CN201581610U - Anti-cracking environment-friendly epoxy quartz stone floor - Google Patents
Anti-cracking environment-friendly epoxy quartz stone floor Download PDFInfo
- Publication number
- CN201581610U CN201581610U CN2009200447378U CN200920044737U CN201581610U CN 201581610 U CN201581610 U CN 201581610U CN 2009200447378 U CN2009200447378 U CN 2009200447378U CN 200920044737 U CN200920044737 U CN 200920044737U CN 201581610 U CN201581610 U CN 201581610U
- Authority
- CN
- China
- Prior art keywords
- terrace
- epoxy quartz
- quartz
- cracking
- epoxy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model discloses an anti-cracking environment-friendly epoxy quartz stone floor which comprises a moisture-proof undercoat (1). An undercoat (2) is arranged on the moisture-proof undercoat (1); an epoxy quartz stone interlayer (3) is arranged on the undercoat (2); an accurate grinding and polishing layer (4) is arranged on the epoxy quartz stone interlayer (3); an anti-cracking slit (5) is formed on the environment-friendly epoxy quartz stone floor; elastic slit-filling glue is filled in the anti-cracking slit (5) until the surface of the slit is level with that of the accurate grinding and polishing layer (4). The utility model has favorable abrasion resistance, temperature resistance, pressure resistance, corrosion resistance, instant impact resistance, skid resistance, and the like, and can not only realize the advantages of high rigidity and wear resistance of Granite and marble floor, but also avoid the defects of common epoxy resin floor, such as easy scratching, non-abrasion resistance, easy cracking, and the like. Additionally, the environment-friendly epoxy quartz stone floor is provided with an anti-cracking structure, thereby effectively solving cracking problem caused by concrete slit and shrinkage of the floor self, and achieving simple cleaning and maintenance, as well as long service life.
Description
Technical field
The utility model relates to the terrace technical field, particularly relates to a kind of anticracking type environment-friendly epoxy quartz terrace.
Background technology
Development along with modern industrial technology and production, cleanliness factor for working condition and environment requires more and more higher, modern production workshop terrace requires wear-resisting, withstand voltage, corrosion-resistant, and its clean and aseptic degree also becomes the key factor of measurement modern production level, because production environment is very big to the influence of product quality, so it is low as much as possible that the room air dustiness needs, requirement to floor material also improves constantly like this, such as the traditional cement bonded pulpstone terrace that is that adopted the earliest in the past, developing into the granite terrace afterwards replaces, to the epoxy resin terrace that progressively was widely adopted in recent years, all be again in order more to meet the requirement of production development.
At the pluses and minuses of various terraces, general cement terrazzo concrete terrace has relatively more outstanding surface aspect abrasion performance, but because of itself being porous matrix, very easily be subjected to contaminating impurity, cleaning inconvenience does not particularly have advantage, so be eliminated substantially aspect dustproof.
Through development after a while, can replace the granite of terrazzo concrete and marble terrace only to need a little maintenance and be subjected to the favor of builing industry with its high-quality outward appearance, wear-resisting durable while.But granite and marble terrace also exist vulnerable to pollution, not anti-skidding, shop is connected to too much slit and easily hides dirt, have stronger radioactivity, renovation cost more high many disadvantages in addition in addition, thus not environmental protection and can not adapt to the requirement of the production environment that improves day by day.
The ordinary epoxy resin terrace that grew up afterwards has high strength because of it, wear-resistant, no seam, quality is solid, resistance to chemical reagents is good, anticorrosion, dustproof, easy maintenance, advantage that the cheap and construction of maintenance cost is fast succinct or the like, but itself also exists surface reflection to spend height, easily scratch, not wear-resisting, shortcoming such as easy to crack, generally through in a few years use, the surface of epoxy resin mortar terrace very easily is worn, scratch, and the surface is in case after being worn and destroying, will residual spot, fork truck vestige etc., general cleaning mode all can not reach good effect, can only be coated with by the recoat face again every one or two years and renovate, this mode has not only increased use cost, and need stopping production to construct, normal production there is certain influence.
