CN203066780U - Environment-friendly, energy-saving, high-strength, anti-impacting and anti-scratching special public door - Google Patents
Environment-friendly, energy-saving, high-strength, anti-impacting and anti-scratching special public door Download PDFInfo
- Publication number
- CN203066780U CN203066780U CN 201320098829 CN201320098829U CN203066780U CN 203066780 U CN203066780 U CN 203066780U CN 201320098829 CN201320098829 CN 201320098829 CN 201320098829 U CN201320098829 U CN 201320098829U CN 203066780 U CN203066780 U CN 203066780U
- Authority
- CN
- China
- Prior art keywords
- veneer
- flaggy
- layers
- door
- glue
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model provides an environment-friendly, energy-saving, high-strength, anti-impacting and anti-scratching special public door. A traditional single-board drying method commonly adopts two manners of natural drying and rotary drum type drying. A traditional natural drying method is high in water content of a single board and poor in flatness; and a rotary drum type drying method is serious in warping, deformation and cracking of the single board and difficult for guaranteeing the quality. The environment-friendly, energy-saving, high-strength, anti-impacting and anti-scratching special public door comprises a plurality of plate layers 5; the upper surfaces of the plate layers and the lower surfaces of the plate layers are connected with solid-wood board layers (6) or high-density board layers (7); and the solid-wood board layers or the high-density board layers are connected with melamine varnished paper layers (4); and the melamine varnished paper layers are connected with aluminum oxide surface layers (3). The utility model is used for manufacturing the environment-friendly, energy-saving, high-strength, anti-impacting and anti-scratching special public door.
Description
Technical field
The utility model type relates to a kind of production technology of public special-purpose door, relates in particular to the anti-wound of environmental protection and energy saving high strength and hits the public special-purpose door of scratch resistance
Background technology
Because China's virgin forest resource is being faced with the predicament that reduces year by year, fells and grows imbalance, causes the wood supply amount very in short supply.Therefore the problem of national correlation department great attention saving timber resources is felled minimizing year by year though the forest reserves in implementing wildwood protected project, have progressively been accomplished by country, but the timber of felling, but do not accomplish effectively to take full advantage of, it is big that demand has appearred in timber resources, the problem that cost is high; The timber industry has selected for use some composite materials to replace timber resources at above-mentioned practical problem one after another, by facts have proved over several years, composite material such as density board, shaving board is not only non-watertight but also nail power for sleeping in is bad, especially door use is in public places filled with honeycomb paper in inside, is not broken exactly by the people in an unguarded moment lacquer painting is scratched; Steel door, steel timber are accidentally created the hole and are come, and have a strong impact on the attractive in appearance of PE; For example; The public place that school, hospital etc. are special, because the people of school is many, open frequency is high, and the student is just as the sun in morning eight, 9, and is vibrant, full of life and energy, bounces about, and fighting in jest or for fun is student's nature, therefore collides with, the scuffing rate is high; Hospital also is a place that working environment is more special, the nurse is pushing away the medicine car and is hitting friction with door knob everyday, hospital door collides with, scratches phenomenon and is seen everywhere, the engineers of industry has been taked safeguard measure again, often sticked corrosion resistant plate protected by the position that wound is hit at door, he does not only fundamentally solve impact resistance, scratch resistant problem, and corrosion resistant plate coming unglued in various degree phenomenon such as comes off in rapid succession after 1 year, loses elegant from angle attractive in appearance; Solid Door is the high also easy modification cracking of price not only.In sum, Solid Door one is resource-constrained, the 2nd, yielding cracking, the 3rd, cost is too high, reduce cost in order to economize on resources, the door that present China uses the public place, various raw material and the technology of employing all exist very serious problem, have brought great economic loss for country, the people, enterprise.
Veneer traditional drying method generally adopts air dry, drum-type drying dual mode.Tradition air dry method-veneer moisture content height, poor flatness; And drum-type drying method-veneer warpage modification serious cracking is difficult to ensure the quality of products
Summary of the invention
The utility model bumps wound, the too high problem of Solid Door cost at existing Men Bukang, and a kind of artificial rapid-result woods and two, three grades of materials such as discarded veneer of taking full advantage of are provided, and has saved resource, realize turning waste into wealth, strong protection the forest reserves; Reduced the cost of timber, improved the application life of timber greatly, anti-wound is hit degree, and surperficial scratch resistance degree is hit the public special-purpose door of scratch resistance thereby prolonged 5-10 in the application life anti-wound of environmental protection and energy saving high strength doubly.
