CN204343136U - People's Bank of China's Anti-skid adhesive piece - Google Patents
People's Bank of China's Anti-skid adhesive piece Download PDFInfo
- Publication number
- CN204343136U CN204343136U CN201320890636.9U CN201320890636U CN204343136U CN 204343136 U CN204343136 U CN 204343136U CN 201320890636 U CN201320890636 U CN 201320890636U CN 204343136 U CN204343136 U CN 204343136U
- Authority
- CN
- China
- Prior art keywords
- skid
- bank
- people
- china
- resistant course
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Abstract
The utility model belongs to anti-slip technology field, be specifically related to a kind of People's Bank of China Anti-skid adhesive piece, it is characterized in that described People's Bank of China Anti-skid adhesive piece at least comprises double-layer structure: skid resistant course and adhesion layer, described skid resistant course soffit fits tightly with described adhesion layer upper surface and is connected, described skid resistant course upper surface is non skid matting, described adhesion layer soffit is adhesive surface, and described skid resistant course is made up of PET grain crystalline substance and water-based glue mixing.The utility model has the advantages that, People's Bank of China's Anti-skid adhesive piece structure is simple, easy to use, attractive in appearance beautiful, applied range; In addition, the raw material of its skid resistant course obtains simple, and cost is lower, has excellent skid resistance, weatherability, abrasion resistance, water resistance, alkali resistance and tack, and skid resistant course proportion less, there is certain elasticity and pliability.
Description
Technical field
The utility model belongs to anti-slip technology field, is specifically related to a kind of People's Bank of China Anti-skid adhesive piece.
Background technology
In the mode of anti-skidding process, comparatively conventional is brushing anti-slip material, lays slipmat or anti-slip carpet at present.
Brushing anti-slip material is more effective slip-proof way, can be used in various surface state, also can give body surface different colors, play beautify, decoration function.Anti-slip material is a kind of functional material, its effect is the frictional property improving body surface, form a kind of non slip surface of great friction coefficient, the frictional force of increment surface, to reduce the sliding of the personnel of body surface, vehicle and other objects, reduction personnel slip the generation of tumble injury accident, are used for mill floor, parking lot, pedestrian overcrossing, ship deck and packaging industry.Its shortcoming is, is not suitable for direct brushing, and there is noxious material in anti-slip material for ground such as existing floor, floor tiles, and after brushing, indoor need unlimited certain hour to ventilate, and are not suitable for common residential settings.
Laying slipmat or anti-slip carpet is comparatively convenient and efficient way, but its scope of application is comparatively limited to, more be used in the less homestead of visitors flowrate or office block, when being used in the larger public place of visitors flowrate, more easily there is sliding phenomenon in slipmat or anti-slip carpet, and collect a large amount of dust after being trampled in a large number, clean constant; In addition, laying slipmat or anti-slip carpet belong to provisional anti-skidding processing mode, cannot combine together, be repugnant to the eye, non-long-term plan with the style on existing ground.
Obviously, all there is its respective limitation in slip-proof way known today, extensively cannot adopt for masses.
Summary of the invention
The purpose of this utility model is according to above-mentioned the deficiencies in the prior art part, provides a kind of People's Bank of China Anti-skid adhesive piece, this People's Bank of China's Anti-skid adhesive piece by arranging skid resistant course on adhesion layer, to form the outstanding and People's Bank of China's Anti-skid adhesive piece of applied range of non-skid property.
The utility model object realizes being completed by following technical scheme:
A kind of People's Bank of China Anti-skid adhesive piece, it is characterized in that described People's Bank of China Anti-skid adhesive piece at least comprises double-layer structure: skid resistant course and adhesion layer, described skid resistant course soffit fits tightly with described adhesion layer upper surface and is connected, described skid resistant course upper surface is non skid matting, described adhesion layer soffit is adhesive surface, and described skid resistant course is made up of PET grain crystalline substance and water-based glue mixing.
Described adhesion layer soffit and a diaphragm fit tightly.
Described PET grain crystalline substance is coated with aluminium film to form diamante.
Described PET grain crystalline substance is hexagon cylinder, square column, rectangle cylinder or any polygonal cylinder.
The cylinder thickness of described PET grain crystalline substance is 0.01mm ~ 0.3mm, and the cylinder width of described PET grain crystalline substance is 0.1mm ~ 0.85mm.
