CN204138840U - The container bag production line of high-strength PET flat filament - Google Patents
The container bag production line of high-strength PET flat filament Download PDFInfo
- Publication number
- CN204138840U CN204138840U CN201420554267.0U CN201420554267U CN204138840U CN 204138840 U CN204138840 U CN 204138840U CN 201420554267 U CN201420554267 U CN 201420554267U CN 204138840 U CN204138840 U CN 204138840U
- Authority
- CN
- China
- Prior art keywords
- flat filament
- pet
- utility
- production line
- stress
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model provides a kind of production line of container bag high-strength PET flat filament, comprises the steps: that (1) adds screw extruder after pre-crystallized for PET raw material drying, after extruding, through water-bath cooling, obtains diaphragm; (2) drawing-off: the diaphragm obtained after step (1) being cooled breaks through broken cutting apparatus and cuts, and carries out a drawing-off, again carry out secondary drawing-off after heating after heating; (3) shape: material drawing-off obtained carries out adding heat abstraction stress again, then rolling after setting roll sizing, namely obtain high-strength PET flat filament.Optimize draft process parameter in the utility model, avoid the problem of fracture of wire in drafting process, the PET flat filament intensity of production is high; Add destressing technique, the stress that flat filament is produced in drafting process is removed, thus can not produce retraction distortion due to the existence of stress at flat filament fabric; Discarded PET bottle is applicable to the utility model too, achieves the Collection and utilization of discarded PET bottle.
Description
Technical field
The utility model belongs to field of high polymer material processing, particularly relates to a kind of production technology of high-strength PET flat filament.
Background technology
The plastic flat fiber manufacturing both at home and abroad at present, sell, use, is the flat filament manufactured for raw material with PP or PE, is then woven into plastic packaging bag connection with wrapping of piece.And the mechanical property of PET, uvioresistant performance, resistance to low temperature etc. all go with PE than PP, therefore PET material has huge potential value.And PET raw material sources are extensive, as filled the Packaging Bottle of mineral water or beverage etc. in life, mostly being PET material, reclaiming discarded PET bottle material as raw material, further reducing production cost.
But because the vitrification point of PET is higher, melt viscosity is less, molecular rigidity is comparatively large, and reset motion slowly, crystalline rate is low, makes easily to occur fracture of wire in remaining PET flat filament process, cannot quantity-produced problem.But be all add as consideration in additives such as flexibilizer etc. to PET section about this research in prior art, solve the problem of fracture of wire, technique is improved less.And PET flat filament prepared by existing technique, owing to there is stress, after being woven into container bag or after flat filament places a period of time, there will be the problem of container bag or the distortion of flat filament retraction, cause container bag to occur non-serviceable problem, that easily cause container bag with waste that is flat filament, although can heat while sizing in prior art, but the object of heating is that ensureing that flat filament is smooth when rolling does not send out wrinkle, and stress still exists, and still there will be the problem of retraction distortion in later stage fabric.
Utility model content
The utility model overcomes in prior art and holds yielding deficiency after the drawing-off of PET flat filament, a kind of container bag high-strength PET Flat Yarn Production technique and equipment thereof are provided, the utility model changes existing Flat Yarn Production technique, makes PET flat filament can not produce deformation after rolling or after being woven into container bag.
For solving the problems of the technologies described above, the technical scheme that the utility model reality adopts is: a kind of container bag high-strength PET Flat Yarn Production technique, comprises the steps:
(1) after pre-crystallized for PET raw material drying, add screw extruder, after extruding, through water-bath cooling, obtain diaphragm;
(2) drawing-off: the diaphragm obtained after step (1) being cooled breaks through broken cutting apparatus and cuts, and carries out a drawing-off, again carry out secondary drawing-off after heating after heating;
(3) shape: material step (2) drawing-off obtained carries out adding heat abstraction stress again, then rolling after setting roll sizing, namely obtain high-strength PET flat filament.