Described purpose is achieved by the following scheme:
The anti-wound of a kind of environmental protection and energy saving high strength is hit the public special-purpose door of scratch resistance, its composition comprises: the multilayer flaggy, below the multilayer flaggy, all be connected solid wood flaggy or high density flaggy above the described multilayer flaggy, described solid wood flaggy or described high density flaggy connect melamine dipping lacquer ply of paper, and described melamine dipping lacquer ply of paper connects the alundum (Al top layer.
The anti-wound of described environmental protection and energy saving high strength is hit the public special-purpose door of scratch resistance, described multilayer flaggy comprises the central core veneer that cross grain is arranged, the intermediate layer veneer that connects vertical texture arrangement above the central core that described cross grain is arranged, below by glue-line simultaneously, the intermediate layer veneer that described vertical texture is arranged connects cross grain alignment layer veneer by glue-line, described cross grain alignment layer connects vertical texture alignment layer by glue-line, and described vertical texture alignment layer is connected with described cross grain alignment layer mutual superposition.
The beneficial effects of the utility model are:
Rapid-result woods that the utility model takes full advantage of artificial growth is as the Chinese parasol tree tree of limit, road willow and every place of the village, paulownia etc., change people and often use it for rudimentary purposes, not as fuel combustion, be made into veneer, use it for disposable uses such as external packing, construction formwork exactly, utilization rate is extremely low, has wasted the resource of timber greatly; Also taken full advantage of present plywood factory; veneer factory; composite board factory is in process; part two; three grades of veneers or veneer; because of became uneven; color exception; factors such as it is too much to scab; a part is used for the low disposable use of level plywood; a part is as the waste deposit corner; often worry because can not find customer resources at last; of long duration can moldy metamorphism; can only burn as burning material; not only pollute environment, also wasted timber resources greatly, improved raw-material cost; the application has utilized waste wood; it is turned waste into wealth, also reduced cost greatly, enlarged the competitiveness in market; save a large amount of timber forest reserves, protected ecological environment.
The utility model adopts the heat pressing type seasoning to carry out the dry planeness that ensures veneer, eliminate internal stress, the planeness of veneer and dry mass are one of key factors of composite board quality quality, and the heat pressing type seasoning has not only played effect dry and the pressing veneer and the more important thing is the effect of having played preliminary setting; The heat pressing type seasoning is far superior to the traditional drying method.
The utility model is selected uneven thickness for use, and it is many to scab, and blueness turns black, and core is done in the peeler core variable color, has saved raw material, has improved the utilization rate of timber.
The utlity model has good water resistance, the composite board after synthesizing boils through boiling water and did not come unglued in 32 hours, do not ftracture in 168 hours through cold water soak.
Pressure size during the HTHP typing that the utility model adopts is handled, the temperature height, time length, be directly connected to product quality, compression ratio has destroyed the fiber of timber with Wooden modifying optimization, has further strengthened the stability of timber, improved the density of timber, made composite board more solid.
The sheet material that the utility model is good with pressing is placed on the platform, leaves standstill and deposits about 25 days, has realized stable shaped purpose.
The utility model adopts alundum (Al to do the top layer, the wear-resisting tests that can bear 6000 commentaries on classics.The real core that base material is made by 100% plates of solid wood, thickness 30-50mm, this thickness are can twice synthetic effect better; The finish material alundum (Al is called diamond again, it has remedied the deficiency of the existing timber in public place, solved the problem of not environmental protection of timber, non-watertight, non-moistureproof, the nail property difference that crouches, this product has fundamentally solved the hole wound and has hit scratch resistant problem, has filled up technological gap of China.
The door that use the utility model is made and door are with respect to existing door, can reach the 5-10 effect doubly at least that increases the service life, the utility model will become the anti-wound of best environmental protection and energy saving high strength and hit the scratch resistance public door, quality is extremely stable, cheap, of many uses, be more conducive to applying of existing market.
Description of drawings
In order to be easy to explanation, the utility model is done to describe in detail by following specific embodiment and accompanying drawing.
Accompanying drawing 1 is flow chart of the present utility model.
Accompanying drawing 2 is composite board structure configuration maps of the present utility model.
Accompanying drawing 3 is multiple-plate exterior views of the present utility model.
Accompanying drawing 4 is multiple-plate cross-sectional drawings of the present utility model.
