CN204946915U

CN204946915U - Solar module

Info

Publication number: CN204946915U
Application number: CN201520278149.6U
Authority: CN
Inventors: 孙翔; 王申存; 薛金鑫; 赵志强; 姜占锋
Original assignee: BYD Co Ltd
Current assignee: BYD Co Ltd
Priority date: 2015-04-30
Filing date: 2015-04-30
Publication date: 2016-01-06
Anticipated expiration: 2025-04-30

Abstract

The utility model discloses a kind of solar module, solar module comprises: upper glass plates stacked successively, front adhesive film, solar cell chip arrays, back side adhesive film and backboard, solar cell chip arrays comprises multiple cell piece, be connected by wire between adjacent cell sheet, between the surface of the cell piece of wire in adjacent cell sheet and the surface of another cell piece, reciprocation extension is to form multiple conductor wire, the front of cell piece is provided with secondary grid line, conductor wire welds with secondary grid line, the thickness of at least one in front adhesive film and back side adhesive film is more than or equal to wire and is less than 400 microns at the thickness perpendicular to cell piece direction.According to solar module of the present utility model, the wire of conductor wire by reciprocation extension is formed, not only manufacture simple, cost is low, and weatherability is strong, and the life-span is long, fail safe is high, high to uv absorption rate, and is conducive to the electricity conversion improving solar module.

Description

Solar module

Technical field

The utility model relates to area of solar cell, relates to solar module particularly.

Background technology

Photovoltaic module, by being got up by the photovoltaic cell matrix package of serial or parallel connection, can resist the destruction of external environment, corrosion and aging while allowing it keep the function of generating.Current photovoltaic market there is the assembly of two kinds of structures usually: the first is followed successively by coated toughened glass, EVA encapsulating film, cell piece matrix, EVA encapsulating film, macromolecule backboard from top to bottom, use the aluminium frame protection of rigidity around, and the terminal box that the back side uses terminal box assembly wiring to be drawn; The second is followed successively by the encapsulating film such as coated toughened glass, EVA or PVB, cell piece matrix, EVA encapsulating film, toughened glass from top to bottom, and terminal box is arranged on the back side toughened glass of boring or fluting.

About conventional batteries sheet matrix, current primary structure: the main grid of battery is welded with the back side of adjacent cell by welding, the slurry main component making grid line is the noble silver that price is higher, and welding great majority are for being coated with the copper strips of leypewter.

Wherein the assembly of the first structure is the most general, is here called " common component " relative to two glass assembly.Common component uses EVA as encapsulating film, uses macromolecular material as backboard, has found the following defect in long-term use.

First: backboard is the macromolecule back veneer material with certain water vapor transmittance, the steam in environment and corrosive gas can enter in assembly through backboard, corrosion cell sheet and welding, reduce assembly life-span; Second: the TPT backboard cost of better performances is very high, and common non-Tedler backboard is easy to occur xanthochromia, cracking, efflorescence etc. after a period of time uses, the power of assembly and life-span all can be affected, and the reason of the assembly lightning line found in the recent period is also this; The second, the resistance to wear of macromolecular material is lower, and in windy and dusty area, the anti-aging layer on backboard is worn very soon, and cause pet layer (or copper functional layer) to expose in atmosphere, and pet layer is more easy to wear, the resistance to wear of component integration is lower.This not only greatly reduces the life-span of assembly, also has potential safety hazard.4th, backboard self is flexible material, overleaf for cell piece substantially without physical protection, when being under pressure or clashing into cell piece be easy to cracking; 5th, although with the addition of ultraviolet absorber in EVA, under be exposed to the sun in open air for a long time, ultraviolet absorber can be consumed gradually.Under ultraviolet light and steam comprehensive function, can there is xanthochromia of degrading in EVA, reduces component power and export, and produce the Small molecular such as acetic acid, can corrode welding and cell piece equally, shorten assembly life-span and lower efficiency.

The defect of conventional batteries sheet matrix: one, sunlight enters battery from battery front side, and the metal electrode in front can block a part of silicon chip, and this part luminous energy impinged upon on electrode also just cannot be transformed into electric energy; From this angle, it is more carefully better that we wish that grid line does, and the responsibility of grid line is conduction current, and from the angle analysis of resistivity, grid line more detailed rules and regulations conduction cross-sectional area is less, and ohmic loss is larger.The factor that shading and conduction these two restrict mutually limits the lifting of component power.Its two, after silicon chip cost significantly glides in recent years, the share of silver-colored pulp material in battery production cost for front electrode promotes gradually.

Utility model content

The application makes the discovery of the following fact and problem and understanding based on inventor:

In correlation technique, the front of solar battery sheet is provided with main gate line and secondary grid line usually, for deriving the electric current that cell piece is produced by photoelectric effect or Photochemical effects.In order to improve the efficiency of cell piece, current solar breeder commercial city is being devoted to study the quantity how improving main gate line.Successful in prior art main grid is brought up to 3 from 2, be even increased to 5.

But in prior art, main gate line is that the slurry being expensive silver by printing main component is prepared from, and therefore, its preparation cost is very high, and the radical increasing silver-colored main gate line must cause the increase of cost.Meanwhile, the width large (such as, width reaches more than 2mm) of existing silver-colored main gate line, the radical increasing silver-colored main gate line also can increase to shading-area, causes the conversion efficiency of cell piece to reduce.

Therefore, from the angle reducing costs, reduce shading-area, in correlation technique, the script silver-colored main gate line be printed on cell piece is replaced with wire, as copper wire, welded with secondary grid line by copper wire, and then copper wire is as main gate line derived current.Owing to not re-using silver-colored main gate line, its cost can significantly reduce, and simultaneously because the diameter of copper wire is less, can reduce shading-area, therefore, further the quantity of main gate line can be risen to 10.This cell piece can be called many main grids cell piece or dereliction grid cell sheet, and wherein, wire substituted for silver-colored main grid in conventional solar cell sheet and welding.

Present inventor finds through long-term research experiment, if employing pulls out many parallel wires simultaneously, then many one metal wires are cut off, again by many one metal wires simultaneously the preparation method be fixedly soldered on cell piece prepare cell piece, this kind of mode is due to equipment and preparation precision, the restriction of technique etc., such as due to the effect of stress, when solar battery sheet is placed in a free state, have certain bending, therefore (experiment proves to need wire to keep certain rate of tension cell piece could be flattened, concerning the copper wire of string diameter 0.2mm, its minimum tensile force at least will have 2N).For keeping this tensile force, need the device that similar clip is set at every one metal wire two ends, this device needs to take certain space, and the space of cell piece is limited, therefore, can only pull out on a cell piece at most at present in prior art simultaneously and fix the wire of welding about 10, will be very difficult if want to increase radical wiry again.Because wire radical is more, its free end is more, and equipment needs to control more wire simultaneously, and this requires very high to wire-drawing equipment.Meanwhile, the limited space of solar battery sheet, such as, general single battery sheet is of a size of 156mm*156mm, needs accurately to control many one metal wires in so limited space simultaneously, and this is very high to equipment requirement, especially very high to required precision.Therefore in current actual production, can not control preferably simultaneously and weld many one metal wires, the radical of the conductor wire that can increase be still limited, and generally maximum only have about 10, and realizes difficulty.

In order to address this problem, Patents (US20100275976, and US20100043863) proposes a kind of technical scheme be fixed on by many one metal wires on transparent film layer.That is, first many parallel wires are fixed on transparent film layer by the mode of bonding, then fit on cell piece by being bonded with many parallel hyaline membranes wiry, finally by laminating technology, wire being contacted with the secondary grid line on cell piece.The program fixes many one metal wires by transparent film layer, solve the problem simultaneously controlling many one metal wires, radical wiry can be increased further, but this scheme has almost abandoned welding procedure, namely wire is not connected with secondary grid line by welding procedure, but wire is contacted by laminating technology with secondary grid line, thus derived current.

Although this scheme can promote radical wiry further, due to the existence of transparent film layer, the absorption of light can be affected, cause certain shading, thus cause the reduction of conversion efficiency.

The more important thing is, the scheme of this employing transparent film layer fixing metal silk cannot adopt welding procedure connection metal silk and secondary grid line.This is because on the one hand, if adopt welding procedure, the fusion temperature of transparent film layer must higher than welding temperature (welding temperature be generally at about 140 DEG C).Otherwise if the fusion temperature of transparent film layer is lower than welding temperature, when welding, adhesive film can melt, thus loses the effect of its fixing metal silk, and wire can drift about, and greatly reduces welding effect.

On the other hand, as well known to those skilled in the art, solar battery sheet needs to be in sealing state in use, to prevent water, air etc. from entering in cell piece, causes producing burn into short circuit etc.; And existing encapsulating material is generally EVA, its fusing point is generally 70-80 DEG C, well below welding temperature.If employing welding procedure, as mentioned above, the fusion temperature of transparent film layer needs higher than welding temperature, it is inevitable also higher than the fusing point of encapsulating material, therefore when encapsulation, under package temperature, encapsulating material (EVA) melts, and transparent film layer can not melt, thus, when encapsulating, the encapsulating material of fusing is cannot through the adhesive film of solid, thus cell piece is sealed up completely, therefore, the non-constant of its sealing effectiveness, actual product is easy to lose efficacy.Therefore, from the angle of encapsulation, need again the fusion temperature of transparent film layer lower than welding temperature, this is obviously an antinomy.

Therefore, the scheme of this employing adhesive film fixing metal silk cannot adopt welding procedure wire and secondary grid line to be welded together, and its wire only actually just contacts with the secondary grid line on cell piece, that is, wire just rides on secondary grid line.Therefore, the bonding strength of wire and secondary grid line is very low, in lamination process or in use procedure, is very easy to depart from, causes loose contact, thus cause the efficiency of cell piece significantly to reduce, or even lost efficacy between wire and secondary grid line.Therefore, inreal being promoted and commercialization of the product of this scheme is adopted.Therefore, unripe in the market dereliction grid solar cell.

