored paint
Formed after being coated in described aqueous polyurethane colored paint layer surface.
The thickness of described aqueous polyurethane anti-skid cover top coat layer is limited by this utility model the most especially
System, with the thickness for polyurethane floor well known to those skilled in the art, this area skill
Art personnel can select according to practical situations, combining case and properties of product and adjust
Whole, the thickness of aqueous polyurethane anti-skid cover top coat layer described in the utility model is preferably
0.1～0.3mm, more preferably 0.15～0.25mm, most preferably 0.2mm.
This utility model preferably employs waterborne polyurethane glass microballon anti-skid cover top coat layer, i.e. comprises
The aqueous polyurethane anti-skid cover top coat layer of glass microballoon, glass microballoon is entirely prominent or is partially protrude through
Anti-skid cover top coat layer surface, thus the aqueous polyurethane forming the surface texture with class frosted is prevented
Sliding cover enamelled coating.Glass microballoon of the present utility model by borosilicate raw material through high-tech processing and
Becoming, have the advantages such as light weight, higher intensity, good chemical stability, its surface is passed through
Special handling has oleophyllie hydrophobic performance, is very easy to be scattered in organic material system, thus
Achieve above-mentioned special construction, effectively raise skidproof effect.
See the structure of the anti-skidding aqueous polyurethane floor that Fig. 1, Fig. 1 provide for this utility model
Sketch；Wherein, 1 is basic unit, and 2 is aqueous polyurethane prime coat, and 3 is aqueous polyurethane colored paint
Layer, 4 it is the aqueous polyurethane anti-skid cover top coat layer with class matte surface structure.
The antiskid polyurethane terrace that this utility model provides, includes: basic unit from bottom to top；Compound
Aqueous polyurethane prime coat in described basic unit；It is compounded on described aqueous polyurethane prime coat
Aqueous polyurethane colored paint layer；It is compounded in the aqueous polyurethane on described aqueous polyurethane colored paint layer
Anti-skid cover top coat layer；And this utility model preferably employs waterborne polyurethane glass microballon anti-skid cover
Top coat layer, i.e. comprises the aqueous polyurethane anti-skid cover top coat layer of glass microballoon, and glass microballoon is dashed forward entirely
Go out or be partially protrude through anti-skid cover top coat layer surface, thus form the surface texture with class frosted
Aqueous polyurethane anti-skid cover top coat layer, effectively raise skidproof effect.Solve existing poly-
Urethane terrace surface smoother, has, there being water, the problem easily skidded in greasy dirt ground；And color
Good luster, easy to clean, resistance to greasy dirt.
In order to be further appreciated by this utility model, below in conjunction with embodiment, this utility model is provided
One anti-skidding aqueous polyurethane floor illustrate, protection domain of the present utility model by with
The restriction of lower embodiment.
Embodiment 1
Composite aqueous polyurethane prime coat on ground layer successively, aqueous polyurethane colored paint layer and
Waterborne polyurethane glass microballon anti-skid cover top coat layer, obtains anti-skidding aqueous polyurethane floor.
Wherein, priming paint uses the MOOJU-NPU aqueous of Shanghai Mu Ju new material company limited
Polyurethane primer, thickness is 0.2mm, obtains MOOJU-NPU aqueous polyurethane prime coat；
Colored paint uses the MOOJU-NPU aqueous polyurethane of Shanghai Mu Ju new material company limited
Colored paint, thickness is 0.2mm, obtains MOOJU-NPU aqueous polyurethane colored paint layer；
Finish uses the poly-ammonia of MOOJU-TPU aqueous of Shanghai Mu Ju new material company limited
Ester colored paint, thickness is 0.2mm, adds the 220 mesh glass of 0.1Kg in every 6 kilograms of finishes
Microballon, obtains MOOJU-TPU waterborne polyurethane glass microballon anti-skid cover top coat layer.
The anti-skidding aqueous polyurethane floor preparing said process carries out anti-skid factor test and lead
Hardness test, wherein, anti-skid factor test is with reference to industry standard " JCT1050-2007 ground
Stone material non-skid property grade classification and test method " in relevant regulations carry out, pencil hardness survey
Examination uses the test of Portable pencil hardness tester.
Testing result shows, in this utility model embodiment 1, anti-skidding aqueous polyurethane floor is anti-
Sliding coefficient is 0.7, and pencil hardness is 4H.
Embodiment 2
Composite aqueous polyurethane prime coat on ground layer successively, aqueous polyurethane colored paint layer and
Waterborne polyurethane glass microballon anti-skid cover top coat layer, obtains anti-skidding aqueous polyurethane floor.
Wherein, priming paint uses the MOOJU-NPU aqueous of Shanghai Mu Ju new material company limited
Polyurethane primer, thickness is 0.2mm, obtains MOOJU-NPU aqueous polyurethane prime coat；
Colored paint uses the MOOJU-NPU aqueous polyurethane of Shanghai Mu Ju new material company limited
Colored paint, thickness is 0.2mm, obtains MOOJU-NPU aqueous polyurethane colored paint layer；
Finish uses the poly-ammonia of MOOJU-TPU aqueous of Shanghai Mu Ju new material company limited
Ester colored paint, thickness is 0.2mm, adds the 320 mesh glass of 0.1Kg in every 6 kilograms of finishes
Microballon, obtains MOOJU-TPU waterborne polyurethane glass microballon anti-skid cover top coat layer.
