CN205242165U - Mix flocking surface fabric - Google Patents
Mix flocking surface fabric Download PDFInfo
- Publication number
- CN205242165U CN205242165U CN201520933951.4U CN201520933951U CN205242165U CN 205242165 U CN205242165 U CN 205242165U CN 201520933951 U CN201520933951 U CN 201520933951U CN 205242165 U CN205242165 U CN 205242165U
- Authority
- CN
- China
- Prior art keywords
- viscose glue
- carbon fibre
- bamboo
- flocking
- suede
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model provides a mix flocking surface fabric belongs to flocking technical field. It has solved the not good or not good problem of adsorptivity of current flocking surface fabric resilience. Tapetum on this mix flocking surface fabric, this surface fabric include the backer and link firmly to the side of the backer, have the bond line between backer and the tapetum, above -mentioned tapetum links firmly at the backer lateral part through the bond line, the bond line is epoxy glue, bamboo charcoal fiber portion and viscose fine hair portion that the tapetum set up for the interval. This mix flocking surface fabric's flocking technology, this technology includes following step A, prepares material, B, flocking, C, dry by the fire and evaporate, D, washing. Still has good adsorptivity when this mix flocking surface fabric resilience is good.
Description
Technical field
The utility model belongs to flocking field, relates to a kind of mix flocked fabric and mixingThe flocking technique of flocked fabric.
Background technology
Flocked fabric is taking all kinds of clothes as base fabric, and nylon fine hair or viscose glue suede are planted in frontHair, then through steaming and washing processes, matte is plentiful, feel is soft, color and luster is brightBeautiful, novel in style, win consumer's favor.
The principle of flocking is to utilize the electric charge two like magnetic poles repel each other physical characteristic that there is a natural attraction between the sexes, makes suedeNegative electrical charge on hair-videotape, is placed on the object that needs flocking under zero potential or grounding requirement suedeHair is subject to different current potential by the attraction of plant, is vertical configuration and accelerates to ascend to heaven to and need flockingOn body surface, owing to being scribbled adhesive by plant, fine hair is just vertically bonded at and is plantedOn object.
Flocking feature is: third dimension is strong, bright-colored, feel is soft, luxurious noble quality,Magnificent warmth, lifelike image, nonpoisonous and tasteless, heat-holding dampproof, non-lint, rub resistance,Smooth zero-clearance.
The surface of various product base materials all can flocking, and is not subject to by plant shape, largeLittle restriction. As: paper, cloth, nonwoven, artificial leather, plastics, glass, metal,Rubber, plank, sponge, plasterboard, wood-based plate, plastic uptake sheet, foam, pottery, treeFat etc.
Flocking industry field is boundless, representational industry:
1, handicraft industry: the toy of various patterns, various materials, handicraft, phaseFrame backboard, gift, art calligraphy, artificial flower, technique plastic lantern etc.
2, packaging industry: casket, health-care product package box, wine box, spectacle case, knotWedding certificate, high-grade certificate epidermis, bottle, case and bag, adhesive sticker, leatheroid (plate) etc.
3, automobile industry: Rubber Seal Strip for Automobile, automotive trim plastic parts etc.
4, other industry: motorcycle helmet, clothes hanger, fire resistant doorsets, safety cabinet, lampThe clothes hanger of tool, kitchen utensils, sanitary equipment, furniture, sponge, EVA, various materials etc.
5, resin, pottery, gypsum, glass, plastics, regenerated plastics handicraft, object for appreciationTool surface flocking.
Its publication number of Chinese patent CN103437073A provides " a kind of water thorn flocking plantAnd method ", it comprises flocking wheel hub or trawlnet curtain, is arranged on flocking wheel hub or trawlnetThe high pressure flocking water jet in curtain outside; On flocking wheel hub or trawlnet curtain, have multiple fineAperture; Fleece after positive aspect is Hydroentangled, through flocking rotary drum or trawlnet curtain,Under the water thorn effect of high pressure flocking water jet, microfibre one end is goed deep in fine aperture,In the time that nonwoven separates with flocking rotary drum or trawlnet curtain, go deep into one end quilt of fiber in shrinkage poolBring out, thereby form lint in the one side of nonwoven, complete the flocking of flocking nonwovenTechnique.