Particularly solar cell always high cost cannot large batch ofly use, cannot enter into common people house, become the high-end product of green energy resource, the reduction of cost is the problem that this area endeavours to solve always.The Consideration that any parts in battery component can reduce as cost.

The utility model is intended to one of solve the problems of the technologies described above at least to a certain extent.

The utility model provides a kind of dereliction grid solar cell, and the conductor wire number that its cell piece can be arranged can not only be increased to more than 20, even more.The utility model forms conductor wire by the wire reciprocation extension that radical is less, decrease free end, namely the wire radical needing to control is decreased, solve the problem of spatial limitation, but can more conductor wire be set on cell piece, and easily realizes welding between many conductor wires with the secondary grid line of cell piece.Simultaneously, in the dereliction grid solar cell that the utility model provides, owing to conducting electricity between filament and the secondary grid line of cell piece by being welded together, its connection is very reliable, preparation is simple and easy to realize, and good seal performance, efficiency is high, can meet actual operation requirements completely and can produce by commercial.Particularly because the technical solution of the utility model can prepare the solar cell of more more suitably conductor wires, it is more flat that cell piece can draw by conductor wire, cell piece is stress warpage more not easily, prevent contacting of cell piece and upper glass plates and backboard, reduce short-circuit risks, thus the thickness of adhesive film can be reduced, do not affect the performance of battery while reducing costs, well reduce further the cost of battery.

For this reason, the utility model proposes a kind of solar module, this solar module manufacture is simple, cost is low, and electricity conversion is high.

The utility model also proposes a kind of preparation method of above-mentioned solar module.

According to the solar module of the utility model first aspect, comprise: upper glass plates stacked successively, front adhesive film, solar cell chip arrays, back side adhesive film and backboard, described solar cell chip arrays comprises multiple cell piece, be connected by wire between adjacent cell sheet, between the surface of the cell piece of at least one described wire in adjacent cell sheet and the surface of another cell piece, reciprocation extension is to form at least two conductor wires, the front of described cell piece is provided with secondary grid line, described conductor wire welds with described secondary grid line, the thickness of at least one in described front adhesive film and described back side adhesive film is more than or equal to wire and is less than 400 microns at the thickness perpendicular to cell piece direction.

According to solar module of the present utility model, by the wire of conductor wire by reciprocation extension is formed, wire adopts coiling arrangement mode reciprocation extension between adjacent two cell pieces to form collapsed shape, and the conductor wire formed and secondary grid line are weldingly connected, and the conductor wire of this structure not only manufactures simply, cost is low, weatherability is strong, and the life-span is long, and fail safe is high, high to uv absorption rate, and be conducive to the electricity conversion improving solar module.

Conductor wire adopts the mode of coiling arrangement can avoid the problem that in the conductor wire of parallel wire composition, the disconnection of single electrical line or rosin joint etc. cause whole piece conductor wire to lose efficacy, and avoids the situation of cell piece instability to occur.

And due to the utility model adopt coiling arrangement mode, easily can prepare the conductor wire of any number, and conductor wire is better distributed on cell piece, better tension is on cell piece, can cell piece draw more flat, cell piece is warpage more not easily, can arrange and be more than or equal to wire is less than 400 microns adhesive film at the thickness perpendicular to cell piece direction, not only the performance of assembly is not affected, and encapsulating material reduces, old can be reduced largely, the reduction of the thickness of glued membrane simultaneously, even can directly be reduced to wire thickness suitable, also the light transmittance etc. of light can be increased, the electricity conversion of further raising assembly.

According to the preparation method of the solar module of the utility model second aspect, comprise: form at least two conductor wires by between the surface of the cell piece of wire reciprocation extension in adjacent cell sheet and the surface of another cell piece, many conductor wires are welded with the secondary grid line on cell piece surface and forms cell piece array; Upper glass plates, front adhesive film, described cell piece array, back side adhesive film and backboard are stacked successively, and make the front of cell piece in the face of front adhesive film, the back side of cell piece is in the face of back side adhesive film, then carry out lamination and obtain described solar module, the thickness of at least one in described front adhesive film and described back side adhesive film is be more than or equal to wire to be less than 400 microns at the thickness perpendicular to cell piece direction.

The application adopts the method for coiling, not only be more conducive to the electrical connection of wire and cell piece, switching performance is good is beneficial to welding of wire and cell piece especially, there will not be the situations such as a large amount of conductor wire rosin joints, the solar battery sheet of preparation is not only attractive in appearance, and performance is good.And the suitable conductor wire of number can be prepared, preparation technology is simple and easy to realize, and only two clips need be adopted to meet stress and can realize the utility model, and equipment and process is all simple, is easy to technology.

Accompanying drawing explanation

Fig. 1 is the floor map of the solar cell chip arrays according to the application's embodiment.

Fig. 2 is the sectional view of the solar cell chip arrays according to the application's embodiment.

Fig. 3 is the schematic cross-section of the solar cell chip arrays according to the application's embodiment.

Fig. 4 is the schematic diagram wiry for the formation of conductor wire according to the embodiment of the present application.

Fig. 5 is the floor map of the solar cell chip arrays according to another embodiment of the application.

Fig. 6 is the floor map of the solar cell chip arrays according to the another embodiment of the application.

Fig. 7 is the schematic diagram of the reciprocation extension wiry according to the embodiment of the present application.

Fig. 8 is the schematic diagram of two cell pieces of solar cell chip arrays according to the embodiment of the present application.

Fig. 9 is that two cell pieces shown in Fig. 8 are formed by connecting by wire the schematic diagram of solar cell chip arrays.

Figure 10 is the schematic diagram of the solar module according to the embodiment of the present application.

Figure 11 is the schematic partial cross-sectional view of solar module shown in Figure 10.

Figure 12 is the schematic diagram according to the application's solar cell chip arrays of an embodiment again.

Figure 13 is the assembling schematic diagram of the solar cell chip module according to the application.

Figure 14 is the wire in tension schematic diagram of comparative example 1.

Reference numeral:

Cell piece assembly 100;

Upper glass plates 10;

Front adhesive film 20;

Cell piece array 30; Cell piece 31; First cell piece 31A; Second cell piece 31B; Cell piece matrix 311; Secondary grid line 312; The secondary grid line 312A in front; The secondary grid line 312B in the back side; The secondary grid line 3121 in edge; Middle secondary grid line 3122; Weld part 3123; Back of the body electric field 313; Back electrode 314;

Conductor wire 32 (32C); Front side conductive line 32A; Back side conductor wire 32B; Wire body 321; Weld layer 322; Short grid line 33; Clip 34;

Back side adhesive film 40;

Backboard 50; Reflecting coating 51;

U-shaped frame 60;

Terminal box 70;

Mounting blocks 80.

Embodiment

Be described below in detail embodiment of the present utility model, the example of described embodiment is shown in the drawings, and wherein same or similar label represents same or similar element or has element that is identical or similar functions from start to finish.Be exemplary below by the embodiment be described with reference to the drawings, be intended to for explaining the utility model, and can not be interpreted as restriction of the present utility model.

In this application, in order to clearly describe with being convenient to, below part term is made an explanation.Term " cell piece 31 " comprises cell piece matrix 311, the secondary grid line 312 be located on cell piece matrix 311 front, the back of the body electric field 313 being located at the back side of cell piece matrix 311 and the back electrode 314 be located on back of the body electric field 313, thus, secondary grid line 312 also can be called the secondary grid line 312 of cell piece 31, back of the body electric field 313 also can be called the back of the body electric field 313 of cell piece 31, and back electrode 314 also can be called the back electrode 314 of cell piece 31.

The intermediate products that " cell piece matrix 311 " such as can be obtained after the operations such as making herbs into wool, diffusion, etching edge, deposited silicon nitride layer by silicon chip, but it is to be appreciated that in the application, cell piece matrix 311 is not limited to be made up of silicon chip.

In other words, cell piece 31 comprises silicon chip, to the back of the body electric field 313 of some processing layers of silicon chip surface, the secondary grid line of sensitive surface and shady face and back electrode 314, or equivalent other class solar cells not having front electrode.

The conductor wire 32 that term " battery unit " comprises cell piece 31 and is made up of wire S.

Term " solar cell chip arrays 30 " comprises multiple cell piece 31 and is connected with by adjacent cell sheet 31 and the conductor wire 32 be made up of wire S, and in other words, solar cell chip arrays 30 is arranged by multiple cell piece 31 be connected by conductor wire 32 and forms.

In solar cell chip arrays 30, wire S forms the conductor wire 32 of battery unit, broad understanding should be made between the surface that wire S extends in adjacent cell sheet 31, wire S can extend between the front of adjacent cell sheet 31, between the front that also can extend in a cell piece 31 in adjacent cell sheet 31 and the back side of another cell piece 31.When wire S extends between the front of a cell piece 31 in adjacent cell sheet 31 and the back side of another cell piece 31, conductor wire 32 can comprise extend in cell piece 31 front on and the front side conductive line 32A be electrically connected with the secondary grid line 312 of cell piece 31, and on the back side extending in cell piece 31 and the back side conductor wire 32B be electrically connected with the back electrode 314 of cell piece 31, the part of wire S between adjacent cell sheet 31 can be called connection conductor wire.

In this application, cell piece matrix 311, cell piece 31, battery unit, cell piece array 30 and solar module are only used to be convenient to describe, and can not be interpreted as the restriction to the application.

The all scopes disclosed in the application all comprise end points and can independently combine.The end points of the scope disclosed in the application and any value are all not limited to this accurate scope or value, and these scopes or value should be understood to the value comprised close to these scopes or value.

In this application, except as otherwise noted, directional terminology is as shown in the drawings upper and lower in " upper and lower " typically refers to; " front " refers to solar module one side towards light in application process, is also sensitive surface; " back side " refers to solar module one side back to light in application process.

The solar cell chip module according to the embodiment of the present application is specifically described below in conjunction with accompanying drawing.

