CN204603302U - A kind of equipment peeling off the waste and old surface of Nd-Fe-B permanent magnet coat of metal - Google Patents
A kind of equipment peeling off the waste and old surface of Nd-Fe-B permanent magnet coat of metal Download PDFInfo
- Publication number
- CN204603302U CN204603302U CN201520252568.2U CN201520252568U CN204603302U CN 204603302 U CN204603302 U CN 204603302U CN 201520252568 U CN201520252568 U CN 201520252568U CN 204603302 U CN204603302 U CN 204603302U
- Authority
- CN
- China
- Prior art keywords
- hydrogen
- permanent magnet
- waste
- metal
- coat
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn - After Issue
Abstract
Peel off an equipment for the waste and old surface of Nd-Fe-B permanent magnet coat of metal, relate to waste and old Nd-Fe-B permanent magnet recovery technology field.It comprises realize permanent magnet expose fresh fracture disintegrating apparatus, realize NdFeB Permanent Magnets principal phase inhale hydrogen be broken into graininess treatment step tubular type hydrogen crushing furnace, realize physical separation and obtain NdFeB magnetic powder and keep the separation equipment of complete coat of metal treatment step because not reacting and be connected the motion of tubular type hydrogen crushing furnace and separation equipment.The equipment of the waste and old surface of Nd-Fe-B permanent magnet coat of metal of stripping of the present utility model, realizes the high-efficiency operation of whole process by the cooperation of motion.Nd Fe B alloys powder after adopting glove box can avoid fragmentation is still adequately protected and can not be oxidized.Complete equipment structure is comparatively compact, is applicable to industrial applications, low cost of manufacture.
Description
Technical field
The utility model relates to waste and old Nd-Fe-B permanent magnet recovery technology field, specifically relates to a kind of equipment peeling off the waste and old surface of Nd-Fe-B permanent magnet coat of metal.
Background technology
Rare earth metal is the strategic resource of country, the important source material of particularly new and high technology industry.Utilization is continually developed along with industrial, and rare-earth products outlet, the reserves of China's rare-earth original ore decline fast, and China, with the use amount in the global 30% rare earth reserves supply whole world 90%, causes the exhaustive exploitation of rare earth resources.Therefore, rational exploitation and utilization rare earth resources becomes the most important thing that country " 12 " plans.
Sintered NdFeB is as third generation rare earth permanent magnet, and it has high magnetic energy product, and excellent anti-demagnetization capability, is widely used in auto industry, electromechanics trade, energy-conservation household electrical appliances, the industries such as wind-power electricity generation.Within 2010, Chinese neodymium iron boron output has reached 80,000 tons, and just have the neodymium iron boron magnetic body in the processing waste material of nearly five kilotons and used facilities every year, wherein waste and old neodymium iron boron motor magnet is typical secondary rare earth resources, and added value is high.The effective recycling of rare earth secondary resource, not only meets national energy-saving and reduces discharging, advocate the road for development of green energy resource, at utmost play the value of secondary resource especially, create good economic and social benefit.
The recovery of neodymium iron boron magnetic body mainly carries out Rare Earth Separation to the magnet of the waste material produced in process and used facilities both at home and abroad at present, but Rare Earth Separation cost is high, also comparatively serious to environmental disruption.Meanwhile, China's waste and old neodymium iron boron way of recycling is backward, the rate of recovery is low, pollution is large.Along with the extensive use of neodymium iron boron product, the waste and old neodymium iron boron magnetic body enormous amount of scrapping every year, the recycling carrying out waste and old magnet by the Rare Earth Separation of waste and old magnet is merely not the method for high efficiency, low cost.And the rare earth policy that country puts into effect, also require that saving utilizes rare earth resources and efficiency utilization rare earth resources.The recycling of neodymium iron boron magnetic body in neodymium iron boron magnetic body processing waste material and used facilities and waste and old neodymium iron boron is not still had to prepare the technical requirement standard of High-performance magnetic steel at present.Therefore, develop a kind of easy to operate, cost recovery is low, and environmentally friendly waste and old Magnet Technology becomes the key factor that Sintered NdFeB magnet reclaims.
