CN1995414A - Vitriol intensified leach extraction method for nickel oxide ore - Google Patents
Vitriol intensified leach extraction method for nickel oxide ore Download PDFInfo
- Publication number
- CN1995414A CN1995414A CNA2006100225509A CN200610022550A CN1995414A CN 1995414 A CN1995414 A CN 1995414A CN A2006100225509 A CNA2006100225509 A CN A2006100225509A CN 200610022550 A CN200610022550 A CN 200610022550A CN 1995414 A CN1995414 A CN 1995414A
- Authority
- CN
- China
- Prior art keywords
- nickel
- weight
- nickel oxide
- leach
- leach liquor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses an extracting method of nickel, which comprises the following steps: breaking nickel oxide into small blocks; pouring ore pulp with density at 20-60% into autoclave; adding sulfuric acid and reducer; heating; pressurizing; heating; reinforcing the leach; controlling the temperature between 100 and 200 deg. c; controlling the pressure below 1. 6Mpa; sedimenting leached liquid to obtain nickel through solid sediment agent; or extracting leached liquid; separating nickel out of liquid; condensing; purifying; obtaining the electrodeposited nickel or nickel sulfate.
Description
Affiliated technical field
The present invention relates to a kind of sulfuric acid that from nickel oxide ore, utilizes and leach the method for extracting nickel element.
Background technology
From nickel oxide ore, reclaim at present the method for nickel metal,---ammonia soaks or the reduces---pickling process that adopts roasting more.(" non-ferrous extractive metallurgy handbook (the copper nickel volume) " that adopt sulfuric acid process to extract also arranged, metallurgical press, in July, 2000 first version, P724~727), but its method that adopts must be could leach down at high temperature (249 ℃) high pressure (3.4Mpa), and leach liquor also need be heated to pressurize and be reclaimed the nickel metal with hydrogen sulfide.This method one-time investment is very high, needs to build the reactor of high temperature high voltage resistant, huge boiler.Also to produce the hydrogen sulfide of coprecipitated nickel hydroxide metal in the recovery after leaching the nickel metal, and the pressurization of when precipitation, also will heating, not only investment is high, and technical process is also complicated, and the output cost is also high.The inventor has proposed a kind ofly at normal temperature and pressure sulfuric acid leach extraction method (ZL200310110839.2) in 2003 in addition, though the investment of this method is little, easy to operate, its leaching yield is lower, causes the waste to nickel resources, and its production cycle is longer.
Summary of the invention
Purpose of the present invention exactly for overcome above-mentioned will be more than 200 ℃ at high temperature, more than the high pressure 3.0Mpa, investment is big, the demanding weak point of equipment performance; It is low to overcome simultaneously under normal temperature, normal pressure its leaching yield again, yield poorly, and the shortcoming that the nickel resources waste is big, and a kind of less investment is provided, easy to operate, nickel resources can be saved and make full use of to the leaching yield height, nickel oxide ore vitriol intensified leach extraction method with short production cycle.
The objective of the invention is to reach by following technical measures: this extraction method is that nickel oxide ores is crushed to 0.074mm~2mm size, make concentration and be 20%~60% nickel oxide ore pulp, add the vitriol oil again under stirring state earlier, its weight is 15%~80% of nickel oxide ores weight.Its innovation part is also will add reductive agent then, reductive agent is any one in sulfurous gas or the sodium sulphite anhydrous 99.3, its weight is 0.1%~2% of nickel oxide ores weight, and temperature is controlled between 100~200 ℃, operating pressure is controlled at below the 1.6Mpa, strengthen and leached 4-8 hour, leaching the terminal point pH value is 1-3.Natural subsidence is carried out solid-liquid separation afterwards, isolates nickeliferous leach liquor.Add precipitation agent to leach liquor again, precipitation agent can be chosen any one kind of them from sodium sulphite, sodium hydroxide and yellow soda ash, and nickel ion is precipitated out, and thickening filtration is the nickel ore concentrate product.
If to the precipitation agent sodium sulphite that leach liquor adds, adding weight is 2~5 times of nickel weight metal; If sodium hydroxide, adding weight are 1~4 times of nickel weight metal; If yellow soda ash, adding weight are 1~4 times of nickel weight metal.
Preferred plan of the present invention is that nickel oxide ores is crushed to granularity is about 1mm, make concentration and be 35% ore pulp and inject reactor, add earlier weight and be 30% the vitriol oil of nickel oxide ores weight, adding weight afterwards again is the reductive agent sodium sulphite anhydrous 99.3 of nickel oxide ores weight 0.8%, strengthen leaching in heating, pressurization with under stirring, and controlled temperature is about 180 ℃, pressure is below 1.6Mpa, the leach liquor pH value is 2~3 when leaching terminal point, about 5 hours of extraction time.Natural subsidence is carried out solid-liquid separation then, isolates leach liquor.Add the precipitation agent of 3 times of weight nickel metals again to leach liquor, precipitation agent can be chosen any one kind of them from sodium sulphite, sodium hydroxide and yellow soda ash, and nickel ion is precipitated out, and thickening filtration promptly gets the nickel ore concentrate product.
The present invention is owing to adopt temperature below 200 ℃, and the pressure that 1.6Mpa is following is not high to the performance requriements of equipment, and its reactor only need be used carbon steel liner heatproof, acidproof, withstand voltage brick, just can meet the demands, and its cost is with 20m
3Reactor meter, separate unit cost only need 300,000 yuan, and temperature is 249 ℃, and pressure is that the reactor separate unit cost of 3.4Mpa just reaches more than 3,000,000 yuan.When heating, produce a large amount of heat during because of ore pulp and strong sulfuric acid response, only need a small amount of heating just can meet the demands, and the leaching yield of this invention is just significantly improved, and can reach more than 95%, has reached 249 ℃ basically, 3.4Mpa the leaching yield under the high-temperature and high-pressure conditions, the used reductive agent of the present invention is cheap, in production cost, and proportion less than 5%.Therefore, the present invention compares with existing other method, has less investment, and technology is simple, and is easy to operate, and the leaching yield advantages of higher is fit to exploitation and the nickel resources that effectively utilizes worsening shortages very much.