Can find out, above-mentioned flocking method has been simplified the flocking technique of nonwoven, useApparatus structure is simple, reduced occupation of land space, when having reduced equipment, material cost,Also effectively ensured the flocking effect of nonwoven.
But its fine hair of above-mentioned flocked fabric is single, or traditional making herbs into wool mode,With acrylic, or adopt viscose glue suede. Certainly its resilience is better, but adsorptivity is notReach.
Although its excellent adsorption of existing employing bamboo-carbon fibre fine hair, resilience is too poor,Subdue after distortion, resilience is more difficult.
Existing other flocked fabric also all exists similar problem.
Summary of the invention
First object of the present utility model is the problems referred to above that exist for prior art,The mixing flocked fabric that a kind of resilience is good is provided.
Second object of the present utility model is to provide the flocking work of above-mentioned mixing flocked fabricSkill.
First object of the present utility model can realize by following technical proposal:
A kind of flocked fabric that mixes, this fabric comprises base fabric and is connected on base fabric sideTapetum, is characterized in that, between described base fabric and tapetum, has adhesive layer, above-mentionedTapetum is connected in base fabric sidepiece by adhesive layer, and described adhesive layer is epoxide-resin glue,Described tapetum is spaced bamboo-carbon fibre portion and viscose glue suede portion.
Can make firmly to link together between base fabric and tapetum by adhesive layer, meanwhile,Because adhesive layer is epoxy resin. Because the molecular structure of epoxy resin is with in strandContain active epoxide group for its feature, epoxide group can be positioned at strand end,Centre or circlewise structure. Owing to containing active epoxide group in molecular structure, make itCan form with polytype curing agent generation cross-linking reaction the insoluble three-dimensional net that hasThe high polymer of shape structure. In all molecular structures, contain the macromolecular compound system of epoxide groupBe called epoxy resin. Epoxy resin after solidifying has good physics, chemical property,It is to having excellent adhesive strength between base fabric and tapetum, dielectric properties are good, becomesDetermine shrinkage factor little, product size good stability, hardness is high, pliability is better, to alkali andMost of solvent-stable.
Due to bamboo-carbon fibre portion and the interval setting of viscose glue suede portion, therefore, it combines viscose glueThe advantage of suede and bamboo-carbon fibre, tool also when making this mixing flocked fabric excellent adsorptionThere are enough resiliences.
In above-mentioned mixing flocked fabric, described bamboo-carbon fibre portion and viscose glue suede portion are allStrip, above-mentioned bamboo-carbon fibre portion and viscose glue suede portion one by one interval arrange.
In above-mentioned mixing flocked fabric, described bamboo-carbon fibre portion and viscose glue suede portion are allZigzag, above-mentioned bamboo-carbon fibre portion and viscose glue suede portion one by one interval arrange.
In above-mentioned mixing flocked fabric, described bamboo-carbon fibre portion and viscose glue suede portion are allWaveform, above-mentioned bamboo-carbon fibre portion and viscose glue suede portion one by one interval arrange.
In above-mentioned mixing flocked fabric, described bamboo-carbon fibre portion and viscose glue suede portion are allAnnular, above-mentioned bamboo-carbon fibre portion and viscose glue suede portion one by one interval arrange and above-mentioned bamboo charcoal fibreDimension portion and viscose glue suede portion concentric arrange.
No matter bamboo-carbon fibre portion and which kind of spaced mode of viscose glue suede portion, it can makeBamboo-carbon fibre portion and viscose glue suede portion are disposed on base fabric uniformly.
