CN205036032U - Antique floor - Google Patents

Antique floor Download PDF

Info

Publication number
CN205036032U
CN205036032U CN201520697889.3U CN201520697889U CN205036032U CN 205036032 U CN205036032 U CN 205036032U CN 201520697889 U CN201520697889 U CN 201520697889U CN 205036032 U CN205036032 U CN 205036032U
Authority
CN
China
Prior art keywords
layer
parts
official
antique
coating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201520697889.3U
Other languages
Chinese (zh)
Inventor
倪月忠
马琳
沈丽华
史蔷
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ZHEJIANG SHIYOU WOOD INDUSTRY Co Ltd
Original Assignee
ZHEJIANG SHIYOU WOOD INDUSTRY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ZHEJIANG SHIYOU WOOD INDUSTRY Co Ltd filed Critical ZHEJIANG SHIYOU WOOD INDUSTRY Co Ltd
Priority to CN201520697889.3U priority Critical patent/CN205036032U/en
Application granted granted Critical
Publication of CN205036032U publication Critical patent/CN205036032U/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The utility model belongs to the floor field relates to an antique floor, be in including plain sheet layer modelled after an antique, setting stereoeffect layer, coating on the plain sheet layer modelled after an antique are in crosslinked layer on the stereoeffect layer, scribble in filling layer on the crosslinked layer is in with the coating protective layer on the filling layer and being located surface course on the protective layer, the protective layer including the wearing course that sets gradually or set up in turn, increase hard formation and the anti layer of scraping. The utility model discloses a component to each coating layer is improved, combines every layer component characteristics, improves antique floor's hiberarchy, each coating layer of reasonable distribution, and the roughness on product surface is better, connection reinforce between each layer, the quality of product is protected, and the product superficial hardness gets a promotion, has increased surperficial anti scratch and surface abrasion -resistant revolution, has also guaranteed the toughness of coating layer simultaneously, has improved the comfort level of feel.

Description

A kind of ancient imitation floor board
Technical field
The utility model belongs to field, floor, relates to a kind of ancient imitation floor board.
Background technology
Current ancient imitation floor board has very large market.The sheet material of consolidated floor is medium and high density fibre panel, and inherently hot pressing is formed, and changes its surface to form concavo-convex texture, reach antique effect by hot pressing.And solid wood blank directly hot pressing cannot generate antique effect.If application number is the Chinese utility model patent of 201110025680.9, disclose a kind of manufacture method of solid wood composite antique floor, first composite plate made from solid wood front is made to have the imitative wood texture of depression to composite plate made from solid wood front by engraving roller process, by having the hot-pressing roller protruding texture, surperficial hot pressing charing process being carried out to described composite plate made from solid wood front again, finally sanding surface and application process being carried out to composite plate made from solid wood front; Protrusion texture on described hot-pressing roller and the imitative wood texture of described depression match.This utility model solves solid wooden compound floor cannot directly hot pressing thus generate the problem of antique effect after wire drawing.But due to the imitative wood texture of ancient imitation floor board, its surface irregularity is very large on the application impact in later stage, existing application techniques and existing coating, still be adapted to plane floor, the surface texture poor effect special to ancient imitation floor board, even cannot be suitable for.Mainly solve by thickening coating layer now, but also not only the coating layer of various function function originally cannot be embodied, the quality degradation on floor, feel is poor, and cost is high.
Utility model content
The purpose of this utility model is to provide a kind of ancient imitation floor board, and by improving the structure on floor, the component of coating, no matter the floor obtained is in quality, outward appearance or in feel, all more optimizes than existing ancient imitation floor board.
The utility model realizes above-mentioned purpose by following technical scheme: a kind of ancient imitation floor board, it is characterized in that, comprise plain flaggy modelled after an antique, the stereoeffect layer be arranged on described plain flaggy modelled after an antique, the cross-linked layer be coated on described stereoeffect layer, be applied to the packed layer on described cross-linked layer and the topping be coated on described packed layer and the surface layer be positioned on described topping; Described topping comprises the wearing course, Hardening layer and the scratch-resistant layer that set gradually or be arranged alternately.
As preferably, the order of the wearing course be arranged alternately, Hardening layer and scratch-resistant layer is wearing course, scratch-resistant layer, Hardening layer, wearing course, Hardening layer and scratch-resistant layer.A best combination is had to the surperficial scratch-resistant on floor, surface abrasion resistance revolution and pliability.
