Abstract

The utility model discloses a titanium-plated stainless steel metal photo, which aims to provide the titanium-plated stainless steel metal photo which is suitable for storage for a long time. The titanium-plated stainless steel metal photo comprises a stainless steel layer and a titanium metal layer which are stacked from inside to outside, and a photo image is graved on the face of the photo, on which the titanium metal layer is located. The titanium-plated stainless steel metal photo disclosed by the utility model can be used for manufacturing digital photos so as to replace the traditional digital photos developed and printed on photographic paper.

Description

A kind of titanizing stainless steel metal photograph

Technical field

The utility model relates to a kind of photograph, especially relates to a kind of metal photograph that can preserve for a long time.

Background technology

Existing general photograph all is image to be developed and printed on printing paper or canvas through developing and printing mode, these photographs are after after a while, and the image color and luster can fade because of the light irradiation, and printing paper also can, flavescence mouldy because of wet weather, even might be damaged by worms, thereby can not preserve for a long time.

Therefore, how a kind of photograph that can preserve for a long time of development and Design has become the technical problem of being badly in need of solution.

The utility model content

The utility model provides a kind of titanizing stainless steel metal photograph in order to solve the technical problem that the prior art photograph can't be preserved for a long time.

For solving the problems of the technologies described above, the technical solution adopted in the utility model is a kind of titanizing stainless steel metal photograph of design, and described photograph comprises stacked from the inside to the outside stainless steel layer and titanium coating, and described photograph is carved with the photomap picture at titanium coating place face.

Described titanium coating vacuum plating is on the stainless steel layer surface.

The outermost layer of described photograph also electrophoresis has an electrophoretic paint layer.

The utility model is by electroplating titanium coating at stainless steel surfaces, then at titanium coating place face engraving photomap picture, thereby make photograph mouldy, flavescence can not occur or situation such as damaged by worms, and is more suitable for long-time preservation compared to existing technology.

Description of drawings

Below in conjunction with embodiment and accompanying drawing the utility model is elaborated, wherein:

Fig. 1 is the structural representation of the utility model titanizing stainless steel metal photograph;

Fig. 2 is the making flow chart of the utility model titanizing stainless steel metal photograph.

The specific embodiment

See also Fig. 1.Fig. 1 is the generalized section of the utility model titanizing stainless steel metal photograph.Titanizing stainless steel metal photograph comprises stacked from the inside to the outside stainless steel layer 1, titanium coating 2 and electrophoretic paint layer 3.Titanium coating 2 adopts the mode of vacuum plating to be plated on the stainless steel layer 1.Photograph is carved with photomap as 4 at titanium coating place face, and described titanium coating comprises ground floor titanium 21 and the second layer titanium 22 different with ground floor titanium color.Certainly, also can use the electrophoretic paint replacement second layer titanium 22 different with ground floor titanium color.Electrophoretic paint layer 3 is arranged on the outermost layer of photograph, is used for to photomap as painted and protection stainless steel and titanium coating is not oxidized.

This specific embodiment only shows the embodiment at an electroplating surface titanium of stainless steel; certainly, also can all plate titanium, form titanium coating at stainless all faces; and outside all titanium coatings equal electrophoresis electrophoretic paint layers 3, to protect whole photograph not oxidized.

See also Fig. 2.The preparation method of the utility model titanizing stainless steel metal photograph is as follows:

1,, makes surperficial grit blasting and handle to cutting or the stainless steel substrates of drawing

The purpose that grit blasting is handled is more firm the combining with stainless steel substrates of titanium in order to make plating.

The preferred stainless steel substrates model of this specific embodiment: 304; Thickness: 1mm; Steel sand model: No. zero sand.

2, with the vacuum plating technology, at steel disc electroplating surface ground floor titanium

The technological parameter of vacuum plating is: the process time: 3～6 hours; Coating layer thickness: 0.3～5um; Processing temperature: 180 ℃～250 ℃.

