CN203174798U - Rubber and plastic foaming acoustical board with corrugated surface - Google Patents
Rubber and plastic foaming acoustical board with corrugated surface Download PDFInfo
- Publication number
- CN203174798U CN203174798U CN 201320029119 CN201320029119U CN203174798U CN 203174798 U CN203174798 U CN 203174798U CN 201320029119 CN201320029119 CN 201320029119 CN 201320029119 U CN201320029119 U CN 201320029119U CN 203174798 U CN203174798 U CN 203174798U
- Authority
- CN
- China
- Prior art keywords
- ripple glaze
- rubber
- baseplane
- abatvoix
- depth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Abstract
The utility mode provides a rubber and plastic foaming acoustical board with a corrugated surface. The thickness from the root of each wave to the bottom surface of a base flat plate is 2mm-20mm, and the depth of each wave is 3mm-50mm. The rubber and plastic foaming acoustical board with the corrugated surface has the advantages of being sound-proof, adiabatic, capable of reducing noise and insulating heat and the like. The waves and the base flat plate are integrally formed through foaming, the waves are of conical structures and are firm, and the rubber and plastic foaming acoustical board has wide application prospects.
Description
Technical field
The utility model relates to heat preservation and soundproof noise reduction field, is specifically related to the rubber-plastic foamed plate that sound-absorbing, sound insulation, decrease of noise functions are arranged that the decorations of all kinds of public places are used.
Background technology
The abatvoix of the various materials of using in the prior art, various in style, each tool eternal lasting.
Traditional mineral wool abatvoix is used for sound-absorbing sound insulation occasion, makes influence because of its material and extruding, exists smooth surface, sound-absorbing effect poor, and echo, sound insulation are bad, and exists and be afraid of tide, be afraid of defectives such as wet.In addition, because mineral wool abatvoix material is crisp, the construction breakage is many, the decoration cost height.
Though the theory that the metal abatvoix is decorated in conjunction with modern architecture is carried out surperficial multi-form design, pursues preferable sound-absorbing effect, has the price height, easily resonates defectives such as energy-saving heat preserving weak effect.
Wooden abatvoix also has the defective that easily produces deformation with ambient humidity, variations in temperature.
Summary of the invention
The purpose of this utility model is effectively to overcome deficiency and the defective of above-mentioned abatvoix, a kind of rubber-plastic foamed abatvoix in ripple glaze surface that adapts to all kinds of sound-absorbings, noise reduction place is provided, the utlity model has sound-absorbing, excellent noise reduction effect, cost is low, easy construction, advantages such as environmental protection and energy saving.
For achieving the above object, the technical solution of the utility model is: utilize rubber-plastic foamed raw material and manufacture craft, adopt moulding roll extrusion technology and device, producing ripple glaze root and baseplane sheet metal thickness continuously is 2mm～20mm, and the ripple glaze degree of depth is the rubber-plastic foamed abatvoix in many specifications ripple glaze surface of 3mm～50mm.
Described ripple glaze root and baseplane sheet metal thickness are preferably 5mm～10mm, and the ripple glaze degree of depth is preferably 5mm～10mm.
Described ripple glaze root and baseplane sheet metal thickness be 6mm～8mm more preferably, and the ripple glaze degree of depth is 6mm～8mm more preferably.
Described ripple glaze is cone-shaped, but the ripple glaze degree of depth, ripple glaze root and baseplane sheet metal thickness regulated at will.
Described ripple glaze and baseplane sheet material are that foaming forms.
Described baseplane sheet material is the planar closed pore structure.
Described rubber-plastic foamed raw material be by the prescription requirement be primary raw material with NBR, PVC, be aided with blowing agent, vulcanization accelerator, filler, fire retardant, plasticizing agent, age resistor etc. and become the uniform film of material through banbury, mill mixing.
Described manufacture craft is the rubber-plastic foamed goods manufacture craft of flexible foam: the accurate weighing proportioning of raw material is through mixer mixing, dropping into the continuous backing of mill mixes, making film extrudes by cold feed extruder, through cylinder calender roll forming, and enter the foaming furnace sulfur foam continuously, cut into described goods packing warehouse-in through cooling again.
Described through cylinder calender rolling and forming technology and device, be to carry out on the improved basis of multi-rolling mill cylinder top roll, carry out embedding by the live part to the calender top roll and carve processing, be made into ripple glaze embedding needle drawing shape, relative rolling through calender bowl top roll and cylinder lower roll, make film under pressure ripple glaze embedding needle drawing shape is rolled into film and enter the foaming furnace foaming, cooling then cuts into required abatvoix specification.
The utlity model has following beneficial effect:
1. the sound-absorbing sheet material that has the adiabatic function of insulation, both sound insulations, noise reduction, adiabatic heat-insulation again.
2. rubber-plastic foamed abatvoix surface, the utility model ripple glaze surface is foaming ripple glaze type shape, the absorption of favourable high-low sound frequency, and echo is little.
3. the material softness is used convenient transportation, Environmental Safety.
4. beautiful and comfortable, can be processed into required tone, with low cost.
5. ripple glaze and baseplane sheet material are that foaming forms, and the ripple glaze cone is firm.