As preferably, described cross-linked layer comprises the component of following weight portion: the mono-official's urethane acrylate of 10-20 part UV, 5-20 part UV pure acrylic resin, 10-20 part UV propylene oxide olefin(e) acid ester, 10-30 part single official UV monomer, 5-20 part modified glass powder filler, 3-15 part composite photoinitiator.
UV mono-official urethane acrylate that cross-linked layer adopts, UV pure acrylic resin, single official UV monomer have the feature of lower shrinkage and high attachment, UV modified epoxy propylene olefin(e) acid ester has good intensity and adhesive power, modified glass powder filler is with silane coupler modified, base material can not only be embedded and follow-up coating can be embedded, form the interlocking formed a connecting link, and good compatibility can be had with whole coating system.Improve the transparency of coating and the comprehensive strength of coating.Adopt composite photoinitiator, taken into account deep cure and shallow-layer solidification effect, the coating that part immerses base material fully can be solidified, finally make coating have good adhesive power.
As preferably, described packed layer comprises the component of following weight portion: 15-25 part UV propylene oxide olefin(e) acid ester, 10-15 part UV two official urethane acrylate, 5-15 part UV polyester acrylate, 10-20 part two official UV monomer or three official UV monomer, 5-15 part compounded mix, 3-6 part composite photoinitiator.
As preferably, the compounded mix in described packed layer is glass dust and talcous mixture, and described glass dust and talcous mass mixing ratio are 1:0.1-5.
The UV propylene oxide olefin(e) acid ester that packed layer adopts has the good advantage of intensity, UV two official urethane acrylate can balance the toughness of paint film, UV polyester acrylate can improve wetting, levelability, compounded mix is composited by glass dust and French chalk, glass dust can improve whole paint film strength and hardness, French chalk can improve the filling of paint film and polishing characteristic, and not only fillibility is good, and strength of coating, toughness are all very excellent.
As preferably, described surface layer comprises the component of following weight portion: 30-40 part UV6 ~ 9 official's urethane acrylate, 10-20 part UV two official urethane acrylate, 30-40 part UV compound monomer, 3-8 part UV composite nano inoganic material, 0.5-3 part tetrafluoro wax powder, 0.2-1 part organosilyl surface controlling agent.
UV6 ~ 9 official's urethane acrylate of surface layer can provide good cross-linking effect, the UV two official urethane acrylate of collocation good toughness, can the hardness of balanced tree resin system and toughness well, makes resistance to scratch finish paint firmly and not crisp.Again in conjunction with UV composite nano inoganic material, good scratch resistant can be improved, introduce tetrafluoro wax powder and photo curable organosilyl surface state controlling agent, make product have good scratch resistant, feel and antifouling effect, finally make film have high rigidity, good resistance to marring and feel.
As preferably, described wearing course comprises the component of following weight portion: 15-25 part UV6 ~ 9 official's urethane acrylate, 15-25 part UV modified epoxy propylene olefin(e) acid ester, 15-25 part two official UV monomer or three official UV monomer, the wear-resistant powder of 10-20 part modification high rigidity, 1-5 part anti-settling agent, 2-4 part light trigger.
As preferably, the wear-resistant powder of described modification high rigidity is the alundum (Al2O3) through surface modification.
UV6 ~ 9 official's urethane acrylate that wearing course adopts can provide good cross-linking effect, UV modified epoxy propylene olefin(e) acid ester has the good advantage of intensity, two/three official UV monomers can carry out chemical crosslinking well with UV6 ~ 9 official's urethane acrylate, formation has highdensity tridimensional network, the wear-resistant powder of modification high rigidity is the highly purified alundum (Al2O3) (AL2O3) through surface modification, mix with resin system height, fully can show the ultrahigh hardness super-high wear-resistant of alundum (Al2O3), highly cross-linked resin system is in conjunction with the filler reinforcement of ultrahigh hardness, make the abrasion resistant effect that whole coating reaches best.
As preferably, described Hardening layer comprises the component of following weight portion: 20-30 part UV propylene oxide olefin(e) acid ester, 5-10 part UV two official urethane acrylate, 5-10 part UV many officials urethane acrylate, 20-35 part two official UV monomer or three official UV monomer, 3-6 part composite photoinitiator.
