CN204508809U - By the device of sulfur gas reduction gypsum Sulphuric acid jointly producing cement grog - Google Patents
By the device of sulfur gas reduction gypsum Sulphuric acid jointly producing cement grog Download PDFInfo
- Publication number
- CN204508809U CN204508809U CN201520038836.0U CN201520038836U CN204508809U CN 204508809 U CN204508809 U CN 204508809U CN 201520038836 U CN201520038836 U CN 201520038836U CN 204508809 U CN204508809 U CN 204508809U
- Authority
- CN
- China
- Prior art keywords
- sulphur
- sulfur gas
- sulfur
- reduction
- gas
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
By a device for sulfur gas reduction gypsum Sulphuric acid jointly producing cement grog, comprise sulfur gas preparation facilities, multi-cyclone, reduction furnace, rotary calciner and chamotte cooler; Wherein sulfur gas preparation facilities comprises the sulfur melting groove be connected by pipeline order, thick sulphur transferpump, sulphur filter, smart sulphur groove, smart sulphur transferpump, atomizer, gasifier and Venturi transmission ejector, and Venturi transmission ejector is connected directly between the rear end of gasifier and is connected with reduction furnace by pipeline.The purity of the sulfur gas adopting device of the present utility model to prepare can remain on 95 ~ 100%, effectively controls the transformation efficiency of calcium sulfate in calcining kiln the highest, and calcining and decomposing controls convenient.And have that plant investment is low, energy consumption is low, level of automation advantages of higher.
Description
Technical field
The utility model relates to Chemical Manufacture, particularly relates to a kind of device by sulfur gas reduction gypsum Sulphuric acid jointly producing cement grog.
Background technology
Existing Chemical Manufacture and a large amount of technique waste residue gypsum of coal-fired flue gas desulfurization by-product, these gypsum offscums utilize on a small quantity and make building materials, cement setting retarder etc., all save as master with heap in a large number.In order to alleviate environmental stress, the recycling around gypsum is the direction that scientific worker makes great efforts for many years always.Decomposition gypsum Sulphuric acid by-product Portland clinker is the key subjects that gypsum resourceization utilizes.According to this technique, chemical industry produces by-product gypsum, and gypsum decomposes produces calcium oxide and sulfurous gas, Sulphur Dioxide again can Sulphuric acid, calcium oxide makes silicate further as cement clinker or other Chemicals, and recycle like this, gypsum obtains and utilizes completely.
The reduction of existing suitability for industrialized production gypsum mostly adopts coke or sulfur-bearing coal to be reductive agent, belongs to solid reductant, Gu reduction reaction is solid--reaction, and carbon reduzate is finally CO
2, be present in system and not only reduce system useful component SO
2volumetric molar concentration, also add the discharge of carbon, contaminate environment.
Have the technology of many bibliographical informations sulphur sulphate reducing, sulphur reduzate is SO
2, the product S O be reduced with vitriol
2superposition, can make SO in system gas phase product component
2volumetric molar concentration improve, to subsequent production optimization of process conditions, device capbility improves, energy consumption reduces, cost declines very favourable, and does not have carbon emission problem of environmental pollution.
Chinese patent application the method for calcium sulfate and sulfur cream sulfurous gas " a kind of by " (application number 201110334126.9), disclose a kind of method utilizing Molten sulphur reduction calcium sulfate to produce sulfurous gas, the cement slurry prepared is joined in multi-cyclone pre-heating system and carries out preheating, temperature of charge enters reduction furnace after being elevated to 600 ~ 950 DEG C, Molten sulphur is sprayed in reduction furnace, be 0.7 ~ 1.4 to control by Molten sulphur with entering cyclonic separator gypsum raw meal quality ratio, and control the volume ratio < 1.5% of oxygen in reduction furnace.Reduction furnace reaction production material together with gas by reduction furnace top out, gas-particle separation is carried out through minimum one cyclonic formula preheater, solid materials 0 ~ 90% recirculation enters reduction furnace, the material of 10 ~ 100% enters rotary kiln, enter the sulfurated lime of rotary kiln and unreacted mixture of calcium sulfate, the oxidizing atmosphere, the temperature that are 2 ~ 9% at carrier of oxygen volume concentrations are obtained by reacting SO under being the condition of 900 ~ 1450 DEG C
2and cement clinker.