Therefore, if can invent a kind of terrace, can reach the outward appearance of granite and marble terrace and hardness height, anti abrasive advantage, can avoid the easy scratch, not wear-resisting of ordinary epoxy resin terrace again, particularly avoid shortcoming easy to crack, just can satisfy the needs of terrace industry development.
The utility model content
The purpose of this utility model is: a kind of anticracking type environment-friendly epoxy quartz terrace is provided; the outward appearance of granite and marble terrace and hardness height, anti abrasive advantage can be reached, the easy scratch of ordinary epoxy resin terrace, shortcoming such as not wear-resisting, easy to crack can be avoided again.
The technical solution of the utility model is: a kind of anticracking type environment-friendly epoxy quartz terrace, it comprises moistureproof scratch coat, described moistureproof scratch coat is provided with then scratch coat, and then scratch coat is provided with epoxy quartz intermediate layer, and epoxy quartz intermediate layer is provided with the fine-grinding and polishing layer; Offer anti-crack on the described epoxy quartz terrace, be filled with the elasticity gap-filling glue in the described anti-crack.
Described moistureproof scratch coat is the moistureproof scratch coat that epoxy resin and curing compound proportioning mix, and its thickness is 0.1～0.15mm.
Described then scratch coat is the then scratch coat that epoxy resin and curing compound proportioning mix, and its thickness is 0.3～0.5mm.
Described epoxy quartz intermediate layer is the epoxy quartz intermediate layer that epoxy resin adhesive and grating quartz mix, and its thickness is 5～12mm.
The grating quartz that the quartz grating that described grating quartz is a different meshes mixes; Described epoxy resin adhesive is the epoxy resin adhesive that epoxy resin and curing compound proportioning mix.
Described grating quartz and epoxy resin adhesive proportioning are 8: 1～15: 1.
Described fine-grinding and polishing layer is that the diamond disk by different meshes carries out the fine-grinding and polishing layer that fine-grinding and polishing forms to grouting surface, epoxy quartz intermediate layer.
About 3～the 8mm of the width in described anti-crack, anti-crack is through to the concrete structure seam.
Described elasticity gap-filling glue is a polyurethanes elasticity gap-filling glue.
The upper surface of the elasticity gap-filling glue of filling in the described anti-crack and the upper surface flush of fine-grinding and polishing layer.
The anticracking type environment-friendly epoxy quartz terrace that the utility model provides, the advantage in conjunction with present granite, marble and common epoxide terrace has following good characteristic:
1, high-quality outward appearance, good decorative property are arranged.
2, no matter the selected complete compliance with environmental protection requirements of material is in the work progress or make in the process in the future, and nontoxic, nonirritant gaseous volatilization is radiationless to human body, and the quality and the environment for use of product are not had any pollution.
3, adopt the aggregate of grating quartz,, can make the terrace of making have characteristics such as high-wearing feature, corrosion resistance, resistance to impact because the quartz material has the characteristic of high rigidity as the intermediate layer.
4, can well cohere with concrete base layer, not come off, do not flake.
5, perfect anticracking is handled and can be solved the shortcomings such as cracking that cause such as distress in concrete or terrace contraction itself fully.
6, have good wear-resisting, heatproof, withstand voltage, corrosion-resistant, anti-moment impact, performance such as anti-skidding.
7, daily cleaning is safeguarded simply, and general maintenance gets final product.
8, long service life need not regular renewal and reform.
Description of drawings
The utility model will be further described below in conjunction with drawings and Examples:
Fig. 1 is structural representation of the present utility model (cross section);
Fig. 2 is the structural representation (cross section) that is positioned at anti-position, crack of the present utility model.
Wherein: 1 moistureproof scratch coat; 2 follow scratch coat; 3 epoxy quartz intermediate layers; 4 fine-grinding and polishing layers; 5 anti-cracks.
The specific embodiment
Embodiment: as shown in Figure 1 and Figure 2; a kind of anticracking type environment-friendly epoxy quartz terrace, it comprises moistureproof scratch coat 1, described moistureproof scratch coat 1 is provided with then scratch coat 2; then scratch coat 2 is provided with epoxy quartz intermediate layer 3, and epoxy quartz intermediate layer 3 is provided with fine-grinding and polishing layer 4.Offer anti-crack 5 on this epoxy quartz terrace, be filled with polyurethanes elasticity gap-filling glue in the described anti-crack 5.