Hardening layer adopts UV propylene oxide olefin(e) acid ester to have the good advantage of intensity, UV two official urethane acrylate can balance the toughness of paint film, reduce cure shrinkage, UV many officials urethane acrylate all adopts phenyl ring hard segment structure to improve coating hardness, two/three official UV monomers can provide good cross-linking effect, two/three official UV monomers and UV modified epoxy propylene olefin(e) acid ester is caused by composite photoinitiator, UV two official urethane acrylate, UV many officials urethane acrylate carries out degree of depth chemical crosslinking, paint film is made to have high strength, good toughness, lower shrinkage, the advantage of high attachment, coating is made to reach good Hardening effect.
As preferably, described scratch-resistant layer comprises the component of following weight portion: 20-30 part UV propylene oxide olefin(e) acid ester, 10-15 part UV two official urethane acrylate, 20-30 part two official UV monomer or three official UV monomer, 15-25 part glass dust filler, 3-6 part composite photoinitiator.
Scratch-resistant layer adopts UV propylene oxide olefin(e) acid ester to have the good advantage of intensity, UV two official urethane acrylate can balance the toughness of paint film, two/three official UV monomers can provide good cross-linking effect, modified glass powder filler can mix with coating resin well, fully can show the high rigidity of glass dust, high transparency, high scratch resistant, adopt composite photoinitiator, the double bond conversion rate of film can be improved, painting film strength is increased, and residual smell reduces.
The utility model also has an object, be to provide ancient imitation floor board surface specially treated coating method, comprise the following steps: (1) makes plain flaggy modelled after an antique at plain plate polishing grinding modelled after an antique, to described plain flaggy modelled after an antique carry out water-based painted, dry; (2) be coated with cross-linked layer, treat that it is half-dried; Cross-linked layer is coated with packed layer coating, after it is half-dried, is again coated with filling paint, treat its surface drying, obtain packed layer; (3) carry out sanding process to packed layer, coating wearing course, treats its surface drying, and coating Hardening layer, treats that it is half-dried, and coating scratch-resistant layer, treats its surface drying, then carry out sanding process, and coating surface layer, treats that it is absolutely dry, obtain finished product.
By implementing technique scheme, the utility model, by improving the component of each coating layer, in conjunction with the component feature of every layer, improves the hierarchical structure of ancient imitation floor board, the each coating layer of reasonable layout, the planeness of product surface is better, and the attachment force between each layer is strong, and the quality of product is protected, product surface hardness gets a promotion, add surperficial scratch-resistant and surface abrasion resistance revolution, also ensure that the toughness of coating layer simultaneously, improve the comfort level of feel; Coating process is simple to operate, the feature of each layer can be fully demonstrated, and cost is also low.
Accompanying drawing explanation
Accompanying drawing 1 is the structural representation of the utility model one embodiment.
Detailed description of the invention
Below in conjunction with specific embodiment, the utility model is described in further detail.
Embodiment 1:
A kind of ancient imitation floor board, as shown in Figure 1, comprise solid wood plain flaggy 101 modelled after an antique, be coated in the stereoeffect layer 102 on plain flaggy 101 modelled after an antique, described stereoeffect layer 102 applies cross-linked layer 103, packed layer 104, wearing course 105, Hardening layer 106 and scratch-resistant layer 107, surface layer 108 successively.Wherein, wearing course 105, Hardening layer 106 and scratch-resistant layer 107 3 layers is as topping.
