CN204077213U

CN204077213U - A kind of wall ornamentation compound glass

Info

Publication number: CN204077213U
Application number: CN201420554123.5U
Authority: CN
Inventors: 丁一斌
Original assignee: Individual
Current assignee: Individual
Priority date: 2014-09-25
Filing date: 2014-09-25
Publication date: 2015-01-07
Anticipated expiration: 2024-09-25

Abstract

The utility model relates to a kind of wall ornamentation compound glass, comprises for aging-resistant glassy layer (10) and the clarity plastic layer (20) for embodying described wall ornamentation compound glass stereoeffect; Described clarity plastic layer (20) comprises a transparent plastic shiny surface (21) and the transparent plastic space pattern face (22) that present uneven pattern relative with described transparent plastic shiny surface (21); Color layers (23) is coated with outside described transparent plastic space pattern face (22); Described glassy layer (10) has at least a surface to be glass light sliding surface (11), and its size, shape are corresponding with described transparent plastic shiny surface (21); Described glass light sliding surface (11) and the adhesion of described transparent plastic shiny surface (21).The utility model provide a kind of long service life, easy to clean, be convenient to carve wall ornamentation compound glass.

Description

A kind of wall ornamentation compound glass

Technical field

The utility model relates to a kind of ambetti, particularly a kind of wall ornamentation compound glass.

Background technology

Current sculptured ornament glass such as computer car quarter, manual sandblasting, manual finishing impression technology are not only subject to the restriction of glass self character, and be subject to the limitation of engraving tool, be difficult to reach effect three-dimensional true to nature, if carved on simple glass or safety glass, not only carve difficulty large, and Glass breadks easily, especially for degree of depth engraving, impossible especially; If carved on lucite, as: CN00224507.8, publication date is: provide a kind of lucite pressing mold to carve double-faced picture, painted screen adopts transparent organic glass, be pasted with respectively on painted screen two sides by the identical embossing pattern of the figure of lucite moulded section, although can realize, lucite is easily aging, and service life is short; Because the break joint of cut glass surface irregularity and decorative pattern is narrow, directly exposed in atmosphere by ornament, dust is easy to enter slit, cleans cause certain difficulty to cut glass.

Utility model content

In order to overcome the deficiencies in the prior art, the utility model provide a kind of long service life, easy to clean, be convenient to carve wall ornamentation compound glass.

To achieve these goals, the utility model is by the following technical solutions:

A kind of wall ornamentation compound glass, is characterized in that: described wall ornamentation compound glass comprises for aging-resistant glassy layer and the clarity plastic layer for embodying described wall ornamentation compound glass stereoeffect;

Described clarity plastic layer comprises a transparent plastic shiny surface and the transparent plastic space pattern face that present uneven pattern relative with described transparent plastic shiny surface; Color layers is coated with outside described transparent plastic space pattern face;

Described glassy layer has at least a surface to be glass light sliding surface, and its size, shape are corresponding with described transparent plastic shiny surface;

Described glass light sliding surface and the adhesion of described transparent plastic shiny surface.

Preferably, described glassy layer is water white transparency float glass.

Preferably, described glass light sliding surface is glass smooth flat.

Preferably, described clarity plastic layer is water white lucite, ABS plastic, PS plastics, PC plastics or AS plastics.

Preferably, described transparent plastic shiny surface is transparent plastic smooth flat.

Preferably, described color layers Surface coating matcoveredn.

The preparation method of wall ornamentation compound glass described in the utility model, comprises the following steps:

1) prepare clarity plastic layer that what a surface is transparent plastic shiny surface and have at least a surface to be glass light sliding surface and size, a shape glassy layer corresponding to described clarity plastic layer shiny surface;

2) with adhesive or film, the glass light sliding surface of glassy layer and the transparent plastic shiny surface of clarity plastic layer are bonded together;

3) carve rough space pattern at the outer surface that the transparent plastic shiny surface of clarity plastic layer is relative, form transparent plastic space pattern face;

4) the transparent plastic space pattern face described in step 3) is coated by stain, forms color layers.

Preferably, at described step 4) color layers outer surface spraying protective layer.

Preferably, anticorrisive agent is contained in described colouring agent.

Preferably, described glass light sliding surface and transparent plastic shiny surface are smooth flat.