Moistureproof scratch coat 1 is mixed by epoxy resin and curing compound grating, and thickness is 0.1～0.15mm, and present embodiment is 0.1mm.
Then scratch coat 2 is mixed by epoxy resin and curing compound grating, and thickness is 0.3～0.5mm, and present embodiment is 0.4mm.
Epoxy quartz intermediate layer 3 is mixed by the grating quartz of epoxy resin adhesive and different meshes, and its thickness is 5～12mm, and present embodiment is 5mm.Epoxy resin adhesive is mixed by epoxy resin and curing compound grating, and grating is mixed quartz and the epoxy resin adhesive proportioning is 8: 1～15: 1, and present embodiment is 12: 1.
Epoxy quartz intermediate layer 3 lip-deep fine-grinding and polishing layers 4 carry out forming after the fine processing after to epoxy quartz intermediate layer 3 grout surfaces.
Referring to Fig. 2,, integral terrace is carried out joint-cutting and joint filling processing in fine-grinding and polishing layer 4 construction back in order to prevent the terrace cracking, stitch wide about 3～8mm, the dark about 5mm of seam, the wide 5mm of the present embodiment centre joint, the dark about 5mm of seam adopts polyurethanes elasticity gap-filling glue to carry out joint filling and handles.
The anticracking that the utility model emphasis solves lays particular emphasis on from concrete motion shifting principle sets about, and elimination may cause the various factors of terrace cracking.The cracking of general terrace mainly is because the concrete following several motion displacements of bottom:
1, the concrete transverse shift that expands with heat and contract with cold and cause because of variations in temperature.
2, the concrete vertical shift that causes because of ground settlement.
Because though epoxide resin material itself has certain retractility but is also limited, in case the amplitude of concrete displacement surpasses the flexible value of epoxy resin itself, will cause the passing through property crack of terrace surface, even the reparation of manually going again can not be eliminated this hidden danger fully, the concrete displacement that extraneous later on variation causes still can cause terrace crack, fundamentally head it off once more.
The utility model takes rational joint-cutting and joint filling to handle in construction, can effectively prevent the terrace surface cracking phenomena that causes because of concrete displacement, can not produce because of bringing adverse factors in the crack guaranteeing that terrace has on the basis of epoxy quartz ground plateau characteristic.
Joint-cutting of the present utility model is paid attention to considering from the basis, the joint-cutting of guaranteeing terrace itself is communicated with the structural joint of lower-layer concrete, can make terrace and concrete between seam and the seam become whole synchronous shift, the terrace surface cracking that has caused when having avoided the concrete monodisplacement.
Rubber-like polyurethanes gap-filling glue is adopted in joint filling of the present utility model, to filling in the seam of the cutting after the cleaning, elasticity by the polyurethanes gap-filling glue cushions the influence that the concrete displacement brings terrace greatly, thereby prevented that effectively the terrace that causes because of environmental change from ftractureing, concordant with terrace integral body by joint filling in addition to the surface, not only do not influence the attractive in appearance of former terrace, can prevent to hide in the slit dirty and not easy to clean again.
Because of the utility model is noted processing to the slit; fundamentally solved the reason that causes epoxy quartz terrace cracking; thereby produce environment-friendly epoxy quartz terrace with anti crack performance; make epoxy quartz terrace on basis with good wear-resisting, heatproof, withstand voltage, corrosion-resistant, shock-resistant, attractive in appearance, environmental protection; again can be bonding with concrete base layer well, do not ftracture long service life; need not regular renewal and reform, improved the popularity that epoxy quartz terrace is used greatly.
The utility model finished product terrace (5mm) to apply technology as follows:
1, concrete foundation is handled (containing polishing, leveling etc.), and the concrete structure seam is made marks.
2, applying of moistureproof scratch coat 1: epoxy resin and curing compound that proportioning is good fully mix, and evenly are coated with the about 0.1mm of thickness with the concrete surface of cylinder after processing.