Wherein, described cross-linked layer 103 comprises the component of following weight portion: 10 parts of UV mono-official urethane acrylates, 10 parts of UV pure acrylic resins, 20 parts of UV propylene oxide olefin(e) acid esters, 30 parts of single official UV monomers, 5 parts of modified glass powder fillers, 15 parts of composite photoinitiators;
Described packed layer 104 comprises the component of following weight portion: 15 parts of UV propylene oxide olefin(e) acid esters, 12 parts of UV two official urethane acrylates, 15 parts of UV polyester acrylates, 20 part of three official UV monomer, 5 parts of compounded mixs, 6 parts of composite photoinitiators; Compounded mix is glass dust and talcous mixture, and described glass dust and talcous mass mixing ratio are 1:0.1;
Described wearing course 105 comprises the component of following weight portion: 20 parts of UV6 ~ 9 official's urethane acrylates, 25 parts of UV modified epoxy propylene olefin(e) acid esters, 20 part of two official UV monomer, 10 parts of wear-resistant powder of modification high rigidity, 5 parts of anti-settling agents, 3 parts of light triggers; The wear-resistant powder of described modification high rigidity is carry out the alundum (Al2O3) of surperficial oleophylic modification via stearic acid;
Described Hardening layer 106 comprises the component of following weight portion: 20 parts of UV propylene oxide olefin(e) acid esters, 8 parts of UV two official urethane acrylates, 10 parts of UV many officials urethane acrylates, 35 part of two official UV monomer, 3 parts of composite photoinitiators;
Described scratch-resistant layer 107 comprises the component of following weight portion: 26 parts of UV propylene oxide olefin(e) acid esters, 15 parts of UV two official urethane acrylates, 24 part of three official UV monomer, 15 parts of glass dust fillers, 6 parts of composite photoinitiators;
Described surface layer 108 comprises the component of following weight portion: 35 parts of UV6 ~ 9 official's urethane acrylates, 16 parts of UV two official urethane acrylates, 35 parts of UV compound monomers, 5 parts of UV composite nano inoganic materials, 2 parts of tetrafluoro wax powder, 0.5 part of organosilyl surface controlling agent;
Concrete covering with paint step is as follows: (1) makes plain flaggy 101 modelled after an antique at plain plate polishing grinding modelled after an antique, to described plain flaggy 101 modelled after an antique carry out water-based painted, dry; (2) be coated with cross-linked layer 103, treat that it is half-dried; Cross-linked layer 103 is coated with filling paint, after it is half-dried, is again coated with filling paint, treat its surface drying, obtain packed layer 104; (3) carry out sanding process to packed layer 104, coating wearing course 105, treats its surface drying, and coating Hardening layer 106, treats that it is half-dried, and coating scratch-resistant layer 107, treats its surface drying, then carry out sanding process, and coating surface layer 108, treats that it is absolutely dry, obtain finished product.
Embodiment 2:
A kind of ancient imitation floor board, comprise compound plain flaggy 101 modelled after an antique, plain flaggy 101 modelled after an antique is carved with imitative wood texture as stereoeffect layer 102, described stereoeffect layer 102 applies cross-linked layer 103, packed layer 104, wearing course 105, Hardening layer 106 and scratch-resistant layer 107, surface layer 108 successively.Wherein, wearing course 105, Hardening layer 106 and scratch-resistant layer 107 3 layers is as topping.
Wherein, described cross-linked layer 103 comprises the component of following weight portion: 20 parts of UV mono-official urethane acrylates, 5 parts of UV pure acrylic resins, 10 parts of UV propylene oxide olefin(e) acid esters, 20 parts of single official UV monomers, 15 parts of modified glass powder fillers, 3 parts of composite photoinitiators;
Described packed layer 104 comprises the component of following weight portion: 25 parts of UV propylene oxide olefin(e) acid esters, 10 parts of UV two official urethane acrylates, 5 parts of UV polyester acrylates, 15 part of two official UV monomers or three official UV monomers, 10 parts of compounded mixs, 3 parts of composite photoinitiators; Compounded mix is glass dust and talcous mixture, and described glass dust and talcous mass mixing ratio are 1:5;
Described wearing course 105 comprises the component of following weight portion: 25 parts of UV6 ~ 9 official's urethane acrylates, 15 parts of UV modified epoxy propylene olefin(e) acid esters, 15 part of two official UV monomer, 15 parts of wear-resistant powder of modification high rigidity, 3 parts of anti-settling agents, 2 parts of light triggers; The wear-resistant powder of described modification high rigidity is carry out the alundum (Al2O3) of surperficial oleophylic modification via stearic acid;
Described Hardening layer 106 comprises the component of following weight portion: 30 parts of UV propylene oxide olefin(e) acid esters, 5 parts of UV two official urethane acrylates, 5 parts of UV many officials urethane acrylates, 25 part of three official UV monomer, 5 parts of composite photoinitiators;
Described scratch-resistant layer 107 comprises the component of following weight portion: 30 parts of UV propylene oxide olefin(e) acid esters, 10 parts of UV two official urethane acrylates, 20 part of three official UV monomer, 20 parts of glass dust fillers, 4 parts of composite photoinitiators;
Described surface layer 108 comprises the component of following weight portion: 40 parts of UV6 ~ 9 official's urethane acrylates, 20 parts of UV two official urethane acrylates, 40 parts of UV compound monomers, 8 parts of UV composite nano inoganic materials, 3 parts of tetrafluoro wax powder, 1 part of organosilyl surface controlling agent;
Concrete covering with paint step is as follows: (1) makes plain flaggy 101 modelled after an antique at plain plate polishing grinding modelled after an antique, to described plain flaggy 101 modelled after an antique carry out water-based painted, dry; (2) be coated with cross-linked layer 103, treat that it is half-dried; Cross-linked layer 103 is coated with filling paint, after it is half-dried, is again coated with filling paint, treat its surface drying, obtain packed layer 104; (3) carry out sanding process to packed layer 104, coating wearing course 105, treats its surface drying, and coating Hardening layer 106, treats that it is half-dried, and coating scratch-resistant layer 107, treats its surface drying, then carry out sanding process, and coating surface layer 108, treats that it is absolutely dry, obtain finished product.
