CN204690262U - One refuses water-hydrophilic nonwoven cloth - Google Patents
One refuses water-hydrophilic nonwoven cloth Download PDFInfo
- Publication number
- CN204690262U CN204690262U CN201520382389.0U CN201520382389U CN204690262U CN 204690262 U CN204690262 U CN 204690262U CN 201520382389 U CN201520382389 U CN 201520382389U CN 204690262 U CN204690262 U CN 204690262U
- Authority
- CN
- China
- Prior art keywords
- fiber
- hydrophilic
- finish
- water
- nonwoven cloth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model discloses one and refuse water-hydrophilic nonwoven cloth, comprise and refuse water finish fiber and hydrophilic finish fiber; Describedly refuse water finish fiber and hydrophilic finish fiber is skin-core structure, skin-core structure comprises cortex and sandwich layer, and the cortex by melting between sandwich layer is interconnected.The utility model is produced with the method that the fiber with hydrophilic finish is penetrated by hot blast after mixing by having the fiber refusing water finish, liquid rotating can be moved to guide layer and absorber rapidly by the passage of hydrophilic fibers composition, the existence simultaneously refusing water cellulose can effectively stop liquid to return from absorber to ooze to surface, thus reaches the result of surface dry.This design can overcome existing Through-Air Thermal Bonded Nonwovens liquid and return the problem of oozing the surface of sanitary humidity caused.Enforcement of the present utility model is by using blast heater heating to realize containing refusing water finish and the skin-core structure containing hydrophilic finish or core shift structural fibers, is a kind of production method of novel Through-Air Thermal Bonded Nonwovens.
Description
Technical field
The utility model relates to a kind of non-weaving cloth, particularly relates to one and refuses water-hydrophilic nonwoven cloth.
Background technology
Thermal non-woven fabric has been widely used in feminine hygiene and baby paper diaper, usually top layer is applied in, it can absorb rapidly body fluid (menstruation exudate, urine), and it is imported as far as possible uniformly the absorber of its lower floor, like this, both maintain skin dry and comfortable, prevent again the lateral leakage of body fluid.
Through-Air Thermal Bonded Nonwovens is the one in thermal bonding technology, and it is due to soft, fluffy and user can be made to feel comfortably cool and be widely used in personal hygiene nursing materials.Through-Air Thermal Bonded Nonwovens adopts the bicomponent fiber of parallel construction or skin-core structure, by hot air composite fibre after carding, cortex PE melting in composite fibre makes fiber overlap mutually, eventually passes cooling and becomes the non-weaving cloth having certain strength and extension property.
At present, worldwide hot blast nonwovens process raw materials mainly contains the bicomponent fibers such as PP/PE, PET/PE, the needs of fiber post processing substantially also just in order to meet its fibre process, to use demand but not more concerns of consumer.But for the designer of sanitary napkin, urine pants, owing to being subject to the impact of Through-Air Thermal Bonded Nonwovens infiltration rate and absorber uptake, how by improving, product is dry-ness has become design requirement problems faced.And consumer demand point is also more and more higher, therefore by improving some performance of fiber, making fiber meet characteristic in a certain respect, becoming the innovative point that designer is new, the demand meeting user that also can be higher.
Utility model content
Water-hydrophilic nonwoven cloth is refused for the utility model that solves the problem provides one.With adding through refusing the fiber of water finish process, the non-weaving cloth produced through specific manufacture craft has the performance well preventing from liquid from returning oozing, and the surface layer being used in sanitary napkin or urine pants can effectively improve the dry-ness of health product.
For reaching above-mentioned technique effect, the technical solution of the utility model is:
One refuses water-hydrophilic nonwoven cloth, comprises and refuses water finish fiber and hydrophilic finish fiber; Describedly refuse water finish fiber and hydrophilic finish fiber is skin-core structure, skin-core structure comprises cortex and sandwich layer, and the cortex by melting between sandwich layer is interconnected; The fibre fineness of refusing water finish fiber and hydrophilic finish fiber is 1 ~ 15Dtex, and length is 1 ~ 80mm; Refuse water finish fiber and hydrophilic finish fiber is interconnected to form fiber web, described in refuse water-hydrophilic nonwoven cloth and comprise double layer fibre net, the thickness refusing water-hydrophilic nonwoven cloth is 0.1 ~ 3.0mm.
