CN202116587U - 一种铝包铁脱氧块 - Google Patents
一种铝包铁脱氧块 Download PDFInfo
- Publication number
- CN202116587U CN202116587U CN2011202115694U CN201120211569U CN202116587U CN 202116587 U CN202116587 U CN 202116587U CN 2011202115694 U CN2011202115694 U CN 2011202115694U CN 201120211569 U CN201120211569 U CN 201120211569U CN 202116587 U CN202116587 U CN 202116587U
- Authority
- CN
- China
- Prior art keywords
- aluminium
- deoxidizing
- block
- shaped block
- iron
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
一种铝包铁脱氧块，其特征在于，包括有一圆台形块体，所述圆台形块体内部设有铁芯，铁芯外部包有铝皮，所述圆台形块体的对角线长度为105.5mm～115.5mm，所述圆台形块体的厚度为50mm～60mm。这种铝包铁脱氧块在使用时，与钢水的接触面积大，可加快脱氧块的熔化，在钢水中均匀扩散，有利于钢水的脱氧反应进程。
Description
技术领域
本实用新型涉及一种铝包铁脱氧块。
背景技术
铝材的生产和使用过程中可产生数目可观的废旧铝，炼钢铝锭标准规定的铝含量低于原生铝锭的铝含量，因此可利用废旧铝材制作炼钢脱氧剂，对废旧铝进行再生利用，具有十分重要的意义。
炼钢用脱氧剂的主要作用是与铁水中溶解的氧反应，主要生成非金属化合物，形成沉淀上浮至渣层中，加以除去即可得纯净的铁水。铝在炼钢工艺中可作为脱氧剂、晶粒细化剂及合金添加剂，其应用形式是铝线(喂线法)、小铝锭、铝环、铝饼(投入法)、铝丸、铝弹(发射法)、铝铁块、铝硅钡铁块(复合脱氧法)等。现有铝线一般是电缆厂利用原生铝锭采取熔炼、挤压或轧制工艺生产的，脱氧铝锭、铝环和铝饼是钢厂利用等外原生铝锭制作的，铝硅铁和铝钡铁是利用矿热炉生产的。
实用新型内容
本实用新型的目的是提供一种铝包铁脱氧块。
本实用新型为解决其技术问题所采用的技术方案是，
一种铝包铁脱氧块，其特征在于，包括有一圆台形块体，所述圆台形块体内部设有铁芯，铁芯外部包有铝皮，所述圆台形块体的对角线长度为105.5mm～115.5mm，所述圆台形块体的厚度为50mm～60mm。
本实用新型的有益效果是，这种铝包铁脱氧块在使用时，与钢水的接触面积大，可加快脱氧块的熔化，在钢水中均匀扩散，有利于钢水的脱氧反应进程。
附图说明
图1是本实用新型提出的铝包铁脱氧块的结构示意图。
具体实施方式
为了使本实用新型实现的技术手段、创作特征、达成目的与功效易于明白了解，下面结合图示与具体实施例，进一步阐述本实用新型。
如图1所示，本实用新型提出的铝包铁脱氧块包括有一圆台形块体100，所述圆台形块体100内部设有铁芯，铁芯外部包有铝皮，所述圆台形块体100的对角线长度为105.5mm～115.5mm，所述圆台形块体的厚度为50mm～60mm，每个圆台形块体的重量为0.8～1.2kg。
这种铝包铁脱氧块在使用时，与钢水的接触面积大，可加快脱氧块的熔化，在钢水中均匀扩散，有利于钢水的脱氧反应进程。
以上显示和描述了本实用新型的基本原理、主要特征和本实用新型的优点。本行业的技术人员应该了解，本实用新型不受上述实施例的限制，上述实施例和说明书中描述的只是说明本实用新型的原理，在不脱离本实用新型精神和范围的前提下本实用新型还会有各种变化和改进，这些变化和改进都落入要求保护的本实用新型范围内。本实用新型要求保护范围由所附的权利要求书及其等同物界定。
Claims (1)
1.一种铝包铁脱氧块，其特征在于，包括有一圆台形块体，所述圆台形块体内部设有铁芯，铁芯外部包有铝皮，所述圆台形块体的对角线长度为105.5mm～115.5mm，所述圆台形块体的厚度为50mm～60mm。