Embodiment
The present invention is described further below in conjunction with embodiment.
Embodiment one
Nickel oxide ores is crushed to about granularity 1mm, make concentration and be 35% ore pulp and inject reactor, adding weight earlier is the vitriol oil of nickel oxide sandstone weight 40%, adding weight afterwards again is the reductive agent sodium sulphite anhydrous 99.3 of nickel oxide ores weight 0.8%, strengthen leaching in heating, pressurization with under stirring, and controlled temperature is about 180 ℃, pressure is below 1.6Mpa, the leach liquor pH value is 2~3 when leaching terminal point, about 5 hours of extraction time.Natural subsidence is carried out solid-liquid separation then, isolates leach liquor.Add the sodium sulphite of 3 times of weight nickel metals again to leach liquor, the form of nickel ion with nickelous sulfide is precipitated out, thickening filtration promptly gets the nickel ore concentrate product.
Embodiment two
The leaching process of front is identical with embodiment one, after the leaching solid-liquid separation on ore pulp, adds the sodium hydroxide of 3 times of weight nickel metals again to leach liquor, and the form of nickel ion with nickel hydroxide is precipitated out, and thickening filtration promptly gets the nickel ore concentrate product.
Embodiment three
The leaching process of front is identical with embodiment one, after the leaching solid-liquid separation on ore pulp, adds the yellow soda ash of 3 times of weight nickel metals again to leach liquor, and the form of nickel ion with nickelous carbonate is precipitated out, and thickening filtration promptly gets the nickel ore concentrate product.
Embodiment four
The leaching process of front is identical with embodiment one, after the leaching solid-liquid separation on ore pulp, will leach liquor be extracted with the extraction solvent of routine, and nickel is separated from liquid, concentrates, purifies, and produces electro deposited nickel with the electrodeposition method then.
Embodiment five
The leaching process of front is identical with embodiment one, after the leaching solid-liquid separation on ore pulp, will leach liquor be extracted with the extraction solvent of routine, and nickeliferous clear liquid is separated from leach liquid, concentrates, purifies, and evaporates moisture, makes single nickel salt then.
Claims (7)
1. the vitriol intensified leach extraction method of a nickel oxide ore, be that nickel oxide ores is crushed to 0.074mm~2mm size, make concentration and be 20%~60% nickel oxide ore pulp, under stirring state, add the vitriol oil more earlier, its weight is 15%~80% of nickel oxide ores weight, it is characterized in that also will adding reductive agent then, reductive agent is any one in sulfurous gas or the sodium sulphite anhydrous 99.3, its weight is 0.1%~2% of nickel oxide ores weight, and temperature is controlled between 100~200 ℃, operating pressure is controlled at below the 1.6Mpa, strengthen and leached 4~8 hours, leaching the terminal point pH value is 1~3, afterwards natural subsidence, carry out solid-liquid separation, isolate nickeliferous leach liquor, add precipitation agent to leach liquor again, precipitation agent can be from sodium sulphite, choose any one kind of them in sodium hydroxide and the yellow soda ash, nickel ion is precipitated out, and thickening filtration is the nickel ore concentrate product.
2. according to the vitriol intensified leach extraction method of the described nickel oxide ore of claim 1, it is characterized in that the precipitation agent that adds to leach liquor is a sodium sulphite, adding weight is 2~5 times of nickel weight metal.
3. according to the vitriol intensified leach extraction method of the described nickel oxide ore of claim 1, it is characterized in that the precipitation agent that adds to leach liquor is a sodium hydroxide, adding weight is 1~4 times of nickel weight metal.
4. according to the vitriol intensified leach extraction method of the described nickel oxide ore of claim 1, it is characterized in that the precipitation agent that adds to leach liquor is a yellow soda ash, adding weight is 1~4 times of nickel weight metal.
5. according to the vitriol intensified leach extraction method of the described nickel oxide ore of claim 1, it is characterized in that leach liquor being extracted with conventional extraction solvent, nickel is separated from liquid again concentrated, purify, produce electro deposited nickel with the electrodeposition method then.
6. according to the vitriol intensified leach extraction method of the described nickel oxide ore of claim 1, it is characterized in that leach liquor being extracted, the nickel clear liquid is separated from liquid, concentrate again, purify with conventional extraction solvent, evaporate moisture, make single nickel salt then.
7. according to the vitriol intensified leach extraction method of the described nickel oxide ore of claim 1, it is characterized in that scheme is that nickel oxide ores is crushed to granularity is about 1mm, make concentration and be 35% ore pulp and inject reactor, adding weight earlier is the vitriol oil of nickel oxide ores weight 30%, adding weight afterwards again is the reductive agent sodium sulphite anhydrous 99.3 of nickel oxide ores weight 0.8%, strengthen leaching in heating, pressurization with under stirring, and controlled temperature is about 180 ℃, pressure is below 1.6Mpa, the leach liquor pH value is 2~3 when leaching terminal point, about 5 hours of extraction time.Natural subsidence is carried out solid-liquid separation then, isolates leach liquor, the precipitation agent that adds 3 times of weight nickel metals again to leach liquor, precipitation agent can be chosen any one kind of them from sodium sulphite, sodium hydroxide and yellow soda ash, and nickel ion is precipitated out, and thickening filtration gets the nickel ore concentrate product.