As shown in figure 1 to figure 13, upper glass plates 10 stacked is successively comprised according to the solar module of the embodiment of the present application, front adhesive film 20, solar cell chip arrays 30, back side adhesive film 40 and backboard 50, solar cell chip arrays 30 comprises multiple cell piece 31, be connected by wire between adjacent cell sheet 31, between the surface of the cell piece 31 of at least one one metal wire in adjacent cell sheet 31 and the surface of another cell piece 31, reciprocation extension is to form at least two conductor wires 32, the front of cell piece 31 is provided with secondary grid line 312, conductor wire 32 welds with secondary grid line 312, the thickness of at least one in front adhesive film 20 and back side adhesive film 40 is be more than or equal to wire to be less than 400 microns at the thickness perpendicular to cell piece direction.

In other words, solar module according to the embodiment of the present application comprises upper glass plates 10 from top to bottom successively, front adhesive film 20, solar cell chip arrays 30, back side adhesive film 40 and backboard 50, wherein, solar cell chip arrays 30 is made up of at least two cell pieces 31, be connected by many conductor wires 32 between adjacent two cell pieces 31, article at least two, conductor wire 32 is made up of the wire of reciprocation extension between adjacent two cell pieces 31, the thickness of front adhesive film 20 and/or back side adhesive film 40 is be more than or equal to wire to be less than 400 microns at the thickness perpendicular to cell piece direction.

Wherein, thickness the utility model perpendicular to cell piece direction refers to the thickness from cell piece to upper glass plates direction, thickness wiry refers to the thickness after welding herein, may because of weld layer melting during welding, and be less than the thickness of metal wire feedstock itself, if wire is cylinder, be then slightly less than diameter wiry.

Simultaneously, the utility model does not limit to all conductor wires and is formed by wire coiling, can part from metal filament winding system be formed, also can be whole, reciprocation extension can be back and forth once, and the terminating point of reciprocation extension does not also limit, and starting point and ending point can be on same cell piece, also can be on different cell pieces, as long as contain around reduction free end.

Conductor wire 32 and secondary grid line 312 are weldingly connected, and drift and rosin joint can not occur the conductor wire 32 in solar module, and show relatively high electricity conversion.

According to the solar module of the embodiment of the present application, by the wire of conductor wire 32 by reciprocation extension is formed, wire adopts coiling arrangement mode reciprocation extension between adjacent two cell pieces 31 to form collapsed shape, and the conductor wire 32 formed is weldingly connected with secondary grid line 312, and the conductor wire 32 of this structure not only manufactures simply, cost is low, weatherability is strong, and the life-span is long, and fail safe is high, high to uv absorption rate, and be conducive to the electricity conversion improving solar module.And due to the utility model adopt coiling arrangement mode, easily can prepare the conductor wire of any number, and conductor wire is better distributed on cell piece, better tension is on cell piece, can cell piece draw more flat, cell piece is warpage more not easily, can arrange and be more than or equal to wire is less than 400 microns adhesive film at the thickness perpendicular to cell piece direction, not only the performance of assembly is not affected, and encapsulating material reduces, old can be reduced largely, the reduction of the thickness of glued membrane simultaneously, even can directly be reduced to wire thickness suitable, also the light transmittance etc. of light can be increased, the electricity conversion of further raising assembly.

Here, cell piece 31 forms battery unit with the conductor wire 32 be made up of the wire S extended on this cell piece 31 surface, in other words, solar cell chip arrays 30 according to the embodiment of the present application is made up of multiple battery unit, and the conductor wire 32 of multiple battery unit is made up of the wire S of reciprocation extension on the surface of adjacent cell sheet 31.

It is to be appreciated that in this application, term " reciprocation extension " also can be called " coiling ", can refer to that wire S extends along reciprocal stroke between the surface of cell piece 31.

In this application, " wire S reciprocation extension is between the surface of cell piece 31 " should make broad understanding, such as, wire S can between the surface of the cell piece 31 of reciprocation extension in adjacent cell sheet 31 and the surface of another cell piece 31, wire S also can extend through the surface of intermediate cell sheet 31 surface to last cell piece 31 of predetermined quantity from the surface of first cell piece 31, then return from the surface of last cell piece 31 and extend through the surface of surface to the first cell piece 31 of the intermediate cell sheet 31 of described predetermined quantity, repetition like this.

In addition, when cell piece 31 is in parallel by wire S, wire S can reciprocation extension on the front of two cell pieces, in the case, wire S forms the front side conductive line 32A of two cell pieces of this parallel connection, alternatively, wire S reciprocation extension is on the front of a cell piece 31 and by another wire S reciprocation extension on the back side of this cell piece 31, in the case, the wire S extended on cell piece 31 front forms front side conductive line 32A, and the wire S extending in the back side of cell piece 31 forms back side conductor wire 32B.

When cell piece 31 is one another in series by wire S, between the front of the cell piece 31 of wire S reciprocation extension in adjacent cell sheet 31 and the back side of another cell piece 31, in the case, the part that wire S extends on the front of a cell piece 31 forms front side conductive line 32A, and the part that wire S extends on the back side of another cell piece 31 adjacent forms back side conductor wire 32B.In this application, unless expressly stated otherwise, conductor wire 32 can be understood as front side conductive line 32A, back side conductor wire 32B, or front side conductive line 32A and back side conductor wire 32B.

Here, term " reciprocation extension " be can be understood as wire S extension " one back and forth " formation two conductor wires 32, two conductor wires 32 and is formed by an one metal wire S coiling, such as, adjacent two conductor wires form U-shaped structure or v-shaped structure, but the application is not limited to this.

According to the cell piece array 30 of the embodiment of the present application, multiplely be positioned at the conductor wire 32 on cell piece and be made up of the wire S of reciprocation extension, and be connected by conductor wire 32 between adjacent cell sheet 31, therefore, the surface of cell piece is without the need to printing expensive silver-colored main grid, and manufacturing process is simple, connects cell piece without the need to using welding, the secondary grid line of wire S and cell piece and the easy to connect of back electrode, the cost of cell piece reduces greatly.

In addition, because the wire S of conductor wire 32 by reciprocation extension is formed, the width (i.e. the width of the projection of wire on cell piece) of conductor wire 32 can reduce, reduce the shading-area of battery, and the quantity of conductor wire 32 can adjust easily, compared with starching with silver the main gate line that formed, the resistance of conductor wire 32 reduces, and improves photoelectric conversion efficiency.Because wire S reciprocation extension forms conductor wire, when using cell piece array 30 to manufacture solar module 100, wire S is not easily shifted, and namely wire is less likely to occur " drift ", can not photoelectric conversion efficiency be affected, further increase photoelectric conversion efficiency.

According to embodiment of the present utility model, the front of cell piece 31 is provided with secondary grid line 312 and short grid line 33, the secondary grid line 3121 in edge that secondary grid line 312 comprises the secondary grid line 3122 in the centre crossing with conductor wire 32 and do not intersect with conductor wire 32, short grid line 33 is connected with the secondary grid line 3121 in edge, and short grid line 33 is connected with secondary grid line 3122 in the middle of conductor wire 32 or at least one.

The solar cell that the application connects for this type of conductor wire 32, the front of cell piece 31 arranges short grid line 33 and solves the precision problem that conductor wire 32 is connected with cell piece 31, prevent current loss, technique is simple, easily realizes, significantly reduces process costs.

Wherein, the secondary grid line 312 being positioned at a side surface of cell piece matrix 311 comprises two parts, wherein a part of secondary grid line 312 is crossing with conductor wire 32, the secondary grid line 312 of this part is positioned at the centre position of cell piece matrix 311 and forms middle secondary grid line 3122, and the secondary grid line 312 of another part is not crossing with conductor wire 32, the secondary grid line 312 of this part is positioned at the edge of the side away from conductor wire 32 of cell piece matrix 311, forms the secondary grid line 3121 in edge.

The secondary grid line 3121 in edge is provided with the short grid line 33 be connected with secondary grid line 3122 in the middle of conductor wire 32 or at least one, in specific embodiment, short grid line 33 is arranged in conductor wire 32 cannot arrive cell piece 31 edge portions in coiling arrangement process, can avoid cannot reaching in the process owing to arranging in conductor wire 32 coiling the secondary grid line 312 of the edge portions of cell piece 31 and the portion of electrical current waste that causes.

Alternatively, after wire is connected with cell piece 31, wire disconnects at the place of turning back that reciprocation extension is formed.

Preferably, the secondary grid line 3122 in centre that short grid line 33 is nearest with the secondary grid line 3121 in distance edge is connected.

In other embodiments of the application, short grid line 33 is connected with conductor wire 32.Preferably, the place of turning back that short grid line 33 is formed with the wire reciprocation extension on the front of cell piece 31 is connected, and can increase a solder joint, reduces the possibility that welding position, edge disconnects, further enhances the adhesion of wire and cell piece.Can be understood as being connected with the place of turning back herein short grid 33 and there is intersection point with the place of turning back, namely short grid 33 not stop at the place of turning back.

According to an embodiment of the application, short grid line 33 is perpendicular to secondary grid line 312.Short grid line 33 is preferably electrically connected with the bending part (end near edge portions) of the conductor wire 32 on the sensitive surface of cell piece 31, more preferably, arranges at least one short grid line 33 corresponding to each bending part.

Under normal circumstances, because the distance between the bending part of conductor wire 32 and the edge of cell piece 31 is shorter, the length of this short grid line 33 can be 1-10 millimeter usually, is preferably 2.4-7mm.The width of this short grid line 33 can be 0.05-0.5mm, and thickness can be 0.01-0.02mm.The radical of short grid line 33 is 3-40 root, is preferably 6-20 root.

The set-up mode of short grid line 33 can be identical with the secondary grid line 312 on the sensitive surface of cell piece 31, such as, can print by method for printing screen and secondary grid line 312 simultaneously, and the secondary grid line 3121 in during printing and front be same half tone, and its material can be silver-colored slurry.