This method provide sulphur reduction calcium sulfate and produce SO
2with the basic technology of cement clinker, but also there is following problem in the aspects such as the consumption of system device configuration, process control condition, sulphur, reduction and follow-up calcining and decomposing control:
(1) temperature is that the Molten sulphur of 120 ~ 160 DEG C is when adding reduction furnace, solid materials temperature decrease can be made, Molten sulphur is caused not gasify rapidly, and parcel phenomenon is produced to calcium sulphate solid material, cause being adhered between solid materials, thus have a strong impact on the suspension fluidization effect of solid materials, reduce the reduction efficiency of vitriol and the utilization ratio of sulphur reductive agent and speed of reaction.Therefore, in practice, almost cannot accomplish " speed of response is fast, completes reduction reaction in several seconds " described by the method.
(2) in the method, the add-on of control Molten sulphur is Molten sulphur is 0.7 ~ 1.4 with the mass ratio of the gypsum raw material entering cyclonic separator, if raw material are all calcium sulfate, the mol ratio being equivalent to calcium sulfate in sulphur and raw material is: 2.975 ~ 5.95:1.
The reaction of sulphur reduction decomposition gypsum is:
CaSO
4(S)+2S(g)＝CaS(S)+2SO
2(g)
CaS(S)+3CaSO
4(S)＝4CaO(S)+4SO
2(g)。
Net reaction is: 2CaSO
4(S)+S (g)=2CaO (S)+3SO
2(g).
From net reaction, decompose 1 mol sulfuric acid calcium and only need 0.5 mole of sulphur, so the add-on of sulphur is 6 ~ 12 times of theoretical value in the method.Sulphur reductive agent consumption is too large, and reductive agent cost is too high, uneconomical.
(3) control the volume ratio of oxygen in reduction furnace in the method and be less than 0.5%, the mol ratio of gaseous state sulphur and calcium sulfate is 2 ~ 4:1, temperature 750 ~ 1000 DEG C, controls sulfurated lime and unreacted calcium sulfate mol ratio 1:2 ~ 9:1.
First, in reduction furnace under temperature 750 ~ 1000 DEG C of conditions, when having sulfur gas to exist, aerobic can not be gone back and exist.Be greater than 250 DEG C, under aerobic environment in temperature, sulphur spontaneous combustion at once generates SO
2.Therefore, in reduction furnace, sulphur and oxygen can not coexist.
Secondly, the mol ratio adding calcium sulfate in reduction furnace Molten sulphur and raw material is 6 ~ 12:1, and requires that the mol ratio controlling reduction furnace gas sulphur and calcium sulfate is 2 ~ 4:1, and these two indexs are in fact all control sulphur amount, Con trolling index is contradiction, also cannot control to two values simultaneously.See by gas sulphur and calcium sulfate mol ratio, the reduction dosage added is high too.
In addition, sulfurated lime and unreacted calcium sulfate mol ratio 1:2 ~ 9:1 is controlled by Con trolling index, also namely reduction furnace generates sulfurated lime and unreacted calcium sulfate mol ratio in material is 0.5 ~ 9:1, show that the method controls the calcium sulfate reduction ratio 33 ~ 90% of reduction furnace, exceed too much with the reduction ratio 25 ~ 26% of actual needs, reductive agent consumption is large.
(4) in reduction furnace, sulfurated lime content is much higher, does not need to be recycled in reduction furnace, increases fluidization power consumption.
(5) discharged the material adding calcining kiln by reduction furnace too high because of Containing Sulfur ca proportion, can calcinating consumption be increased, reduce calcium sulfate rate of decomposition.