Further improvement, described in refuse water finish fiber and hydrophilic finish fiber fibre fineness be 1 ~ 6Dtex, length is 30 ~ 60mm; The thickness of described non-weaving cloth is 0.5 ~ 2.0mm.
Further improvement, described in refuse water-hydrophilic nonwoven cloth cloth cover on carry out groove and embossed.
The utility model is produced with the method that the fiber with hydrophilic finish is penetrated by hot blast after mixing by having the fiber refusing water finish, liquid rotating can be moved to guide layer and absorber rapidly by the passage of hydrophilic fibers composition, the existence simultaneously refusing water cellulose can effectively stop liquid to return from absorber to ooze to surface, thus reaches the result of surface dry.This design can overcome existing Through-Air Thermal Bonded Nonwovens liquid and return the problem of oozing the surface of sanitary humidity caused.Enforcement of the present utility model is by using blast heater heating to realize containing refusing water finish and the skin-core structure containing hydrophilic finish or core shift structural fibers, is a kind of production method of novel Through-Air Thermal Bonded Nonwovens.
Advantage of the present utility model:
1, the utility model use terylene-polyethylene composite fibre or polypropylene fibre-polyethylene composite fibre, the polyethylene (PE) of cortex is different with the percent thermal shrinkage of sandwich layer terylene (PET) or polypropylene fibre (PP), be sticked together through hot-blast stove melting compared with the polyethylene (PE) of low melting point, in this process, fiber has occurred that distortion makes product have good fluffy sense.
2, due to the existence of hydrophilic fibers, the non-weaving cloth that the procedure of fibre production used by the utility model goes out has good liquid single penetration capacity, rapidly liquid rotating can be moved to guide layer and absorber.
3, due to the existence of hydrophilic fibers, the non-weaving cloth that the procedure of fibre production used by the utility model goes out has good liquid barrier ability, can effectively place liquid and be transferred to surface from absorber.
Accompanying drawing explanation
Fig. 1 manufactures the fine step schematic diagram containing plant finish non-weaving cloth;
Fig. 2 manufactures the fiber schematic diagram containing plant finish non-weaving cloth.
Detailed description of the invention
Embodiment 1
One as shown in Figure 2 refuses water-hydrophilic nonwoven cloth, and the manufacture fiber manufacturing described non-weaving cloth is by refusing water finish fiber and the manufacture of hydrophilic finish fiber blend forms.Manufacture fiber in described non-weaving cloth is terylene-polyethylene composite fibre or polypropylene fibre-polyethylene composite fibre; Manufacture fiber is skin-core structure, comprises cortex 1 and sandwich layer 2, and cortex 1 is polyethylene, and sandwich layer 2 is terylene or polypropylene fibre; Manufacture fibre fineness is 1 ~ 15Dtex, and length is 1 ~ 80mm; Refuse water finish fiber and hydrophilic finish fiber is interconnected to form fiber web, described in refuse water-hydrophilic nonwoven cloth and comprise double layer fibre net, the thickness refusing water-hydrophilic nonwoven cloth is 0.1mm, and grammes per square metre is 10g/m
2.
Embodiment 2
One as shown in Figure 2 refuses water-hydrophilic nonwoven cloth, and the manufacture fiber manufacturing described non-weaving cloth is by refusing water finish fiber and the manufacture of hydrophilic finish fiber blend forms.Non-weaving cloth by containing refusing water finish fiber and forming containing the fiber blend manufacture of hydrophilic finish, therefore has and reduces liquid preferably and return the performance of oozing.Manufacture fiber in described non-weaving cloth is terylene-polyethylene composite fibre or polypropylene fibre-polyethylene composite fibre; Manufacture fiber is skin-core structure, comprises cortex 1 and sandwich layer 2, and cortex 1 is polyethylene, and sandwich layer 2 is terylene or polypropylene fibre; Manufacture fibre fineness is 1 ~ 6Dtex, and length is 30 ~ 60mm; Refuse water finish fiber and hydrophilic finish fiber is interconnected to form fiber web, described in refuse water-hydrophilic nonwoven cloth and comprise double layer fibre net, the thickness refusing water-hydrophilic nonwoven cloth is 0.5mm, and grammes per square metre is 20g/m
2.