Further, described PET raw material is discarded PET bottle material or PET virgin material.
As preferably, a drawing-off described in step (2) is heating water bath (100 DEG C), and one time degree of draft is 2.5 ~ 3 times; Described secondary drawing-off is baking oven heating, and heating-up temperature is 180 ~ 200 DEG C, and secondary degree of draft is 1.5 ~ 3.5 times.Secondary drawing temperature improves greatly compared to a drawing temperature, and secondary drawing-off is carried out smoothly.
As preferably, the heat abstraction stress temperature that adds described in step (3) is 250 DEG C ~ 280 DEG C.Effectively can remove the stress that produces of PET flat filament in drafting process at this temperature, ensure that the high-strength PET flat filament of production in use there will not be the phenomenon of retraction distortion.
As preferably, the pulling speed of described setting roll is lower than the pulling speed of secondary drawing-off by 5 ~ 10%.Because in destressing process, flat filament there will be rebound phenomenon, general length can produce the retraction of 5% ~ 10%, if setting roll keeps the speed of secondary drawing-off, then flat filament can be caused cannot to be fully heated shortening, therefore need the pulling speed reducing setting roll accordingly.
Further, for reaching the temperature required for secondary drawing-off and destressing, described secondary drawing-off is heated and is added heat abstraction stress and carries out in an oven.
The equipment of above-mentioned container bag high-strength PET Flat Yarn Production technique, comprise connect in turn extruder, measuring pump, die head, cooling bath, broken cutting apparatus, drawing-off boiler, the first drawing roller, drawing-off baking oven, the second drawing roller, retraction baking oven, setting roll and winder.
Break for reclaiming brokenly cutting apparatus the limit silk waste material cutting through and produce in journey, as preferably, also have the limit silk retracting device for reclaiming limit silk between described broken cutting apparatus and drawing-off boiler, the described limit silk retracting device port of export is connected with extruder entrance.
For reclaiming the waste silk produced in setting roll type-approval process, as preferably, also have between described setting roll and winder for collecting the waste silk retracting device reclaiming waste silk.
The beneficial effects of the utility model are, optimize draft process parameter in the utility model, drafting process is carried out smoothly, avoids the problem of fracture of wire in drafting process, and the PET flat filament intensity of production is high; In addition, add destressing technique originally in the utility model, the stress that flat filament is produced in drafting process is removed, thus can not produce retraction, distortion due to the existence of stress at flat filament fabric; And can not only with PET virgin material as raw material in the utility model, discarded PET bottle is applicable to the utility model too, turns waste into wealth, and achieves the Collection and utilization of discarded PET bottle.
Accompanying drawing explanation
Fig. 1 is the device structure schematic diagram of the utility model high-strength PET Flat Yarn Production technique;
1. measuring pumps, 2. extruder, 3. cooling bath in figure, 4. broken cutting apparatus, 5. drawing-off boiler, 6. the first drawing roller, 7. drawing-off baking oven, 8. the second drawing roller, 9. bounce back baking oven, 10. setting roll, 11. winders, 12. limit silk retracting devices, 13. waste silk retracting devices.
Detailed description of the invention
Embodiment 1
As shown in Figure 1, (1) discarded PET bottle material (mineral water bottle of recovery) (is added appropriate additive if desired, as flexibilizer, antioxidant or filler etc., determine according to needs of production) be ground into the particle being less than 15x15mm, after drying, add extruder 2, extruder temperature is set to 260 ~ 270 DEG C, raw material becomes molten condition to enter measuring pump 1 through extruder, the PET of molten condition is expected metering input die head on request by measuring pump 1, and extrude from the narrow slit of die head, namely PET film sheet is formed after cooling bath 3 water cooling that excess temperature is 50 ~ 60 DEG C,
(2) utilize broken cutting apparatus 4 longitudinally to be cut by diaphragm to carry out broken cutting, then under the first drawing roller 6 (drawing-off five roller) acts on by its by drawing-off boiler 5 under 100 DEG C of conditions, carry out a drawing-off, draft ratio is 2.5 ~ 3 times; Under the second drawing roller 8 (drawing-off five roller) effect, by after a drawing-off flat filament by drawing-off baking oven 7, carry out secondary drawing-off, wherein the temperature of drawing-off baking oven 7 is 200 DEG C, and draft ratio is 1.5 ~ 3.5 times;
(3) then the flat filament after secondary drawing-off is passed into retraction baking oven 9 and carry out heating destressing, temperature in retraction baking oven 9 is 280 DEG C, then flat filament is shaped through setting roll 10 (three rollers of shaping), final through winder 11 rolling, flat filament retracted in length 5% in destressing process, setting roll 10 pulling speed is lower than the pulling speed of secondary drawing-off by 5% ~ 10% in the process accordingly.