3, follow applying of scratch coat 2: epoxy resin and curing compound that proportioning is good fully mix, with even blade coating in the moistureproof primary coat 1 of scraper plate, the about 0.4mm of thickness.
4, applying of epoxy quartz intermediate layer 3: the quartz aggregate that level is prepared adds in the agitator, epoxy resin and curing compound that adding fully mixes by proportioning, after fully stirring, use paver special to lay, evenly spread the back out and carry out mechanical ramming, the about 7～8mm of laying depth on suitable opportunity.According to construction experience when appropriate machine to terrace repeatedly polish, grouting treatment, make epoxide resin material fully permeate the quartz layer making on the further smooth basis of epoxy quartz layer, guarantee that the intermediate layer is closely knit full.Epoxy quartz intermediate layer thickness after the processing is about 5mm.
5, applying of fine-grinding and polishing layer 4: use the diamond disk of different meshes to carry out fine-grinding and polishing on the surface in the epoxy quartz intermediate layer 3 that abundant grouting is polished, form smooth fine-grinding and polishing layer 4 attractive in appearance.
What 6, anticracking was handled applies: the concrete structural joint mark according to being done in above-mentioned 1, and integral terrace to be carried out joint-cutting handle, depth penetration is guaranteed to communicate up and down to the structural joint of layer of concrete, stitches wide about 5mm.Anti-crack 5 to cutting is cleared up, and thoroughly clean back is adopted the elastic polyurethane gap-filling glue to carry out joint filling and handled, and seam is filled and led up to fine-grinding and polishing layer 4 surface.The complete anticracking type environment-friendly epoxy quartz terrace of final formation.
Epoxy resin and curing compound can adopt identical or different proportioning to make according to concrete construction requirement in the said process.
Should be pointed out that for the utility model also to have the embodiment of multiple conversion and remodeling, be not limited to the specific embodiment of above-mentioned embodiment through proving absolutely.The foregoing description is as just explanation of the present utility model, rather than restriction.In a word, protection domain of the present utility model should comprise those conspicuous to those skilled in the art conversion or substitute and remodeling.
Claims (8)
1. anticracking type environment-friendly epoxy quartz terrace, it is characterized in that: it comprises moistureproof scratch coat (1), described moistureproof scratch coat (1) is provided with then scratch coat (2), then scratch coat (2) is provided with epoxy quartz intermediate layer (3), and epoxy quartz intermediate layer (3) is provided with fine-grinding and polishing layer (4); Offer anti-crack (5) on the described epoxy quartz terrace, be filled with the elasticity gap-filling glue in the described anti-crack (5).
2. anticracking type environment-friendly epoxy quartz terrace according to claim 1, it is characterized in that: described moistureproof scratch coat (1) thickness is 0.1～0.15mm.
3. anticracking type environment-friendly epoxy quartz terrace according to claim 1 is characterized in that: described then scratch coat (2) thickness is 0.3～0.5mm.
4. anticracking type environment-friendly epoxy quartz terrace according to claim 1, it is characterized in that: described epoxy quartz intermediate layer (3) thickness is 5～12mm.
5. anticracking type environment-friendly epoxy quartz terrace according to claim 1 is characterized in that: described fine-grinding and polishing layer (4) is that the diamond disk by different meshes carries out the fine-grinding and polishing layer that fine-grinding and polishing forms to grouting surface, epoxy quartz intermediate layer (3).
6. anticracking type environment-friendly epoxy quartz terrace according to claim 1 is characterized in that: the about 3～8mm of width in described anti-crack (5), anti-crack (5) is through to the concrete structure seam.
7. anticracking type environment-friendly epoxy quartz terrace according to claim 1, it is characterized in that: described elasticity gap-filling glue is a polyurethanes elasticity gap-filling glue.
8. anticracking type environment-friendly epoxy quartz terrace according to claim 1 is characterized in that: the upper surface of the elasticity gap-filling glue of filling in the described anti-crack (5) and the upper surface flush of fine-grinding and polishing layer (4).