Hot melt nethike embrane composite glass fiber weak point is cut felt
Technical field
The utility model relates to a kind of fiber glass reinforcement, and particularly hot melt nethike embrane composite glass fiber weak point is cut felt.
Background technology
Glass chopped strand mats is after continuous glass fiber yarn weak point is cut, omnidirectional evenly distribution at random, add the mat that adhesive and oven dry bonding form, this mat is used for various roof gadgets, the transformer insulating materials, cleaners and polishes, the chemical anticorrosion pipeline, basin, boats and ships, seat, reinforcing material in the various glass fiber reinforced plastic decorating boards such as building element, during use, need between glass chopped strand mats and other material to adopt organic bond bonding, not only can produce irritative gas, contaminated air influence the health of health, and the amount of adhesive must be controlled accurately, otherwise it is wrinkling that finished product easily bubbles, and influences end product quality.
Summary of the invention
The utility model purpose provides a kind of hot melt nethike embrane composite glass fiber weak point and cuts felt, and this glass chopped strand mats can be directly bonding well with nonwoven fabric, the foaming PU material of various decorative panels, need not to add in addition adhesive, and binding face is smooth, and is wrinkle resistant.
This hot melt nethike embrane composite glass fiber weak point is cut felt and is made up of glass chopped strand mats and the organic hot melt nethike embrane that is bonded in its surface.Said hot melt nethike embrane has low-melting characteristics, and nethike embrane can melt under a little more than 100 ℃ temperature.
Said organic hot melt nethike embrane is a polyesters hot melt nethike embrane, is preferably polyesteramine hot melt nethike embrane.
Said glass chopped strand mats is 100 ± 10g/m
2Slim glass chopped felt.
The heat pressure adhesive that passes through of polyester hot melt nethike embrane and glass chopped strand mats cools off subsequently and forms complex.
This glass chopped strand mats is because compound low-melting hot melt nethike embrane, can adopt the mode of hot pressing, make hot melt nethike embrane fusing wherein and see through glass chopped strand mats, need not to add adhesive with other, can be directly and the nonwoven fabric of decorative panel such as roof or foaming PU material bond compoundly well, and it is smooth tight to fit, bubble not, wrinkle resistant, no lamination, intensity height; Owing to need not to add adhesive, thereby can avoid producing organic solvent gas and overflow and problem of environment pollution caused.
Description of drawings
Accompanying drawing is the section structure schematic diagram that the compound weak point of this hot melt nethike embrane glass fibre is cut felt.
Among the figure, the compound weak point of 1-glass fibre is cut felt, 2-hot melt nethike embrane.
The specific embodiment
Accompanying drawing is the section structure for amplifying schematic diagram that this hot melt nethike embrane composite glass fiber weak point is cut felt, represents among the figure, and this felt is made up of glass chopped strand mats 1 and the organic hot melt nethike embrane 2 that is bonded in its surface.
The preparation example is as follows:
Select 100 ± 10g/m for use
2Slim glass chopped felt 1 and 28g/m
2Polyester amine hot melt nethike embrane 2 (fusing point is about 110 ℃), the two is compound as shown, add powder adhesive between the two, heat to 120-150 ℃, after pressing boiling hot 20s, promptly be bonded into integral body, cool off to such an extent that the compound weak point of the utility model hot melt nethike embrane glass fibre is cut felt, the composite bed peel strength rapidly 20 (N/2.5cm).