CN205576612U - Organosilicon polychrome leather - Google Patents
Organosilicon polychrome leather Download PDFInfo
- Publication number
- CN205576612U CN205576612U CN201620198273.6U CN201620198273U CN205576612U CN 205576612 U CN205576612 U CN 205576612U CN 201620198273 U CN201620198273 U CN 201620198273U CN 205576612 U CN205576612 U CN 205576612U
- Authority
- CN
- China
- Prior art keywords
- layer
- organosilicon
- leather
- polychrome
- primer layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model discloses an organosilicon polychrome leather, include by substrate (1), primer layer (2), color spot layer (3) and transparent area glue film (4) that set gradually that coat the silica gel coating of primer in from type paper or epimembranal from the type, laminating substrate (1) vulcanizes, peels off from type paper or from the type membrane, makes substrate (1) and primer layer (2) on going, the silo of primer layer surface through being equipped with color spot layer sizing material, some color spots of adhesive tape on the primer layer through vulcanizing, get the color spot layer, gluing the sizing material with the transparent area and coating in from type paper or epimembranal from the type, vulcanize on laminating color spot layer (3), peels off from type paper or leave the type membrane, can make organosilicon polychrome leather. The utility model discloses the double -colored leather of organosilicon that makes not only antifouling, ventilative, resistant high low temperature, water -fastly separate, ageing -resistant, the color is changeable in addition, the colour is firm, the simple environmental protection of its preparation method.
Description
Technical field
This utility model relates to the preparation method of a kind of organosilicon polychrome leather, belongs to organosilicon synthetic leather technical field.
Background technology
Mostly synthetic leather is to be formed what surface layer was made by TPU, PU, PVC etc. at present, but the current conjunction of these materials
Mostly finished leather is to be formed what surface layer was made by TPU, PU, PVC etc., however the soil resistance of these materials, breathability,
High-low temperature resistant, hydrolysis, the physical and chemical performance such as ageing-resistant are the most not ideal enough, and the making raw material of these materials is to ring
There is harm in border, can produce harmful substance during waste products burn processing.Organosilicon synthetic leather can solve these problems, but
The color of organosilicon synthetic leather is the most single at present, in appearance not as above-mentioned synthetic leather.
Utility model content
This utility model, for the deficiency of the problems referred to above, proposes a kind of organosilicon polychrome leather, obtained organosilicon bicolor leather
The most antifouling, ventilative, high-low temperature resistant, hydrolysis, ageing-resistant, and color desktop, color fast.
This utility model is that the technical scheme solving the proposition of above-mentioned technical problem is:
A kind of organosilicon polychrome leather, including the base material (1) set gradually from down to up, primer layer (2), mottle layer (3)
And transparent area glue-line (4).
Preferred: described base material (1), primer layer (2), mottle layer (3) and transparent area glue-line (4) are combined successively
Link together.
Preferred: described clear layer (4) is to be formed by the sulfuration of transparent or semitransparent silica gel, and THICKNESS CONTROL is at 0.01-0.05mm.
Preferred: described mottle layer (3) is to be formed by the silica gel sulfuration adding Masterbatch.
Preferred: described primer layer (2) is to be formed by the silica gel sulfuration adding color, and THICKNESS CONTROL is 0.10~0.20mm.
Preferred: described base material (1) be in super fine, the glass of chemistry super fine, cotton, numb, paper, metal any one or
Multiple it is made.
Preferred: the color of described mottle layer (3) and primer layer (2) is different.
The preparation method of a kind of organosilicon polychrome leather, comprises the following steps:
A. being coated in release paper or mould release membrance by the Silica gel coatings of primer, laminating base material (1), at 80~200 DEG C
At a temperature of vulcanize 1~30 minute, peel off release paper or mould release membrance, prepare base material (1) and primer layer (2);
B. primer layer (2) surface is through the hopper equipped with mottle layer sizing, and some mottles of adhesive tape on primer layer, through sulfur
Change, obtain mottle layer;
C. transparent area glue-line sizing material is coated on release paper or mould release membrance, the mottle layer obtained in laminating step b
(3), vulcanize 1~30 minute at a temperature of 80~200 DEG C, peel off release paper or mould release membrance, can be prepared by organic
Silicon polychrome is removed from office.
Preferred: in the upper method coating mottle layer of primer layer (2) in described step b: contain coloured in hopper
Speckle layer sizing, and deflector roll is arranged at above hopper, by primer layer (2) through deflector roll and hopper, can be by color
Speckle layer sizing is coated on primer layer (2), structure such as Fig. 2.
A kind of organosilicon polychrome leather of the present utility model, compared to existing technology, has the advantages that
This utility model prepare organosilicon bicolor leather is the most antifouling, ventilative, high-low temperature resistant, hydrolysis, ageing-resistant, and
And color desktop, color fast, its preparation method is simple and environmentally-friendly.
Accompanying drawing explanation
Fig. 1 is the structural representation of this utility model embodiment.
Fig. 2 is this embodiment mottle layer coating schematic diagram;
Wherein, 1 is base material, and 2 is primer layer, and 3 is mottle layer, and 4 is transparent or semitransparent glue-line, and 5 is deflector roll, and 6 are
Hopper, 7 is mottle layer sizing.
