CN202968612U - Pure calcium/aluminum composite core-spun thread - Google Patents
Pure calcium/aluminum composite core-spun thread Download PDFInfo
- Publication number
- CN202968612U CN202968612U CN 201220578171 CN201220578171U CN202968612U CN 202968612 U CN202968612 U CN 202968612U CN 201220578171 CN201220578171 CN 201220578171 CN 201220578171 U CN201220578171 U CN 201220578171U CN 202968612 U CN202968612 U CN 202968612U
- Authority
- CN
- China
- Prior art keywords
- calcium
- pure
- composite core
- spun yarn
- aluminium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
Description
Claims (7)
- A kind of pure calcium/aluminium composite core-spun yarn, comprise: inner core is solid pure metal calcium silk or rod (1), skin is the steel belt layer (3) of middle layer outer cladding, it is characterized in that: inner core is solid pure metal calcium silk or rod (1) and outer for being coated with aluminum metal layer (2) between the steel belt layer (3) of middle layer outer cladding.
- (deletion)
- Pure calcium according to claim 1/aluminium composite core-spun yarn is characterized in that: the outside dimension of described pure calcium/aluminium composite core-spun yarn is 7mm~20mm.
- Pure calcium according to claim 1/aluminium composite core-spun yarn is characterized in that: the diameter of described calcium metal silk or rod is 5mm~15mm.
- Pure calcium according to claim 1/aluminium composite core-spun yarn is characterized in that: the granularity of aluminium powder or grain is 0~3mm.
- Pure calcium according to claim 1/aluminium composite core-spun yarn is characterized in that: the granularity of the mixture that is mixed by different ratios with other powder by aluminium powder or grain is 0~3mm.
- Pure calcium according to claim 1/aluminium composite core-spun yarn is characterized in that: al zone thickness is 1mm~15mm; Band can be rolled into aluminum pipe.