In above-mentioned mixing flocked fabric, area and the bamboo-carbon fibre of described viscose glue suede portionPortion's Area Ratio is 1:1-5.
The arranging of this ratio can make this mixing flocked fabric have enough the elastic while itsAdsorptivity is also relatively good.
Second object of the present utility model realizes by following technical proposal:
Mix a flocking technique for flocked fabric, this technique comprises the following steps:
A, get the raw materials ready: the fabric of the standby preseting length of choosing and width is as base fabric, the standby viscose glue suede of choosingWith bamboo-carbon fibre suede as tapetum raw material;
B, flocking: viscose glue suede and sticking on base fabric of bamboo-carbon fibre suede interval are plantedVelvet fabric blank;
C, steam: in the environment by above-mentioned flocked fabric blank in 140-160OCCarry out 5-20 minutes;
D, washing: the flocked fabric blank after steaming is put into clear water and wash, treatFlocked fabric blank after washing obtains the mixing flocked fabric of finished product after being dried.
After getting the raw materials ready, just can carry out flocking operation, interval sticks to the bamboo charcoal on base fabricFiber portion and viscose glue suede just form and mix flocked fabric blank, will mix flocked fabric blankCarry out subsequent treatment and just can obtain finished product mixing flocked fabric.
Subsequent treatment, for steaming and washing, can make tapetum and base fabric stable connection after steaming,After washing, can remove the fine hair dropping, the rear mixing flocked surface that just can obtain finished product to be driedMaterial.
In the flocking technique of above-mentioned mixing flocked fabric, in described step B at base fabricOn be coated with binding agent.
In the flocking technique of above-mentioned mixing flocked fabric, the bonding in described step BAgent is acrylate adhesive.
In the flocking technique of above-mentioned mixing flocked fabric, the bonding in described step BAgent is polyurethane binding.
No matter adopting above-mentioned that binding agent can make tapetum stablize is connected on base fabric.
In the flocking technique of above-mentioned mixing flocked fabric, in described binding agent, addThere is the additive that can control its viscosity and eliminate bubble.
In the flocking technique of above-mentioned mixing flocked fabric, described additive be ammoniacal liquor,Melamine and calcium carbonate, the mass ratio of said components is followed successively by 1:1:2-5, described stickyThe mass ratio of knot agent and additive is 10:1-2.
In the flocking technique of above-mentioned mixing flocked fabric, described additive be ammoniacal liquor,ADC blowing agent, calcium carbonate, the mass ratio of said components is followed successively by 1:1:2-5, described inThe mass ratio of binding agent and additive is 10:1-2.
In the flocking technique of above-mentioned mixing flocked fabric, the length of described bamboo-carbon fibre suedeDegree is 0.8-1.1 millimeters.
In the flocking technique of above-mentioned mixing flocked fabric, the length of described viscose glue suede is1.2-1.4 millimeters.
In the flocking technique of above-mentioned mixing flocked fabric, the base fabric in described steps AFor nonwoven.
In the flocking technique of above-mentioned mixing flocked fabric, the base fabric in described steps AFor knitted fabric.
In the flocking technique of above-mentioned mixing flocked fabric, the base fabric in described steps AFor woven base fabric.
Compared with prior art, this mixing flocked fabric is because tapetum is bamboo-carbon fibre portionWith the interval setting of viscose glue portion, therefore, this mixing flocked fabric has enough elastic sameTime its adsorptivity also relatively good.
Meanwhile, the flocking technique of this mixing flocked fabric is by between bamboo-carbon fibre portion and viscose suedeEvery setting, therefore, partes villosa is independent of each other, and combines the advantage of bi-material,Obtain eventually high performance mixing flocked fabric.
Brief description of the drawings
Fig. 1 is the sectional structure schematic diagram of this mixing flocked fabric.
In figure, 1, base fabric; 2, tapetum; 2a, bamboo-carbon fibre portion; 2b, viscose glue suedePortion; 3, adhesive layer.