(6) in this utility model method, importing and exporting at the pipeline of reduction furnace Outlet Gas Temperature > 450 DEG C or tornado preheater adds containing oxygen warm air, the volume ratio controlling oxygen in pre-heating system is 2 ~ 13%, and excessive sulfur burning is become SO
2.The measure processing excessive sulphur with this is correct, but the volume ratio of oxygen controls 2 ~ 13% too high, corresponding fill into just large containing oxygen air capacity, SO in reduction furnace outlet gas phase must be reduced
2volumetric concentration, to subsequent sulphuric acid produce unfavorable.
(7) the carrier of oxygen volume concentrations in the rotary kiln described in the method controls 2 ~ 9%, and the combustion air amount namely adding calcination rotary kiln is large, and the gas volume of system is large, must affect SO in final gas phase
2concentration, affects subsequent sulphuric acid and produces.Secondly, under so high oxygen concn atmosphere, sulfurated lime can produce calcium oxide with oxygen reaction, have impact on sulfurated lime and calcium sulfate reacts, and reduces the rate of decomposition of calcium sulfate.
Application number be 200910216325.2 Chinese patent application disclose " a kind of method of sulphur reducing and decomposing phosphogypsum ", phosphogypsum is put into reactor also in an inert atmosphere, be warming up to 500 ~ 900 DEG C of preheatings 10 ~ 30 minutes, then by mole fraction be 10 ~ 50% gas sulphur and phosphogypsum carry out reduction reaction after 1 ~ 2 hour, by gained sulfurated lime material block grind after again with phosphogypsum in molar ratio 1 ~ 1.5:3 mix, in non-oxidizing atmosphere, 1000 ~ 1400 DEG C of roastings 0.5 ~ 3 hour, in the solid slag of gained, calcium oxide is used for manufacture of cement as cement clinker, the tail gas SO produced
2as the unstripped gas producing sulfuric acid.
Disclose the certain operations Con trolling index that phosphogypsum first carries out sulphur reduction reaction decomposing phosphogypsum before roasting in aforesaid method, but all there is the problems such as operation runs difficulty, energy consumption is high, exploitativeness is poor in real industrialization used:
(1) reductive agent adopts gas sulphur, but not about how to obtain and produce gaseous state sulphur, and gas sulphur is difficult to metering, the reduction reaction operation of phosphogypsum controls difficulty.
(2), under inert atmosphere, passing into mole fraction is that 10 ~ 50% sulfur gas and phosphogypsum carry out reduction reaction 1 ~ 2 hour, long reaction time; The gas-solid reduction of sulfur gas and phosphogypsum can complete in fact a few second.And before the grinding of sulfurated lime material block in process of cooling, unreacted unnecessary sulfury is known from experience condensation and is entered in sulfurated lime product, there is spontaneous combustion or hidden peril of explosion in process of lapping.
(3) reduce before being mixed into roasting with phosphogypsum again after sulfurated lime cooling grinding in solid product, must preheating again, both increased grinding power consumption, increase again pre-thermal energy consumption, system energy consumption is high.
(4) there is unnecessary gas sulphur in reduction reactor gas phase, bring subsequent sulphuric acid production system into and can produce sulphur and solidify, occluding device pipeline, cleaning difficulty.
Application number be 201310063173.3 Chinese patent application disclose that " a kind of sulphur reduction decomposition vitriol produces SO
2method ".The method to be that forerunner's reactant by vitriol puts into reactor, and do not participating under reaction atmosphere, in 100 ~ 900 DEG C of preheatings 20 ~ 90 minutes, then be the gaseous state sulphur of 20 ~ 80% by mole fraction, temperature 500 ~ 900 DEG C reaction 0.5 ~ 4 hour, obtain massive sulphide and SO
2tail gas; After above-mentioned sulfurated lime material block is ground to 1 ~ 1000 μm, then mix 1:1 ~ 3 in molar ratio with vitriol, in non-oxidizing atmosphere, 600 ~ 1400 DEG C reaction 0.5 ~ 5 hour, obtain solid slag metal oxide and SO
2tail gas.