3,, on the ground floor titanium, electroplate and the different second layer titanium of ground floor titanium color with the vacuum plating technology

4, in the electrophoresis mode electrophoretic paint attached on the steel disc that has plated titanium, and Fang Ru oven oven dry and solidifying

The technological parameter of electrophoresis electrophoretic paint is: fluid temperature: 25～40 ℃, and voltage: 30～35V; Electrophoresis time: 15～25 seconds; The preliminary drying time: 10～20 minutes; Preliminary drying temperature: 50～70 ℃; Hardening time: 20～40 minutes; Solidification temperature: 160～180 ℃.

5, with laser engraving machine the photomap picture of putting computer in advance into, engraving is in the titanium coating of photograph institute on the whole

The laser engraving technological parameter is: brightness: 0; Contrast: 0; Resolution ratio: 240; Laser pass: 0 time; Pin certainty ratio: be; Pass: 1 time; Power: 85%; The mark frequency: 50,000Hz; Sweep speed: 1,000; Number of times: 1; Pixel postpones: 30.

6, in the electrophoresis mode electrophoretic paint attached to the photograph surface, and Fang Ru oven oven dry and solidifying, thus finish the making of photograph.

The technological parameter of electrophoresis electrophoretic paint is: fluid temperature: 30～40 ℃, and voltage: 30～35V; Electrophoresis time: 15～25 seconds; The preliminary drying time: 10～20 minutes; Preliminary drying temperature: 50～70 ℃; Hardening time: 20～40 minutes; Solidification temperature: 160～180 ℃.

In the utility model preparation method, wherein step 3 and 4 is alternative processing step.

Can change electrophoretic paint at last attached to the color on the photograph by the technological parameter that changes electrophoresis, the preferred electrophoresis process parameter of the utility model is: fluid temperature: 34 ℃; Voltage: 30-35V; Electrophoresis time: 15-20 second; The preliminary drying time: 15 minutes; Preliminary drying temperature: 60 ℃; Hardening time: 30 minutes; Solidification temperature: 170 ℃.The described electrophoresis process parameter of the utility model embodiment also is not used in qualification the utility model, and all adjustment to technological parameter all should be in the utility model protection domain in technical conceive of the present utility model.

Certainly, also can adopt alternate manner to substitute the vacuum plating titanium coating, as when plating ground floor titanium and second layer titanium, adopt the water depositing process, its technological parameter is: 15-40 ℃ of water bath temperature, water plating time 30-45 minute.

The utlity model has following characteristics:

1, be main coloring pigment with electrophoretic paint.Because electrophoretic paint lacquer material is hard, adhesive force is good, can produce that pigment peels off and the phenomenon of fading to being subjected to burn into oxidation, wearing and tearing and the UV-irradiation of general chemicals.

2, the utility model titanium is compared with printing paper and canvas, and titanium can not occur that material is mouldy, flavescence or phenomenon such as damaged by worms.

3, titanium and stainless steel top layer are covered by electrophoretic paint, and obstruct air and metal be low and deep look because of oxidation produces.

4, electrophoretic paint can be deployed into different colors.

The utility model be with the digital photo image carving on the pure stainless steel substrates of titanizing, becoming with the metal is the photo of material, can preserve for a long time.

Claims

1. titanizing stainless steel metal photograph, it is characterized in that: described photograph comprises stacked from the inside to the outside stainless steel layer and titanium coating, described photograph is carved with the photomap picture at titanium coating place face.

2. titanizing stainless steel metal photograph according to claim 1 is characterized in that: described titanium coating vacuum plating is on the stainless steel layer surface.

3. titanizing stainless steel metal photograph according to claim 1 is characterized in that: the outermost layer of described photograph also electrophoresis has an electrophoretic paint layer.

4. titanizing stainless steel metal photograph according to claim 1 is characterized in that: described titanium coating comprises a ground floor titanium and the second layer titanium different with ground floor titanium color.