Embodiment 3
One as shown in Figure 2 refuses water-hydrophilic nonwoven cloth, and the manufacture fiber manufacturing described non-weaving cloth is by refusing water finish fiber and the manufacture of hydrophilic finish fiber blend forms.Non-weaving cloth by containing refusing water finish fiber and forming containing the fiber blend manufacture of hydrophilic finish, therefore has and reduces liquid preferably and return the performance of oozing.Manufacture fiber in described non-weaving cloth is terylene-polyethylene composite fibre or polypropylene fibre-polyethylene composite fibre; Manufacture fiber is skin-core structure, comprises cortex 1 and sandwich layer 2, and cortex 1 is polyethylene, and sandwich layer 2 is terylene or polypropylene fibre; Manufacture fibre fineness is 1 ~ 6Dtex, and length is 30 ~ 60mm; Refuse water finish fiber and hydrophilic finish fiber is interconnected to form fiber web, described in refuse water-hydrophilic nonwoven cloth and comprise double layer fibre net, the thickness refusing water-hydrophilic nonwoven cloth is 2.0mm, and grammes per square metre is 40g/m
2.
Embodiment 4
One refuses water-hydrophilic nonwoven cloth as shown in Figure 2, and the manufacture fiber manufacturing described non-weaving cloth is by refusing water finish fiber and the manufacture of hydrophilic finish fiber blend forms.Non-weaving cloth by containing refusing water finish fiber and forming containing the fiber blend manufacture of hydrophilic finish, therefore has and reduces liquid preferably and return the performance of oozing.Manufacture fiber in described non-weaving cloth is terylene-polyethylene composite fibre or polypropylene fibre-polyethylene composite fibre; Manufacture fiber is skin-core structure, comprises cortex 1 and sandwich layer 2, and cortex 1 is polyethylene, and sandwich layer 2 is terylene or polypropylene fibre; Manufacture fibre fineness is 1 ~ 6Dtex, and length is 30 ~ 60mm; Refuse water finish fiber and hydrophilic finish fiber is interconnected to form fiber web, described in refuse water-hydrophilic nonwoven cloth and comprise double layer fibre net, the thickness refusing water-hydrophilic nonwoven cloth is 3.0mm, and grammes per square metre is 100g/m
2.
The preparation method of the non-weaving cloth containing plant finish of embodiment 1-4 as shown in Figure 1, comprises the following steps:
Step one) preliminary treatment: water cellulose will be refused and hydrophilic fibers two kinds of raw materials mix after abundant shredding;
Step 2) heat bonding: send into hot air apparatus Hot-blast Heating after the material combing after shredding is become fibre web, the cortex melting of the fiber of skin-core structure, make sandwich layer be welded to each other together, form the state of non-weaving cloth; During heating, temperature is 130 DEG C-140 DEG C, and blast is 20Hz-50Hz.
Step 3) cooling and shaping: will the fiber cooling and shaping of the state of non-weaving cloth be formed, reinforce and export; The temperature of cooling and shaping is not higher than 60 DEG C.Before cooling and shaping, carry out groove and embossed to containing cotton non-weaving cloth.
The explanation of above example just understands core concept of the present utility model for helping; Meanwhile, for one of ordinary skill in the art, according to thought of the present utility model, all will change in specific embodiments and applications, in sum, this description should not be construed as restriction of the present utility model.
Claims (3)
1. refuse water-hydrophilic nonwoven cloth, it is characterized in that, comprise and refuse water finish fiber and hydrophilic finish fiber; Describedly refuse water finish fiber and hydrophilic finish fiber is skin-core structure, skin-core structure comprises cortex (1) and sandwich layer (2), and the cortex (1) by melting between sandwich layer (2) is interconnected; The fibre fineness of refusing water finish fiber and hydrophilic finish fiber is 1 ~ 15Dtex, and length is 1 ~ 80mm; Refuse water finish fiber and hydrophilic finish fiber is interconnected to form fiber web, described in refuse water-hydrophilic nonwoven cloth and comprise double layer fibre net, the thickness refusing water-hydrophilic nonwoven cloth is 0.1 ~ 3.0mm.
2. refuse water-hydrophilic nonwoven cloth as claimed in claim 1, it is characterized in that, described in refuse water finish fiber and hydrophilic finish fiber fibre fineness be 1 ~ 6Dtex, length is 30 ~ 60mm; The thickness of described non-weaving cloth is 0.5 ~ 2.0mm.
3. refuse water-hydrophilic nonwoven cloth as claimed in claim 1, it is characterized in that, described in refuse water-hydrophilic nonwoven cloth cloth cover on carry out groove and embossed.