CN202640873U - Metal workpiece with composite ceramic membrane - Google Patents
Metal workpiece with composite ceramic membrane Download PDFInfo
- Publication number
- CN202640873U CN202640873U CN 201120493307 CN201120493307U CN202640873U CN 202640873 U CN202640873 U CN 202640873U CN 201120493307 CN201120493307 CN 201120493307 CN 201120493307 U CN201120493307 U CN 201120493307U CN 202640873 U CN202640873 U CN 202640873U
- Authority
- CN
- China
- Prior art keywords
- composite ceramic
- ceramic membrane
- metal workpiece
- metal works
- composite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Abstract
The utility model relates to a metal workpiece with a composite ceramic membrane which comprises a metal workpiece body, and a composite ceramic membrane is coated on the metal workpiece body. The composite ceramic membrane comprises a five-element composite alloy film at the bottom layer and a two-element alloy film or a graphite film at the surface layer. The ceramic metal composite membrane has good wear resistance and corrosion resistance properties. By using the metal workpiece with the composite ceramic membrane, the service life of the metal workpiece can be greatly improved, therefore reducing the cost of workpiece replacement. The composite ceramic membrane can be used in surface treatment for tools, cutters, dies and mechanical components with high demand for wear resistance, especially for the stiffening and anticorrosion treatment for the injection machine screw surface.
Description
Technical field
The utility model relates to a kind of metal works, especially a kind of metal works with composite ceramic film.
Background technology
It is very extensive that metal works is used, but some metal works is applied in some special environment, is subject to for a long time friction and the serious corrosion of working environment of work particular interface, tested greatly wearability and the corrosion resistance of workpiece.
Adopt the water power plating to process such as existing screw in injection molding machine surface, not only easy weighting ring environment pollution, and this screw rod corrodes when pressure injection Halogen material easily, and weares and teares easily when pressure injection adds glass 20%～60% material more.
The utility model content
The purpose of this utility model is to provide a kind of metal works with composite ceramic film, can improve greatly the wear-resisting and decay resistance of metal works.
The utility model is achieved through the following technical solutions: the metal works with composite ceramic film comprises: the metal works body is compounded with one deck composite ceramic film on the described metal works body; Described composite ceramic film comprises the five elements alloy rete of bottom and Was Used alloy rete or the graphite rete of surface layer; Described five elements alloy rete is produced by nickel chromium triangle aluminium titanium yttrium alloy target, and nickel chromium triangle aluminium titanium yttrium alloy target comprises: titanium 1～5%, yttrium 0.1～2%, aluminium 1～5%, chromium 30～50%, nickel are surplus; Described Was Used alloy rete is produced by the aluminum titanium alloy target, and the aluminum titanium alloy target comprises: titanium 20～50%, aluminium 50～80%.
This metal ceramic composite membrane has good wearability and corrosion resistance.The utility model can increase substantially the service life of metal works, reduces the cost of changing workpiece.The surface treatment that can be applied to instrument, cutter, mould and high abrasion requirement component of machine is arranged.Relate in particular to screw in injection molding machine surface stiffened, anti-corrosion treatment.
Description of drawings
Fig. 1 is the structural representation of the utility model embodiment.
Fig. 2 is composite ceramic film structural representation among the utility model embodiment two.
Fig. 3 is composite ceramic film structural representation among the utility model embodiment three.
Among the figure: 1, metal works body; 2, composite ceramic film; 3, nickel chromium triangle aluminium titanium yttrium alloy target; 4, graphite target; 5, aluminum titanium alloy target.
The specific embodiment
Below in conjunction with drawings and Examples the utility model technology is described further.
Embodiment one
With reference to shown in Figure 1, the metal works with composite ceramic film comprises: metal works body 1 is compounded with one deck composite ceramic film 2 on the described metal works body 1.
Embodiment two
With reference to shown in Figure 1, the metal works with composite ceramic film comprises: metal works body 1 is compounded with one deck composite ceramic film 2 on the described metal works body 1.
With reference to shown in Figure 2, described composite ceramic film comprises the nickel chromium triangle aluminium titanium yttrium alloy target 3 of bottom and the graphite target 4 of surface layer.Nickel chromium triangle aluminium titanium yttrium alloy target in the present embodiment comprises: titanium 5%, yttrium 1%, aluminium 5%, chromium 50%, nickel 39%.
Embodiment three
With reference to shown in Figure 1, the metal works with composite ceramic film comprises: metal works body 1 is compounded with one deck composite ceramic film 2 on the described metal works body 1.
With reference to shown in Figure 3, described composite ceramic film comprises the nickel chromium triangle aluminium titanium yttrium alloy target 3 of bottom and the aluminum titanium alloy target 5 of surface layer.Nickel chromium triangle aluminium titanium yttrium alloy target in the present embodiment comprises: titanium 5%, yttrium 1%, aluminium 5%, chromium 50%, nickel 39%.
Described aluminum titanium alloy target 5 comprises: titanium 20, aluminium 80%.
Learn that according to above three embodiment the utility model is by can greatly improving wearability and the corrosion resistance of metal works body 1 after being compounded with composite ceramic film 2 at metal works body 1.
The according to the above description announcement of book and guidance, the utility model those skilled in the art can also carry out suitable change and modification to above-mentioned embodiment.Therefore, the specific embodiment that discloses and describe above the utility model is not limited to also should fall in the protection domain of claim of the present utility model modifications and changes more of the present utility model.In addition, although used some specific terms in this specification, these terms do not consist of any restriction to the utility model just for convenience of description.
Claims (1)
1. with the metal works of composite ceramic film, comprise: the metal works body, it is characterized in that: be compounded with one deck composite ceramic film on the described metal works body, described composite ceramic film comprises the five elements alloy rete of bottom and Was Used alloy rete or the graphite rete of surface layer.