Embodiment 3:
A kind of ancient imitation floor board, comprise solid wood plain flaggy modelled after an antique, plain flaggy modelled after an antique is carved with imitative wood texture as stereoeffect layer, described stereoeffect layer 102 applies cross-linked layer 103, packed layer 104, wearing course 105, Hardening layer 106 and scratch-resistant layer 107, surface layer 108 successively.Wherein, wearing course 105, Hardening layer 106 and scratch-resistant layer 107 3 layers is as topping.
Wherein, described cross-linked layer 103 comprises the component of following weight portion: 15 parts of UV mono-official urethane acrylates, 20 parts of UV pure acrylic resins, 15 parts of UV propylene oxide olefin(e) acid esters, 10 parts of single official UV monomers, 20 parts of modified glass powder fillers, 10 parts of composite photoinitiators;
Described packed layer 104 comprises the component of following weight portion: 20 parts of UV propylene oxide olefin(e) acid esters, 12 parts of UV two official urethane acrylates, 10 parts of UV polyester acrylates, 10 part of two official UV monomer, 15 parts of compounded mixs, 5 parts of composite photoinitiators; Compounded mix is glass dust and talcous mixture, and described glass dust and talcous mass mixing ratio are 1:1;
Described wearing course 105 comprises the component of following weight portion: 15 parts of UV6 ~ 9 official's urethane acrylates, 20 parts of UV modified epoxy propylene olefin(e) acid esters, 25 part of three official UV monomer, 20 parts of wear-resistant powder of modification high rigidity, 1 part of anti-settling agent, 4 parts of light triggers; The wear-resistant powder of described modification high rigidity is carry out the alundum (Al2O3) of surperficial oleophylic modification via stearic acid;
Described Hardening layer 106 comprises the component of following weight portion: 26 parts of UV propylene oxide olefin(e) acid esters, 10 parts of UV two official urethane acrylates, 8 parts of UV many officials urethane acrylates, 20 part of three official UV monomer, 6 parts of composite photoinitiators;
Described scratch-resistant layer 107 comprises the component of following weight portion: 20 parts of UV propylene oxide olefin(e) acid esters, 12 parts of UV two official urethane acrylates, 30 part of three official UV monomer, 25 parts of glass dust fillers, 3 parts of composite photoinitiators;
Described surface layer 108 comprises the component of following weight portion: 30 parts of UV6 ~ 9 official's urethane acrylates, 10 parts of UV two official urethane acrylates, 30 parts of UV compound monomers, 3 parts of UV composite nano inoganic materials, 0.5 part of tetrafluoro wax powder, 0.2 part of organosilyl surface controlling agent;
Concrete covering with paint step is as follows: (1) makes plain flaggy 101 modelled after an antique at plain plate polishing grinding modelled after an antique, to described plain flaggy 101 modelled after an antique carry out water-based painted, dry; (2) be coated with cross-linked layer 103, treat that it is half-dried; Cross-linked layer 103 is coated with filling paint, after it is half-dried, is again coated with filling paint, treat its surface drying, obtain packed layer 104; (3) carry out sanding process to packed layer 104, coating wearing course 105, treats its surface drying, and coating Hardening layer 106, treats that it is half-dried, and coating scratch-resistant layer 107, treats its surface drying, then carry out sanding process, and coating surface layer 108, treats that it is absolutely dry, obtain finished product.
Embodiment 4:
A kind of ancient imitation floor board, comprise solid wood plain flaggy 101 modelled after an antique, be coated in the stereoeffect layer 102 on plain flaggy 101 modelled after an antique, described stereoeffect layer 102 applies cross-linked layer 103, packed layer 104, wearing course 105, scratch-resistant layer 107, Hardening layer 106, wearing course 105, Hardening layer 106 and scratch-resistant layer 107, surface layer 108 successively.Wherein, the wearing course 105 be arranged alternately, Hardening layer 106 and scratch-resistant layer 107 are as topping.