The recovery adopting the broken reheating technique of waste and old magnet to carry out Sintered NdFeB magnet is one both economic environmental protection, recovery process method simply and easily again, but current motor by waste and old neodymium iron boron magnetic body major part all with the coat of metal (as metallic nickel plated layer, ambrose alloy nickel coating etc.), the mode of chemical strip is adopted to remove coating, not only increase cost recovery, and have certain pollution to environment.Nickel metal is also national strategy resource, and recovering rare earth metal and nickel coating become the study hotspot of current Sintered NdFeB magnet industry simultaneously therefore to adopt physics mode.
Utility model content
For the technical problem existed in prior art, the purpose of this utility model is the equipment of the waste and old surface of Nd-Fe-B permanent magnet coat of metal of stripping providing a kind of structure simple, easy and simple to handle.
To achieve these goals, the technical scheme that the utility model adopts is: a kind of equipment peeling off the waste and old surface of Nd-Fe-B permanent magnet coat of metal, comprise realize permanent magnet expose fresh fracture disintegrating apparatus, realize NdFeB Permanent Magnets principal phase inhale hydrogen be broken into graininess treatment step tubular type hydrogen crushing furnace, realize physical separation and obtain NdFeB magnetic powder and keep the separation equipment of complete coat of metal treatment step because not reacting and be connected the motion of tubular type hydrogen crushing furnace and separation equipment.
The equipment of the waste and old surface of Nd-Fe-B permanent magnet coat of metal of stripping of the present utility model, its beneficial effect shows:
1), first interrupting for needing the Nd-Fe-B permanent magnet of the stripper surface coat of metal to carry out simple and mechanical fragmentation, making magnet expose fresh fracture; Then the neodymium iron boron magnetic body after fragmentation is put into tubular type hydrogen crushing furnace, pass into hydrogen and make neodymium iron boron principal phase suction hydrogen be broken into graininess, and outer nickel coating keeps complete owing to not reacting; Mixed-powder after finally broken to hydrogen revolves to shake and sieves, and is separated and obtains nickel coating and NdFeB magnetic powder.The inside neodymium iron boron principal phase of permanent magnet is inhaled hydrogen and is broken into Powdered, and external metallization coating keeps complete owing to not reacting, and effectively remove outside coating, and physical separation efficiency is high by physical separation.
2), to reclaim the performance obtaining neodymium iron boron powder after stripping metal coating substantially constant, re-starts the sintering of Sintered NdFeB magnet, after composition regulation and control, be directly used in production by certain technique.Relative to traditional chemical strip method, this stripping means greatly reduces rare earth cost recovery, reduces environmental pollution, adds rare earth recovery utilization rate.
3), by appropriate design device structure make itself and stripping means perfect matching, realized the high-efficiency operation of whole process by the cooperation of motion.Nd Fe B alloys powder after adopting glove box can avoid fragmentation is still adequately protected and can not be oxidized.Complete equipment structure is comparatively compact, is applicable to industrial applications, low cost of manufacture.
Accompanying drawing explanation
Fig. 1 a-1c is respectively the photo of annulus pattern neodymium iron boron, the rear coat of metal of stripping, the rear neodymium iron boron powder of stripping before stripping in embodiment 1.
Fig. 2 a-2c is respectively the photo of annulus pattern neodymium iron boron, the rear coat of metal of stripping, the rear neodymium iron boron powder of stripping before stripping in embodiment 2.
Fig. 3 a-3c is respectively the photo of disk pattern neodymium iron boron, the rear coat of metal of stripping, the rear neodymium iron boron powder of stripping before stripping in embodiment 3.
Fig. 4 a-4c is respectively the photo of square pattern neodymium iron boron, the rear coat of metal of stripping, the rear neodymium iron boron powder of stripping before stripping in embodiment 4.
Fig. 5 is the structural representation of the equipment peeling off the waste and old surface of Nd-Fe-B permanent magnet coat of metal.
Detailed description of the invention
For further describing the equipment of the waste and old surface of Nd-Fe-B permanent magnet coat of metal of stripping of the present utility model, below in conjunction with accompanying drawing 5, it is described in further detail.