Disclose vitriol in aforesaid method before pyroreaction, first carry out the certain operations Con trolling index that sulphur reduction reaction decomposition vitriol obtains sulfide, but there is problems such as operating operation difficulty, energy consumption is high, exploitativeness is poor equally in real industrialization is used:
(1) reductive agent adopts gas sulphur, but not about how to obtain and produce gaseous state sulphur, and gas sulphur is difficult to metering, the reduction reaction operation of phosphogypsum controls difficulty.
(2), under inert atmosphere, passing into mole fraction is that 20 ~ 80% sulfur gas and phosphogypsum carry out reduction reaction 0.5 ~ 4 hour, long reaction time.And before the grinding of sulfuration material block in process of cooling, unreacted unnecessary sulfury is known from experience condensation and is entered in sulphide products, there is nature or hidden peril of explosion in process of lapping.
(3) reduce before being mixed into pyroreaction with vitriol again after solid product medium sulphide content cooling grinding, must preheating again, both increased grinding power consumption, increase again pre-thermal energy consumption, system energy consumption is high.
(4) there is unnecessary gas sulphur in reduction reactor gas phase, bring subsequent sulphuric acid production system into and can produce sulphur and solidify, occluding device pipeline, cleaning difficulty.
Application number be 201410089746.4 patent application " the spouted fluidized decomposition technique of a kind of gypsum " disclose the spouted fluidized decomposing and calcining process for preparing sulfuric acid of a kind of gypsum, adopt gypsum calcination containing SO
2stack gas indirect heating Molten sulphur sulfur gas, the SO after cooling
2stack gas is again through secondary preheating material gypsum raw material, and the gypsum after preheating prepares sulfurated lime by spouted fluidized decomposing gypsum; Spouted fluidized employing extra fuel hotblast stove is gypsum reduction reaction heat supply, and sulfur gas mixes laggard spouted fluidized stove with hot furnace gas, and tail gas merges with gypsum calcination stack gas and goes Sulphuric acid operation after dedusting.But there are the following problems for the method:
(1) lack the refining step of Molten sulphur, the usual impure height of Molten sulphur, easily cause pipeline and heat-exchange equipment fouling, blocking.
(2) Molten sulphur is gasified by high temperature sulfur-bearing stack gas indirect heating in interchanger, and because of heat transfer tube line length, during system shutdown, Molten sulphur is difficult to thorough emptying, meeting frozen plug pipeline, and cannot remove, and system is difficult to long period continuous and steady operation.
(3) gasifier material rate is high, and manufacture requirements is high, and cost is high: sulphur gasifier is arranged on gypsum calcination kiln exhaust gas relief outlet, and this place contains SO
2effluent gas temperature is up to 900 ~ 1100 DEG C, and therefore gasifier tube side and shell side material all need high temperature resistant, sulfur corrosion resistant, and gasifier is equivalent to a heat exchanger structure, and device structure is more complicated, and difficulty of processing is large.
(4) sulphur vapourizing furnace is arranged in the technique after rotary kiln stack gas by employing, have impact on the heat integration of gypsum calcination stack gas, gypsum reduction is made to need to increase heating fuel system in addition, additionally need increase blower fan, increase power consumption, totally add system energy consumption, belong to uneconomic combination process.
(5) in fluidized-bed tail gas containing remaining sulfur gas, bring subsequent sulphuric acid production system into and can produce sulphur and solidify, occluding device pipeline, cleaning difficulty.
(6) furnace gas SO
2concentration is low, and system investments is high: the hot furnace gas adopting other fuel hot air stove to produce mixes as spouted fluidized power and reducing gas with sulfur gas, adds total tolerance of gypsum calcination and gypsum reduction, makes SO in whole system furnace gas
2concentration reduces, and subsequent sulphuric acid production system equipment capacity reduces, and transformation efficiency declines, and affects transition heat balance.
Utility model content
The purpose of this utility model, exactly in order to solve the problem, provides a kind of device by sulfur gas reduction gypsum Sulphuric acid jointly producing cement grog.