The utility model has the advantages that, People's Bank of China's Anti-skid adhesive piece structure is simple, easy to use, attractive in appearance beautiful, applied range; In addition, the raw material of its skid resistant course obtains simple, and cost is lower, has excellent skid resistance, weatherability, abrasion resistance, water resistance, alkali resistance and tack, and skid resistant course proportion less, there is certain elasticity and pliability.
Accompanying drawing explanation
Fig. 1 is the structural representation of People's Bank of China's Anti-skid adhesive piece in the utility model.
Detailed description of the invention
Feature of the present utility model and other correlated characteristic are described in further detail by embodiment below in conjunction with accompanying drawing, so that the understanding of technician of the same trade:
Be respectively as marked 1-4 in Fig. 1, figure: skid resistant course 1, adhesion layer 2, cementing agent 3, diaphragm 4.
As shown in Figure 1; the utility model is specifically related to a kind of People's Bank of China Anti-skid adhesive piece; this People's Bank of China's Anti-skid adhesive piece is made up of skid resistant course 1, adhesion layer 2, cementing agent 3 and diaphragm 4 from top to bottom successively; the two sides of adhesion layer 2 is rough surface; to increase its adhesion property; skid resistant course 1 is formed after the upper surface volatilization by the anti-slip material in solid-liquid mixing being painted on adhesion layer 2 is done; cementing agent 3 is then that the soffit by binder material being painted on adhesion layer 2 is formed, and forms isolated protection to guarantee its viscosity by diaphragm 4 to it.
The base material of adhesion layer 2 is chosen not unique, and can select according to actual conditions, usual adhesion layer 2 can select the base materials such as film, rubber, plastics, plank to form, and in the utility model, adhesion layer 2 selects flexible film substrates to form.
Skid resistant course 1 formed by brushing anti-slip material on adhesion layer 2, anti-slip material is specifically made up of diamante and water-based glue mixing, the mass percent that wherein diamante accounts for anti-slip material should be not more than 35%, preferred value is 35%, the mass percent that water-based glue accounts for anti-slip material should be not less than 65% accordingly, and preferred value is 65%.
Diamante in anti-slip material is the PET grain crystalline substance that surface is coated with aluminium film, and wherein the brilliant mass percent accounting for diamante of PET grain is not less than 95%, and the mass percent that aluminium film accounts for diamante is not more than 5% accordingly.The external form of PET grain crystalline substance can be hexagon cylinder, square column, rectangle cylinder or any polygonal cylinder, the respective thickness of grain crystal column body is 0.01mm ~ 0.3mm, the width of grain crystal column body is 0.1mm ~ 0.85mm, and small particle diameter and PET grain crystalline substance in polygonal cylinder can promote uniformity and the skid resistance on anti-slip material surface.
What the water-based glue in anti-slip material specifically adopted is polyvinyl acetate emulsion, nuisance quality contained in it is extremely low, meet the regulation of GB18583-2001 " in indoor decorating and refurnishing materials bonding adhesive limits of harmful substances ", therefore the application scenario of anti-slip material (People's Bank of China's Anti-skid adhesive piece) can be widened greatly, shown in the testing result table specific as follows of hazardous substances:
| Interventions Requested title and unit | Technical requirements | Assay | Unidirectional judgement |
| Free formaldehyde: g/kg | ≤1 | ＜0.05 | Meet |
| Benzene: g/kg | ≤0.2 | ＜0.02 | Meet |
| Toluene+dimethylbenzene: g/kg | ≤10 | ＜0.02 | Meet |
| Total volatile organism: g/L | ≤50 | 22 | Meet |
The preparation method of this anti-slip material specifically comprises the following steps:
1. select in membranaceous PET material, carry out vacuum aluminum-coated to its surface, by resin and pigment, PET material is painted afterwards, after waiting to paint, crushing operation is carried out to PET material, the PET material making to be coated with aluminium film is pulverized as particle diameter is the grain crystalline substance of 0.1mm ~ 0.85mm, to form diamante;
2. after treating that diamante making is complete, choose water-based glue (i.e. polyvinyl acetate emulsion), diamante is undertaken mixing and mixing well by the mass ratio of 35:65 with water-based glue, the final anti-slip material obtaining solid-liquid mixing shape.