The anti-skidding aqueous polyurethane floor preparing said process carries out anti-skid factor test and lead
Hardness test, wherein, anti-skid factor test is with reference to industry standard " JCT1050-2007 ground
Stone material non-skid property grade classification and test method " in relevant regulations carry out, pencil hardness survey
Examination uses the test of Portable pencil hardness tester.
Testing result shows, in this utility model embodiment 2, anti-skidding aqueous polyurethane floor is anti-
Sliding coefficient is 0.8, and pencil hardness is 6H.
Comparative example 1
Composite aqueous polyurethane prime coat on ground layer successively, aqueous polyurethane colored paint layer and
Aqueous polyurethane cover enamelled coating, obtains aqueous polyurethane terrace.
Wherein, priming paint uses the MOOJU-NPU aqueous of Shanghai Mu Ju new material company limited
Polyurethane primer, thickness is 0.2mm, obtains MOOJU-NPU aqueous polyurethane prime coat；
Colored paint uses the MOOJU-NPU aqueous polyurethane of Shanghai Mu Ju new material company limited
Colored paint, thickness is 0.2mm, obtains MOOJU-NPU aqueous polyurethane colored paint layer；
Finish uses the poly-ammonia of MOOJU-TPU aqueous of Shanghai Mu Ju new material company limited
Ester colored paint, thickness is 0.2mm, obtains MOOJU-TPU aqueous polyurethane cover enamelled coating.
The aqueous polyurethane terrace preparing said process carries out anti-skid factor test and pencil is hard
Degree test, wherein, anti-skid factor test is with reference to industry standard " JCT1050-2007 ground stone
Non-skid property grade classification and test method " in relevant regulations carry out, pencil hardness test makes
Test with Portable pencil hardness tester.
Testing result shows, the anti-skidding system of aqueous polyurethane terrace in this utility model comparative example 1
Number is 0.5, and pencil hardness is 2H.
The one anti-skidding aqueous polyurethane floor provided this utility model above has been carried out in detail
Introduction, principle of the present utility model and embodiment are carried out by specific case used herein
Illustrate, the explanation of above example be only intended to help to understand method of the present utility model and
Core concept, it is noted that for those skilled in the art, is not taking off
On the premise of this utility model principle, it is also possible to this utility model is carried out some improvement and repaiies
Decorations, these improve and modification also falls in this utility model scope of the claims.
Claims (10)
1. an antiskid polyurethane terrace, it is characterised in that including:
Basic unit；
The aqueous polyurethane prime coat being compounded in described basic unit；
The aqueous polyurethane colored paint layer being compounded on described aqueous polyurethane prime coat；
It is compounded in the aqueous polyurethane anti-skid cover top coat layer on described aqueous polyurethane colored paint layer；
Described aqueous polyurethane anti-skid cover top coat layer has the surface texture of class frosted.
Antiskid polyurethane terrace the most according to claim 1, it is characterised in that described
Aqueous polyurethane anti-skid cover top coat layer is waterborne polyurethane glass microballon anti-skid cover top coat layer；
Described waterborne polyurethane glass microballon anti-skid cover top coat layer comprises glass microballoon.
Antiskid polyurethane terrace the most according to claim 2, it is characterised in that described
Glass microballoon granule entirely prominent on described waterborne polyurethane glass microballon anti-skid cover top coat layer surface or
Part is prominent.
4. according to the antiskid polyurethane terrace described in claim 2～3 any one, its feature
Being, the particle diameter of described glass microballoon is 220～320 mesh.
Antiskid polyurethane terrace the most according to claim 1, it is characterised in that described
The thickness of aqueous polyurethane prime coat is 0.1～0.3mm；
The thickness of described aqueous polyurethane colored paint layer is 0.1～0.3mm；
The thickness of described aqueous polyurethane anti-skid cover top coat layer is 0.1～0.3mm.
Antiskid polyurethane terrace the most according to claim 1, it is characterised in that described
Aqueous polyurethane colored paint layer includes the first aqueous polyurethane colored paint layer and the second aqueous polyurethane colored paint
Layer；
Described first aqueous polyurethane colored paint layer is compounded on described aqueous polyurethane prime coat；
Described second aqueous polyurethane colored paint layer is compounded in described first aqueous polyurethane colored paint layer
On；
Described aqueous polyurethane anti-skid cover top coat layer is compounded in described second aqueous polyurethane colored paint
On layer.
Antiskid polyurethane terrace the most according to claim 6, it is characterised in that described
The thickness of the first aqueous polyurethane colored paint layer is 0.05～0.15mm；
The thickness of described second aqueous polyurethane colored paint layer is 0.05～0.15mm.
Antiskid polyurethane terrace the most according to claim 1, it is characterised in that described
Aqueous polyurethane prime coat is by NPU aqueous polyurethane priming paint roller coating or is sprayed on described basic unit table
Formed behind face；
Described aqueous polyurethane prime coat is NPU aqueous polyurethane prime coat.
Antiskid polyurethane terrace the most according to claim 1, it is characterised in that described
Aqueous polyurethane colored paint layer is by NPU aqueous polyurethane colored paint roller coating or is sprayed on described aqueous and gathers
Formed after urethane primer coat surface；
Described aqueous polyurethane colored paint layer is NPU aqueous polyurethane colored paint layer.
Antiskid polyurethane terrace the most according to claim 2, it is characterised in that described
Waterborne polyurethane glass microballon anti-skid cover top coat layer is by TPU aqueous polyurethane finish and glass
After microballon mixing, then roller coating is formed behind described aqueous polyurethane colored paint layer surface；
Described waterborne polyurethane glass microballon anti-skid cover top coat layer is TPU waterborne polyurethane glass
Microballon anti-skid cover top coat layer.