CN1974645A - Completely biodegradable plastic - Google Patents
Completely biodegradable plastic Download PDFInfo
- Publication number
- CN1974645A CN1974645A CN 200610128352 CN200610128352A CN1974645A CN 1974645 A CN1974645 A CN 1974645A CN 200610128352 CN200610128352 CN 200610128352 CN 200610128352 A CN200610128352 A CN 200610128352A CN 1974645 A CN1974645 A CN 1974645A
- Authority
- CN
- China
- Prior art keywords
- temperature
- starch
- insulation
- agent
- under
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The completely biodegradable plastic consists of degradable resin 33-40 wt%, glycerin starch ester 10-14 wt%, modified starch 35-42 wt%, dispersant 3-5 wt%, composite coupling agent 2-3 wt%, plasticizer 4-8 wt%, antioxidant 2-5 wt%, fluorescence brightener 1-3 wt%, ultraviolet absorber 0.5-2 wt% and filler 2.5-8 wt%. It is prepared through mixing the materials in a mixer and extruding and palletizing the mixture in a single screw extrude at 150-165 deg.c. The present invention has the advantages of simple production process and low production cost, and is suitable for industrial production.
Description
Technical field
The present invention relates to degradable plastics, especially relate to complete biodegradable plastics.
Background technology
Along with improving constantly of human environment protection consciousness, more and more higher to the environmental requirement of plastics, therefore, the development work of degradable plastics has obtained developing rapidly, and the degradative plastics kind is more and more many.Photodegradable plastics, composite degradable plastics, W-Gum blended with polyolefins mass degradation plastics etc. are arranged.The PLA poly(lactic acid) is exactly a kind of complete biodegradable plastics, and it not only has biological degradability, and nontoxic, harmless; but PLA poly(lactic acid) complex manufacturing, cost is higher, and film forming properties is bad; thereby be only applicable to goods, and be difficult to realize large-scale industrial production.
Summary of the invention
The object of the invention be to provide a kind of production technique simple, with low cost, use wide, be convenient to a kind of complete biodegradable plastics of realizing that large-scale industrial is produced.
For achieving the above object, the present invention can take following technical proposals:
Complete biodegradable plastics of the present invention, it is by the degraded resin 33-40% of weight percent, starch glycerite ester 10-14%, modified starch 35-42%, dispersion agent 3-5%, composite coupler 2-3%, softening agent 4-8%, oxidation inhibitor 2-5%, white dyes 1-3%, UV light absorber 0.5-2%, weighting agent 2.5-8% prepares according to following step:
The first step, the resin of will degrading in proportion, starch glycerite ester, modified starch are sent into kneading machine and were kneaded 15-20 minute;
Second goes on foot, the raw material that it is good that the first step is kneaded is sent in the high speed mixing roll, adds dispersion agent, composite coupler, softening agent, oxidation inhibitor, fluorescent whitening agent, UV light absorber, weighting agent successively; Uniform mixing is made compound;
The 3rd goes on foot, the second step compound is sent in the single screw extrusion machine, and temperature is controlled between 150-165 ℃, produces granular article and gets final product.
Described degraded resin is 31% hydrochloric acid, sodium bicarbonate according to following weight parts proportioning and step preparation by polyvinyl alcohol, butyraldehyde-n, concentration:
A, proportioning:
50 parts of polyvinyl alcohol, 30 parts of butyraldehyde-ns, concentration are 31% 50 parts of hydrochloric acid, 0.4 part of sodium bicarbonate;
B, step:
Getting 600 parts of distilled water adds in the dissolution kettle, when being warming up to 70 ℃, under agitation slowly add polyvinyl alcohol, progressively be warmed up to 95 ℃, in dissolution kettle, constant temperature dissolving 4 hours, make polyvinyl alcohol become the aqueous solution fully, change over to after the filtration in the acetal still, add butyraldehyde-n after being cooled to 50 ℃, continue to be cooled to 18 ℃ ± 5 ℃, add hydrochloric acid, be incubated 1 hour then under 18-20 ℃ of temperature, insulation is 1.5 hours under 20-25 ℃ of temperature, and insulation is 0.5 hour under 25-30 ℃ of temperature, insulation is 0.5 hour under 30-35 ℃ of temperature, insulation is 0.5 hour under 35-40 ℃ of temperature, and insulation is 0.5 hour under 40-45 ℃ of temperature, and insulation is 0.5 hour under 45-50 ℃ of temperature; Insulation is cooled to 30 ℃ after finishing, and puts into the filter of washing still from the taking-up of acetal still and does, and with tap water material is washed to pH value 6-7 earlier, is washed with distilled water to no chlorion again, adds the sodium bicarbonate ambient stable again, 120 minutes steady time; Stable good liquid material is moved into drying plant, through atomizing, be drying to obtain described degraded resin powder.