In order to achieve the above object, the utility model have employed following technical scheme: a kind of device being reduced gypsum Sulphuric acid jointly producing cement grog by sulfur gas, comprises sulfur gas preparation facilities, primary cyclone, secondary cyclone, three-stage cyclone separator, tetra-cyclone, five-stage whirlwind separator, reduction furnace, rotary calciner and chamotte cooler; Wherein sulfur gas preparation facilities is connected to reduction furnace with reduction furnace provides sulfur gas; Described sulfur gas preparation facilities comprises the sulfur melting groove be connected by pipeline order, thick sulphur transferpump, sulphur filter, smart sulphur groove, smart sulphur transferpump, atomizer, gasifier and Venturi transmission ejector; Wherein atomizer is connected directly between the front end of gasifier, and Venturi transmission ejector is connected directly between the rear end of gasifier and is connected with reduction furnace by pipeline.
Steam heater and agitator are set in described sulfur melting groove, and are provided with sulphur import.
Described sulphur filter is diatomite medium filter, metal film filter or non-metallic film strainer.
Described gasifier comprises the evaporation vaporizer of order setting and crosses hot cell, and evaporation vaporizer and overheated indoor are separately installed with independently electric heater unit.
The heating unit of described electric heater unit is carbon fiber-quartz electric heating tube, and suspension is arranged on gasifier inner chamber.
The utility model, owing to have employed above technical scheme, makes it compared with prior art, has following characteristics:
1, Molten sulphur enters gasifier after refining after filtration, avoids the fouling and clogging to pipeline and shower nozzle, ensures smooth long term running.
2, the purity of sulfur gas component can remain on 95 ~ 100%, because sulphur gasification is quick and thorough, therefore, the amount of namely having reacted gas sulphur is measured by Molten sulphur, enter the Molten sulphur amount of sulphur gasifier and gypsum raw material amount to be easy to realize proportion adjustment and to control, as long as control reduction furnace temperature, namely controlled the reduction efficiency of reduction furnace by the add-on of finely tuning sulfur gas, reduction furnace operation controls simple and convenient.
3, sulfur gas is mixed with rotary kiln exhaust gas add bottom reduction furnace, 25 ~ 27% gypsum are made to carry out fluidization gas-solid reaction in reduction furnace by the add-on controlling sulfur gas, speed of response is fast, reduction reaction can complete in 5 ~ 20 seconds, reduction reaction temperature can reduce to 850 ~ 950 DEG C, there is larger decline than traditional rotary kiln interior reaction temperature 1100 ~ 1300 DEG C, reduce reduction reaction energy consumption, shorten the reaction times.
4, adopt highly purified sulfur gas as the reducing gas of solid gypsum material in reduction furnace, utilize rotary kiln exhaust gas as the solids fluidized power of reduction furnace, the heat of high temperature kiln tail gas is utilized to maintain reduction process temperature, do not need extra fuel hot blast to supplement heat energy, efficiently solve the thermal equilibrium of system; As long as control kiln exhaust gas temperature by adjust fuel amount can control whole system temperature, temperature operation controls convenient.
5, plant investment is low, energy consumption is low, level of automation is high.
Accompanying drawing explanation
Fig. 1 is the structural representation of the utility model by the device of sulfur gas reduction gypsum Sulphuric acid jointly producing cement grog;
Fig. 2 is the structural representation of the sulfur gas preparation facilities in the utility model.
Embodiment
Fig. 1 is the structural representation of the utility model by the device of sulfur gas reduction gypsum Sulphuric acid jointly producing cement grog, shown in figure: 1, sulfur gas preparation facilities; 2, primary cyclone; 3, secondary cyclone; 4, three-stage cyclone separator; 5, tetra-cyclone; 6, five-stage whirlwind separator; 7, reduction furnace; 8, rotary calciner; 9, chamotte cooler.
See Fig. 2, sulfur gas preparation facilities in the utility model comprises the sulfur melting groove 11 be connected by pipeline order, thick sulphur transferpump 12, sulphur filter 13, smart sulphur groove 14, smart sulphur transferpump 15, atomizer 16, gasifier 17 and Venturi transmission ejector 18, wherein atomizer 16 is connected directly between the front end of gasifier 17, and Venturi transmission ejector 18 is connected directly between the rear end of gasifier 17.