Brokenly in above process cut through the limit silk produced in journey and drawing-off, type-approval process or waste silk reclaims through limit silk retracting device 12 and waste silk retracting device 13 respectively, and be added in extruder 2 or disintegrating machine and again process.
Embodiment 2
(1) low viscosity (0.68 ~ 0.8d1/g) PET virgin material (is added appropriate additive if desired, as flexibilizer, antioxidant or filler etc., determine according to needs of production) pre-crystallized under 150 ~ 170 DEG C of conditions, then extruder 2 is added, arranging extruder temperature is 250 ~ 270 DEG C, raw material becomes molten condition to enter measuring pump 1 through extruder, the PET of molten condition is expected metering input die head on request by measuring pump 1, and extrude from the narrow slit of die head, after cooling bath 3 water cooling, namely form PET film sheet;
(2) utilize broken cutting apparatus 4 longitudinally to be cut by diaphragm to carry out broken cutting, then under the first drawing roller 6 (drawing-off five roller) effect by its by drawing-off boiler 5 under 100 DEG C of conditions, carry out a drawing-off, drawing multiplying power is 2.5 ~ 3 times; Under the second drawing roller 8 (drawing-off five roller) effect, by after a drawing-off flat filament by drawing-off baking oven 7, carry out secondary drawing-off, wherein the temperature of drawing-off baking oven 7 is 180 DEG C, and traction multiplying power is 1.5 ~ 3.5 times;
(3) then the flat filament after secondary drawing-off is passed into retraction baking oven 9 and carry out heating destressing, temperature in retraction baking oven 9 is 250 DEG C, then flat filament is shaped through setting roll 10, final through winder 11 rolling, retraction baking oven 9 in flat filament retracted in length 10%, accordingly in the process setting roll 10 pulling speed than the pulling speed 5% ~ 10% of secondary drawing-off.
Brokenly in above process cut through the limit silk produced in journey and drawing-off, type-approval process or waste silk reclaims through limit silk retracting device 12 and waste silk retracting device 13 respectively, and be added in extruder 2 or disintegrating machine and again process.
In addition, only need dried feed when using the PET virgin material of viscosity higher, pre-crystallized without the need to carrying out separately, but want the temperature of corresponding raising extruder, correspondingly can bring up to 290 ~ 305 DEG C.
Claims (3)
1. a container bag production line for high-strength PET flat filament, is characterized in that: comprise the extruder (2), measuring pump (1), die head, cooling bath (3), broken cutting apparatus (4), drawing-off boiler (5), the first drawing roller (6), drawing-off baking oven (7), the second drawing roller (8), retraction baking oven (9), setting roll (10) and the winder (11) that connect in turn.
2. production line according to claim 1, it is characterized in that: also have limit silk retracting device (12) for reclaiming limit silk between described broken cutting apparatus (4) and drawing-off boiler (5), with extruder (2), described limit silk retracting device (12) port of export expects that mouth is connected.
3. production line according to claim 1, is characterized in that: also have between described setting roll (10) and winder (11) for collecting the waste silk retracting device (13) reclaiming waste silk.