Detailed description of the invention
Embodiment mono-
As shown in Figure 1, this mixing flocked fabric comprises base fabric 1 and is connected in base fabric 1 sideTapetum 2 on face, has adhesive layer 3 between described base fabric 1 and tapetum 2, above-mentionedTapetum 2 is connected in base fabric 1 sidepiece by bonding 3 layers, and described adhesive layer 3 is epoxyResin glue, described tapetum 2 is the spaced bamboo-carbon fibre 2a of portion and viscose glue suede portion2b。
The set-up mode of the 2a of bamboo-carbon fibre portion and the viscose glue suede 2b of portion is multiple, as follows:
One, the described bamboo-carbon fibre 2a of portion and the viscose glue suede 2b of portion are all strip, above-mentioned bambooThe charcoal fiber 2a of portion and the viscose glue suede 2b of portion one by one interval arrange.
Two, the described bamboo-carbon fibre 2a of portion and the equal indentation of the viscose glue suede 2b of portion, above-mentioned bambooCharcoal fiber portion and viscose glue suede portion one by one interval arrange.
Three, the described bamboo-carbon fibre 2a of portion and the equal undulate of the viscose glue suede 2b of portion, above-mentioned bambooThe charcoal fiber 2a of portion and the viscose glue suede 2b of portion one by one interval arrange.
Four, the described bamboo-carbon fibre 2a of portion and the viscose glue suede 2b of portion all ringwise, above-mentioned bamboo charcoalThe 2a of fiber portion and the viscose glue suede 2b of portion one by one interval arrange and the above-mentioned 2a of bamboo-carbon fibre portionArrange with the viscose glue suede 2b of portion concentric.
The area of the described viscose glue suede 2b of portion and the 2a of bamboo-carbon fibre portion Area Ratio are 1:1.
Can make firmly to link together between base fabric 1 and tapetum 2 by adhesive layer 3,Meanwhile, because adhesive layer 3 is epoxy resin. Due to the molecular structure of epoxy resin be withIn strand, contain active epoxide group for its feature, epoxide group can be positioned at moleculeThe end of chain, centre or circlewise structure. Owing to containing active epoxy in molecular structureGroup, makes them form insoluble with polytype curing agent generation cross-linking reactionThere is the cancellated high polymer of three-dimensional. In all molecular structures, contain the high score of epoxide groupSub-compound is referred to as epoxy resin. Solidify after epoxy resin have good physics,Chemical property, it is to having excellent adhesive strength, dielectricity between base fabric and tapetumCan be good, set shrinkage factor is little, product size good stability, hardness is high, and pliability isGood, to alkali and most of solvent-stable.
Due to bamboo-carbon fibre portion and the interval setting of viscose glue suede portion, therefore, it combines viscose glueThe advantage of suede and bamboo-carbon fibre, tool also when making this mixing flocked fabric excellent adsorptionThere are enough resiliences.
The flocking technique of this mixing flocked fabric comprises the following steps:
A, get the raw materials ready: the fabric of the standby preseting length of choosing and width is as base fabric, the standby viscose glue suede of choosingWith bamboo-carbon fibre suede as tapetum raw material.
In the present embodiment, the base fabric in described steps A is nonwoven. Certainly, according to realityBorder situation, it is also feasible adopting knitted fabric or woven base fabric.
B, flocking: viscose glue suede and sticking on base fabric of bamboo-carbon fibre suede interval are plantedVelvet fabric blank.
In the present embodiment, on base fabric, be coated with binding agent. Bonding in described step BAgent is acrylate adhesive. According to actual conditions, the binding agent in described step B isPolyurethane binding is also feasible.
In described binding agent, add and have the additive that can control its viscosity and eliminate bubble.
Described additive is ammoniacal liquor, melamine and calcium carbonate, the quality of said componentsThan being followed successively by 1:1:2, the mass ratio of described binding agent and additive is 10:1.