Every inspect on colligated-function result of this anti-slip material is as shown in the table:
| Test item title | Unit | Technical requirements | Assay | Unidirectional judgement | Method of testing |
| Condition in container | / | Should, without caking, skinning, be easy to stir evenly | Meet | Qualified | JT/T280-2004 6.3.1 |
| Viscosity | KU | ≥70 | 73 | Qualified | GB/T9269-2009 |
| Workability | / | Air or airless spraying (or blade coating) workability good | Meet | Qualified | JT/T280-2004 6.3.4 |
| Paint film appearance | / | Answer the phenomenons such as acomia wrinkle, general flower, foaming, cracking, stickup, film color and outward appearance should be little with model difference | Meet | Qualified | JT/T280-2004 6.3.6 |
| Drying time (volatilization is dry) | min | ≤15 | 15 | Qualified | JT/T280-2004 6.3.7 |
| Hiding rare | % | ≥95 | 95 | Qualified | JT/T280-2004 6.3.8 |
| Chroma characteristic (45/0) | / | The scope that the chromaticity coordinate of coating and luminance factor should conform with the regulations | Meet | Qualified | JT/T280-2004 6.3.9 |
| Abrasion resistance (200 turns/1000g) | mg | ≤ 40(JM-100 elastic grinding wheel) | 40 | Qualified | JT/T280-2004 6.3.10 |
| Water resistance | / | In water, soak 24h should phenomenon without exception | Meet | Qualified | JT/T280-2004 6.3.11 |
| Alkali resistance | / | Soaking in calcium hydroxide saturated solution 24 hours should phenomenon without exception | Meet | Qualified | JT/T280-2004 6.3.12 |
| Freeze-thaw stability | / | Place 18h under-5 DEG C ± 2 DEG C conditions after, placing 6h under being placed in 23 DEG C ± 2 DEG C conditions is immediately one-period, 3 all after dates, should, without caking, skinning, be easy to stir | Meet | Qualified | JT/T280-2004 6.3.16 |
| Early stage water resistance | / | Temperature be 23 DEG C ± 2 DEG C, under humidity is the condition of 90% ± 3%, the time of doing solid work≤120min | Meet | Qualified | JT/T280-2004 6.3.17 |
| Tack (drawing circle method) | Level | ≤5 | 3 | Qualified | JT/T280-2004 6.3.13 |
As shown in Figure 1, the preparation method of this People's Bank of China Anti-skid adhesive piece comprises the steps: first at the above-mentioned anti-slip material of upper surface brushing of adhesion layer 2, leaves standstill and after its volatilization is dry, forms skid resistant course 1 in about 15 minutes; Afterwards at soffit brushing one layer binder of adhesion layer 2, to form cementing agent 3; Volatilize for preventing cementing agent 3 and dryly lose viscosity, cover layer protecting film 4 thereon, form People's Bank of China's Anti-skid adhesive piece.
The beneficial effect of this People's Bank of China Anti-skid adhesive piece is:
A. the structure of People's Bank of China's Anti-skid adhesive piece is simple, and cost is lower, and cost is about 15 yuan/square metre, and easy to use, tears diaphragm off and can post use;
B. the skid resistant course raw material on People's Bank of China's Anti-skid adhesive piece, i.e. diamante and water-based glue, obtain simple, cost is lower, can manufacture production in enormous quantities;
C. the skid resistant course surface of People's Bank of China's Anti-skid adhesive piece has excellent skid resistance, weatherability, abrasion resistance, water resistance, alkali resistance and tack;
D. the skid resistant course proportion of People's Bank of China's Anti-skid adhesive piece is less, and namely the proportion of PET material is only 1.35, and it has certain elasticity, though therefore human body fall down thereon also can not be injured or feel pain;
The skid resistant course of e. People's Bank of China's Anti-skid adhesive piece is coated with aluminium matter, attractive in appearance beautiful;
F. People's Bank of China's Anti-skid adhesive piece applied range, namely pastes i.e. use, is applicable to large-scale promotion application.
