CN205031070U - Ceramic boiler - Google Patents
Ceramic boiler Download PDFInfo
- Publication number
- CN205031070U CN205031070U CN201520303132.1U CN201520303132U CN205031070U CN 205031070 U CN205031070 U CN 205031070U CN 201520303132 U CN201520303132 U CN 201520303132U CN 205031070 U CN205031070 U CN 205031070U
- Authority
- CN
- China
- Prior art keywords
- conductive film
- magnetic conductive
- ceramic pot
- ceramic
- utility
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model provides a ceramic boiler, includes the ceramic boiler body, covers ceramic boiler body internal and external surface's glaze layer, characterized in that: the interior bottom surface of the ceramic boiler body is pasted and is had the magnetic conduction membrane to by glaze layer cover. The utility model discloses in being used in the electromagnetism stove, heating panel, it is efficient, use undampedly repeatedly, very ideal electric rice cooker courage, can keep the genuineness of food, can avoid the infringement to the harmful to the human body element such as chromium in the cooking utensil made of iron, antimony, aluminium, lead again.
Description
Technical field
The utility model belongs to ceramic fabrication technique field, relates to the Design and manufacture of ceramic pot.
Technical background
Pottery is the general name of pottery and porcelain.The mankind just employ pottery the Neolithic Age before about 8000.Ceramic material is oxide, nitride, boride and carbide etc. mostly.Common ceramic material has clay, aluminium oxide, kaolin etc.Pottery is mainly used in feeder, decoration.The character tool toughness of ceramic raw material clay, it is plastic that normal temperature meets water, micro-ly dry can to carve, and absolutely dryly grinds; Burning can become pottery to fill water to 700 degree; Burn to 1230 degree of then porcelain, can almost not absorb water completely and corrosion-and high-temp-resistant.Production of Ceramics industrialization degree and common technology are very high and universal.
At present, various electric heating appliance has entered popular family, and electromagnetic oven is wherein one of electric heating appliance that everybody accepts.As everyone knows, ceramic feeder in the mind of people, healthy, environmental protection and cultural in occupy an important position always.But ceramic pot can not be used in electromagnetic oven.If therefore there is a kind of ceramic pot to be used in conventional electromagnetic oven, be bound to be subject to everybody welcome.But, until so far, still do not have this ceramic pot be used in conventional electromagnetic oven commercially to sell.
Summary of the invention
The purpose of this utility model manufactures and designs a kind of ceramic pot, to produce the ceramic pot being subject to everybody welcome that can be used in conventional electromagnetic oven.
The purpose of this utility model is achieved in that a kind of ceramic pot, comprises ceramic pot body 1, covers the glaze layer 2 of ceramic pot body 1 surfaces externally and internally, it is characterized by: the inner bottom surface of ceramic pot body 1 is pasted with magnetic conductive film 3, and is covered by glaze layer 2.
Magnetic conductive film 3 material that can be magnetized is made.
Magnetic conductive film 3 is made with iron thin film.
The mixing of magnetic conductive film 3 lithia powder, stick, fine silver powder is pressed into film, and after drying, sintering forms.
The thickness of magnetic conductive film 3 is 0.1mm-15mm.
Take the utility model of above measure, be used in electromagnetic oven, heat transfer is fast, and efficiency is high, and Reusability is undamped, can keep the genuineness of food, can avoid again the infringement of the harmful elements such as chromium in iron cooker, antimony, aluminium, lead.
Below in conjunction with the accompanying drawings and embodiments the utility model is described in further detail again.
Accompanying drawing explanation
Accompanying drawing 1 is structural representation of the present utility model;
Accompanying drawing 2 is production technological process of the present utility model.
Description of reference numerals: 1, ceramic pot body; 2, glaze layer; 3, magnetic conductive film.
Below in conjunction with drawings and Examples, the utility model is described in further detail.
Detailed description of the invention
Accompanying drawing 1 is the structural representation of the ceramic pot that the utility model is produced.With reference to accompanying drawing 1.
Accompanying drawing 1 is the structural representation that ceramic pot part is analysed and observe.Ceramic pot body 1 is same with the profile of ceramic pot common at present, and the utility model difference just posts magnetic conductive film 3 at inner bottom part.Glaze layer 2 has inside and outside two layers, covers ceramic pot body 1 surfaces externally and internally.Magnetic conductive film 3 is first pasted on the inside bottom of ceramic pot inner container with adhesive, then covers with glaze layer 2.
Accompanying drawing 2 is production technological process of the present utility model.With reference to accompanying drawing 2.
First the utility model carries out product design, Mold Making, formula of size, slurry preparation, glaze formula, glaze preparation, carry out Working mould cast again, after injection forming, carry out repaired biscuit, carry out drying again, then base is examined, then magnetic conductive film preparation, then carry out subsides magnetic conductive film 3, and then enter into glazing operation, loading of kiln again, burns till rear inspection, finally packs warehouse-in.
Magnetic conductive film 3 preparation makes film with the material that can be magnetized.
Pasting magnetic conductive film 3 is the inside bottom with binding agent, magnetic conductive film 3 being affixed on ceramic pot body 1.
Embodiment 1:
First product design, Mold Making, formula of size, slurry preparation, glaze formula, glaze preparation is carried out, carry out Working mould cast again, after injection forming, carry out repaired biscuit, carry out drying again, then examine base, prepared by magnetic conductive film 3, then carries out subsides magnetic conductive film, and then enter into glazing operation, loading of kiln again, burns till rear inspection, finally packs warehouse-in.
Magnetic conductive film 3 is made with iron thin film.The thickness of magnetic conductive film 3 is 2mm.
Paste the inside bottom that iron thin film is affixed on ceramic pot body 1 by magnetic conductive film binding agent.
Embodiment 2:
First product design, Mold Making, formula of size, slurry preparation, glaze formula, glaze preparation is carried out, carry out Working mould cast again, after injection forming, carry out repaired biscuit, carry out drying again, then examine base, prepared by magnetic conductive film 3, then carries out subsides magnetic conductive film 3, and then enter into glazing operation, loading of kiln again, burns till rear inspection, finally packs warehouse-in.
The mixing of magnetic conductive film lithia, stick, fine silver powder is pressed into film, through 400 degrees Celsius after oven dry---and 700 degrees Celsius of sintering, become magnetic conductive film 3.The thickness of magnetic conductive film 3 is 2mm.
Subsides magnetic conductive film binding agent is affixed on the inside bottom of ceramic pot body 1 by sintering magnetic conductive film 3 into.
High-quality kaolin chosen by the raw material of embodiment, import spodumene, Guizhou clay carry out proportioning mixing and ball milling and become mud, sieve press filtration, vacuum pugmill is refined into mud bar, after delivering to workshop moulded section, repair embryo, polishing, oven dry, glazing, then be fired into finished product through 1300 degrees Celsius.
Claims (4)
1. a ceramic pot, comprise ceramic pot body (1), cover the glaze layer (2) of ceramic pot body (1) surfaces externally and internally, it is characterized by: the inner bottom surface of ceramic pot body (1) is pasted with magnetic conductive film (3), and covered by glaze layer (2).
2. Ju ceramic pot according to claim 1, is characterized by: magnetic conductive film (3) material that can be magnetized is made.
3. Ju ceramic pot according to claim 1, is characterized by: magnetic conductive film (3) is made with iron thin film.
4. Ju ceramic pot according to claim 1, is characterized by: the thickness of magnetic conductive film (3) is 0.1mm-15mm.