CN202808920U - Solder splash reducing mechanism - Google Patents
Solder splash reducing mechanism Download PDFInfo
- Publication number
- CN202808920U CN202808920U CN2012203435548U CN201220343554U CN202808920U CN 202808920 U CN202808920 U CN 202808920U CN 2012203435548 U CN2012203435548 U CN 2012203435548U CN 201220343554 U CN201220343554 U CN 201220343554U CN 202808920 U CN202808920 U CN 202808920U
- Authority
- CN
- China
- Prior art keywords
- tin
- slag reduction
- melting furnace
- reduction according
- solder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model discloses a solder splash reducing mechanism, comprising a solder melting furnace which is arranged on a working platform, and further comprising a purifying boiler which is communicated with the bottom of the solder melting furnace and is used for collecting the molten solder, and a control box for controlling the melting temperature of the solder melting furnace, wherein the communicating pipe is a metal piece; and the bottom of the solder melting furnace conducts upwards until the sidewall of the purifying boiler. The solder splash reducing mechanism disclosed by the utility model has an advantage of completely separating the molten solder and the solder liquid.
Description
Technical field
The utility model relates to the scruff process field, is specially a kind of tin slag reduction mechanism.
Background technology
Scolding tin is in melted state during wave soldering, the oxidation that it is surperficial and to generate some residues with other metallic element (mainly being Cu) effect all be inevitably also is vital but rationally correctly use Wave soldering apparatus and clear up in time for the minimizing scruff.
The stanniferous amount of scruff itself is higher, and utilizing tin slag reduction mechanism to be recycled also is that people are for the selecting properly of recycling economy.
But in the process of molten tin, the impurity such as useless ash and rosin often are mixed in the tin liquor in the scruff, and how separating impurity and tin liquor have been separated into people's problem.
The utility model content
For solving above problem, the utility model provides a kind of molten tin and the distinct tin slag reduction of tin liquor energy mechanism.
The utility model provides a kind of tin slag reduction mechanism, comprise the tin melting furnace that is installed on the worktable, tin slag reduction mechanism also comprises with described tin melting furnace by the purification pot that is used for the molten tin of collection that is communicated with communicating pipe and the controlling box that the melt temperature of described tin melting furnace and purification pot is controlled, described communicating pipe is metalwork, and the tin melting furnace bottom makes progress conducting to the sidewall that purifies pot.
In tin slag reduction described in the utility model mechanism, the tin bar shaping mould is set also on the described worktable.
In tin slag reduction described in the utility model mechanism, produce the smoke collection cover of waste gas when being provided for collecting the melting block tin on the described tin melting furnace.
In tin slag reduction described in the utility model mechanism, described smoke collection cover is cylindrical.
In tin slag reduction described in the utility model mechanism, described smoke collection cover has multi-layered filtering element and activated carbon layer.
In tin slag reduction described in the utility model mechanism, be provided for stirring the impeller of scruff in the described tin melting furnace.
In tin slag reduction described in the utility model mechanism, described tin slag reduction mechanism also comprises motor, and described impeller is connected in described motor, and described motor can carry out lifting/lowering with described impeller.
In tin slag reduction described in the utility model mechanism, be provided for cooling off the cooling water tank of molten tin under the described tin bar shaping mould.
In tin slag reduction described in the utility model mechanism, the melt temperature of described tin melting furnace is 320 ℃, and the melt temperature that purifies pot is 270 ℃.
The utility model provides tin slag reduction mechanism, has following beneficial effect:
1, simple to operate:
2, molten tin can separate fully with tin liquor.
Description of drawings
In order to be illustrated more clearly in the utility model embodiment or technical scheme of the prior art, the below will do to introduce simply to the accompanying drawing of required use in embodiment or the description of the Prior Art, apparently, accompanying drawing in the following describes only is embodiment more of the present utility model, for those of ordinary skills, under the prerequisite of not paying creative work, can also obtain according to these accompanying drawings other accompanying drawing.
Fig. 1 is the structural representation of a kind of tin slag reduction of the utility model mechanism;
Fig. 2 is the sectional view on the A-A direction among this Fig. 1;
Fig. 3 is the stereographic map of a kind of tin slag reduction of the utility model mechanism.
Embodiment
Can further understand the utility model by specific embodiment of the utility model given below, but they not to restriction of the present utility model.Some nonessential improvement and adjustment for those skilled in the art does according to above-mentioned utility model content also are considered as dropping in the protection domain of the present utility model.
See also Fig. 1, Fig. 2, Fig. 3, a kind of tin slag reduction mechanism, comprise the tin melting furnace 2 that is installed on the worktable 1, tin slag reduction mechanism also comprises the purification pot 3 that is used for the molten tin of collection that is communicated with tin melting furnace 1 bottom and the controlling box 4 that tin melting furnace 1 melt temperature is controlled.