Alternatively, after being connected with cell piece 31 by wire, wire disconnects at the place of turning back.Wire disconnects wire and forms multiple relatively independent conductor wire 32 after welding with cell piece 31 at the place of turning back wiry.

Wire is disconnected at the place of turning back wiry after wire welds with cell piece 31, make between multiple conductor wire 32 relatively independent, the stress between cell piece can be reduced, reduce the peeling force of wire and cell piece binding site, further increase the electricity conversion of solar cell chip arrays 30.

Therefore, according to the solar cell chip module 100 of the embodiment of the present application, cost is low, photoelectric conversion efficiency is high.

Preferably, the thickness of at least one in front adhesive film 20 and back side adhesive film 40 is 250-400 micron.Further preferably, the thickness of at least one in front adhesive film 20 and back side adhesive film 40 is 250-350 micron.Thus, the front adhesive film 20 of this structure and the material usage of back side adhesive film 40 can reduce further, thus reduce overall preparation cost further.

The backboard 50 of the application can be glass plate.Compared with the macromolecule back veneer material of routine, there is excellent decay resistance, weatherability and resistance to wear, by the electronic component of inside and external environment is completely isolated comes, extend assembly life-span.

According to an embodiment of the application, conductor wire 32 is welded with secondary grid line 312 by weld layer,

Particularly, according to a kind of preferred implementation of the application, secondary grid line 312 and conductor wire 32 are by being located on secondary grid line 312 or coated weld layer on the metal filament welds.Alternatively, the position contacted with secondary grid line 312 and/or the back electrode 314 of cell piece 31 at conductor wire 32 is provided with weld layer, and more preferably, the position contacted with back electrode 314 at conductor wire 32 and the secondary grid line 312 of cell piece 31 is provided with weld layer.Weld layer only can be executed and be overlying on secondary grid line 312 and back electrode 314, also can execute and be overlying on conductor wire 32.Weld layer can be low-melting-point metal or alloy.

In cell piece array 30, the thickness of weld layer and the diameter ratio of conductor wire 32 (comprising front side conductive line 32A and back side conductor wire 32B) can be 0.02-0.5:1.

In this application, when the position contacted with secondary grid line 312 and/or the back electrode 314 of cell piece 31 at conductor wire 32 (comprising front side conductive line 32A and back side conductor wire 32B) is provided with weld layer,

Conductor wire 32 can be the wire of the non-clad welded layer of this area routine, such as copper wire.

In one embodiment, conductor wire 32 (comprising front side conductive line 32A and back side conductor wire 32B) has the wire of low-melting alloy layer for Surface coating.Low-melting alloy layer can be surface completely coated, also can surface portion coated.When low-melting alloy layer surface portion is coated, low-melting alloy layer is preferably formed in the position of welding with the secondary grid line 312 of cell piece 31 and/or back electrode 314.When low-melting alloy layer surface complete coated time, low-melting alloy layer can be coated on the periphery of wire body with the form of ring-type.The thickness of low-melting alloy layer can be selected in the larger context.Under preferable case, the thickness of low-melting alloy layer is 1-100 micron, is more preferably 1-30 micron.The low-melting alloy forming low-melting alloy layer can be the low-melting alloy of this area routine, and its fusing point can be 100-220 DEG C.

In cell piece array 30, cell piece 31 can adopt the cell piece 31 of this area routine, such as, can be polycrystalline silicon battery plate 31.Secondary grid line 312 on the sensitive surface of cell piece 31 can be silver, copper, tin, ashbury metal etc.The width of secondary grid line 312 can be 40-80 micron, and thickness can be 5-20 micron, and secondary grid line 312 can be 50-120 bar, and the spacing of adjacent two secondary grid lines 312 can be 0.5-3mm.The material of the back electrode 314 on the back side of cell piece 31 can be silver, copper, tin, ashbury metal etc., and back electrode 314 is generally banded, and its width can be 1-4mm, and thickness can be 5-20 micron.

Below with reference to the accompanying drawings solar cell chip arrays 30 according to the application's specific embodiment is described.

With reference to figure 1-3, the solar cell chip arrays 30 according to the application's specific embodiment is described.

In the embodiment shown in Fig. 1-3, show two cell pieces of solar cell chip arrays 30, in other words, two cell pieces 31 that the conductor wire 32 shown by being made up of wire S is connected with each other.

Be understandable that, cell piece 31 comprises cell piece matrix 311, the secondary grid line 312 (i.e. the secondary grid line 312A in front) be located on the front of cell piece matrix 311, the back electrode 314 being located at the back of the body electric field 313 on the back side of cell piece matrix 311 and being located on back of the body electric field 313.In this application, it will be appreciated that, unless expressly stated otherwise, back electrode 314 can be the back electrode of conventional batteries sheet, such as, starch printing by silver and formed, and also can be the secondary grid line 312B in the back side of the secondary grid line be similar on cell piece front side of matrix, also can be discrete multiple weld parts, in this application, unless expressly stated otherwise, secondary grid line refers to the secondary grid line 312 on the front of cell piece matrix 311.

As Figure 1-3, in this embodiment, solar cell chip arrays comprises two cell pieces (for convenience, referred to herein as the first cell piece 31A, second cell piece 31B), wire S reciprocation extension is at the front (sensitive surface of the first cell piece 31A, upper surface in Fig. 2) and the back side of the second cell piece 31B between, thus, wire S constitutes the front side conductive line of the first cell piece 31A and the back side conductor wire of the second cell piece 31B, and wire S welds with the secondary grid line of the first cell piece 31A and welds with the back electrode of the second cell piece 31B.

In an embodiment of the application, the back side of pond sheet matrix 311 is provided with back electrode 314, and wire and back electrode 314 are weldingly connected.

That is, in this embodiment, the front of cell piece matrix 311 is provided with the secondary grid line 312A in front, the back side of this cell piece matrix 311 is provided with back electrode 314, when conductor wire 32 is positioned at the front of cell piece matrix 311, conductor wire 32 is weldingly connected with the secondary grid line 312A in front, when conductor wire 32 is positioned at the back side of cell piece matrix 311, is then weldingly connected with the back electrode 314 at the back side of this cell piece matrix 311.

In certain embodiments, wire reciprocation extension 10-60 time between the first cell piece 31A and the second cell piece 31B, in embodiments more of the present utility model, wire can be one.Particularly, an one metal wire through repeatedly back and forth bending can form many conductor wires, the number of conductor wire, in the scope of 20-40, is preferably 24-28 bar.Preferably, as shown in Figure 1, wire reciprocation extension 12 times is to form 24 conductor wires, and wire is single, and in other words, single metal wire reciprocation extension forms 24 conductor wires 12 times, and the spacing between adjacent conductive line can be 2.5 millimeters-15 millimeters.Certainly, the utility model wire is not limited to single, can be many, also can be the independent coiling of many one metal wires.According to this embodiment, compared with the conductor wire of conventional batteries sheet, quantity increases, thus reduces electric current from secondary grid line to the distance of conductor wire, decreases resistance, improves electricity conversion.In the embodiment shown in fig. 1, adjacent conductive line forms U-shaped structure, is convenient to coiling wiry thus.Alternatively, the application is not limited to this, and such as, adjacent conductive line also can form v-shaped structure.

More preferably, as shown in Figure 4, wire S comprises wire body 321 and the coated weld layer 322 of outer surface thereof, wire is welded with secondary grid line and/or back electrode by coated weld layer 322, thus, be convenient to the electrical connection of wire and secondary grid line and/or back electrode, avoid wire drift in connection procedure and affect photoelectric conversion efficiency.Certainly, the electrical connection of wire and cell piece can be carried out in the lamination process of solar module, also can carry out before being laminated, preferably, connect before being laminated.

Wherein it should be noted that, in this application, wire S refers to that reciprocation extension forms the wire of conductor wire 32 on cell piece 31, conductor wire 32 can comprise the weld layer 322 of wire body 321 and wire body 321 external sheath, namely wire S also can comprise wire body 321 and be coated on the outer field weld layer 322 of wire body 321, in the embodiment of the application, if without specified otherwise, wire refers to that reciprocation extension forms the wire S of conductor wire 32 on cell piece 31.

In certain embodiments, preferably, wire body 321 is copper wire, and certainly, wire S also can be copper wire, i.e. wire S not clad welded layer 322, but the application is not limited to this, and such as wire body 321 also can be aluminium wire.Preferably, wire S has circular cross section, and thus, more sunlight can be irradiated on cell piece matrix, improves photoelectric conversion efficiency further.

In certain embodiments, preferably, before wire contacts with cell piece, wire extends in a tensioned state, stretching by wire, after being connected with the secondary grid line and back electrode of cell piece, tensile force wiry can be discharged, avoid the conductor wire drift when preparing solar module thus further and affect photoelectric conversion efficiency.

Fig. 5 shows the schematic diagram of the cell piece array of another embodiment according to the application.As shown in Figure 5, wire reciprocation extension is between the front of the first cell piece 31A and the front of the second cell piece 31B, thus, wire forms the front side conductive line of the first cell piece 31A and the front side conductive line of the second cell piece 31B, in the case, first cell piece 31A and the second cell piece 31B is connected in parallel to each other, certainly, be understandable that, preferably, the back side conductor wire that the back electrode of the first cell piece 31A and the back electrode of the second cell piece 31B also can be formed by another wire reciprocation extension is connected, alternatively, the back electrode of the first cell piece 31A also can be connected by traditional mode with the back electrode of the second cell piece 31B.

Below with reference to Fig. 6, the solar cell chip arrays 30 according to another embodiment of the application is described.

Comprise n × m cell piece 31 according to the solar cell chip arrays 30 of the embodiment of the present application, in other words, multiple cell pieces 31 are arranged into the matrix form of n × m, and wherein n is columns, and m is row.More specifically, in this embodiment, 36 cell pieces 31 are arranged in 6 row and 6 rows, i.e. n=m=6.Be understandable that, the application is not limited to this, and such as, row and columns can be unequal.For convenience, in figure 6, along direction from left to right, cell piece 31 in same row's cell piece 31 is called the first, second, third, fourth, the 5th and the 6th cell piece 31 successively, along direction from the top down, the row of cell piece 31 is called the first, second, third, fourth, the 5th and the 6th row's cell piece 31 successively.