Additive can also adopt another scheme, that is: described additive be ammoniacal liquor,ADC blowing agent, calcium carbonate, the mass ratio of said components is followed successively by 1:1:2, described bondingThe mass ratio of agent and additive is 10:1.
C, steam: in the environment by above-mentioned flocked fabric blank in 140OC, carry out 5Minute.
D, washing: the flocked fabric blank after steaming is put into clear water and wash, treatFlocked fabric blank after washing obtains the mixing flocked fabric of finished product after being dried.
In the flocking technique of above-mentioned mixing flocked fabric, the length of described bamboo-carbon fibre suedeDegree is 0.8 millimeter.
In the flocking technique of above-mentioned mixing flocked fabric, the length of described viscose glue suede is1.2 millimeter.
Embodiment bis-
As shown in Figure 1, this mixing flocked fabric comprises base fabric 1 and is connected in base fabric 1 sideTapetum 2 on face, has adhesive layer 3 between described base fabric 1 and tapetum 2, above-mentionedTapetum 2 is connected in base fabric 1 sidepiece by bonding 3 layers, and described adhesive layer 3 is epoxyResin glue, described tapetum 2 is the spaced bamboo-carbon fibre 2a of portion and viscose glue suede portion2b。
The set-up mode of the 2a of bamboo-carbon fibre portion and the viscose glue suede 2b of portion is multiple, as follows:
One, the described bamboo-carbon fibre 2a of portion and the viscose glue suede 2b of portion are all strip, above-mentioned bambooThe charcoal fiber 2a of portion and the viscose glue suede 2b of portion one by one interval arrange.
Two, the described bamboo-carbon fibre 2a of portion and the equal indentation of the viscose glue suede 2b of portion, above-mentioned bambooCharcoal fiber portion and viscose glue suede portion one by one interval arrange.
Three, the described bamboo-carbon fibre 2a of portion and the equal undulate of the viscose glue suede 2b of portion, above-mentioned bambooThe charcoal fiber 2a of portion and the viscose glue suede 2b of portion one by one interval arrange.
Four, the described bamboo-carbon fibre 2a of portion and the viscose glue suede 2b of portion all ringwise, above-mentioned bamboo charcoalThe 2a of fiber portion and the viscose glue suede 2b of portion one by one interval arrange and the above-mentioned 2a of bamboo-carbon fibre portionArrange with the viscose glue suede 2b of portion concentric.
The area of the described viscose glue suede 2b of portion and the 2a of bamboo-carbon fibre portion Area Ratio are 1:5.
Can make firmly to link together between base fabric 1 and tapetum 2 by adhesive layer 3,Meanwhile, because adhesive layer 3 is epoxy resin. Due to the molecular structure of epoxy resin be withIn strand, contain active epoxide group for its feature, epoxide group can be positioned at moleculeThe end of chain, centre or circlewise structure. Owing to containing active epoxy in molecular structureGroup, makes them form insoluble with polytype curing agent generation cross-linking reactionThere is the cancellated high polymer of three-dimensional. In all molecular structures, contain the high score of epoxide groupSub-compound is referred to as epoxy resin. Solidify after epoxy resin have good physics,Chemical property, it is to having excellent adhesive strength, dielectricity between base fabric and tapetumCan be good, set shrinkage factor is little, product size good stability, hardness is high, and pliability isGood, to alkali and most of solvent-stable.
Due to bamboo-carbon fibre portion and the interval setting of viscose glue suede portion, therefore, it combines viscose glueThe advantage of suede and bamboo-carbon fibre, tool also when making this mixing flocked fabric excellent adsorptionThere are enough resiliences.
The flocking technique of this mixing flocked fabric comprises the following steps:
A, get the raw materials ready: the fabric of the standby preseting length of choosing and width is as base fabric, the standby viscose glue suede of choosingWith bamboo-carbon fibre suede as tapetum raw material.
