CN202246928U - Compound positive plate - Google Patents
Compound positive plate Download PDFInfo
- Publication number
- CN202246928U CN202246928U CN2011203414161U CN201120341416U CN202246928U CN 202246928 U CN202246928 U CN 202246928U CN 2011203414161 U CN2011203414161 U CN 2011203414161U CN 201120341416 U CN201120341416 U CN 201120341416U CN 202246928 U CN202246928 U CN 202246928U
- Authority
- CN
- China
- Prior art keywords
- copper
- anode plate
- composite anode
- plumbous
- conducting beam
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model discloses a compound positive plate, which includes a copper conductive beam and a copper plate, wherein the copper plate is 0.5 to 5.0mm in thickness, 120 to 2000mm in length and 90 to 1000mm in width; pure lead with the thickness of 1 to 5mm is covered outside the copper plate; 10 to 200mm of the upper end of the copper plate is exposed; and a compound bar is arranged in the copper conductive beam. By additionally arranging the compound bar in the copper conductive beam, the mechanical strength of the copper conductive beam is enhanced, so as to prevent the copper conductive beam from being easily bent, and prolong the service life of the compound positive plate.
Description
Technical field:
The utility model relates to the electrolysis tech field, particularly relates to a kind of composite anode plate with high conduction performance.
Background technology:
For many years, the investigator attempted graphite, Z 250, Manganse Dioxide, plumbic oxide and titanium alloy etc materials both at home and abroad, and there is variety of issue technically in the result, fails to be applied to industrial practice.Therefore if can solve than great, intensity is low, the problem of poorly conductive, LY should be best suited for doing the metal of positive plate.
For example application number is 200720104834.2, and publication number is that " lead-copper composite anode plate discloses a kind of lead-copper composite anode plate; comprise that thickness is 0.5-5.0MM; length is 120-2000MM, and width is the copper coin of 90-1000MM, copper coin outer wrap thickness is pure lead of 1-5MM or pb-ag alloy; the exposed 10-200MM in copper coin upper end, and copper coin upper end exposed part has a copper conducting beam for 201116309 Chinese patent.In the middle of the copper coin uniform distribution perforate can be arranged.The composition of copper coin can be fine copper or red copper or brass or bronze.Pb-ag alloy can be for by weight: silver-colored 0.1-0.5%, all the other are plumbous.But this utility model is owing to copper conducting beam insufficient strength, and crooked easily, work-ing life is short.
The utility model content:
The purpose of the utility model is to overcome the problems referred to above that composite anode plate exists in the prior art, proposes a kind of composite anode plate.The utility model is set up a compound bar through being employed in the copper conducting beam, increased the physical strength of copper conducting beam, has played the phenomenon that prevents that copper conducting beam is crooked easily, the effect that has prolonged the life-span of composite anode plate.
The utility model adopts following technical scheme to realize:
A kind of composite anode plate comprises copper conducting beam and copper coin, and said copper plate thickness is 0.5-5.0mm, and length is 120-2000mm, and width is 90-1000mm; Said copper coin outer wrap thickness is the pure lead of 1-5mm, and the exposed 10-200mm in said copper coin upper end is characterized in that: be provided with compound bar in the said copper conducting beam.
Said compound bar is excellent core with rod iron.
Said rod iron outside surface cold drawing coats copper sheathing.
The cold drawing coating is plumbous again on the said copper sheathing overlaps.
Said copper sheathing adopts soldering with plumbous cover end face.
The utility model compared with prior art, its advantage is:
The utility model adopts in the copper conducting beam and is provided with compound bar; Compound bar is excellent core with rod iron, and rod iron coats copper sheathing and plumbous cover outward successively, has played the phenomenon that prevents that copper conducting beam is crooked easily; The physical strength copper sheathing that has increased copper conducting beam adopts soldering with plumbous cover end face; The brazed joint place is smooth, the coefficient of can reducing friction, the effect that has prolonged the life-span of composite anode plate.
Description of drawings:
Fig. 1 is the utility model structural representation
Fig. 2 is the utility model sectional view figure
Mark among the figure: 1, copper coin, 2, pure lead, 3, copper conducting beam, 4, compound bar.
Embodiment:
Embodiment 1:
A kind of composite anode plate comprises copper conducting beam 3 and copper coin 1, and said copper coin 1 thickness is 0.5mm, and length is 120mm, and width is 90mm; Said copper coin 1 outer wrap thickness is pure plumbous 2 of 1mm; Said copper coin 1 upper end exposes 10mm; Be provided with compound bar 4 in the said copper conducting beam 3, said compound bar 4 is excellent core with rod iron, and the cold drawing of rod iron outside surface coats copper sheathing; The cold drawing coating is plumbous again on the copper sheathing overlaps, and copper sheathing adopts soldering with the plumbous end face that overlaps.
Embodiment 2:
A kind of composite anode plate comprises copper conducting beam 3 and copper coin 1, and said copper coin 1 thickness is 2mm, and length is 1010mm, and width is 650mm; Said copper coin 1 outer wrap thickness is pure plumbous 2 of 3mm; Said copper coin 1 upper end exposes 80mm; Be provided with compound bar 4 in the said copper conducting beam 3, said compound bar 4 is excellent core with rod iron, and the cold drawing of rod iron outside surface coats copper sheathing; The cold drawing coating is plumbous again on the copper sheathing overlaps, and copper sheathing adopts soldering with the plumbous end face that overlaps.
Embodiment 3:
A kind of composite anode plate comprises copper conducting beam 3 and copper coin 1, and said copper coin 1 thickness is 5mm, and length is 2000mm, and width is 1000mm; Said copper coin 1 outer wrap thickness is pure plumbous 2 of 5mm; Said copper coin 1 upper end exposes 200mm; Be provided with compound bar 4 in the said copper conducting beam 3, said compound bar 4 is excellent core with rod iron, and the cold drawing of rod iron outside surface coats copper sheathing; The cold drawing coating is plumbous again on the copper sheathing overlaps, and copper sheathing adopts soldering with the plumbous end face that overlaps.
Claims (5)
1. a composite anode plate comprises copper conducting beam (3) and copper coin (1), and said copper plate thickness is 0.5-5.0mm, and length is 120-2000mm, and width is 90-1000mm; Said copper coin (1) outer wrap thickness is the pure lead (2) of 1-5mm, and the exposed 10-200mm in said copper coin (1) upper end is characterized in that: be provided with compound bar (4) in the said copper conducting beam (3).
2. a kind of composite anode plate according to claim 1 is characterized in that: said compound bar (4) is excellent core with rod iron.
3. a kind of composite anode plate according to claim 2 is characterized in that: said rod iron outside surface cold drawing coats copper sheathing.
4. a kind of composite anode plate according to claim 3 is characterized in that: the cold drawing coating is plumbous again on the said copper sheathing overlaps.
5. a kind of composite anode plate according to claim 4 is characterized in that: said copper sheathing adopts soldering with plumbous cover end face.