In same row's cell piece 31, wire reciprocation extension is between the surface of a cell piece 31 and the surface of another adjacent cell piece 31, in adjacent two row's cell pieces 31, between the surface of a cell piece 31 during the surface of the cell piece 31 of wire reciprocation extension in a row and a+1 arrange, and m-1 >=a >=1.

As shown in Figure 6, in concrete example, in same row's cell piece 31, wire reciprocation extension is between the front of a cell piece 31 and the back side of another adjacent cell piece 31, and thus, the cell piece 31 in same row is one another in series.In adjacent two row's cell pieces 31, wire reciprocation extension is in the front of the cell piece 31 of an end of arranging at a and between the back side of a cell piece 31 of the end that a+1 arranges, and adjacent two row's cell pieces 31 are one another in series thus.

More preferably, in adjacent two row's cell pieces 31, wire reciprocation extension is on the surface of the cell piece 31 of an end of arranging at a and between the surface of the cell piece 31 of the end that a+1 arranges, the end that an end of a row and a+1 arrange is positioned at the same side of matrix, such as in figure 6, the right side of matrix is positioned at.

More specifically, in the embodiment shown in fig. 6, in the first row, between the back side between the front of one one metal wire reciprocation extension first cell piece 31 and the second cell piece 31, between the back side between the front of the second one metal wire reciprocation extension second cell piece 31 and the 3rd cell piece 31, between the back side between the front of the 3rd one metal wire reciprocation extension the 3rd cell piece 31 and the 4th cell piece 31, between the back side between the front of the 4th one metal wire reciprocation extension the 4th cell piece 31 and the 5th cell piece 31, between the back side between the front of the 5th one metal wire reciprocation extension the 5th cell piece 31 and the 6th cell piece 31, thus, adjacent cell sheet 31 in first row is one another in series by corresponding wire.

Between the back side between the 6th cell piece 31 in the front of the 6th cell piece 31 in six roots of sensation wire reciprocation extension first row and adjacent second row, thus, first row and second row are one another in series, between the back side in the front of the 6th cell piece 31 in the 7th one metal wire reciprocation extension second row and second row between the 5th cell piece 31, between the back side in the front of the 5th cell piece 31 in the 8th one metal wire reciprocation extension second row and second row between the 4th cell piece 31, until between the back side in the front of the second cell piece 31 in the 11 one metal wire reciprocation extension second row and second row between the first cell piece 31, then, the front and the 3rd of the first cell piece 31 in the 12 one metal wire reciprocation extension second row arrange between the back side between the first cell piece 31, second row and the 3rd is arranged and is one another in series thus.Then, successively the 3rd row and the 4th is arranged and connect, 4th row and the 5th arranges and connects, 5th row and the 6th arranges and connects, complete the preparation of cell piece array 30 thus, in this embodiment, busbar is set in the left side of the left side of the first cell piece 31 of first row and the 6th the first cell piece 31 arranged, a busbar connects the conductor wire extended from the left side of the first cell piece 31 of first row, and another busbar connects the conductor wire extended from the left side of first cell piece 31 of the 6th row.

As shown in the figure and above-mentioned, connection between the cell piece of the embodiment of the present application adopts conductor wire series connection, conductor wire is all adopted to realize series connection between first row, second row, the 3rd row, the 4th row, the 5th row and the 6th row, wire can extend outside cell piece for connecting other loads as shown in the figure, such as alternatively, also can be in parallel for preventing the diode of spottiness between second row and the 3rd row, between the 4th row and the 5th row, the connection of diode can adopt the technology of well known to a person skilled in the art, such as busbar.

But, the application is not limited to this, such as, can connect between first row and second row, the 3rd row and the 4th row's series connection, the 5th row and the 6th row's series connection, second row and the 3rd row's parallel connection simultaneously, 4th row and the 5th row's parallel connection, in the case, can arrange in the left side of respective row or right side and arrange busbar respectively.

Alternatively, the cell piece 31 in same row can be in parallel, and such as, an one metal wire passes through the front of the second to the 6th cell piece 31 from the front reciprocation extension of the first cell piece 31 first row.

According to an embodiment of the application, the width of secondary grid line 312 is 40-80 micron, and thickness is 5-20 micron, and secondary grid line is 50-120 bar, and the spacing of adjacent pair grid line is 0.5-3mm.Thus, the secondary grid line 312 of this structure can weld with conductor wire 32 better, and improves photoelectric conversion efficiency.

Preferably, front adhesive film 20 and back side adhesive film 40 are silica gel.Be through the ultraviolet light absorbed by EVA ultraviolet absorber, electric energy to be converted to relative to traditional its advantage of EVA encapsulating film, increase the output of photovoltaic module; Second point is that novel encapsulating film is very stable under UV-irradiation, and the Small molecular such as non-degradable generation acetic acid, corrosion cell sheet, weatherability is better.

Polyolefin hypodynamic problem bonding with macromolecule backboard is there is in polyolefin film when general components uses, easily there is the problems such as delamination afterwards in long-time use, the silica gel that the pellosil assembly of current use uses is a kind of membrane structure, for thermoplasticity, be solid-state under normal temperature, temperature is softened after raising gradually.Transparent liquid silica gel is a kind of two component silica gel, and be liquid under normal temperature, can be solidified into heat cured transparent silica gel 70 ~ 130 DEG C of laminated after two components are good with 1:1 Homogeneous phase mixing, laminating temperature is low, saves the energy, and contributes to the prolonged layer press life-span.The upper glass plates 10 of two glass assembly and backboard 50 are all the glass of rigidity, to be more convenient for gluing and lamination than the Normal back plate of macromolecular material.Assembly temperature when reality uses may reach 80 ~ 100 DEG C, and thermoplastic film can soften, and have certain mobility, and thermosetting film does not have this problem, and assembly heat resistance is higher.

As shown in Figure 10, further, the inner side of backboard 50 is coated with the reflecting coating 51 of adularescent.The inner side of the application's glass is overleaf coated with the reflecting coating 51 of adularescent, the light reflection through cell piece 31 gap can be gone back to reduce encapsulation loss.

The application uses glass as backboard 50, compared with the macromolecule lower-glass of routine or metallic sheet material, has excellent decay resistance, weatherability and resistance to wear, by the electronic component of inside and external environment is completely isolated comes, extends assembly life-span.

In a preferred embodiment, the sealant sealing of butyl rubber or Oppanol is clamped between the outer of upper glass plates 10 and the outer of backboard 50.

The application uses the butyl rubber or Oppanol that water vapor transmittance is extremely low inside most outer between layer glass, compensate for original photovoltaic module edge and encapsulating material is exposed to outer deficiency, in conjunction with the glass that levels is closely knit, can be good at intercepting the steam in environment, corrosive gas enters component internal, the assembly that slows down is decayed, and extends assembly life-span.

Further preferably, upper glass plates 10 and backboard 50 outer utilize silica gel or butyl rubber or two-sided tape to fix by U-shaped frame 60, and are filled with fluid sealant between the outer of upper glass plates 10 and backboard 50 and U-shaped frame 60.

The application uses silica gel or butyl rubber or two-sided tape to be fixed by U-shaped frame in the outer of layer glass, frame material is aluminium or macromolecular material.Two glass assembly outer is not usually protected or is only used adhesive tape protection, the assembly of this structure due to the corner of toughened glass easily stressed and cracked, fail safe is lower, transport and when installing risk larger.After using the protection of U-shaped rigid border, two edge of glass assembly and the impact resistant capability of corner have had and have improved greatly, and further enhance the sealing effectiveness of assembly.

As shown in figure 14, according to the solar module of the embodiment of the present application, also comprise terminal box 70, terminal box 70 is located at the edge of upper glass plates 10 and backboard 50.

In the application, terminal box 70 is arranged on the edge of solar module, instead of at the perforate of the solar module back side or fluting, maintains the complete structure of back glass, and can not form stress concentration point, fail safe is higher.In addition, this distribution of terminal box 70 can reduce the length of the inner busbar of solar module and External cable relative to traditional components, provide cost savings, and decreases resistance increase power stage.

In the preparation process of the solar module provided in the application, can first conductor wire 32 be bondd with the secondary grid line 312 on cell piece and back electrode or weld, then each layer be carried out stacked and lamination.

A specific embodiment of the present utility model, solar module 100 comprises upper cover plate 10, front adhesive film 20, cell piece array 30, back side adhesive film 40 and backboard 50.Cell piece array 30 comprises multiple cell piece 31, be connected by many conductor wires 32 between adjacent cell sheet 31, conductor wire 32 is formed by the wire S of reciprocation extension between the surface of adjacent cell sheet, conductor wire 32 welds with secondary grid line, and front adhesive film 20 directly contacts with conductor wire 32 and is filled between adjacent conductor wire 32.

In other words, stacked upper cover plate 10, front adhesive film 20, cell piece array 30, back side adhesive film 40 and backboard 50 is successively comprised along the vertical direction according to the solar module 100 of the embodiment of the present application, cell piece array 30 comprises multiple cell piece 31 and the many conductor wires 32 being connected multiple cell piece 31, conductor wire 32 is made up of wire S, and wire S reciprocation extension is on the surface of adjacent two cell pieces 31.

Conductor wire 32 is electrically connected with cell piece 31, wherein, front adhesive film 20 on cell piece 31 directly contacts with conductor wire 32 and is filled between adjacent conductor wire 32, front adhesive film 20 both can play the effect of fixing conductor wire 32, conductor wire 32 can be completely cut off with outside air and steam again, thus avoid conductor wire 32 oxidized, ensure that photoelectric conversion efficiency.