Detailed description of the invention
Accompanying drawing discloses the structural representation of one preferred embodiment of this utility model without limitation, below with reference to accompanying drawing
Explain the technical solution of the utility model.
Embodiment 1
A kind of organosilicon polychrome leather of the present embodiment, as it is shown in figure 1, include that composite joint is put the most successively together
Base material 1, primer layer 2, mottle layer 3 and transparent area glue-line 4.Base material 1 is super fine for 0.8mm thickness.
Composition and weight proportion that described transparent area glue-line 4 uses are as follows:
Composition and weight proportion that described mottle layer 3 uses are as follows:
Composition and weight proportion that described primer layer 2 uses are as follows:
The preparation method of a kind of organosilicon polychrome leather, comprises the following steps:
A. being coated in release paper by the Silica gel coatings of primer, THICKNESS CONTROL is at 0.15mm, and laminating 0.8mm thickness is super fine,
Vulcanize 5 minutes at a temperature of 130 DEG C, peel off release paper, prepare base material (1) and primer layer (2);
B. primer layer (2) surface is through the hopper equipped with mottle layer sizing, and some mottles of adhesive tape on primer layer, through 130
DEG C sulfuration 5 minutes, obtain mottle layer;Vulcanize 1~30 minute at a temperature of 80~200 DEG C.
C. transparent area glue-line sizing material being coated on release paper, THICKNESS CONTROL obtains in 0.05mm laminating step b
Mottle layer (3), vulcanizes 10 minutes at a temperature of 130 DEG C, peels off release paper, can be prepared by organosilicon polychrome leather.
Difference between each glue-line of embodiment 2 to 9 and each comparative example see table, and embodiment is same as in Example 1.
The organosilicon synthetic leather obtaining embodiment 1-9 and comparative example 1-4 carries out following experiment:
1. wearability
Test by the regulation of QB/2726-2005, use CS-10 emery wheel, loading 1000g, test revolution 1000 turns
Stamp wearability evaluation criteria:
1 grade entirely without
2 grades have residual or the marking
3 grades can resolution patterns or word
4 grades of patterns or word are clear
5 grades of patterns or word are unchanged
2. scoring resistance
Repeatedly swipe 10 times at leather surface by the identical dynamics of unitary coin, erasure will be scraped compared with not scraping erasure
A: surface is unchanged
B. surface pattern change is inconspicuous
C: surface pattern obscures
Can't see lines the most completely
3. pliability
With reference to CN100400678 " leather coating composition, coating process and application leather ", grade is as follows:
A is the most soft
B is soft
C is medium
D is hard
E is very rigid
4. smooth feeling
A is dry and comfortable smooth
B is smooth
C on-slip.
5. soil resistance
Ball pen ink is sprinkled upon on leather, contrasts after clearing up with ethanol after 24 hours:
5 grades: inviolateness remains
4 grades: slightly stain residual
3 grades: some stains remain
2 grades: many stain residuals
1 grade: dirty.
The enforcement data of each embodiment and comparative example and test data such as table 1 time:
Table 1
Above example and comparative example with regard to the thickness of transparent area glue-line and primer layer to the wearability of leather, scoring resistance, soft
The impact of two-color effect is contrasted by softness, the impact of smooth feeling and mottle layer.1. transparent area glue-line provides for leather
Smooth feeling, wearability, scoring resistance;Simultaneously because transparent area glue-line glue is hard, if the thickest pliability that can affect leather,
So thickness should control in the range of 0.01-0.05mm.2. primer layer plays the effect of transparent area glue-line and base material bonding, but
If the thickest leather softness that can affect, the thinnest bonding that can affect with base material, thus affect wear-resisting, scratch resistance, thickness should
Control at 0.10-0.20mm.3. mottle layer mainly makes leather have double-colored effect.
It is merely to illustrate enforcement of the present utility model above in conjunction with this utility model preferred embodiment described by accompanying drawing
Mode rather than as to aforementioned utility model purpose and claims content and the restriction of scope, every according to this
The technical spirit of utility model, to any simple modification made for any of the above embodiments, equivalent variations and modification, the most still belongs to this reality
With new technique and rights protection category.
Claims (4)
1. an organosilicon polychrome leather, it is characterised in that: include base material (1), primer layer (2), mottle layer (3) and the transparent area glue-line (4) set gradually from down to up;Described transparent area glue-line (4) is to be formed by the sulfuration of transparent or semitransparent silica gel;Described mottle layer (3) is to be formed by the silica gel sulfuration adding Masterbatch;Described primer layer (2) is to be formed by the silica gel sulfuration adding color.
Organosilicon polychrome the most according to claim 1 is removed from office, it is characterised in that: described base material (1), primer layer (2), mottle layer (3) and transparent area glue-line (4) composite joint successively are together.
Organosilicon polychrome the most according to claim 1 is removed from office, it is characterised in that: described primer layer (2) thickness is at 0.01-0.05mm.
Organosilicon polychrome the most according to claim 1 is removed from office, it is characterised in that: described transparent area glue-line (4) thickness is 0.01~0.10mm.