Accompanying drawing 5 is multiple-plate perpendicular profiles of the present utility model.
Accompanying drawing 6 is multiple-plate outside drawings of the present utility model.
Accompanying drawing 7 is surface structure schematic diagrames of the present utility model.
Accompanying drawing 8 is structural representations that have the plates of solid wood layer of the present utility model.
Accompanying drawing 9 is structural representations that have the high density flaggy of the present utility model.
The veneer 1 that vertical texture is arranged in the accompanying drawing, the veneer 2 that cross grain is arranged, alundum (Al layer 3, melamine layer 4, multilayer flaggy 5, plates of solid wood layer 6, high density flaggy 7, public special-purpose door 8.
The specific embodiment
Embodiment one
The anti-wound of a kind of environmental protection and energy saving high strength is hit the public special-purpose door of scratch resistance, and as shown in Figure 1, may further comprise the steps: this method comprised for four steps, and what first step making veneer was arranged in length and breadth carries out dry composite board with the heat pressing type seasoning; Second step was made the high strength scratch resistance facing plate that has the alundum (Al surface layer
The 3rd step was adopted the cold-hot-cold synthetic door-plate of heat pressing process and high strength scratch resistance facing plate; The 4th step sprayed or roller coat for the reveal limit.
Embodiment two
The difference of present embodiment and embodiment one is that the anti-wound of described environmental protection and energy saving high strength hits the public special-purpose door of scratch resistance, described making composite board comprises three process, first procedure softens processing with log earlier, with 1.5~3 atmospheric steam water is sprayed steaming then;
Second operation work is made veneer, with the log slicing or be peeled into veneer, at first log is stuck on slicer or the peeler, and adjustment thickness is 2mm, and log is cut into the 1.8-2mm veneer;
Three process is made the composite board that veneer is arranged in length and breadth.
Embodiment three
The difference of present embodiment and embodiment two is that the anti-wound of described environmental protection and energy saving high strength hits the public special-purpose door of scratch resistance, and shown in accompanying drawing 2, accompanying drawing 3, accompanying drawing 4, accompanying drawing 5, accompanying drawing 6, described three process is made the composite board that veneer is arranged in length and breadth,
The 1st step was carried out selection and the processing of veneer: at first veneer being classified is divided into superfine veneer, one-level veneer, secondary veneer, three grades of veneers: the superfine that will select, one-level veneer are used as panel and use, and secondary veneer, three grades of veneers are used as core;
What the 2nd step adopted is that the heat pressing type seasoning is carried out drying with veneer, described heat pressing type seasoning is to use multi-daylight press, earlier veneer is tiled in the hot press, pressure is adjusted into 0.1-1.9mpa after the pressurization of heating, temperature is adjusted into 80-120 ℃, pressing time is that 30-60 after second makes zero pressure, repeatedly 1-5 time with the control of the moisture content of veneer at 6-12 ﹪; Carry out jigsaw and repairing then, the grain direction picked out is done to cut edge for superfine, one-level veneer longitudinally handle, press composite board specification reservation surplus 50mm, be spliced into whole plate with sewing machine and make panel; Defective secondary veneer, three grades of veneers are done core through the veneer that repairing reaches technological standards requirement, fillet through after being spliced into whole plate;
The 3rd step was carried out gluing, and last deck panels and lower floor's panel are the reverse side uniform gluing, and middle veneer is two-sided uniform gluing; Environmental protection E0 level natural plant gum; The mass concentration of glue is 60-80%; Environmental protection E0 level natural plant gum is the green frog non-toxic herb glue that the biological Co., Ltd of the green frog in Shenzhen produces.
The 4th step adopted the mode of the symmetric arrays of the vertical texture stack of one deck one deck cross grain to lay glue-coated veneer, and the number of plies is that odd number is arranged, through the moulding of HTHP one step press;
The 5th step was put into hot press to glue-coated veneer with HTHP processings of finalizing the design, and first pressure was adjusted into 10-20kg/ ㎝ 2, and compression ratio is adjusted into 80-100%, and hot pressing time is 10-20 minute/㎝, and temperature is controlled at 110-115 ℃;
The 6th step was carried out the health Balance Treatment, and the sheet material that pressing is good is placed on the platform, leaves standstill and deposits 15-25 days;
The 7th step was dismissed four limits on demand;
The 8th step was carried out thick surely sanding, and preceding sand roller carries out sanding with 60# abrasive band, back sand roller with the 120# abrasive band and decides thick.