In sum, the beneficial effects of the utility model are:

1, wall ornamentation compound glass comprises for aging-resistant glassy layer and the clarity plastic layer for embodying described wall ornamentation compound glass stereoeffect, in engraving process, because transparent plastic has certain toughness, so easily engraving is not easily broken in engraving, and can solve and on glass, to carve the degree of depth not in the cards engraving, to reach better stereoeffect; By the combination by glassy layer and clarity plastic layer, in use, be arranged on wall, only have outside being exposed to for aging-resistant glassy layer, because glass hard (HRC65Yi Shang) is high, scratch-resistant, clarity plastic layer is between wall and glassy layer, and transparent plastic color layers also can play certain protective effect to transparent plastic, thus isolated air, greatly reduce the aging speed of transparent plastic, thus extend the service life of wall ornamentation compound glass; The outer surface of the wall ornamentation compound glass decorated is glassy layer, comparatively smooth, easy to clean.

2, wall ornamentation compound glass comprises glassy layer and clarity plastic layer, and glassy layer is water white transparency float glass and surface is smooth flat, and in this case, stereoeffect is better, the more dirt of easy cleaning Float Glass Surface.

3, due to the painted rear fugitive color of long duration of color layers, layer protective layer can be applied outward in color layers, so just completely cut off color layers and extraneous contact, thus protected color layers.

Accompanying drawing explanation

Fig. 1 is structural representation of the present utility model;

Fig. 2 is the utility model assembling pre-structure schematic diagram;

Fig. 3 is the utility model structural representation of band matcoveredn

Description of symbols: 10-glassy layer; 11-glass light sliding surface; 20-clarity plastic layer; 21-transparent plastic shiny surface; 22-transparent plastic space pattern face; 23-color layers; 24-protective layer.

Detailed description of the invention

Below in conjunction with the drawings and specific embodiments, the utility model is further described, therefore the utility model is not limited among described scope of embodiments.

embodiment 1

Composition graphs 1,2 illustrates the present embodiment:

In the present embodiment, transparent plastic is colourless lucite, glassy layer 10 is clear float glass layer:

Wall ornamentation compound glass comprises transparent glass layer 10 and clarity plastic layer 20; Clarity plastic layer 20 comprises a transparent plastic shiny surface 21 and the transparent plastic space pattern face 22 that present uneven pattern relative with transparent plastic shiny surface 21; Color layers 23 is coated with outside transparent plastic space pattern face 22; Glassy layer 10 has at least a surface to be glass light sliding surface 11, and its size, shape are corresponding with described transparent plastic shiny surface 21; Described glass light sliding surface 11 and the adhesion of described transparent plastic shiny surface 21.

embodiment 2

Composition graphs 3 illustrates the present embodiment:

Difference from Example 1 is, goes back matcoveredn 24 in color layers 23, color layers is hedged off from the outer world, prevents color fading.

embodiment 3

A preparation method for wall ornamentation compound glass, comprises the following steps:

1) prepare perspex layer that what a surface is lucite shiny surface and have at least a surface to be glass light sliding surface and size, a shape glassy layer 10 corresponding to the lucite shiny surface of described perspex layer;

2) with adhesive, glass light sliding surface and lucite shiny surface are bonded together;

3) carve rough space pattern at the outer surface that the lucite shiny surface of perspex layer is relative, form transparent plastic space pattern face;

Embodiment 4

Difference from Example 3 is, at the color layers outer surface protective layer that step 4) is formed, color layers is hedged off from the outer world, prevents color fading.

In above-described embodiment, color layers can add anticorrisive agent protected; Colourless lucite can replace with water white ABS plastic, PS plastics, PC plastics or AS plastics.

Claims

1. a wall ornamentation compound glass, is characterized in that: described wall ornamentation compound glass comprises for aging-resistant glassy layer (10) and the clarity plastic layer (20) for embodying described wall ornamentation compound glass stereoeffect;

Described clarity plastic layer (20) comprises a transparent plastic shiny surface (21) and the transparent plastic space pattern face (22) that present uneven pattern relative with described transparent plastic shiny surface (21); Color layers (23) is coated with outside described transparent plastic space pattern face (22);

Described glassy layer (10) has at least a surface to be glass light sliding surface (11), and its size, shape are corresponding with described transparent plastic shiny surface (21);

Described glass light sliding surface (11) and the adhesion of described transparent plastic shiny surface (21).

2. a kind of wall ornamentation compound glass according to claim 1, is characterized in that: described glassy layer (10) is water white transparency float glass.

3. a kind of wall ornamentation compound glass according to claim 1, is characterized in that: described glass light sliding surface (11) is glass smooth flat.

4. a kind of wall ornamentation compound glass according to claim 1, is characterized in that: described clarity plastic layer (20) is water white lucite, ABS plastic, PS plastics, PC plastics or AS plastics.

5. a kind of wall ornamentation compound glass according to claim 4, is characterized in that: described transparent plastic shiny surface (21) is transparent plastic smooth flat.

6. a kind of wall ornamentation compound glass according to claim 1, is characterized in that: described color layers (23) Surface coating matcoveredn (24).