CN1990574A - High stability high viscosity modified asphalt and preparation method thereof - Google Patents
High stability high viscosity modified asphalt and preparation method thereof Download PDFInfo
- Publication number
- CN1990574A CN1990574A CN 200510112324 CN200510112324A CN1990574A CN 1990574 A CN1990574 A CN 1990574A CN 200510112324 CN200510112324 CN 200510112324 CN 200510112324 A CN200510112324 A CN 200510112324A CN 1990574 A CN1990574 A CN 1990574A
- Authority
- CN
- China
- Prior art keywords
- styrene
- modified asphalt
- viscosity modified
- high viscosity
- asphalt
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a high-dispersity high-viscosity modified asphalt which comprises the following constituents (by weight ratio): asphalt 100, styrene-polyethylene / butylene-styrene segmented copolymer 3-12 having an average molecular weight of 30-350 thousand, petroleum resin 5-30 with a softening point of 70-150 deg C, polypropene wax 1-4 having an average molecular weight of 500-15000 and a softening point of 90-160 deg, by mixing styrene-ethane/butylenes-styrene segmented copolymer and petroleum resin into the asphalt, high viscosity, good dispersity and stability can be achieved, the PG classification can reach 82-28. The obtained high-performance modified asphalt can be used for both the general water seeping pavements, and specific sites such as bridge pavement and stress absorption layer.
Description
Technical field
The present invention relates to a kind of high viscosity modified asphalt for water seeping pavement.
Background technology
Asphaltum with high viscosity is meant the pitch of 60 ℃ of viscosity greater than 20,000 Pa.s, is suitable for spreading out and putting on of traffic road surface and drainage pavement.Asphaltum with high viscosity mainly makes by add polymer modification in petroleum pitch at present.Add polymkeric substance petroleum pitch is carried out modification, can obviously improve bituminous high and low temperature performance, the anti-rut of high temperature, the low temperature cracking resistance ability of bituminous pavement is provided.But,, make the polymer modified asphalt difficulties in dispersion owing to have differences such as molecular weight, viscosity between polymkeric substance and the pitch; Simultaneously, because most polymers and pitch can be compatible fully, and exist density difference, at high temperature storage stability is bad to cause the modifying asphalt system, and layering easily influences asphalt quality and normal construction.
For solving the problem of asphaltum with high viscosity difficulties in dispersion, Chinese patent cn1089349c has reported and has adopted elder generation with polymkeric substance and pitch and other Synergist S-421 95 blend, is prepared into easily dispersive masterbatch in pitch, this masterbatch is dispersed in the pitch preparation modifying asphalt again.
Be to solve the high temperature storing stabilization problem of modifying asphalt, United States Patent (USP) us3,634,293 when having proposed use polymer modified asphalt, adding superoxide, the method for linking agents such as sulphur; International monopoly wo45,488 have proposed SB two blocks and SBS triblock copolymer and usefulness are added the method for a spot of linking agent; Chinese patent cn1386790A discloses by earlier with polymkeric substance and the carbon black blend method of modifying asphalt again.
But all good water seeping pavement of dispersed and stability yet there are no report with modifying asphalt.
Summary of the invention
The purpose of this invention is to provide a kind of new high-viscosity modified asphalt, this pitch not only disperses easily, and also has high temperature storing stabilization preferably.
For achieving the above object, the technical scheme that the present invention takes is:
A kind of high stability high viscosity modified asphalt, it contains following component: pitch 100, styrene-ethylene/butylene-styrene block copolymer (SEBS) 3~12, petroleum resin 5~30, Poly Propylene Wax 1~4 (more than be parts by weight).
Described SEBS is the segmented copolymer that vinylbenzene (S)-ethene (E)/butylene (B)-vinylbenzene (S) constitutes, it is combined in the thermoplastic characteristics of polystyrene and the elastomeric characteristic of ethylene-butene copolymer in the same polymkeric substance, and its molecular configuration is the triblock copolymer of A-B-A type.Because elastomeric blocks hydrogenation fully among the SEBS, so SEBS has good ageing resistance and also can at high temperature process.Its molecular weight is better 3~350,000 o'clock effects, and the preferable scope of content is 5~10 parts, most preferably is 6~9 parts.
The preferred weight fraction of described petroleum resin is 10~20.
The molecular-weight average of described Poly Propylene Wax is 500~15000, and softening temperature is 90~160 ℃.
The preparation method of easy dispersive high viscosity modified asphalt for water seeping pavement of the present invention is: earlier pitch is heated to flowable state, add styrene-ethylene/butylene-styrene block copolymer, petroleum resin and Poly Propylene Wax then successively, the powerful stirring gets final product.
Beneficial effect of the present invention: the present invention mixes styrene-ethylene/butylene-styrene block copolymer, petroleum resin and Poly Propylene Wax in pitch, not only viscosity is very high, and it is dispersed and stability is also fine, the PG classification reaches 82-28, belong to high performance modifying asphalt, can be used for general water seeping pavement, also can be used for special occasions such as deck paving and stress absorbing layer.
Embodiment
Get penetration degree and be 100 kilograms of 300 basic asphalts, be heated to 180 ℃, (molecular-weight average is 5000 to add 8 kilograms of styrene-ethylene/butylene-styrene block copolymer (molecular-weight average is 160,000), 12 kilograms of petroleum resin and Poly Propylene Wax successively, softening temperature is 130 ℃) 1 kilogram, the employing machine,massing stirred 6 hours with 200 rev/mins stirring velocity, prepare modifying asphalt, the results are shown in Table one.
Table one
The index of modifying asphalt | |
25 ℃ of penetration degrees, dmm | 70 |
5 ℃ of ductilities, 5cm/min (cm) | 26 |
Softening temperature T R&B(℃) | 90 |
135 ℃ of kinematic viscosity (Pa.s) | 2.8 |
25 ℃ of recovery of elasticity (%) | 94 |
Ductility is 5 ℃ behind the RTFOT, 5cm/min (cm) | 16 |
60 ℃ of viscosity (10000Pa.s) | 4.5 |
The PG classification | 82-28 |
As can be seen from the table, prepare high performance modifying asphalt, 60 degree viscosity are greater than 20,000 Pa.s, and the PG classification reaches 82~28, and high performance modifying asphalt can be used for OGFC, also can be used for special occasions such as deck paving, stress absorbing layer in addition.
Claims (5)
1, a kind of high stability high viscosity modified asphalt, the weight fraction of its each component is as follows: styrene-ethylene/butylene-styrene block copolymer 3~12 between 3~350,000 of pitch 100, molecular weight, petroleum resin 5~30, the molecular-weight average that softening temperature is 70~150 ℃ are 500~15000, and softening temperature is 90~160 ℃ a Poly Propylene Wax 1~4.
2, high stability high viscosity modified asphalt as claimed in claim 1 is characterized in that: the weight fraction of styrene-ethylene/butylene-styrene block copolymer is 5~10.
3, high stability high viscosity modified asphalt as claimed in claim 2 is characterized in that: the weight fraction of styrene-ethylene/butylene-styrene block copolymer is 6~9.
4, high stability high viscosity modified asphalt as claimed in claim 1 is characterized in that: the weight fraction of petroleum resin is 10~20.
5, the preparation method of the described arbitrary high stability high viscosity modified asphalt of claim 1~4, this method is: earlier pitch is heated to flowable state, add styrene-ethylene/butylene-styrene block copolymer, petroleum resin and Poly Propylene Wax then successively, stirring gets final product.