In the present embodiment, the base fabric in described steps A is nonwoven. Certainly, according to realityBorder situation, it is also feasible adopting knitted fabric or woven base fabric.
B, flocking: viscose glue suede and sticking on base fabric of bamboo-carbon fibre suede interval are plantedVelvet fabric blank.
In the present embodiment, on base fabric, be coated with binding agent. Bonding in described step BAgent is acrylate adhesive. According to actual conditions, the binding agent in described step B isPolyurethane binding is also feasible.
In described binding agent, add and have the additive that can control its viscosity and eliminate bubble.
Described additive is ammoniacal liquor, melamine and calcium carbonate, the quality of said componentsThan being followed successively by 1:1:5, the mass ratio of described binding agent and additive is 10:2.
Additive can also adopt another scheme, that is: described additive be ammoniacal liquor,ADC blowing agent, calcium carbonate, the mass ratio of said components is followed successively by 1:1:5, described bondingThe mass ratio of agent and additive is 10:2.
C, steam: in the environment by above-mentioned flocked fabric blank in 160OC, carry out20 minutes.
D, washing: the flocked fabric blank after steaming is put into clear water and wash, treatFlocked fabric blank after washing obtains the mixing flocked fabric of finished product after being dried.
In the flocking technique of above-mentioned mixing flocked fabric, the length of described bamboo-carbon fibre suedeDegree is 1.1 millimeters.
In the flocking technique of above-mentioned mixing flocked fabric, the length of described viscose glue suede is1.4 millimeter.
Embodiment tri-
As shown in Figure 1, this mixing flocked fabric comprises base fabric 1 and is connected in base fabric 1 sideTapetum 2 on face, has adhesive layer 3 between described base fabric 1 and tapetum 2, above-mentionedTapetum 2 is connected in base fabric 1 sidepiece by bonding 3 layers, and described adhesive layer 3 is epoxyResin glue, described tapetum 2 is the spaced bamboo-carbon fibre 2a of portion and viscose glue suede portion2b。
The set-up mode of the 2a of bamboo-carbon fibre portion and the viscose glue suede 2b of portion is multiple, as follows:
One, the described bamboo-carbon fibre 2a of portion and the viscose glue suede 2b of portion are all strip, above-mentioned bambooThe charcoal fiber 2a of portion and the viscose glue suede 2b of portion one by one interval arrange.
Two, the described bamboo-carbon fibre 2a of portion and the equal indentation of the viscose glue suede 2b of portion, above-mentioned bambooCharcoal fiber portion and viscose glue suede portion one by one interval arrange.
Three, the described bamboo-carbon fibre 2a of portion and the equal undulate of the viscose glue suede 2b of portion, above-mentioned bambooThe charcoal fiber 2a of portion and the viscose glue suede 2b of portion one by one interval arrange.
Four, the described bamboo-carbon fibre 2a of portion and the viscose glue suede 2b of portion all ringwise, above-mentioned bamboo charcoalThe 2a of fiber portion and the viscose glue suede 2b of portion one by one interval arrange and the above-mentioned 2a of bamboo-carbon fibre portionArrange with the viscose glue suede 2b of portion concentric.
The area of the described viscose glue suede 2b of portion and the 2a of bamboo-carbon fibre portion Area Ratio are 1:2.
Can make firmly to link together between base fabric 1 and tapetum 2 by adhesive layer 3,Meanwhile, because adhesive layer 3 is epoxy resin. Due to the molecular structure of epoxy resin be withIn strand, contain active epoxide group for its feature, epoxide group can be positioned at moleculeThe end of chain, centre or circlewise structure. Owing to containing active epoxy in molecular structureGroup, makes them form insoluble with polytype curing agent generation cross-linking reactionThere is the cancellated high polymer of three-dimensional. In all molecular structures, contain the high score of epoxide groupSub-compound is referred to as epoxy resin. Solidify after epoxy resin have good physics,Chemical property, it is to having excellent adhesive strength, dielectricity between base fabric and tapetumCan be good, set shrinkage factor is little, product size good stability, hardness is high, and pliability isGood, to alkali and most of solvent-stable.