Embodiment four
The difference of present embodiment and embodiment three is that the anti-wound of described environmental protection and energy saving high strength hits the public special-purpose door of scratch resistance, as shown in Figure 6, the pressure of the hot press that described the 2nd step adopts is adjusted into 1mpa, and temperature is adjusted into 100 ℃, and the moisture content control of veneer is at 8 ﹪;
The mass concentration of described the 3rd step glue is 70%, and glue is natural plant gum (vegetable glue) or isocyanates (PMDI) or the phenolic resin glue (PF) of zero formaldehyde;
The pressure in described the 5th step is adjusted into 15kg/ ㎝ 2, and the pressure of high-quality veneer is adjusted into 4 kg/ ㎝ 2; Compression ratio is adjusted into 90%, and hot pressing time is 15 minutes/㎝, and temperature is controlled at 113 ℃;
The resting period of leaving standstill in described the 6th step is 20 days.
Embodiment five
The difference of present embodiment and embodiment two is that the anti-wound of described environmental protection and energy saving high strength hits the public special-purpose door of scratch resistance, it is when depositing below 0 ℃ that log in described first procedure is placed on outside temperature, earlier log is transported to indoor 25-35 ℃ of water logging bubble 6-10 hour, with 1.5~3 atmospheric steam water is sprayed steaming then again.
Embodiment six
The difference of present embodiment and embodiment one is that the anti-wound of described environmental protection and energy saving high strength hits the public special-purpose door of scratch resistance, shown in accompanying drawing 7, accompanying drawing 8, accompanying drawing 9, the superfine veneer that described second step making high strength scratch resistance facing plate will be selected or superfine composite board or E1 level high-density plate are done primer, described superfine veneer and described superfine composite board thickness are 2-5mm, described E1 level high-density plate thickness 2.5-5mm; Do intermediate layer material with 70-135 gram melamine dipping lacquer paper; Do skin-material with 18-45 gram alundum (Als; The primer, intermediate layer material, the skin-material that arrange are put into hot press, hot pressing temperature is adjusted into 50-135 ℃, adopt cold-hot-cold heat pressing process, hot plate temperature is lower than 50 ℃ when namely entering hot press, be warmed to 135 ℃ then, cool to 50 ℃ again, hot pressing time is adjusted into 2-3 minute, and pressure is adjusted into 14mpa.
Embodiment seven
The difference of present embodiment and embodiment one is that the anti-wound of described environmental protection and energy saving high strength hits the public special-purpose door of scratch resistance, described synthetic door-plate of the 3rd step and high strength scratch resistance facing plate are with the composite board double spread, high strength scratch resistance facing plate reverse side gluing, glue-coated composite board and high strength scratch resistance facing plate are put into hot press make door-plate, hot pressing temperature is adjusted into 50-100 ℃, adopt cold-hot-cold heat pressing process, hot pressing time is adjusted into 5-9 minute, and pressure is adjusted into 10mpa; Glue is environmental protection E0 level natural plant gum or melamine resin adehsive.
Embodiment eight
The difference of present embodiment and embodiment one is that the anti-wound of described environmental protection and energy saving high strength hits the public special-purpose door of scratch resistance, and as shown in Figure 7, described the 4th step sprays or roller coat for the reveal limit; The door-plate that will post the facing plate earlier keeps flat on vacuum spray limit machine or the roll coater, and adjusting ultraviolet light polymerization UV priming paint mass concentration is 98%, and it is consistent with panel to adjust ultraviolet light polymerization UV priming paint color, starts power supply, and ultraviolet photo-curing lamp automatic drying is handled; The sanding dedusting is topcoating then, the door-plate that the bottom surface has been sprayed priming paint is put in vacuum spray painting machine or the roll coater, and adjusting ultraviolet light polymerization UV finish paint lacquer mass concentration is 98%, and it is consistent with panel to adjust ultraviolet light polymerization UV finish paint color, start power supply, ultraviolet photo-curing lamp automatic drying is handled.
Embodiment nine
The difference of present embodiment and embodiment two is that the anti-wound of described environmental protection and energy saving high strength hits the public special-purpose door of scratch resistance, described making composite board comprises three process, first procedure softens processing with log earlier, with 1.5 or 2 or 2.5 or 3 atmospheric steam water is sprayed steaming then;
Second operation work is made veneer, with the log slicing or be peeled into veneer, at first log is stuck on slicer or the peeler, and adjustment thickness is 2mm, and log is cut into 1.8 or 1.9 or the 2mm veneer;
Three process is made the composite board that veneer is arranged in length and breadth.