Thus, according to the solar module 100 of the embodiment of the present application, replaced main gate line and the welding of conventional batteries sheet by the conductor wire 32 be made up of the wire S of reciprocation extension, reduce cost; The wire S of reciprocation extension decreases the number of the free end of wire S, and when arranging wire S, requisite space is little, and not by spatial limitation, the radical of the conductor wire 32 be made up of wire S reciprocation extension can significantly improve, and preparation is simple, can produce in batches; Front adhesive film 20 directly contacts with conductor wire 32 and is filled between adjacent conductor wire 32, effectively by isolated to conductor wire 32 and outside air, steam etc., can avoid the oxidation of conductor wire 32, effectively can ensure electricity conversion.

In some embodiments of the application, reciprocation extension between the front of the cell piece 31 of wire S in adjacent cell sheet 31 and the back side of another cell piece 31, front adhesive film 20 directly contacts with the conductor wire 32 on the front of a cell piece 31 and is filled between the adjacent conductive line 32 on the front of a cell piece 31, and back side adhesive film 40 directly contacts with the conductor wire 32 at the back side of another cell piece 31 and is filled between the adjacent conductive line 32 at the back side of another cell piece 31.

That is, in this application, adjacent two cell pieces 31 are connected by wire S-phase, and in adjacent two cell pieces 31, the front of a cell piece 31 and wire S-phase connect, and the back side of another cell piece 31 and wire S-phase connect.

Wherein, front adhesive film 20 on the cell piece 31 that front and wire S-phase connect directly contacts with the wire S in this cell piece 31 front and is filled between adjacent conductor wire 32, and the back side adhesive film 40 of the cell piece 31 that the back side connects with wire S-phase directly contacts with the wire S at this cell piece 31 back side and is filled between adjacent conductor wire 32 (as shown in Figure 2).

Thus, according to the solar module 100 of the embodiment of the present application, not only the conductor wire 32 in the front of a part of cell piece 31 can separate with the external world by front adhesive film 20, the conductor wire 32 at the back side of percentage of batteries sheet 31 also can separate with the external world by back side adhesive film 40, can ensure the photoelectric conversion efficiency of solar module 100 further.

In some embodiments of the application, the size for the cell piece of routine is 156mm × 156mm; The series resistance of solar module is 380-440 milliohm/60 slice, and simultaneously the application is not limited to 60, can be 30,72 etc., when being 456-528 milliohm for the series resistance of solar module when 72, and the excellent electrical property of battery.

In some embodiments of the application, the size for the cell piece of routine is 156mm × 156mm; The open circuit voltage of solar module is 37.5-38.5V/60 sheet, and same the application is not limited to 60, can be 30,72 etc.Short circuit current is 8.9-9.4A, and the number of short circuit current and cell piece has nothing to do.

In some embodiments of the application, the fill factor, curve factor of solar module is 0.79-0.82, and it is not by the size of cell piece and the impact of number, and it affects the electrical property of battery.

In some embodiments of the application, the size for the cell piece of routine is 156mm × 156mm; The operating voltage of solar module is 31.5-32V/60 sheet, and same the application is not limited to 60, can be 30,72 etc.Operating current is 8.4-8.6A, and the number of operating current and cell piece has nothing to do.

In some embodiments of the application, the size for the cell piece of routine is 156mm × 156mm; The conversion efficiency of solar module is 16.5-17.4%.Power is 265-280W/60 sheet.

Specifically describe the preparation method of the solar module according to the embodiment of the present application below.

Particularly, comprise the following steps according to the preparation method of the solar module of the embodiment of the present application:

Form many conductor wires 32 by between the surface of the cell piece 31 of wire reciprocation extension in adjacent cell sheet 31 and the surface of another cell piece 31, many conductor wires 32 are welded with the secondary grid line 312 on cell piece 31 surface and forms cell piece array 30.

Upper glass plates 10, front adhesive film 20, cell piece array 30, back side adhesive film 40 and backboard 50 are stacked successively, and make the front of cell piece 31 in the face of front adhesive film 20, the back side of cell piece 31 is in the face of back side adhesive film 40, then carry out lamination and obtain solar module, the thickness of at least one in front adhesive film 20 and back side adhesive film 40 is be more than or equal to wire to be less than 400 microns at the thickness perpendicular to cell piece direction.

Front adhesive film 20 and back side adhesive film 40 can be the adhesive film that this area routine uses, preferably, front adhesive film 20 and back side adhesive film 40 polyethylene octene elastomer (POE) and/or ethylene-vinyl acetate copolymer (EVA).In this application, polyethylene octene elastomer (POE) and ethylene-vinyl acetate copolymer (EVA) can adopt the product of this area routine use or prepare according to method well known to those skilled in the art.

Comprise according to the preparation method of the solar module 100 of the embodiment of the present application and first prepare cell piece array 30, then stacked upper cover plate 10, front adhesive film 20, cell piece array 30, back side adhesive film 40 and backboard 50 successively, finally carries out lamination and obtains solar module 100.Be understandable that, the preparation of solar module 100 also comprises other steps, such as, use the space between sealant sealing upper cover plate 10 and backboard 50, and utilizes U-shaped frame to be tightened together by said elements, this it is known to those skilled in the art that, is not described in detail here.

The preparation of solar cell chip arrays 30 comprises and is connected with the surface electrical of described cell piece 31 and forms many conductor wires between the surface of cell piece 31 by wire reciprocation extension, and cell piece 31 adjacent thus connected by described many conductor wires and form cell piece array 30.

Particularly, as shown in Figure 7, in a tensioned state, by an one metal wire reciprocation extension 12 times.Then, as shown in Figure 8, the first cell piece 31A and the second cell piece 31B is prepared.Next, as shown in Figure 9, the front of the first cell piece 31 is connected with wire and the back side of the second cell piece 31B is connected with wire, form cell piece array 30 thus, two cell pieces 31 have been shown in Fig. 9, as mentioned above, when cell piece array 30 has multiple cell piece 31, utilize the wire of reciprocation extension to be connected at the back side of the front of a cell piece 31 with another adjacent cell piece 31, be connected with the back electrode wire of another cell piece 31 by the secondary grid line of a cell piece 31.Wire is by reciprocation extension under two clip tensionings laying respectively at these rhizoid two ends, and this wire only needs two clips to realize coiling, greatly reduces the consumption of clip, saves assembly space.

In the embodiment shown in fig. 9, adjacent cell sheet is one another in series, and as mentioned above, as required, adjacent cell sheet can be connected in parallel to each other by wire.

By stacked successively with upper cover plate 10, front adhesive film 20, back side adhesive film 40 and backboard 50 for the cell piece array 30 prepared, and make the front of described cell piece 31 in the face of the back side of described front adhesive film 20, described cell piece 31 in the face of back side adhesive film 40, then carry out lamination and obtain solar module 100.Be understandable that, wire welds with cell piece 31, and the connection of wire and cell piece 31 can be carried out in lamination process, certainly, also can first connect, rear lamination.

Wherein, according to the solar module of the embodiment of the present application in the preparation, wire is reciprocation extension in a tensioned state, and wire reciprocation extension is between the front of a cell piece 31 and the back side of another cell piece 31.Conductor wire comprises the front side conductive line 32A be connected with the secondary grid line on the front of a cell piece 31 and back side conductor wire 32B be connected with the back electrode on the back side of a cell piece 31.Wire reciprocation extension 10-60 time, the spacing between adjacent two conductor wires is 2.5-15mm, and adjacent two conductor wires form U-shaped structure or v-shaped structure.

Alternatively, wire is one, cell piece 31 is arranged into the matrix form of n × m, wherein n is columns, and m is row, in same row's cell piece 31, make wire reciprocation extension between the surface of a cell piece 31 and the surface of another adjacent cell piece 31, in adjacent two row's cell pieces 31, between the surface of a cell piece 31 during the surface of the cell piece 31 of wire reciprocation extension in a row and a+1 are arranged, wherein m-1 >=a >=1.

Preferably, in adjacent two row's cell pieces 31, make wire reciprocation extension on the surface of the cell piece 31 of an end of arranging at a and between the surface of the cell piece 31 of the end that a+1 arranges, the end that an end of a row and a+1 arrange is positioned at the same side of matrix.

Further, in same row's cell piece 31, make wire reciprocation extension between the front of a cell piece 31 and the back side of another adjacent cell piece 31, in adjacent two row's cell pieces 31, make wire reciprocation extension in the front of the cell piece 31 of an end of arranging at a and between the back side of a cell piece 31 of the end that a+1 arranges, with adjacent two row's cell pieces 31 of connecting.

In some embodiments of the application, the wire of reciprocation extension between the adjacent cell sheet 31 of same row is one, and the wire of reciprocation extension between the cell piece 31 of adjacent row is one.Wire is copper wire, and wire has circular cross section.

In other words, following two steps are comprised according to the preparation method of the solar module of the embodiment of the present application:

(1) at least two cell pieces are arranged with a matrix type, and between adjacent two cell pieces 31, make conductor wire between the surface of a cell piece 31 and the surface of another cell piece 31 reciprocation extension to form collapsed shape, and the secondary grid line on the sensitive surface of a cell piece 31 is welded with conductor wire, the back electrode on the back side of another cell piece 31 is welded with conductor wire;

(2) cell piece array 30, back side adhesive film 40 and backboard 50 that upper glass plates 10, front adhesive film 20, step (1) obtain are stacked from top to bottom successively, and make the sensitive surface of cell piece 31 in the face of front adhesive film 20, make the back side of cell piece 31 in the face of back side adhesive film 40, then carry out lamination.

In step (1), preferably, between contiguous two row's cell pieces 31, conductor wire is made to extend to the surface of a cell piece 31 in a+1 row from the surface of a cell piece 31 a row; More preferably, conductor wire is made to extend to the surface of the cell piece 31 of an end in a+1 row from the surface of the cell piece 31 of an end a row.

In one embodiment, further preferably, in same row's cell piece 31, conductor wire is made to extend to the back side of another adjacent cell sheet 31 from the sensitive surface bending of a cell piece 31; Between contiguous two row's cell pieces 31, conductor wire is made to extend to the back side of the cell piece 31 of the adjacent end in a+1 row from cell piece 31 sensitive surface of an end a row.