Sulphur filter in the utility model is diatomite medium filter, metal film filter or non-metallic film strainer.
Steam heater 111 and agitator 112 are set in sulfur melting groove 11, and are provided with sulphur import 113.
Gasifier 17 in the utility model comprises the evaporation vaporizer 171 of order setting and crosses hot cell 172, and evaporation vaporizer and overheated indoor are separately installed with independently electric heater unit 173,174.
Gasifier 17 shell in the utility model adopts carbon steel to make, liner composite insulating brick, and electric heater unit hangs and is arranged on gasifier inner chamber, and its heating unit is carbon fiber-quartz electric heating tube.
The technological process of the sulfur gas preparation facilities in the utility model is as follows:
Solid or Molten sulphur are added sulfur melting groove 11, under the heat effect of steam heater 111, when heating temperatures is to when being greater than 103 DEG C, solid melting becomes liquid, along with temperature is increased to more than 140 DEG C further, the mobility of Molten sulphur reaches optimum regime, send into sulphur filter 13 through thick sulphur transferpump 12 to filter, remove the solid impurity in sulphur, obtain refining Molten sulphur and send into smart sulphur groove 14 buffer storage, steam heating keeps smart sulphur groove temperature at 140 ~ 150 DEG C, the atomizer 16 being arranged on gasifier feed end is delivered to again by smart sulphur transferpump 15.
Gasifier 17 adopts carbon fiber-quartz electric heating tube to heat, and controls internal temperature at 450 ~ 800 DEG C.Under this temperature environment, first the Molten sulphur droplet sprayed by atomizer 16 is electrically heated that device 173 heats and rapid temperature increases to 450 ~ 550 DEG C become sulfur gas at evaporation vaporizer 171, be electrically heated device 174 and be heated to 550 ~ 800 DEG C further crossing hot cell 172 again, then by the Venturi transmission ejector 18 being connected to gasifier tail end, gas velocity is promoted to 20 ~ 30m/s and send follow-up system to use as reductive agent.
Embodiment
As shown in Figure 1, desulfurated plaster (containing free-water 8 ~ 15%) is added rotary dryer and drying and dewatering process is carried out in heat smoke heat exchange, remove free-water wherein and partial crystallization water, produce semi-hydrated gypsum.Gypsum after dehydration adds pyrite slag, flyash, bauxitic clay, be made into cement slurry by three ratio and send into feed bin by lift, raw material send into the import of one to tetra-cyclone 2,3,4,5 after metering successively, with from calcination rotary kiln 8 and reduction furnace 7 containing SO
2gas carries out the heat exchange of gas-solid counter current contact formula, and solid raw material are from up to down through 4 heat exchange, and material temperature rises to 600 ~ 800 DEG C, enter reduction furnace 7.By the overheated sulfur gas of sulfur gas preparation facilities 1, temperature is 550 ~ 800 DEG C, sends into bottom reduction furnace 7 through Venturi transmission ejector 18; Also sent into bottom reduction furnace 7 in the lump by the high-temperature tail gas (900 ~ 1100 DEG C) of rotary calciner 8 simultaneously, make cement slurry in reduction furnace be tending towards fluidization suspended state.At this, there is rapidly gas-solid reduction reaction in the calcium sulfate in sulfur gas and raw material, generates sulfurated lime and SO
2gas.
Control reduction furnace top exit temperature 800 ~ 850 DEG C, by regulating the Molten sulphur amount entering sulfur gas preparation facilities 1, the mol ratio controlling calcium sulfate in sulfur gas and raw material is 0.5 ~ 0.55:1, and the mol ratio using sulfurated lime and unreacted calcium sulfate in reducer material controls 25 ~ 26%.
The gas-solid mixture that reduction furnace top is discharged carries out gas solid separation through five-stage whirlwind separator, gas continues upwards to carry out heat exchange through tetra-cyclone-three-stage cyclone separator-secondary cyclone-primary cyclone and raw material, supplement appropriate warm air at the gas exit line of five-stage whirlwind separator, make sulfur gas burning remaining in gas phase generate SO completely
2as long as the volumetric concentration of oxygen remains on 1.5 ~ 2% in detection control primary cyclone exit gas, can make in primary cyclone exit gas no longer containing sulfur gas.Primary cyclone exit gas is containing SO
2volumetric concentration, 15 ~ 25%, sends into follow-up system for preparing sulfuric acid through further dedusting, purification.
