CN203546130U - Iron container for copper alloy smelting - Google Patents
Iron container for copper alloy smelting Download PDFInfo
- Publication number
- CN203546130U CN203546130U CN201320745972.4U CN201320745972U CN203546130U CN 203546130 U CN203546130 U CN 203546130U CN 201320745972 U CN201320745972 U CN 201320745972U CN 203546130 U CN203546130 U CN 203546130U
- Authority
- CN
- China
- Prior art keywords
- container
- alloy
- copper alloy
- melting point
- smelting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
An iron container for copper alloy smelting comprises a container body, ears and a pouring hole. The container body is made of alloy steel with a melting point more than 1500 DEG C, and the ears and the pouring hole are arranged on the container body. The method for preparing the iron container made of alloy steel with a melting point more than 1500 DEG C is unique. Due to the fact that the melting point of the alloy is more than 1500 DEG C, the melting point temperature of the copper alloy is less than 1200 DEG C, and the melting point temperature difference exists, alloy steel is suitable for smelting copper alloy. Meanwhile, when alloy steel is used for smelting copper alloy, such advantages as high melting speed, small fuel consumption, high heat efficiency, small metal burning loss, and low alloy gettering quantity are achieved. Many defects caused when a crucible is used for smelting copper alloy are overcome. In addition, when the alloy steel container is used for replacing the crucible, the container also has the advantages of being not prone to damage, low in cost, and the like, thereby being worth popularizing vigorously.
Description
Technical field
The utility model belongs to a kind of melting container, is specifically related to a kind of smelting copper alloy container made of iron.
Technical background
At present, the alloy of general medium-sized and small enterprises melting copper and aluminium is fusing and the container of containing metal liquid with crucible conventionally.Crucible is a kind of container made from pottery, graphite or silicon carbide and clay, and because its characteristic makes so, so crucible has, molten speed is slow, fuel consumption is large, thermal effect is low, metal loss is large, alloy inspiratory capacity headlight shortcomings.In order to change this situation, also someone developed container made of iron, but container made of iron fusing point is low, in when more than 1153 ℃, can become the metal of liquid or melting, and the smelting temperature of copper alloy requires to reach more than 1100 ℃, so container made of iron can only be for low melting point alloys such as smelting aluminums, and can not be for the melting of the high-meltiing alloys such as copper.Therefore, use crucible is thrown away during smelting copper alloy by most enterprise, and therefore, the shortcomings of crucible still exists in smelting copper alloy.
Utility model content
In order to overcome the deficiency of above-mentioned technology and facility, the utility model provides brand-new a kind of smelting copper alloy container made of iron.Specifically comprise: this container is comprised of container, ear, the mouth that falls; Wherein, container is with fusing point, to reach 1500 ℃ of above steel alloys to make, and on container, is provided with ear and falls mouth.The utility model proposes reaches 1500 ℃ of above steel alloys by fusing point to make method and measure prepared by container made of iron unique.Meanwhile, because alloy melting point is up to more than 1500 ℃, and the melting temperature of copper alloy is below 1200 ℃, and the existence of the fusing point temperature difference, makes steel alloy be applicable to smelting copper alloy.By implementing the utility model, use steel alloy smelting copper alloy, there is the advantages such as molten speed is fast, fuel consumption is little, thermal effect is high, metal loss is little, alloy inspiratory capacity is little, the shortcomings while comprehensively having solved with crucible for smelting copper alloy.In addition, with alloy steel container, replace crucible, also there is the advantages such as not fragile, cost is little, be worth promoting.
The utility model is achieved through the following technical solutions:
1, a smelting copper alloy container made of iron, in technical scheme, this container is comprised of container (1), ear (2), the mouth (3) that falls; Wherein, container (1) is with fusing point, to reach 1500 ℃ of above steel alloys to make, and is provided with ear (2) and falls mouthful (3) on container (1).
2, described fusing point reaches 1500 ℃ of above steel alloys, and technical scheme comprises high mangaenese steel and high chromium steel.
The utility model both had the following advantages:
1, the utility model proposes reaches 1500 ℃ of above steel alloys by fusing point to make method and measure prepared by container made of iron unique, and easily implements.
2, because alloy melting point is up to more than 1500 ℃, and the melting temperature of copper alloy is below 1200 ℃, and the existence of the fusing point temperature difference, makes steel alloy be applicable to smelting copper alloy.
3, use steel alloy smelting copper alloy, there is the advantages such as molten speed is fast, fuel consumption is little, thermal effect is high, metal loss is little, alloy inspiratory capacity is little, the shortcomings while comprehensively having solved with crucible for smelting copper alloy.
4, with alloy steel container, replace crucible, also there is the advantages such as not fragile, cost is little, be worth promoting.
Accompanying drawing explanation
Below in conjunction with drawings and Examples, the utility model is further illustrated.
Fig. 1 is structural representation of the present utility model.
In Fig. 1, the 1st, with fusing point, reach the container that 1500 ℃ of above steel alloys are made, the 2nd, the ear of container, the 3rd, the mouth of container.
Embodiment
By reference to the accompanying drawings the utility model is described in detail now:
Shown in Fig. 1.The 1st, with fusing point, reach the container (1) that 1500 ℃ of above steel alloys are made, the 2nd, the ear of container (2), the 3rd, mouthful (3) for container.
Meanwhile, shown in Fig. 1, be structural representation of the present utility model.The utility model is comprised of container (1), ear (2), the mouth (3) that falls; Wherein, container (1) is with fusing point, to reach 1500 ℃ of above steel alloys to make, and is provided with ear (2) and falls mouthful (3) on container (1).
Embodiment 1:
The high mangaenese steel that reaches 1500~1600 ℃ with fusing point is made container (1), is provided with ear (2) simultaneously and falls mouthful (3) on container (1).
Embodiment 2:
The high chromium steel that reaches 1700 ℃ with fusing point is made container (1), is provided with ear (2) simultaneously and falls mouthful (3) on container (1).
Claims (2)
1. a smelting copper alloy container made of iron, is characterized in that: this container by container (1), ear (2), fall 1 mouthful (3) form; Wherein, container (1) is with fusing point, to reach 1500 ℃ of above steel alloys to make, and is provided with ear (2) and falls mouthful (3) on container (1).
2. according to a kind of smelting copper alloy container made of iron described in claim 1, it is characterized in that: described fusing point reaches 1500 ℃ of above steel alloys, comprises high mangaenese steel and high chromium steel.