First refer to Fig. 5, the equipment peeling off the waste and old surface of Nd-Fe-B permanent magnet coat of metal is made up of parts such as tubular type hydrogen crushing furnace 1, glove box 7, mechanical arm 6 and propulsion cylinders 4.The inside of tubular type hydrogen crushing furnace 1 has the broken pipe 2 of hydrogen, has and place the magazine 3 of permanent magnet in the broken pipe 2 of hydrogen, the two ends of the broken pipe of hydrogen 2 have for the magazine 3 loading permanent magnet enter hydrogen broken pipe 2 inner, inhale hydrogen fragmentation after magazine 3 leave the import and export of the broken pipe 2 of hydrogen.
Spin vibration sieve 5 is placed in the port of export of the broken pipe 2 of hydrogen, and the arrival end of spin vibration sieve 5 is placed in the glove box 7 being filled with nitrogen, and glove box 7 side is connected with the discharge end of tubular type hydrogen crushing furnace 1 makes the Nd Fe B alloys powder that fragmentation is formed because inhaling hydrogen be in all the time under nitrogen protection.
Mechanical arm 6 is placed in glove box 7, and the magazine 3 that the broken pipe 2 of hydrogen is left in mechanical arm 6 clamping moves to the top of spin vibration sieve 5 and material in box is poured onto in spin vibration sieve 5 by upset.
The two ends of tubular type hydrogen crushing furnace 1 have the valve of band sealing ring, and control its opening and closing by pneumatic means.Two propulsion cylinders 4 are placed in the both sides of tubular type hydrogen crushing furnace 1, and magazine 3 is moved in the broken pipe 2 of hydrogen.
In actual process, get the waste and old magnet with the coat of metal (comprising metallic nickel plated layer, ambrose alloy nickel coating etc.), waste and old magnet is interrupted to making it expose fresh fracture, collection is placed in polybag and is filled with nitrogen protection.
The waste and old magnet with fresh fracture collected is loaded in tubular type hydrogen crushing furnace in magazine (magazine can be positioned over a certain fixed position in pipe), closed tubular type hydrogen crushing furnace two ends valve.Then positive/negative-pressure leak detection is carried out to hydrogen crushing furnace, hunt leak qualified after vacuumize in stove, reach after requirement until vacuum, heating hydrogen crushing furnace is also incubated.Then pour hydrogen after being filled with a certain amount of argon gas in the broken pipe of hydrogen, control intraductal pressure simultaneously.After a period of time, after heating hydrogen crushing furnace to uniform temperature, remove gas in pipe.After managing interior gas removal and be clean, cool after being filled with argon gas to certain pressure intensity.
After the broken pipe cooling of hydrogen, button press, hydrogen broken pipe discharging opening valve is opened through pneumatic means, the magazine that mixture of powders is housed in pipe is pushed out to the mouth of pipe through propulsion cylinder, take out through mechanical arm clamping, mixture of powders in magazine is poured in spin vibration sieve by mechanical arm upset, removes, neodymium iron boron powder and the coat of metal are carried out physical separation through spin vibration sieve vibratory sieve.Neodymium iron boron powder to be collected in retracting device through the spin vibration sieve mouth of pipe and to be filled with nitrogen protection.The coat of metal, after accumulation some, after glove box can being opened, takes out from spin vibration sieve top.
Below in conjunction with accompanying drawing 1-4 and embodiment 1-4, the method peeling off the waste and old surface of Nd-Fe-B permanent magnet coat of metal is described in further detail.
Embodiment 1
The waste and old sintered NdFeB circular ring of surface with nickel coating (is of a size of: external diameter is Φ 60mm, internal diameter Φ 10mm) (refer to Fig. 1 and a) carry out simple and mechanical interrupting, the waste and old magnet with fresh fracture to be loaded in tubular type hydrogen crushing furnace in magazine, then positive/negative-pressure leak detection is carried out to hydrogen crushing furnace.
Hunt leak qualified after, will be evacuated to pressure 0.7Pa in stove, heating hydrogen crushing furnace to 200 DEG C, and is incubated 40min.Then in the broken pipe of hydrogen, be filled with argon gas to 0.030MPa, after be filled with hydrogen, control intraductal pressure 0.08MPa.When hydrogen pressure drop≤0.03MPa/15min, inhale hydrogen terminate.Close hydrogen gas valve.Gas in pipe is removed after heating hydrogen crushing furnace to 500 DEG C.After managing interior vacuum < 10Pa, be filled with argon gas and cool to 0.070Mpa.