Wherein, described cross-linked layer 103 comprises the component of following weight portion: 15 parts of UV mono-official urethane acrylates, 20 parts of UV pure acrylic resins, 15 parts of UV propylene oxide olefin(e) acid esters, 10 parts of single official UV monomers, 20 parts of modified glass powder fillers, 10 parts of composite photoinitiators;
Described packed layer 104 comprises the component of following weight portion: 20 parts of UV propylene oxide olefin(e) acid esters, 12 parts of UV two official urethane acrylates, 10 parts of UV polyester acrylates, 10 part of three official UV monomer, 15 parts of compounded mixs, 5 parts of composite photoinitiators; Compounded mix is glass dust and talcous mixture, and described glass dust and talcous mass mixing ratio are 1:1;
Described wearing course 105 comprises the component of following weight portion: 15 parts of UV6 ~ 9 official's urethane acrylates, 20 parts of UV modified epoxy propylene olefin(e) acid esters, 25 part of two official UV monomer, 20 parts of wear-resistant powder of modification high rigidity, 1 part of anti-settling agent, 4 parts of light triggers; The wear-resistant powder of described modification high rigidity is carry out the alundum (Al2O3) of surperficial oleophylic modification via stearic acid;
Described Hardening layer 106 comprises the component of following weight portion: 26 parts of UV propylene oxide olefin(e) acid esters, 10 parts of UV two official urethane acrylates, 8 parts of UV many officials urethane acrylates, 20 part of three official UV monomer, 6 parts of composite photoinitiators;
Described scratch-resistant layer 107 comprises the component of following weight portion: 20 parts of UV propylene oxide olefin(e) acid esters, 12 parts of UV two official urethane acrylates, 30 part of two official UV monomer, 25 parts of glass dust fillers, 3 parts of composite photoinitiators;
Described surface layer 108 comprises the component of following weight portion: 30 parts of UV6 ~ 9 official's urethane acrylates, 10 parts of UV two official urethane acrylates, 30 parts of UV compound monomers, 3 parts of UV composite nano inoganic materials, 0.5 part of tetrafluoro wax powder, 0.2 part of organosilyl surface controlling agent;
Concrete covering with paint step is as follows: (1) makes plain flaggy 101 modelled after an antique at plain plate polishing grinding modelled after an antique, to described plain flaggy 101 modelled after an antique carry out water-based painted, dry; (2) be coated with cross-linked layer 103, treat that it is half-dried; Cross-linked layer 103 is coated with filling paint, after it is half-dried, is again coated with filling paint, treat its surface drying, obtain packed layer 104; (3) carry out sanding process to packed layer 104, coating wearing course 105, treats its surface drying, coating scratch-resistant layer 107, treats that it is half-dried, coating Hardening layer 106, treat that it is half-dried, coating wearing course 105, treats its surface drying, coating Hardening layer 106, treats that it is half-dried, coating scratch-resistant layer 107, treat its surface drying, then carry out sanding process, coating surface layer 108, treat that it is absolutely dry, obtain finished product.

Claims (6)

1. an ancient imitation floor board; it is characterized in that, comprise plain flaggy modelled after an antique, the stereoeffect layer be arranged on described plain flaggy modelled after an antique, the cross-linked layer be coated on described stereoeffect layer, be applied to the packed layer on described cross-linked layer and the topping be coated on described packed layer and the surface layer be positioned on described topping.
2. a kind of ancient imitation floor board according to claim 1, is characterized in that, described topping comprises wearing course and/or Hardening layer and/or scratch-resistant layer.
3. a kind of ancient imitation floor board according to claim 2, it is characterized in that, described topping comprises the wearing course, Hardening layer and the scratch-resistant layer that set gradually or be arranged alternately.
4. a kind of ancient imitation floor board according to claim 3, it is characterized in that, the order of the wearing course be arranged alternately, Hardening layer and scratch-resistant layer is wearing course, scratch-resistant layer, Hardening layer, wearing course, Hardening layer and scratch-resistant layer.
5. a kind of ancient imitation floor board according to claim 1, it is characterized in that, described plain flaggy modelled after an antique is solid wood plain flaggy modelled after an antique or compound plain flaggy modelled after an antique.
6. a kind of ancient imitation floor board according to claim 1, is characterized in that, described stereoeffect layer line on described plain flaggy modelled after an antique is carved and formed or coating and being formed on described plain flaggy modelled after an antique.
CN201520697889.3U 2015-09-10 2015-09-10 Antique floor Active CN205036032U (en)