CN203799037U - Partially-aluminized high refractive index glass bead - Google Patents
Partially-aluminized high refractive index glass bead Download PDFInfo
- Publication number
- CN203799037U CN203799037U CN201420096043.XU CN201420096043U CN203799037U CN 203799037 U CN203799037 U CN 203799037U CN 201420096043 U CN201420096043 U CN 201420096043U CN 203799037 U CN203799037 U CN 203799037U
- Authority
- CN
- China
- Prior art keywords
- resin
- pearl
- refractive index
- glass bead
- high refractive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model relates to a partially-aluminized high refractive index glass bead, which comprises glass bead bodies (1), an aluminum plated layer (2), a substrate (3) and a ball planting resin (4), wherein the ball planting resin (4) is coated on one surface of the substrate (3), the glass bead bodies (1) are evenly embedded on the surface of the ball planting resin (4), and the outer surfaces of the glass bead bodies (1) are evaporated with the aluminum plated layer (2); the area of the aluminum plated layer (2) occupies 0.1%-90% of the surface area of the glass bead bodies (1); and the thickness of the aluminum plated layer (2) ranges from 300 angstrom to 1200 angstrom, and the ball planting resin (4) is a water soluble resin. The partially-aluminized high refractive index glass bead has the advantages of controllable aluminum plating area, good mobility of produced glass beads, high qualified rate of products and relatively low cost.
Description
Technical field
The utility model relates to reflectorized material production technical field, particularly a kind of high refractive index glass micro pearl of partly aluminizing.
Background technology
The high refractive index glass micro pearl of partly aluminizing is a kind of reflectorized material of novelty, in fields such as reflective ink, clothes, ornaments, has unique application, plays effect reflective, warning.At present popular way is mainly coated or prints suitable resin on base material, adheres to after drying high refractive index glass micro pearl, after evaporation plating aluminium, gets off with brush brushing.
This production method, has following several defect: 1. the aluminum plating glass bead surface that brushing is got off easily adheres to a small amount of resin, affects performance and the mobility of glass microballoon; 2. because the resin on base material has viscosity, cannot, by clean thorough glass microballoon brushing, affect qualification rate; 3. for the glass microballoon brushing after aluminizing being got off, the resin on base material just needs very thin, so just cannot adjust the area of aluminizing of glass microballoon, just cannot develop the aluminize glass microballoon of area of more differences.
Utility model content
The purpose of this utility model is to overcome the shortcoming of prior art, and the high cheap part relative to cost of a kind of area of aluminizing glass microballoon good fluidity, product percent of pass controlled, that the produce high refractive index glass micro pearl of aluminizing is provided.
The purpose of this utility model is achieved through the following technical solutions: a kind of high refractive index glass micro pearl of partly aluminizing, it comprises glass microballoon body, aluminium coated, base material and plants pearl resin, it is described that to plant pearl resin-coated in the one side of base material, glass microballoon body is evenly embedded on the surface of planting pearl resin, and on the outside surface of glass microballoon body, evaporation has aluminium coated.
The area of described aluminium coated account for glass microballoon body surface area 0.1%~90%.
The thickness of described aluminium coated is
The described pearl resin of planting is water soluble resin.
The utlity model has following advantage:
1, the control of coating machine coating thickness can be passed through, and the adjustment of the glass microballoon sedimentation degree of depth, the needed glass microballoon area of aluminizing can be controlled easily.
2, be water soluble resin owing to planting pearl resin, soluble in water, can easily the glass microballoon that has plated aluminium be separated from base material, and apparently can not come to harm, ensured the quality of aluminum plating glass microballon, glass microballoon good fluidity, the product percent of pass of producing are high.
3, planting pearl resin can be acrylate resin, vibrin, and urethane resin, polyvinyl alcohol resin, the combination of one or more resins such as polyvinylpyrrolidone resin, the leeway of selection is larger, and cost is relatively low.
Brief description of the drawings
Fig. 1 is the structural representation of the glass microballoon body after part is aluminized;
Fig. 2 is that the glass microballoon body before aluminizing is embedded in the structural representation of planting in pearl resin;
Fig. 3 is that the glass microballoon body after aluminizing is embedded in the structural representation of planting in pearl resin;
In figure: 1-glass microballoon body, 2-aluminium coated, 3-base material, 4-plants pearl resin.
Embodiment
Below in conjunction with accompanying drawing, the utility model is further described, but protection domain of the present utility model is not limited to the following stated.
As shown in Figure 1, Figure 2 and Figure 3, a kind of high refractive index glass micro pearl of partly aluminizing, it comprises glass microballoon body 1, aluminium coated 2, base material 3 and plants pearl resin 4, described one side of planting pearl resin 4 and coat base material 3, glass microballoon body 1 is evenly embedded on the surface of planting pearl resin 4, and on the outside surface of glass microballoon body 1, evaporation has aluminium coated 2.
Further, in the time that pearl resin 4 is planted in coating, can pass through the control of coating machine coating thickness, and the adjustment of the glass microballoon body 1 sedimentation degree of depth, can control easily the area of needed aluminium coated 2, the area of aluminium coated 2 account for glass microballoon body 1 surface area 0.1%~90%; The thickness of aluminium coated 2 is
Described plants pearl resin 4 for water soluble resin, and the water-soluble pearl resin of planting can be acrylate resin, vibrin, and urethane resin, polyvinyl alcohol resin, the combination of one or more in polyvinylpyrrolidone resin, the leeway of selection is larger.
First be coated with and plant pearl resin 4 by knife type coater in the one side of base material 3, before coating, set suitable gap, after dry, plant pearl, glass microballoon body 1 is sticked to equably and planted in pearl resin 4, and partly sink to and plant pearl resin 4, by sputter aluminum plating process, glass microballoon body 1 is exposed to the part of planting pearl resin 4 outsides aluminizes, then will rinse with glass microballoon body 1 water of planting pearl resin 4, owing to planting pearl resin 4 for water soluble resin, make to plant pearl resin 4 and be dissolved in water, the glass microballoon that cutting out partial is aluminized, dry processing after improvement, obtain the glass microballoon that part is aluminized.
Claims (4)
1. the part high refractive index glass micro pearl of aluminizing, it is characterized in that: it comprises glass microballoon body (1), aluminium coated (2), base material (3) and plants pearl resin (4), described one side of planting pearl resin (4) and coat base material (3), glass microballoon body (1) is evenly embedded on the surface of planting pearl resin (4), and on the outside surface of glass microballoon body (1), evaporation has aluminium coated (2).
2. a kind of part according to claim 1 high refractive index glass micro pearl of aluminizing, is characterized in that: the area of described aluminium coated (2) account for glass microballoon body (1) surface area 0.1%~90%.
3. a kind of high refractive index glass micro pearl of partly aluminizing according to claim 1, is characterized in that: the thickness of described aluminium coated (2) is
4. a kind of high refractive index glass micro pearl of partly aluminizing according to claim 1, is characterized in that: the described pearl resin (4) of planting is water soluble resin.