CN202846999U - Aluminum plate with simulated stainless steel wiredrawing coating - Google Patents
Aluminum plate with simulated stainless steel wiredrawing coating Download PDFInfo
- Publication number
- CN202846999U CN202846999U CN201220482477.4U CN201220482477U CN202846999U CN 202846999 U CN202846999 U CN 202846999U CN 201220482477 U CN201220482477 U CN 201220482477U CN 202846999 U CN202846999 U CN 202846999U
- Authority
- CN
- China
- Prior art keywords
- stainless steel
- aluminum alloy
- layer
- wire drawing
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Abstract
The utility model relates to an aluminum plate with a simulated stainless steel wiredrawing coating, belonging to the technical field of aluminum alloy as a standing timber. The aluminum alloy comprises an aluminum alloy substrate; a wiredrawing layer, a first passivation layer and a surface coating are sequentially arranged above the aluminum alloy substrate; a second passivation layer and a back paint layer are sequentially arranged below the aluminum alloy substrate; the upper surface of the surface coating is provided with a protective layer selected from any one of a fingerprint resistant layer, a polyethylene protective film and polyvinylchloride protective film; and the aluminum alloy substrate adopts an aluminum alloy plate which does not belong to the series 1 and is selected from any one of series 2, 3003, 3004, 5052, 5082, 5182, 5083, 5086, 5183 and 7075, wherein the strength of the aluminum alloy substrate is approach to that of stainless steel. The aluminum plate with the simulated stainless steel wiredrawing coating, provided by the utility model, overcomes the defects of single color and icy cold sensation of stainless steel, simultaneously has the effect of metal wiredrawing of the stainless steel and is high in strength and convenient to manufacture so as to be applied to the fields such as indoor decorative sheets, public houses, exhibition halls, household appliances, kitchen appliances (cupboards) and the like.
Description
Technical field
The utility model relates to a kind of artificial stainless steel wire drawing coating layer aluminium plate, belongs to construction timber aluminium alloy technical field.
Background technology
Existing stainless steel is because the nickel valency is unprecedented soaring, and the stainless steel price also has very large amount of increase in recent years.Use stainless steel to be raw material, cause the cost of material that produces household appliances sharply to rise, thereby cause the finished product price to be difficult to corresponding raising, and existing stainless steel surfaces treatment technology can only accomplish wire drawing, frosted finish effect the stainless steel true qualities or through the polishing, the pitch-dark expensive black titanium that makes of application, it is single, ice-cold that surface effect seems, the optional tone of client is restricted.And the coating alloy aluminium sheet is to build aviation, build one of material of the field extensive uses such as indoor and outdoor decoration, has intensity height, light specific gravity, aboundresources, low price, Never-rusty, antiacid alkaline-resisting, the advantage such as rich color is various.
Existing artificial stainless steel sheet material technology mainly adopts stamp, bonding and electrophoresis.What patent 200720103160.4 " a kind of anti-stainless steel toilet dividing plate " adopted is the artificial stainless steel aluminium sheet that surperficial wire drawing, UV coating are processed; What patent 201120457422.3 " PET-PET artificial stainless steel composite color plate " adopted is anti-al stainless steel composite membrane, comprises stamp dyed layer, two-layer PET rete, the first adhesive phase and wire drawing aluminium foil layer; What patent 200710063349.X " aluminum alloy material surface artificial stainless steel treatment surface technique " adopted is the techniques such as electrolytic degreasing, sulfuric acid embathe, electrophoretic coating.The technique that above-mentioned patent adopts obtains puts defective and the deficiencies such as bar section of stainless steel exists the too high unfavorable following process of case hardness, complex procedures, cost is expensive, fastness is not high, not environmental protection.
In order to address the above problem, this case produces thus.
The utility model content
The purpose of this utility model provides that a kind of cost is low, intensity is high, easy to process, artificial stainless steel wire drawing coating layer aluminium plate that color is various.
For achieving the above object, the technical scheme taked of the utility model is as follows:
Artificial stainless steel wire drawing coating layer aluminium plate comprises the alloy aluminum base material, and the top of alloy aluminum base material is followed successively by wire drawing layer, the first passivation layer and finishing coat, and the below is followed successively by the second passivation layer and back of the body enamelled coating.
For realizing better result of use, further arrange as follows:
Described finishing coat upper surface is provided with protective layer, and this protective layer is any in the layer of anti-fingerprint the, polyethylene protective film or the polyvinyl chloride diaphragm.
Described alloy aluminum base material be intensity near the alloy aluminium sheet of stainless non-1 series, i.e. a kind of in 2 series, 3003,3004,5052,5082,5182,5083,5086,5183 and 7075.