Tin melting furnace 1 bottom with by communicating pipe 31 with purify pot 3 and be connected, communicating pipe 31 be metalwork, tin melting furnace 1 bottom makes progress conducting to the sidewall that purifies pots 3.
The benefit of doing like this is: tin liquor can be overflow from tin melting furnace 1 bottom to purifying pot 3, melts tin and tin liquor thereby can all separate, and for the impurity such as useless ash and rosin in the scruff, can float over tin melting furnace 1 tin liquor surface, by manually scooping out to residual slag receiving tank 9.
It is good that the junction of communicating pipe 31 and purification pot 3 is positioned at 1/3 to 4/5 of purification pot 3 body walls.
Tin bar shaping mould 5 also is set on the worktable 1.
Produce the smoke collection cover 6 of waste gas when being provided for collecting the melting block tin on the tin melting furnace 2.
Adopt round shape not only can take full advantage of the space, and can allow waste gas and multi-layered filtering element and activated carbon layer fully be discharged from the air outlet of smoke collection cover 6 after the absorption, filter core can adopt polyester cotton.
Be provided for stirring the impeller 21 of scruff in the tin melting furnace 2, tin slag reduction mechanism also comprises motor, and impeller is connected in described motor, and motor can carry out lifting/lowering with impeller.
The tin bar shaping mould is provided for cooling off the cooling water tank 7 of molten tin for 5 times.
The working process of this tin slag reduction mechanism is: scruff is put in the solder pot 1 each input amount 200～500KG.Then, with its intensification, temperature is controlled at 320 ℃ by controlling box 4, simultaneously, will purify pot 3 temperature controls and open, and its temperature is controlled at 270 ℃.
When the temperature of solder pot 1 is raised to 220 ℃, again the ratio of solubility promoter in 30:1 dropped into.After scruff melts fully, will open for the impeller 21 that stirs, and by lift motor it be dropped to the restriction position.
At the uniform velocity stir by impeller 21, make scruff, fusing assistant fully mixes, stir about 40 minutes, tin liquor in the scruff can be separated fully, and purifies after the pot 3 by flowing to communicating pipe, carries out moulding with spoonful it being scooped out tin bar shaping mould 5, need open cooling during moulding, the temperature of tin bar is descended rapidly.After tin liquor was solidified fully, the handle by tin bar shaping mould 5 ejects it had namely finished once shaped.Every mold forming tin bar weight is 10～12KG approximately.
This tin slag reduction mechanism adopts the 3+1 pattern, i.e. scruff melting, change agent separation, tin bar shaping+smoke treated.
Simultaneously, scruff melting, change agent separation and tin bar are shaped and adopt integral structure, smoke treated to adopt the garden tubular to cross the filter core design, have efficient obstruct flue dust and the effect of effectively eliminating peculiar smell, and its ability can reach the national requirements for environmental protection of PM2.5 fully.
The utility model provides tin slag reduction mechanism, has following beneficial effect:
1, simple to operate:
2, molten tin can separate fully with tin liquor;
The above only is preferred embodiment of the present utility model; not in order to limit the utility model; all within spirit of the present utility model and principle, any modification of doing, be equal to replacement, improvement etc., all should be included within the protection domain of the present utility model.
Claims (9)
1. tin slag reduction mechanism, comprise the tin melting furnace that is installed on the worktable, it is characterized in that: tin slag reduction mechanism also comprises with described tin melting furnace by the purification pot that is used for the molten tin of collection that is communicated with communicating pipe and the controlling box that the melt temperature of described tin melting furnace and purification pot is controlled, described communicating pipe is metalwork, and the tin melting furnace bottom makes progress conducting to the sidewall that purifies pot.
2. tin slag reduction according to claim 1 mechanism is characterized in that, the tin bar shaping mould also is set on the described worktable.
3. tin slag reduction according to claim 1 mechanism is characterized in that: the smoke collection cover that produces waste gas when being provided for collecting the melting block tin on the described tin melting furnace.
4. tin slag reduction according to claim 3 mechanism, it is characterized in that: described smoke collection cover is cylindrical.
5. tin slag reduction according to claim 3 mechanism, it is characterized in that: described smoke collection cover has multi-layered filtering element and activated carbon layer.
6. tin slag reduction according to claim 1 mechanism is characterized in that, is provided for stirring the impeller of scruff in the described tin melting furnace.
7. tin slag reduction according to claim 6 mechanism is characterized in that, described tin slag reduction mechanism also comprises motor, and described impeller is connected in described motor, and described motor can carry out lifting/lowering with described impeller.
8. tin slag reduction according to claim 2 mechanism is characterized in that, is provided for cooling off the cooling water tank of molten tin under the described tin bar shaping mould.
9. tin slag reduction according to claim 1 mechanism is characterized in that the melt temperature of described tin melting furnace is 320 ℃, and the melt temperature that purifies pot is 270 ℃.