CN205223012U - Super thick SGP laminated glass - Google Patents
Super thick SGP laminated glass Download PDFInfo
- Publication number
- CN205223012U CN205223012U CN201520890417.XU CN201520890417U CN205223012U CN 205223012 U CN205223012 U CN 205223012U CN 201520890417 U CN201520890417 U CN 201520890417U CN 205223012 U CN205223012 U CN 205223012U
- Authority
- CN
- China
- Prior art keywords
- sgp
- glass
- super thick
- laminated glass
- thickness
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model belongs to the technical field of glass, concretely relates to super thick SGP laminated glass and preparation method, establish the SGP film between two super thick glass substrate including two at least super thick glass substrate and double -layered, wherein the SGP film and two super thick glass substrate same size, super thick glass substrate's thickness is greater than 10mm, and the thickness of SGP film is greater than 1.52mm, gained super thick SGP laminated glass not only has security higher than ordinary laminated glass and energy -conserving characteristic, has perfect outward appearance moreover, bubble etc. Can not appear.
Description
Technical field
The utility model belongs to glass technology field, is specifically related to a kind of super thick SGP laminated glass.
Background technology
SGP doubling glass is produced by certain production technique by more than 2 glass and SGP film, and SGP doubling glass, as very reliable shatter proof glass, is particularly widely used in some important explosion-proof places at building field.
Wherein, super thick SGP doubling glass, its glass substrate is often referred to tempering or the semi-tempered glass that thickness is greater than 10mm, and SGP film size can require selected according to explained hereafter, after synthesis laminated glass, total thickness is greater than 21.52mm.The SGP doubling glass of super thick has the security higher than common laminated glass and energy conservation characteristic (security can embody in falling-ball impact test and the test of canister shot bag impact property).But prior art cannot make the qualified super thick SGP laminated glass of performance (being mainly reflected in resistance toheat test defective).Existing SGP laminated glass produces and generally adopts below 10mm thickness substrate, and structure is as 10mm glass+1.52mm film+10mm glass, total thickness 21.52mm.If substrate thickness increases, such as, when glass substrate is the SGP laminated glass of 12mm and more than 12mm thickness again, carries out the test of laminated glass resistance toheat and there will be the macroscopic irregularitys such as bubble, do not meet laminated glass performance requriements.
Utility model content
In order to solve the problem, the purpose of this utility model is the super thick SGP laminated glass providing a kind of security higher than common laminated glass and energy conservation characteristic.
Two of the purpose of this utility model there is provided the preparation method of described super thick SGP laminated glass; Super thick SGP laminated glass prepared by the method, through correlation test, outward appearance and properties agreement with experimental laminated glass national standard.
The utility model is achieved through the following technical solutions:
A kind of super thick SGP laminated glass, the SGP film comprising at least two pieces of super thick glass substrates and be folded between two pieces of super thick glass substrates, described SGP film and described two pieces of super thick glass substrates onesize; The thickness of described super thick glass substrate is greater than 10mm.
Preferably, the thickness of described super thick glass substrate is 12mm, 15mm or 19mm.
Preferably, the thickness of described SGP film is greater than 1.52mm.
Preferably, the thickness of described SGP film is 3.04mm.
Preferably, described SGP film is the SGP ionic polymer intermediate coat that du pont company produces.
Prepare described super thick SGP laminated glass, preparation technology is: glass loading → cleaning machine cleaning glass → conjunction sheet → roll-in → vacuumize → send in autoclave to vacuumize to fire → lower the temperature and come out of the stove; Described SGP laminated glass to enter before autoclave cold-draw 30 minutes, and the cooling of described SGP laminated glass control of coming out of the stove is 60 ± 5 DEG C.
Preferably, vacuumize in ablating work procedure in described feeding autoclave, autoclave pressure is promoted to 1.35Mpa.The autoclave pressure of common laminated glass Production Flow Chart generally can only reach 1.1Mpa or following; Promote after autoclave pressure, effectively can improve super thick SGP laminated glass and be produced into power, make glass and film engagement tightr.
Preferably, the SGP laminated glass after described conjunction sheet continues to vacuumize every sheet laminated glass after sending into autoclave, and it is-0.08Mpa that whole sintering procedure controls vacuum tightness.Make every sheet glass be in negative pressure in vacuum bag, reduce the possibility occurring bubble.
Preferably, in described roll process, compression roller heights reduces by 4 ~ 5mm according to laminated glass thickness and arranges.If production specification is 15mm+2.28mm+15mm, total thickness is the laminated glass of 32.28mm, and arranging compression roller heights is 28mm.
In-furnace temperature is arranged: (take production specification as 15mm+2.28mm+15mm glass be example)
Preferably, described in the operation that vacuumizes, every sheet glass configures a plastic vacuum bag, a vacuum tap vacuumizes, to get rid of air in sack.
The SGP film that the utility model comprises at least two pieces of super thick glass substrates and is folded between two pieces of super thick glass substrates, SGP film and described two pieces of super thick glass substrates onesize; The thickness of super thick glass substrate is greater than 10mm, and the thickness of SGP film is greater than 1.52mm, and is prepared by regulable control preparation technology.Not only there is the security higher than common laminated glass and energy conservation characteristic, and there is perfect outward appearance; Carry out the test of laminated glass resistance toheat and there will not be bubble etc.