In another embodiment, further preferably, in same row's cell piece 31, conductor wire is made to extend to the sensitive surface of another adjacent cell sheet 31 from the back side bending of a cell piece 31; Between contiguous two row's cell pieces 31, conductor wire is made to extend to the sensitive surface of the cell piece 31 of the adjacent end in a+1 row from cell piece 31 back side of an end a row.

In step (1), conductor wire is coiling arrangement between same row's cell piece 31, and/or conductor wire coiling arrangement between adjacent two row's cell pieces 31.Most preferably, conductor wire between same row's cell piece 31 and adjacent two row cell pieces 31 between all adopt coiling to arrange mode.

In the preparation method of above-mentioned solar module, conductor wire, secondary grid line, wire, low-melting alloy layer, adhesive film, upper glass plates and backboard etc. all with describe above identical.

Above-mentioned lamination process can carry out in laminating machine.The lamination process implemented in laminating machine generally includes low temperature and vacuumizes and two stages of hot pressing.

In the preparation method of above-mentioned solar module, welding can adopt the welding manner of this area routine to implement.Under preferable case, the mode of welding is contactless, and wherein, non-contact welding method refers to high-frequency welding or far infrared welding.Adopt contactless welding method can realize the welding of multiple-grid line structure cell piece 31, can avoid occurring rosin joint, and can prevent conductor wire from drifting about.

In some embodiments of the application, after upper glass plates 10, front adhesive film 20, cell piece array 30, back side adhesive film 40 and backboard 50 being stacked successively lamination assembling, at the back side of backboard 50 bonding mounting blocks 80, mounting blocks 80 is fixed on support.

In the application, the mounting means of solar module is different from the clamp-type installation of the edge that frame is installed or two glass assembly is more general of traditional components, adopt and to use at the back side of assembly that high strength bond is gluing connects four pieces of mounting blocks, mounting blocks is fixed by screws on support.The stressed of installation Assurance component of this mode more evenly enhances the ability of assembly bearing load, more safe and reliable.

In the application, the connected mode of cell piece array 30 is different from general components, the thin copper wire of single plating low-melting alloy is adopted to connect two panels dereliction grid cell sheet, the thin copper wire that can be understood as plating low-melting alloy instead of main grid on conventional crystalline silicon cell piece and welding, eliminates the busbar of the one end without lead-out wire simultaneously.Conveniently the thin copper wire of plating low-melting alloy is called conductor wire by us.This cell piece retains traditional first step front wire mark, and battery makes the grid line of bottom, and we still follow tradition and are called thin grid.Then by diverse ways, wire being bent into many conductor wires perpendicular to thin grid covers on thin grid, forms the conductive grid structure intersected.Compared with traditional three main grid technology, the cross section due to copper cash is circular, effective shading-area can be reduced, reduce ohmic loss simultaneously after making assembly, improves assembly gross power.Because the distribution of 20-30 bar main grid is more intensive, the contact between conductor wire and thin grid is a lot, and more optimize with the path of fine fisssure position electric current conduction hidden the splitting of silicon chip, the loss therefore caused due to fine fisssure is greatly reduced.What is more important is due to conductor wire material employing copper cash, and the ag material consumption of battery also will greatly reduce.

Example 1

Example 1 is for illustration of the example of the solar module 100 and preparation method thereof of the application.

(1) wire S is prepared

The surface of copper wire is adhered to one deck Sn40%-Bi55%-Pb5% alloy-layer (fusing point is 125 DEG C), and wherein, the cross-sectional area of copper wire is 0.04mm ², the thickness of alloy-layer is 16 microns, thus obtained wire S.

(2) solar module 100 is prepared

The POE adhesive film being of a size of 1630 × 980 × 0.5mm (melt temperature is 65 DEG C) is provided, and correspondingly provides the glass plate that is of a size of 1633 × 985 × 3mm and 60 chip sizes to be the polycrystalline silicon battery plate 31 of 156 × 156 × 0.21mm.Cell piece 31 has 91 secondary grid lines, and (material is silver, width is 60 microns, thickness is 9 microns), the secondary grid line of every bar runs through cell piece 31 substantially in the vertical, and the distance between adjacent pair grid line is 1.7mm, and the back side of cell piece 31 has 5 back electrodes, and (material is tin, width is 1.5 millimeters, thickness is 10 microns), every bar back electrode runs through cell piece 31 substantially in the vertical, and the distance between adjacent two back electrodes is 31mm.

60 cell pieces 31 are arranged with a matrix type (6 row 10 row), between two cell pieces 31 adjacent in same row, make one metal wire state reciprocation extension in tension between the front and the back side of another cell piece of a cell piece 31, two charge off nails are such as set, pin in each row is spaced, wire is reciprocation extension in a tensioned state between two charge ofves nails, wire is by reciprocation extension under two clip tensionings laying respectively at these rhizoid two ends, thus the conductor wire that formation 15 is parallel, and the secondary grid line of a cell piece 31 is welded with conductor wire, the back electrode of another cell piece 31 is welded with conductor wire, , welding temperature is 160 DEG C, and the distance between the adjacent conductive line be parallel to each other is 9.9mm, thus by a row for 10 cell piece series connection, 6 rows this kind of battery strings is connected into array by busbar.Upper glass plates 10, lower glass plate are coated silica gel (thickness of the silica gel of coating is 250 microns) separately towards the one side of cell piece 31, sticks butyl rubber sealant bar in the surrounding of silica gel.Then, upper glass plates, in the matrix form arrangement are stacked from top to bottom successively with multiple cell piece of welded wire and lower glass plate, wherein, make the sensitive surface of cell piece 31 in the face of front adhesive film 20, front adhesive film 20 directly contacts with conductor wire 32, makes the back side of cell piece 31 in the face of back side adhesive film 40, then puts into laminating machine and carry out lamination, front adhesive film 20 is filled between adjacent conductor wire 32, thus obtained solar module A1.

Comparative examples 1

Comparative examples 1 is with the difference of example 1:

Cell piece 31 is arranged with a matrix type, and between adjacent two cell pieces 31, adopt wire drawing mode as shown in figure 14, by clip 34 tensioning of 15 wires parallel to each other by every one metal wire end, cell piece is flattened, the tension force of clip is 2N, these 15 each root of wire parallel to each other are welded with the secondary grid line in the front of a cell piece 31 separately, and weld with the back electrode at the back side of another cell piece, and the distance between the adjacent conductive line 32C be parallel to each other is 9.9mm.Thus obtained solar module D1.

Comparative examples 2

Comparative examples 2 is with the difference of example 1: arranged with a matrix type by cell piece, the wire that 15 are cascaded is pasted at transparent adhesive tape rete, wire is pasted on solar battery sheet, between adjacent two cell pieces, then wire connects the back side of the front of a cell piece and another cell piece, by upper glass plates, upper POE adhesive film, transparent adhesive tape rete, arrange in the matrix form and the multiple cell pieces be connected with wire, transparent adhesive tape rete, lower POE adhesive film and lower glass plate stack from top to bottom successively, thus obtained solar module D2.

Comparative examples 3

Comparative examples 3 is with the difference of example 1: backboard does not adopt glass and adopts PET plate, so obtained solar module D3.

Example 2

Method according to example 1 prepares solar module, is with the difference of example 1: reciprocation extension is to form 20 parallel conductor wires, and the distance between the adjacent conductive line be parallel to each other is 7mm, so obtained solar module A2.

Example 3

Method according to example 2 prepares solar module, is with the difference of example 2: the silica gel thickness of coating is 300 microns, so obtained solar module A3.

Example 4

Method according to example 2 prepares solar module, is with the difference of example 2: the silica gel thickness of coating is 350 microns, so obtained solar module A4.

Example 5

Method according to example 2 prepares solar module, is with the difference of example 2: the silica gel thickness of coating is 400 microns, so obtained solar module A5.

Example 6

Method according to example 2 prepares solar module, be with the difference of example 2: on the secondary grid line of the sensitive surface of cell piece 31, arranging short grid line 33, (material is silver, width is 0.1mm), this short grid line 33 is vertical with secondary grid line, for connecting secondary grid line and the conductor wire of the edge portions of the sensitive surface of cell piece, as shown in figure 12, thus obtained solar module A6.

Example 7

Method according to example 3 prepares solar module, and the difference of example 3 is: the connected mode of array is: arrange between cell piece adjacent two, conductor wire to extend and the back side of the cell piece 31 of adjacent end portion is formed and is electrically connected in arranging with a+1 from the sensitive surface of cell piece of an end a (a >=1) row, for realizing the connection between adjacent two row's cell pieces, and for the conductor wire that connects adjacent two row's cell pieces 31 with for be connected this two arrange in the conductor wire of adjacent cell sheet 31 be mutually arranged vertically.So obtained solar module A7.

Test case 1

(1) whether drifted about by the wire in naked-eye observation method observation solar module;

(2) disclosed in IEC904-1, method adopts single flash operation simulator to test solar module prepared by above-mentioned example and comparative examples, and test condition is standard test condition (STC): light intensity is 1000W/m ²; Spectrum is AM1.5; Temperature is 25 DEG C, records the photoelectric conversion efficiency of each cell piece.

Result is as shown in table 1 below.

Table 1

Wherein, the ratio of the maximum power (open circuit voltage * short circuit current) when the maximum power point power that fill factor, curve factor represents solar module and zero internal resistance in theory, characterize the close degree of actual power to theoretical maximum power, this value is larger, illustrate that photoelectric conversion efficiency is higher, general series resistance is little, and fill factor, curve factor is just large.Photoelectric conversion efficiency is finger assembly (light intensity 1000W/m under standard illumination condition ²), light energy conversion is the ratio of electric energy by assembly; Series resistance is equivalent to the internal resistance of solar components, and its value is larger, and assembly property is poorer; Fill factor, curve factor, represent the actual maximum power of assembly and the ratio of theoretical maximum power, numerical value is larger, and assembly property is better; Open circuit voltage be assembly under standard illumination condition, voltage during open circuit; During short circuit current, assembly is under standard illumination condition, electric current during short circuit; Operating voltage be assembly under standard illumination condition, output voltage when working with maximum power; Operating current be assembly under standard illumination condition, output current when working with maximum power; Power be finger assembly under standard illumination condition, the maximum power that can reach.