After the broken pipe cooling of hydrogen, button press, opens discharging opening valve through pneumatic means.Then the magazine that mixture of powders is housed in pipe is pushed out to the mouth of pipe through propulsion cylinder, take out through mechanical arm clamping, magazine is clamped in upset after above spin vibration sieve charging aperture and pours in spin vibration sieve by mixture of powders in magazine by mechanical arm, remove through spin vibration sieve vibratory sieve, neodymium iron boron powder and the coat of metal are carried out physical separation.Neodymium iron boron powder to be collected in retracting device through the spin vibration sieve mouth of pipe and to be filled with nitrogen protection.The coat of metal after stripping, neodymium iron boron powder are respectively as shown in Fig. 1 b, 1c.
Embodiment 2
The waste and old sintered NdFeB circular ring of surface with nickel coating (is of a size of: external diameter is Φ 30mm, internal diameter Φ 10mm) (refer to Fig. 2 and a) carry out simple and mechanical interrupting, the waste and old magnet with fresh fracture to be loaded in tubular type hydrogen crushing furnace in magazine, then positive/negative-pressure leak detection is carried out to hydrogen crushing furnace.
Hunt leak qualified after, will be evacuated to pressure 0.63Pa in stove, heating hydrogen crushing furnace to 220 DEG C, and is incubated 45min.Then in the broken pipe of hydrogen, be filled with argon gas to 0.030MPa, after be filled with hydrogen, control intraductal pressure 0.085MPa.When hydrogen pressure drop≤0.03MPa/15min, inhale hydrogen terminate.Close hydrogen gas valve.Gas in pipe is removed after heating hydrogen crushing furnace to 520 DEG C.After managing interior vacuum < 10Pa, be filled with argon gas and cool to 0.070Mpa.
After the broken pipe cooling of hydrogen, button press, opens discharging opening valve through pneumatic means.Then the magazine that mixture of powders is housed in pipe is pushed out to the mouth of pipe through propulsion cylinder, take out through mechanical arm clamping, magazine is clamped in upset after above spin vibration sieve charging aperture and pours in spin vibration sieve by mixture of powders in magazine by mechanical arm, remove through spin vibration sieve vibratory sieve, neodymium iron boron powder and the coat of metal are carried out physical separation.Neodymium iron boron powder to be collected in retracting device through the spin vibration sieve mouth of pipe and to be filled with nitrogen protection.The coat of metal after stripping, neodymium iron boron powder are respectively as shown in Fig. 2 b, 2c.
Embodiment 3
The waste and old sintered NdFeB disk (be of a size of: Φ 30mm) of surface with nickel coating (is referred to Fig. 3 and a) carry out simple and mechanical interrupting, the waste and old magnet with fresh fracture to be loaded in tubular type hydrogen crushing furnace in magazine, then positive/negative-pressure leak detection is carried out to hydrogen crushing furnace.
Hunt leak qualified after, will be evacuated to pressure 0.8Pa in stove, heating hydrogen crushing furnace to 240 DEG C, and is incubated 50min.Then in the broken pipe of hydrogen, be filled with argon gas to 0.030MPa, after be filled with hydrogen, control intraductal pressure 0.090MPa.When hydrogen pressure drop≤0.03MPa/15min, inhale hydrogen terminate.Close hydrogen gas valve.Gas in pipe is removed after heating hydrogen crushing furnace to 550 DEG C.After managing interior vacuum < 10Pa, be filled with argon gas and cool to 0.070Mpa.
After the broken pipe cooling of hydrogen, button press, opens discharging opening valve through pneumatic means.Then the magazine that mixture of powders is housed in pipe is pushed out to the mouth of pipe through propulsion cylinder, take out through mechanical arm clamping, magazine is clamped in upset after above spin vibration sieve charging aperture and pours in spin vibration sieve by mixture of powders in magazine by mechanical arm, remove through spin vibration sieve vibratory sieve, neodymium iron boron powder and the coat of metal are carried out physical separation.Neodymium iron boron powder to be collected in retracting device through the spin vibration sieve mouth of pipe and to be filled with nitrogen protection.The coat of metal after stripping, neodymium iron boron powder are respectively as shown in Fig. 3 b, 3c.
Embodiment 4
The waste and old sintered NdFeB square (be of a size of: 60mm*26mm*2mm) of surface with nickel coating (is referred to Fig. 4 and a) carry out simple and mechanical interrupting, the waste and old magnet with fresh fracture to be loaded in tubular type hydrogen crushing furnace in magazine, then positive/negative-pressure leak detection is carried out to hydrogen crushing furnace.