Rotary calciner 8 is sent into by discharge elephant trunk by the isolated solid materials of five-stage whirlwind separator 6, continue to be heated to 1200 ~ 1450 DEG C with high-temperature kiln gas in kiln, and in kiln, in temperature rise process, there is the decomposition reaction of sulfurated lime and calcium sulfate, generate solid oxidation calcium and SO
2gas, when kiln temperature reach ~ 1450 DEG C, other solid materialss in calcium oxide and raw material form Portland clinker through high-temperature calcination in the lump again, discharged enter chamotte cooler 9 by kiln hood.
Rotary kiln rear gas temperature is controlled at 900 ~ 1000 DEG C, by checking that the volumetric concentration controlling oxygen in kiln exhaust gas body remains on 1 ~ 2% and carrys out the combustion air amount that regulable control adds kiln hood by the fuel quantity controlling to add rotary calciner 8.
Be all complete in rotary kiln with the reduction of coke raw material, decomposition, calcining in traditional technology, in kiln, easily because of the change of various condition, reducing atmosphere or oxidizing atmosphere occur, it is large that operation controls difficulty, not easily realizes the Automated condtrol that conventional cement is produced.And aforesaid operations adopts the two-step approach production technique of gypsum decomposing and calcining in the outer partial reduction of kiln, kiln, as long as allow bunker coal energy Thorough combustion, kiln tail oxygen level is less than 2% as far as possible, then can solve the problem that in conventional gypsum acid-making process, operation easier is large preferably, also can solve the Automated condtrol burnt till simultaneously.In addition, because the reduction of calcium sulfate completes outside kiln, the continuation that only assume responsibility for calcium sulfate in kiln is decomposed and calcining, shorten the residence time of material in kiln, so the length of rotary kiln also can shorten accordingly, both the heat lost by radiation of cylindrical shell had been decreased, also the corresponding throughput that improve system.
Claims (5)
1., by a device for sulfur gas reduction gypsum Sulphuric acid jointly producing cement grog, comprise sulfur gas preparation facilities, primary cyclone, secondary cyclone, three-stage cyclone separator, tetra-cyclone, five-stage whirlwind separator, reduction furnace, rotary calciner and chamotte cooler; Wherein sulfur gas preparation facilities is connected to reduction furnace with reduction furnace provides sulfur gas; It is characterized in that: described sulfur gas preparation facilities comprises the sulfur melting groove be connected by pipeline order, thick sulphur transferpump, sulphur filter, smart sulphur groove, smart sulphur transferpump, atomizer, gasifier and Venturi transmission ejector; Wherein atomizer is connected directly between the front end of gasifier, and Venturi transmission ejector is connected directly between the rear end of gasifier and is connected with reduction furnace by pipeline.
2., as claimed in claim 1 by the device of sulfur gas reduction gypsum Sulphuric acid jointly producing cement grog, it is characterized in that, steam heater and agitator are set in described sulfur melting groove, and be provided with sulphur import.
3., as claimed in claim 1 by the device of sulfur gas reduction gypsum Sulphuric acid jointly producing cement grog, it is characterized in that, described sulphur filter is diatomite medium filter, metal film filter or non-metallic film strainer.
4. as claimed in claim 1 by the device of sulfur gas reduction gypsum Sulphuric acid jointly producing cement grog, it is characterized in that: described gasifier comprises the evaporation vaporizer of order setting and crosses hot cell, and evaporation vaporizer and overheated indoor are separately installed with independently electric heater unit.
5., as claimed in claim 4 by the device of sulfur gas reduction gypsum Sulphuric acid jointly producing cement grog, it is characterized in that: the heating unit of described electric heater unit is carbon fiber-quartz electric heating tube, and suspension is arranged on gasifier inner chamber.