As can be seen from the result of table 1, can not there is the problem of wire drift in the solar module of the embodiment of the present application, and can obtain relatively high photoelectric conversion efficiency, and place some months observation wire does not have variable color simultaneously.

Test case 2

(1) welded wire is surperficial to cell piece, wire is vertical with the secondary grid line of cell piece;

(2) cell piece level is placed on the test position of tension tester, places briquetting by cell piece, briquetting is placed in both sides wiry, and when making to test, cell piece is not pulled up;

(3) wire is clipped on the draw ring of tensiometer, direction of pull and cell piece angle at 45 °;

(4) start tensiometer, make tensiometer vertically upwards uniform motion, by wire from cell piece surface pull-up, the pulling force data that record tensiometer records, gets its average and is this pulling force data wiry.

Result is as shown in table 2 below.

Table 2

As can be seen from the result of table 2, the solar module of the embodiment of the present application is larger from the pulling force required for glass cell piece is peeled off by wire, namely illustrates that the connective stability of wire and cell piece in the solar cell establishment of the embodiment of the present application is stronger.

In description of the present utility model, it will be appreciated that, term " " center ", " longitudinal direction ", " transverse direction ", " length ", " width ", " thickness ", " on ", D score, " front ", " afterwards ", " left side ", " right side ", " vertically ", " level ", " top ", " end " " interior ", " outward ", " clockwise ", orientation or the position relationship of the instruction such as " counterclockwise " are based on orientation shown in the drawings or position relationship, only the utility model and simplified characterization for convenience of description, instead of indicate or imply that the device of indication or element must have specific orientation, with specific azimuth configuration and operation, therefore can not be interpreted as restriction of the present utility model.

In addition, term " first ", " second " only for describing object, and can not be interpreted as instruction or hint relative importance or imply the quantity indicating indicated technical characteristic.Thus, be limited with " first ", the feature of " second " can express or impliedly comprise one or more these features.In description of the present utility model, the implication of " multiple " is two or more, unless otherwise expressly limited specifically.

In the utility model, unless otherwise clearly defined and limited, the term such as term " installation ", " being connected ", " connection ", " fixing " should be interpreted broadly, and such as, can be fixedly connected with, also can be removably connect, or connect integratedly; Can be mechanical connection, also can be electrical connection; Can be directly be connected, also indirectly can be connected by intermediary, can be the connection of two element internals.For the ordinary skill in the art, the concrete meaning of above-mentioned term in the utility model can be understood as the case may be.

In the utility model, unless otherwise clearly defined and limited, fisrt feature second feature it " on " or D score can comprise the first and second features and directly contact, also can comprise the first and second features and not be directly contact but by the other characterisation contact between them.And, fisrt feature second feature " on ", " top " and " above " comprise fisrt feature directly over second feature and oblique upper, or only represent that fisrt feature level height is higher than second feature.Fisrt feature second feature " under ", " below " and " below " comprise fisrt feature directly over second feature and oblique upper, or only represent that fisrt feature level height is less than second feature.

In the description of this specification, specific features, structure, material or feature that the description of reference term " embodiment ", " some embodiments ", " example ", " concrete example " or " some examples " etc. means to describe in conjunction with this embodiment or example are contained at least one embodiment of the present utility model or example.In this manual, identical embodiment or example are not necessarily referred to the schematic representation of above-mentioned term.And the specific features of description, structure, material or feature can combine in an appropriate manner in any one or more embodiment or example.

Although illustrate and described embodiment of the present utility model above, be understandable that, above-described embodiment is exemplary, can not be interpreted as restriction of the present utility model, those of ordinary skill in the art can change above-described embodiment when not departing from principle of the present utility model and aim, revising, replacing and modification in scope of the present utility model.

Claims

1. a solar module, it is characterized in that, comprise: upper glass plates stacked successively, front adhesive film, solar cell chip arrays, back side adhesive film and backboard, described solar cell chip arrays comprises multiple cell piece, be connected by wire between adjacent cell sheet, between the surface of the cell piece of at least one described wire in adjacent cell sheet and the surface of another cell piece, reciprocation extension is to form at least two conductor wires, the front of described cell piece is provided with secondary grid line, described conductor wire welds with described secondary grid line, the thickness of at least one in described front adhesive film and described back side adhesive film is more than or equal to wire and is less than 400 microns at the thickness perpendicular to cell piece direction.

2. solar module according to claim 1, is characterized in that, the thickness of at least one in described front adhesive film and described back side adhesive film is 250-400 micron.

3. solar module according to claim 2, is characterized in that, the thickness of at least one in described front adhesive film and described back side adhesive film is 250-350 micron.

4. the solar module according to any one of claim 1-3, is characterized in that, described wire is copper wire.

5. the solar module according to any one of claim 1-3, is characterized in that, described wire has circular cross section.

6. the solar module according to any one of claim 1-3, is characterized in that, described wire reciprocation extension 10-60 time.

7. the solar module according to any one of claim 1-3, is characterized in that, the number of described conductor wire is in the scope of 20-40.

8. solar module according to claim 7, is characterized in that, the number of described conductor wire is 24-28.

9. the solar module according to any one of claim 1-3, is characterized in that, the spacing between adjacent conductive line is 2.5-15mm.

10. the solar module according to any one of claim 1-3, is characterized in that, adjacent conductive line forms U-shaped structure or v-shaped structure.

11. solar modules according to any one of claim 1-3, it is characterized in that, described wire is one.

12. solar modules according to claim 1, is characterized in that, described cell piece is arranged into the matrix form of n × m, and wherein n is columns, and m is row, and m-1 >=a >=1,

In same row's cell piece, described wire reciprocation extension is between the surface of a cell piece and the surface of another adjacent cell piece, in adjacent two row's cell pieces, between the surface of a cell piece during the surface of the cell piece of described wire reciprocation extension in a row and a+1 arrange.

13. solar modules according to claim 12, it is characterized in that, in adjacent two row's cell pieces, described wire reciprocation extension is on the surface of the cell piece of an end of arranging at a and between the surface of the cell piece of the end that a+1 arranges, and the end that an end of described a row and described a+1 arrange is positioned at the same side of described matrix.

14. solar modules according to claim 13, is characterized in that, in same row's cell piece, described wire reciprocation extension between the front of a cell piece and the back side of another adjacent cell piece,

Adjacent two row cell pieces in, described wire reciprocation extension in the front of the cell piece of an end of arrange at a and between the back side of a cell piece of the end that a+1 arranges, with connect adjacent two arrange cell pieces.

15. solar modules according to any one of claim 12-14, it is characterized in that, the wire of reciprocation extension between the adjacent cell sheet of same row is one, and the wire of reciprocation extension between the cell piece of adjacent row is one.

16. solar modules according to claim 1, is characterized in that, described wire reciprocation extension in a tensioned state before being connected with described cell piece.

17. solar modules according to claim 1, is characterized in that, described wire is coated with weld layer.

18. solar modules according to claim 17, is characterized in that, thickness and the described diameter ratio wiry of described weld layer are 0.02-0.5:1.

19. solar modules according to claim 17, is characterized in that, the thickness of described weld layer is 1-100 micron.

20. solar modules according to claim 1, is characterized in that, the width of described secondary grid line is 40-80 micron, and thickness is 5-20 micron, and described secondary grid line is 50-120 bar, and the spacing of adjacent pair grid line is 0.5-3mm.

21. solar modules according to claim 1, is characterized in that, described front adhesive film and described back side adhesive film are silica gel.

22. solar modules according to claim 1, is characterized in that, described backboard is glass plate.

23. solar modules according to claim 1, is characterized in that, the outer of described upper glass plates and described backboard uses butyl rubber or Oppanol sealing.

24. solar modules according to claim 1, it is characterized in that, described upper glass plates and described backboard outer utilize silica gel or butyl rubber or two-sided tape to fix by U-shaped frame, and are filled with fluid sealant between the outer of described upper glass plates and described backboard and described U-shaped frame.

25. solar modules according to claim 1, is characterized in that, also comprise terminal box, described terminal box is located at the edge of upper glass plates and backboard.

26. solar modules according to claim 1, is characterized in that, described front adhesive film directly contacts with described conductor wire and is filled between adjacent conductor wire.

27. solar modules according to claim 1, it is characterized in that, reciprocation extension between the front of the cell piece of described wire in adjacent cell sheet and the back side of another cell piece, described front adhesive film directly contacts with the conductor wire on the front of a described cell piece and is filled between the adjacent conductive line on the front of a described cell piece, and described back side adhesive film directly contacts with the conductor wire at the back side of another cell piece described and is filled between the adjacent conductive line at the back side of another cell piece described.

28. solar modules according to claim 1, is characterized in that, the size of described cell piece is 156mm × 156mm; The series resistance of described solar module is 380-440 milliohm/60 slice.

29. solar modules according to claim 1, is characterized in that, the size of described cell piece is 156mm × 156mm; The open circuit voltage of described solar module is 37.5-38.5V/60 sheet; Short circuit current is 8.9-9.4A.

30. solar modules according to claim 1, is characterized in that, the fill factor, curve factor of described solar module is 0.79-0.82.

31. solar modules according to claim 1, is characterized in that, the size of described cell piece is 156mm × 156mm; The operating voltage of described solar module is 31.5-32V/60 sheet; Operating current is 8.4-8.6A.

32. solar modules according to claim 1, is characterized in that, the size of described cell piece is 156mm × 156mm; The conversion efficiency of described solar module is 16.5-17.4%; Power is 265-280W/60 sheet.