Embodiment ten
The difference of present embodiment and embodiment three is that the anti-wound of described environmental protection and energy saving high strength hits the public special-purpose door of scratch resistance, and shown in accompanying drawing 2, accompanying drawing 3, accompanying drawing 4, accompanying drawing 5, accompanying drawing 6, described three process is made the composite board that veneer is arranged in length and breadth,
The 1st step was carried out selection and the processing of veneer: at first veneer being classified is divided into superfine veneer, one-level veneer, secondary veneer, three grades of veneers: the superfine that will select, one-level veneer are used as panel and use, and secondary veneer, three grades of veneers are used as core;
What the 2nd step adopted is that the heat pressing type seasoning is carried out drying with veneer, described heat pressing type seasoning is to use multi-daylight press, earlier veneer is tiled in the hot press, pressure is adjusted into 0.1 or 0.4 or 0.5 or 0.7 or 0.9 or 1.0 or 1.2 or 1.4 or 1.5 or 1.7 or 1.9mpa after the pressurization of heating, temperature is adjusted into 80 or 90 or 100 or 110 or 120 ℃, pressing time is after 30 or 40 or 50 or 60 seconds pressure to be made zero, repeatedly 1 or 2 or 3 or 4 or 5 time with the control of the moisture content of veneer at 6 or 7 or 8 or 9 or 10 or 11 or 12 ﹪; Carry out jigsaw and repairing then, the grain direction picked out is done to cut edge for superfine, one-level veneer longitudinally handle, press composite board specification reservation surplus 50mm, be spliced into whole plate with sewing machine and make panel; Defective secondary veneer, three grades of veneers are done core through the veneer that repairing reaches technological standards requirement, fillet through after being spliced into whole plate;
The 3rd step was carried out gluing, and last deck panels and lower floor's panel are the reverse side uniform gluing, and middle veneer is two-sided uniform gluing; Environmental protection E0 level natural plant gum; The mass concentration of glue is 60 or 65 or 70 or 75 or 80%;
The 4th step adopted the mode of the symmetric arrays of the vertical texture stack of one deck one deck cross grain to lay glue-coated veneer, and the number of plies is that odd number is arranged, through the moulding of HTHP one step press;
The 5th step is with the HTHP processing of finalizing the design, glue-coated veneer is put into hot press, earlier pressure is adjusted into 10 or 12 or 15 or 18 or 20kg/ ㎝ 2, compression ratio is adjusted into 80 or 85 or 90 or 95 or 100%, hot pressing time is 10 or 12 or 15 or 17 or 18 or 20 minutes/㎝, and temperature is controlled at 110 or 111 or 112 or 113 or 114 or 115 ℃;
The 6th step was carried out the health Balance Treatment, and the sheet material that pressing is good is placed on the platform, leaves standstill and deposits 15 or 16 or 17 or 18 or 19 or 20 or 21 or 22 or 23 or 24 or 25 days;
The 7th step was dismissed four limits on demand;
The 8th step was carried out thick surely sanding, and preceding sand roller carries out sanding with 60# abrasive band, back sand roller with the 120# abrasive band and decides thick.
Embodiment 11
The difference of present embodiment and embodiment five is that the anti-wound of described environmental protection and energy saving high strength hits the public special-purpose door of scratch resistance, it is when depositing below 0 ℃ that log in described first procedure is placed on outside temperature, earlier log is transported to indoor 25 or 26 or 27 or 28 or 29 or 30 or 31 or 32 or 33 or 34 or 35 ℃ of water loggings bubble 6 or 7 or 8 or 9 or 10 hours, with 1.5 or 2 or 2.5 or 3 atmospheric steam water is sprayed steaming then again.