Due to bamboo-carbon fibre portion and the interval setting of viscose glue suede portion, therefore, it combines viscose glueThe advantage of suede and bamboo-carbon fibre, tool also when making this mixing flocked fabric excellent adsorptionThere are enough resiliences.
The flocking technique of this mixing flocked fabric comprises the following steps:
A, get the raw materials ready: the fabric of the standby preseting length of choosing and width is as base fabric, the standby viscose glue suede of choosingWith bamboo-carbon fibre suede as tapetum raw material.
In the present embodiment, the base fabric in described steps A is nonwoven. Certainly, according to realityBorder situation, it is also feasible adopting knitted fabric or woven base fabric.
B, flocking: viscose glue suede and sticking on base fabric of bamboo-carbon fibre suede interval are plantedVelvet fabric blank.
In the present embodiment, on base fabric, be coated with binding agent. Bonding in described step BAgent is acrylate adhesive. According to actual conditions, the binding agent in described step B isPolyurethane binding is also feasible.
In described binding agent, add and have the additive that can control its viscosity and eliminate bubble.
Described additive is ammoniacal liquor, melamine and calcium carbonate, the quality of said componentsThan being followed successively by 1:1:3, the mass ratio of described binding agent and additive is 10:1.5.
Additive can also adopt another scheme, that is: described additive be ammoniacal liquor,ADC blowing agent, calcium carbonate, the mass ratio of said components is followed successively by 1:1:3, described bondingThe mass ratio of agent and additive is 10:1.5.
C, steam: in the environment by above-mentioned flocked fabric blank in 150 DEG C, carry out10 minutes.
D, washing: the flocked fabric blank after steaming is put into clear water and wash, treatFlocked fabric blank after washing obtains the mixing flocked fabric of finished product after being dried.
In the flocking technique of above-mentioned mixing flocked fabric, the length of described bamboo-carbon fibre suedeDegree is 1 millimeter.
In the flocking technique of above-mentioned mixing flocked fabric, the length of described viscose glue suede is1 millimeter.
Claims (6)
1. mix a flocked fabric, this fabric comprises base fabric and is connected on base fabric sideTapetum, it is characterized in that thering is adhesive layer between described base fabric and tapetum, onState tapetum and be connected in base fabric sidepiece by adhesive layer, described adhesive layer is epoxide-resin glue,Described tapetum is spaced bamboo-carbon fibre portion and viscose glue suede portion.
2. mixing flocked fabric according to claim 1, is characterized in that, described inBamboo-carbon fibre portion and viscose glue suede portion are all strip, above-mentioned bamboo-carbon fibre portion and viscose glue suede portionInterval arranges one by one.
3. mixing flocked fabric according to claim 1, is characterized in that, described inThe equal indentation of bamboo-carbon fibre portion and viscose glue suede portion, above-mentioned bamboo-carbon fibre portion and viscose glue suede portionInterval arranges one by one.
4. mixing flocked fabric according to claim 1, is characterized in that, described inThe equal undulate of bamboo-carbon fibre portion and viscose glue suede portion, above-mentioned bamboo-carbon fibre portion and viscose glue suede portionInterval arranges one by one.
5. mixing flocked fabric according to claim 1, is characterized in that, described inBamboo-carbon fibre portion and viscose glue suede portion all ringwise, above-mentioned bamboo-carbon fibre portion and viscose glue suede portion oneOne interval arranges and above-mentioned bamboo-carbon fibre portion and viscose glue suede portion concentric arranges.
6. mixing flocked fabric according to claim 1, is characterized in that, described inThe area of viscose glue suede portion and bamboo-carbon fibre portion Area Ratio are 1:1-5.