Description of drawings
Fig. 1 is the utility model cylinder calender roll forming device schematic diagram.
Among the figure, 1-cylinder lower roll; 2-cylinder top roll; 3-ripple glaze embedding needle drawing shape; 4-ripple glaze film.
Fig. 2 is the rubber-plastic foamed abatvoix structural representation in the utility model ripple glaze surface.
Among the figure, 5-baseplane sheet material; 6,7-ripple glaze; 8-ripple glaze degree of depth; 9-ripple glaze root and baseplane sheet metal thickness.
Wherein, Fig. 2 is Figure of abstract.
The specific embodiment
Below in conjunction with Figure of description the utility model being further described, below only is preferred embodiment of the present utility model, can not limit scope of the present utility model with this.Be every variation and modification of doing according to the utility model claim, all should still belong in the scope that the utility model patent contains.
As shown in Figure 1, the utility model is to carry out on the improved basis of multi-rolling mill cylinder top roll, carry out embedding by the live part to calender top roll 2 and carve processing, be made into ripple glaze embedding needle drawing shape 3, relative rolling through calender bowl top roll 2 and cylinder lower roll 1, make film under pressure ripple glaze embedding needle drawing shape 3 is rolled into film 4, enter the foaming furnace foaming then, cooling then cuts into required abatvoix specification.
By reference to the accompanying drawings 2, do the detailed description of Product Status.
The rubber-plastic foamed abatvoix structure in the utility model ripple glaze surface as shown in Figure 2, baseplane sheet material 5 is planar closed pore structures, ripple glaze 6, the 7th, the finished product ripple glaze after the foaming, ripple glaze degree of depth available adjustment drum pressure is made the ripple glaze degree of depth 8 and is 3mm, and ripple glaze root and baseplane sheet metal thickness 9 are 2mm.
Adopt embodiment 1 described method to prepare the rubber-plastic foamed abatvoix in ripple glaze surface, difference is: the product ripple glaze degree of depth is made the ripple glaze degree of depth 8 with the adjusting drum pressure and is 5mm, and ripple glaze root and baseplane sheet metal thickness 9 are 5mm.
Adopt embodiment 1 described method to prepare the rubber-plastic foamed abatvoix in ripple glaze surface, difference is: the product ripple glaze degree of depth is made the ripple glaze degree of depth 8 with the adjusting drum pressure and is 6mm, and ripple glaze root and baseplane sheet metal thickness 9 are 6mm.
Embodiment 4
Adopt embodiment 1 described method to prepare the rubber-plastic foamed abatvoix in ripple glaze surface, difference is: the product ripple glaze degree of depth is made the ripple glaze degree of depth 8 with the adjusting drum pressure and is 8mm, and ripple glaze root and baseplane sheet metal thickness 9 are 8mm.
Adopt embodiment 1 described method to prepare the rubber-plastic foamed abatvoix in ripple glaze surface, difference is: the product ripple glaze degree of depth is made the ripple glaze degree of depth 8 with the adjusting drum pressure and is 10mm, and ripple glaze root and baseplane sheet metal thickness 9 are 10mm.
Adopt embodiment 1 described method to prepare the rubber-plastic foamed abatvoix in ripple glaze surface, difference is: the product ripple glaze degree of depth is made the ripple glaze degree of depth 8 with the adjusting drum pressure and is 20mm, and ripple glaze root and baseplane sheet metal thickness 9 are 20mm.
Embodiment 7
Adopt embodiment 1 described method to prepare the rubber-plastic foamed abatvoix in ripple glaze surface, difference is: the product ripple glaze degree of depth is made the ripple glaze degree of depth 8 with the adjusting drum pressure and is 6mm, and ripple glaze root and baseplane sheet metal thickness 9 are 10mm.
Claims (9)
1. the rubber-plastic foamed abatvoix in ripple glaze surface is characterized in that ripple glaze root and baseplane sheet metal thickness are 2mm～20mm, and the ripple glaze degree of depth is 3mm～50mm.
2. according to the described abatvoix of claim 1, it is characterized in that ripple glaze root and baseplane sheet metal thickness are 5mm～10mm, the ripple glaze degree of depth is 5mm～10mm.
3. according to the described abatvoix of claim 2, it is characterized in that ripple glaze root and baseplane sheet metal thickness are 6mm～8mm, the ripple glaze degree of depth is 6mm～8mm.
4. according to claim 1,2 or 3 described abatvoixs, it is characterized in that it is cone-shaped that ripple glaze is.
5. according to claim 1,2 or 3 described abatvoixs, it is characterized in that ripple glaze and baseplane sheet material are that foaming forms.
6. according to the described abatvoix of claim 4, it is characterized in that ripple glaze and baseplane sheet material are that foaming forms.
7. according to claim 1,2 or 3 described abatvoixs, it is characterized in that baseplane sheet material is the planar closed pore structure.
8. according to the described abatvoix of claim 4, it is characterized in that baseplane sheet material is the planar closed pore structure.
9. according to the described abatvoix of claim 5, it is characterized in that baseplane sheet material is the planar closed pore structure.