Hunt leak qualified after, will be evacuated to pressure 0.95Pa in stove, heating hydrogen crushing furnace to 260 DEG C, and is incubated 60min.Then in the broken pipe of hydrogen, be filled with argon gas to 0.030MPa, after be filled with hydrogen, control intraductal pressure 0.098MPa.When hydrogen pressure drop≤0.03MPa/15min, inhale hydrogen terminate.Close hydrogen gas valve.Gas in pipe is removed after heating hydrogen crushing furnace to 580 DEG C.After managing interior vacuum < 10Pa, be filled with argon gas and cool to 0.070Mpa.
After the broken pipe cooling of hydrogen, button press, opens discharging opening valve through pneumatic means.Then the magazine that mixture of powders is housed in pipe is pushed out to the mouth of pipe through propulsion cylinder, take out through mechanical arm clamping, magazine is clamped in upset after above spin vibration sieve charging aperture and pours in spin vibration sieve by mixture of powders in magazine by mechanical arm, remove through spin vibration sieve vibratory sieve, neodymium iron boron powder and the coat of metal are carried out physical separation.Neodymium iron boron powder to be collected in retracting device through the spin vibration sieve mouth of pipe and to be filled with nitrogen protection.The coat of metal after stripping, neodymium iron boron powder are respectively as shown in Fig. 4 b, 4c.
Above content is only to design example of the present utility model and explanation; affiliated those skilled in the art make various amendment to described specific embodiment or supplement or adopt similar mode to substitute; only otherwise depart from the design of utility model or surmount this scope as defined in the claims, protection domain of the present utility model all should be belonged to.
Claims (5)
1. peel off the equipment of the waste and old surface of Nd-Fe-B permanent magnet coat of metal, it is characterized in that: comprise realize permanent magnet expose fresh fracture disintegrating apparatus, realize NdFeB Permanent Magnets principal phase inhale hydrogen be broken into graininess treatment step tubular type hydrogen crushing furnace, realize physical separation and obtain NdFeB magnetic powder and keep the separation equipment of complete coat of metal treatment step because not reacting and be connected the motion of tubular type hydrogen crushing furnace and separation equipment.
2. the equipment of the waste and old surface of Nd-Fe-B permanent magnet coat of metal of stripping according to claim 1, it is characterized in that: the inside of described tubular type hydrogen crushing furnace (1) has the broken pipe of hydrogen (2), there is in the broken pipe of hydrogen (2) magazine (3) placing permanent magnet, the magazine (3) that the two ends of the broken pipe of hydrogen (2) have for loading permanent magnet enters the broken pipe of hydrogen (2) inside, after inhaling hydrogen fragmentation, magazine (3) leaves entering of hydrogen broken pipe (2), outlet, the two ends of tubular type hydrogen crushing furnace (1) have the valve of band sealing ring, and control its opening and closing by pneumatic means.
3. the equipment of the waste and old surface of Nd-Fe-B permanent magnet coat of metal of stripping according to claim 2; it is characterized in that: described separation equipment is a spin vibration sieve (5) being placed in the broken pipe of hydrogen (2) port of export; the arrival end of described spin vibration sieve (5) is placed in the glove box (7) being filled with nitrogen, and glove box (7) side is connected with the discharge end of tubular type hydrogen crushing furnace (1) makes the Nd Fe B alloys powder that fragmentation is formed because inhaling hydrogen be in all the time under nitrogen protection.
4. the equipment of the waste and old surface of Nd-Fe-B permanent magnet coat of metal of stripping according to claim 3, it is characterized in that: described motion comprises the mechanical arm (6) be placed in glove box (7), the magazine (3) that the broken pipe of hydrogen (2) is left in mechanical arm (6) clamping moves to the top of spin vibration sieve (5) and material in box is poured onto in spin vibration sieve (5) by upset.
5. the equipment of the waste and old surface of Nd-Fe-B permanent magnet coat of metal of stripping according to claim 4, is characterized in that: described motion also comprises two propulsion cylinders (4) being placed in tubular type hydrogen crushing furnace (1) both sides, magazine (3) is moved at the broken pipe of hydrogen (2).