Operation principle of the present utility model and beneficial effect are as follows:
(1) artificial stainless steel wire drawing coating layer aluminium plate is not only similar in appearance, also will be in processed and applied near stainless requirement of strength, therefore in the utility model, alloy aluminum substrate selection intensity reaches or near the high-strength alloy aluminium sheet of stainless non-1 series, select 2 series of aluminium board such as high strength structure spare, in 3 series 3003,3004 are applied to air line and then select 7075 in 5052,5082,5182,5083,5086,5183 or 7 series in 5 series etc.;
(2) in order to overcome the defective that the stainless steel surfaces color is single, color and luster is ice-cold, the utility model is provided with coating, adopt the colourful transparent lacquer that the alloy aluminum substrate of selecting is applied, true qualities that not only can artificial stainless steel, the artificial stainless steel wire drawing coating layer aluminium plate of the colors such as the bronze of all right artificial stainless steel texture, silvery white, gold, color is various, but the diversified demand in satisfying the market and the field of use;
(3) artificial stainless steel wire drawing coating layer aluminium plate of the present utility model is except can be applicable to general building decoration, when also can be applicable to household electrical appliances and kitchen electricity industry, but when using and add some points with the kitchen electrical domain, satisfy the requirement that does not contain harmful element, in the manufacture process of whole artificial stainless steel wire drawing coating layer aluminium plate, all entering of similar harmful substance can not be arranged, need to adopt Chrome-free or nontoxic trivalent chromium pretreatment liquid in the pretreatment process, the colourful transparent lacquer need to have relevant detection and compulsory certificate etc.
Description of drawings
Fig. 1 is the structural representation of artificial stainless steel wire drawing coating layer aluminium plate in the utility model.
Number in the figure: 1, back of the body enamelled coating; 2, the second passivation layer; 3, alloy aluminum base material; 4, wire drawing layer; 5, the first passivation layer; 6, finishing coat; 7, protective layer.
The specific embodiment
The utility model artificial stainless steel wire drawing coating layer aluminium plate in conjunction with Fig. 1, comprises alloy aluminum base material 3, and (front) is followed successively by wire drawing layer 4, the first passivation layer 5 and finishing coat 6 above alloy aluminum base material 3; (back side) is followed successively by the second passivation layer 2 and back of the body enamelled coating 1 below the alloy aluminum base material 3.
Wherein, alloy aluminum base material 3 is the 3004H24 aluminium sheet, and the top of finishing coat 6 also comprises protective layer 7, and this protective layer 7 is polyethylene protective film.
The physical parameter of the alloy aluminum substrate of selecting in the utility model and conventional stainless performance parameter contrast are specifically referring to table 1.
The alloy aluminum substrate that adopts in table 1 present embodiment and stainless contrast
According to standard-required and the method for testing of " the common decoration composited aluminum and plastic decking of GB/T 22412-2008 " floating coat aluminium sheet, the performance of the artificial stainless steel wire drawing coating layer aluminium plate that present embodiment is made is tested, and the result is referring to table 2.
The performance parameter of table 2 artificial stainless steel wire drawing coating layer aluminium plate
The principle of present embodiment is identical with embodiment 1 with setting, and difference is: alloy aluminum base material 3 is the 5052H24 in aluminium 5 series, and protective layer 7 is polyethylene protective film.
The performance of the artificial stainless steel wire drawing coating layer aluminium plate that present embodiment is made according to embodiment 1 testing standard and method is tested, and the result is referring to table 3:
The performance parameter of table 3 embodiment 2 artificial stainless steel wire drawing coating layer aluminium plates
The principle of present embodiment is identical with embodiment 1 with setting, and difference is: alloy aluminum base material 3 is 7075 in aluminium 7 series, and protective layer 7 is the layer of anti-the fingerprint.
The performance of the artificial stainless steel wire drawing coating layer aluminium plate that present embodiment is made according to embodiment 1 testing standard and method is tested, and the result is referring to table 4.
The performance parameter of table 4 embodiment 3 artificial stainless steel wire drawing coating layer aluminium plates
Claims (5)
1. artificial stainless steel wire drawing coating layer aluminium plate comprises the alloy aluminum base material, it is characterized in that: the top of described alloy aluminum base material is followed successively by wire drawing layer, the first passivation layer and finishing coat, and the below is followed successively by the second passivation layer and back of the body enamelled coating.
2. artificial stainless steel wire drawing coating layer aluminium plate according to claim 1, it is characterized in that: described finishing coat upper surface is provided with protective layer.
3. artificial stainless steel wire drawing coating layer aluminium plate according to claim 2, it is characterized in that: described protective layer is any in the layer of anti-fingerprint the, polyethylene protective film or the polyvinyl chloride diaphragm.
4. artificial stainless steel wire drawing coating layer aluminium plate according to claim 1, it is characterized in that: described alloy aluminum base material is that intensity is near the alloy aluminium sheet of stainless non-1 series.
5. artificial stainless steel wire drawing coating layer aluminium plate according to claim 4 is characterized in that: described non-1 series alloy aluminium sheet is a kind of in 2 series, 3003,3004,5052,5082,5182,5083,5086,5183 and 7075.