Embodiment 12
The difference of present embodiment and embodiment six is that the anti-wound of described environmental protection and energy saving high strength hits the public special-purpose door of scratch resistance, shown in accompanying drawing 7, accompanying drawing 8, accompanying drawing 9, the superfine veneer that described second step making high strength scratch resistance facing plate will be selected or superfine composite board or E1 level high-density plate are done primer, described superfine veneer and described superfine composite board thickness are 2 or 3 or 4 or 5mm, described E1 level high-density plate thickness 2.5 or 3 or 3.5 or 4 or 4.5 or 5mm; Do intermediate layer material with 70 or 75 or 80 or 85 or 90 or 95 or 100 or 115 or 120 or 125 or 130 or 135 gram melamine dipping lacquer paper; Do skin-material with 18 or 20 or 24 or 27 or 30 or 32 or 35 or 38 or 40 or 42 or 44 or 45 gram alundum (Als; The primer, intermediate layer material, the skin-material that arrange are put into hot press, hot pressing temperature is adjusted into 50 or 60 or 70 or 80 or 90 or 100 or 110 or 120 or 125 or 130 or 135 ℃, adopt cold-hot-cold heat pressing process, hot plate temperature is lower than 50 ℃ when namely entering hot press, be warmed to 135 ℃ then, cool to 50 ℃ again, hot pressing time is adjusted into 2-3 minute, and pressure is adjusted into 14mpa.
Embodiment 13
The difference of present embodiment and embodiment seven is that the anti-wound of described environmental protection and energy saving high strength hits the public special-purpose door of scratch resistance, described synthetic door-plate of the 3rd step and high strength scratch resistance facing plate are with the composite board double spread, high strength scratch resistance facing plate reverse side gluing, glue-coated composite board and high strength scratch resistance facing plate are put into hot press make door-plate, hot pressing temperature is adjusted into 50 or 60 or 70 or 80 or 90 or 100 ℃, adopt cold-hot-cold heat pressing process, hot pressing time is adjusted into 5 or 6 or 7 or 8 or 9 minutes, and pressure is adjusted into 10mpa; Glue is environmental protection E0 level natural plant gum or melamine resin adehsive.
The hot pressing temperature of described claim 7 is adjusted into, and hot pressing time is adjusted into.
Embodiment 14
The anti-wound of a kind of environmental protection and energy saving high strength is hit the public special-purpose door of scratch resistance, shown in accompanying drawing 8, accompanying drawing 9, its composition comprises: multilayer flaggy 5, below the multilayer flaggy, all be connected solid wood flaggy 6 or high density flaggy 7 above the described multilayer flaggy, described solid wood flaggy or described high density flaggy connect melamine dipping lacquer ply of paper 4, and described melamine dipping lacquer ply of paper connects alundum (Al top layer 3.
Embodiment 15
The difference of present embodiment and embodiment 14 is that the anti-wound of described environmental protection and energy saving high strength hits the public special-purpose door of scratch resistance, as shown in Figure 2, described multilayer flaggy comprises the central core veneer 8 that cross grain is arranged, above the central core that described cross grain is arranged, connect the intermediate layer veneer 9 that vertical texture is arranged simultaneously below by glue-line, the intermediate layer veneer that described vertical texture is arranged connects cross grain alignment layer veneer 2 by glue-line, described cross grain alignment layer connects vertical texture alignment layer 1 by glue-line, and described vertical texture alignment layer is connected with described cross grain alignment layer mutual superposition.
The above only is the specific embodiment of the present utility model, but protection domain of the present utility model is not limited thereto, and any variation or replacement of expecting without creative work all should be encompassed within the protection domain of the present utility model.Therefore, protection domain of the present utility model should be as the criterion with the protection domain that claims were limited, and in addition, produces this patent infrastructure product with other glue classes, produces this patent infrastructure product with rotary cut venner, all within the protection domain of this patent.Doing this infrastructure product with other timber should be within the protection domain of this patent
Claims (2)
1. the anti-wound of environmental protection and energy saving high strength is hit the public special-purpose door of scratch resistance, its composition comprises: the multilayer flaggy, it is characterized in that below the multilayer flaggy, all being connected above the described multilayer flaggy solid wood flaggy or high density flaggy, described solid wood flaggy or described high density flaggy connect melamine dipping lacquer ply of paper, and described melamine dipping lacquer ply of paper connects the alundum (Al top layer.
2. the anti-wound of environmental protection and energy saving high strength according to claim 1 is hit the public special-purpose door of scratch resistance, it is characterized in that described multilayer flaggy comprises the central core veneer that cross grain is arranged, the intermediate layer veneer that connects vertical texture arrangement above the central core that described cross grain is arranged, below by glue-line simultaneously, the intermediate layer veneer that described vertical texture is arranged connects cross grain alignment layer veneer by glue-line, described cross grain alignment layer connects vertical texture alignment layer by glue-line, and described vertical texture alignment layer is connected with described cross grain alignment layer mutual superposition.