Embodiment one: as shown in Figure 1, the present embodiment relates to a kind of application process of above-mentioned People's Bank of China Anti-skid adhesive piece, that is: the diaphragm 4 of People's Bank of China's Anti-skid adhesive piece is torn off, adhered on bathroom, swimming hall, bus doorway, access, hotel lobby etc. needs the ground of carrying out anti-skidding process, earth's surface is cleaned out before posting, to form beautiful non-slip floor attractive in appearance fast, due to the non-skid property of skid resistant course, anti-wear performance is outstanding, in addition PET material proportion is less, there is certain elasticity, therefore anti-skidding ground surface can effectively prevent from falling down, also can not feels pain even if fall down, and application life is extremely long.
Embodiment two: as shown in Figure 1, the present embodiment relates to a kind of application process of above-mentioned People's Bank of China Anti-skid adhesive piece, because the harmful substance contents of water-based glue in skid resistant course and diamante is extremely low, therefore above-mentioned People's Bank of China Anti-skid adhesive piece can be adhered on external surface or the inner surface of construction wall as wallpaper.
When using as interior wall wallpaper, owing to PET grain crystalline substance being coated with aluminium matter in Anti-skid adhesive piece, therefore decoration wallpaper can be it can be used as, attractive in appearance beautiful, and PET grain crystal grain footpath is less, the smooth exquisiteness of the surface of wall that its skid resistant course is formed and planeness is higher.If when it can be used as exterior wall wallpaper to use, due to PET grain crystalline substance being coated with aluminium matter, can the sunlight of reflected illumination on body of wall, play heat insulation effect.Comprehensive, when being used as body of wall wallpaper by People's Bank of China's Anti-skid adhesive piece, have cheap, adhesion property is good, and the life-span is long, attractive in appearance beautiful, the advantage that effect of heat insulation is outstanding, is applicable to large-scale promotion application.
Embodiment three: as shown in Figure 1; the present embodiment relates to a kind of application process of above-mentioned People's Bank of China Anti-skid adhesive piece; that is: the diaphragm 4 of above-mentioned People's Bank of China Anti-skid adhesive piece is torn off; for guaranteeing sticking effect; clean out ground; the ground being adhered on sport and body-building place afterwards uses as athletic floor; not only cost is extremely low; and People's Bank of China's Anti-skid adhesive piece has excellent pliability, elasticity and non-skid property; be convenient to human body and carry out body-building thereon; also not having pain even if fall down, is excellent athletic floor.
Embodiment four: as shown in Figure 1; the present embodiment relates to a kind of application process of above-mentioned People's Bank of China Anti-skid adhesive piece; that is: the diaphragm 4 of above-mentioned People's Bank of China Anti-skid adhesive piece is torn off; for guaranteeing sticking effect; clean out ground; adhered on afterwards on road to form non-slip floor tag line; relative to traditional land marking line brushing operation; normal operating conditions can be entered after this non-slip floor tag line posts; without the need to the fence isolation curing time after the tag line brushing of traditional ground, the impact that road traffic is caused can be avoided completely.Carry out " portable pendulum tester measures the test of pavement skid resistance value " this non-slip floor tag line, recording its antiskid value is 55, and unit is BPN; In addition, diamante color in this non-slip floor tag line is eye-catching, can cause the attention of driver and passerby the very first time, and this non-slip floor tag line has excellent skid resistance, weatherability, abrasion resistance, water resistance, alkali resistance and tack, therefore application life is extremely long.
Claims (4)
1. People's Bank of China's Anti-skid adhesive piece, it is characterized in that described People's Bank of China Anti-skid adhesive piece at least comprises double-layer structure: skid resistant course and adhesion layer, described skid resistant course soffit fits tightly with described adhesion layer upper surface and is connected, described skid resistant course upper surface is non skid matting, described adhesion layer soffit is adhesive surface, it is brilliant that described skid resistant course comprises PET grain, and described PET grain crystalline substance is in any polygonal cylinder.
2. a kind of People's Bank of China according to claim 1 Anti-skid adhesive piece, is characterized in that described adhesion layer soffit and a diaphragm fit tightly.
3. a kind of People's Bank of China according to claim 1 Anti-skid adhesive piece, is characterized in that described PET grain crystalline substance is coated with aluminium film to form diamante.
4. a kind of People's Bank of China according to claim 1 Anti-skid adhesive piece, it is characterized in that the cylinder thickness of described PET grain crystalline substance is 0.01mm ~ 0.3mm, the cylinder width of described PET grain crystalline substance is 0.1mm ~ 0.85mm.