Accompanying drawing explanation
Super thick SGP laminated glass structural representation in Fig. 1 the utility model.
concrete embodiment
Below in conjunction with embodiment, the utility model is described in further detail, understands the utility model to help those skilled in the art.
A kind of super thick SGP laminated glass, the SGP film 3 comprising at least two pieces of super thick glass substrates (upper glass substrate 11 and lower glass substrate 12) and be folded between two pieces of super thick glass substrates, described SGP film and described two pieces of super thick glass substrates onesize, wherein the thickness of super thick glass substrate is 12mm, 15mm or 19mm, these are several is existing specifications, but does not get rid of the glass being greater than other thickness of 10mm.The thickness of SGP film is greater than 1.52mm (according to circumstances can select 3.04mm or 2.28mm etc.).Super thick SGP laminated glass structure can be single layer structure: super thick glass/SGP film/super thick glass.Also can be multilayered structure: super thick glass/SGP film/super thick glass/SGP film/,, ,/super thick glass.The wherein SGP film SGP ionic polymer intermediate coat of preferably selecting du pont company to produce, this SGP ionic polymer intermediate coat, its excellent performance, tear strength is 5 times of general PVB film, hardness be the 30-l00 of PVB film doubly.
Prepare described super thick SGP laminated glass, preparation technology is: glass loading → cleaning machine cleaning glass → conjunction sheet → roll-in → vacuumize → send in autoclave to vacuumize to fire → lower the temperature and come out of the stove.
Wherein:
One, roll-in optimum configurations:
1, compression roller heights: reduce 4-5mm according to laminated glass thickness and arrange, if production specification is 15mm+2.28mm+15mm, total thickness is the laminated glass of 32.28mm, and arranging compression roller heights is 28mm;
2, in-furnace temperature is arranged: (take production specification as 15mm+2.28mm+15mm glass be example)
| Stove one temperature | Stove two temperature | Stove three temperature | Stove four temperature | Walking speed | Glass tapping temperature |
| 106℃ | 202℃ | 209℃ | 202℃ | 0.9m/min | 63℃ |
The glass temperature of different thickness and walking speed can be finely tuned, and controlling glass tapping temperature is herein 60 ± 5 DEG C.
Two, vacuumize, every sheet glass configures a plastic vacuum bag, a vacuum tap vacuumizes, to get rid of air in sack.
Three, autoclave optimum configurations:
1, glass enters stokehold cold-draw 30 minutes.
2, when previous step vacuumizes, every sheet glass has configured a plastic vacuum bag, a vacuum tap, after autoclave sent into by glass, vacuum pump is utilized to vacuumize process to every sheet laminated glass respectively, it is-0.08Mpa that whole sintering procedure controls vacuum tightness, make every sheet glass be in negative pressure in vacuum bag, reduce the possibility occurring bubble.
3, heat up and reach after 134 DEG C and pressure reaches 1.35Mpa, be incubated 120 minutes; Transform by boost in pressure to 1.35Mpa by autoclave herein, before original autoclave transformation, pressure can only reach 1.1Mpa, promotes the key factor that autoclave pressure is production super thick SGP laminated glass.
4, lower the temperature: drop to 50 DEG C of final vacuums with the cooling rate of per minute 4 DEG C and come out of the stove.
Other operations are prior art, do not repeat them here.
Above-described embodiment, just preferred embodiment of the present utility model, not be used for limiting the utility model practical range, therefore all equivalences done with the feature described in the utility model claim and principle change or modify, and all should be included within the utility model right.
Safety feature test
Respectively the super thick SGP laminated glass that the structure made is the white glass of the white glass of 12mm+2.28mmSGP+12mm, the white glass of the white glass of 15mm+2.28mmSGP+15mm and the white glass of the white glass of 19mm+3.04mmSGP+19mm is carried out:
1, thermal test.Result: bubble-free or crackle;
2, radiation hardness test.Result: without obvious aberration before and after uviolizing;
3, ball falling impact stripping test.Result: steel ball quality 2260g, 12+2.28SGP+12 height of drop 4800mm, glass does not destroy, test OK; 15+2.28SGP+15 height of drop 4800mm, glass does not destroy, test OK; 19+3.04SGP+19 height of drop 4800mm, glass does not destroy, test OK; (in contrast, the laminated glass of 8+1.52+8 thickness, damaged at height 3800mm)
4, canister shot bag impact property test.Result: 1500mm is not damaged for height, test OK.
Claims (5)
1. a super thick SGP laminated glass, the SGP film comprising at least two pieces of super thick glass substrates and be folded between two pieces of super thick glass substrates, described SGP film and described two pieces of super thick glass substrates onesize; It is characterized in that, the thickness of described super thick glass substrate is greater than 10mm.
2. super thick SGP laminated glass as described in the appended claim 1, it is characterized in that, the thickness of described super thick glass substrate is 12mm, 15mm or 19mm.
3. super thick SGP laminated glass as described in claim 1 or 2, is characterized in that, the thickness of described SGP film is greater than 1.52mm.
4. super thick SGP laminated glass as claimed in claim 3, it is characterized in that, the thickness of described SGP film is 3.04mm.
5. super thick SGP laminated glass as claimed in claim 4, is characterized in that, described SGP film is the SGP ionic polymer intermediate coat that du pont company produces.