The preparation method of described starch glycerite ester is:
Squeeze into saponification level glycerine in the enamel reaction still earlier, when being warming up to 50 ℃, the starch that under agitation adds the equivalent weight ratio gradually, keep the even temperature of glycerine and starch to separate, stop after in 60-80 minute, being warmed up to 150 ℃ heating up, constant temperature is 30 minutes under this temperature, is cooled to 40 ℃ then, and blowing is the starch glycerite ester.
The preparation method of described modified starch is:
Get starch 63%, saponification level glycerine 25%, urea 7%, the ethylene acrylic acid co polymer 5% of weight percent, knead by kneading machine, 140 ℃ of granulations promptly in single screw extrusion machine.
Described dispersion agent is polyethylene wax W1080; Described composite coupler is the mixture of silane and titanate coupling agent; Described white dyes is the special-purpose whitening agent of plastics; Described oxidation inhibitor is 1010 and auxiliary antioxidant PS802FL; Described UV light absorber is UV-9; Described weighting agent is the above pure wood powders of 1250 orders; Described softening agent is a Plasticizer Epoxidized Soybean Oil.
The invention has the advantages that production technique is simple, be convenient to realize large-scale industrial production, greatly reduce production cost.With the agricultural-food corn is main raw material(s), make corn on average appreciate more than 30%, after this kind complete biodegradable plastics goods use and discard, be degraded to carbonic acid gas and water fully, no longer produce " white pollution ", purified social environment, and it is nonpoisonous and tasteless, not only can be used for food and drink tool goods, and can be made into food product packing film, guarantee that the health of food and people's is healthy.
Embodiment
Complete biodegradable plastics of the present invention, it is by the degraded resin 33-40% of weight percent, starch glycerite ester 10-14%, modified starch 35-42%, dispersion agent 3-5%, composite coupler 2-3%, softening agent 4-8%, oxidation inhibitor 2-5%, white dyes 1-3%, UV light absorber 0.5-2%, weighting agent 2.5-8% prepares according to following step:
The first step, preparation degradative resin:
30 parts of 50 parts of polyvinyl alcohol, butyraldehyde-ns, the concentration of getting weight part is 31% 50 parts of hydrochloric acid, 0.4 part of sodium bicarbonate;
Getting 600 parts of distilled water adds in the dissolution kettle, when being warming up to 70 ℃, under agitation slowly add polyvinyl alcohol, progressively be warmed up to 95 ℃, in dissolution kettle, constant temperature dissolving 4 hours, make polyvinyl alcohol become the aqueous solution fully, change over to after the filtration in the acetal still, add butyraldehyde-n after being cooled to 50 ℃, continue to be cooled to 18 ℃ ± 5 ℃, add hydrochloric acid, be incubated 1 hour then under 18-20 ℃ of temperature, insulation is 1.5 hours under 20-25 ℃ of temperature, and insulation is 0.5 hour under 25-30 ℃ of temperature, insulation is 0.5 hour under 30-35 ℃ of temperature, insulation is 0.5 hour under 35-40 ℃ of temperature, and insulation is 0.5 hour under 40-45 ℃ of temperature, and insulation is 0.5 hour under 45-50 ℃ of temperature; Insulation is cooled to 30 ℃ after finishing, and puts into the filter of washing still from the taking-up of acetal still and does, and with tap water material is washed to pH value 6-7 earlier, is washed with distilled water to no chlorion again, adds the sodium bicarbonate ambient stable again, 120 minutes steady time; Stable good liquid material is moved into drying plant, through atomizing, be drying to obtain described degraded resin powder.
Second step, preparation starch glycerite ester:
Squeeze into saponification level glycerine in the enamel reaction still earlier, when being warming up to 50 ℃, the starch that under agitation adds the equivalent weight ratio gradually, keep the even temperature of glycerine and starch to separate, stop after in 60-80 minute, being warmed up to 150 ℃ heating up, constant temperature is 30 minutes under this temperature, is cooled to 40 ℃ then, and blowing is the starch glycerite ester.
The 3rd step, preparation modified starch:
Get starch 63%, saponification level glycerine 25%, urea 7%, the ethylene acrylic acid co polymer 5% of weight percent, knead by kneading machine, 140 ℃ of granulations promptly in single screw extrusion machine.
The 4th step, the resin of will degrading in proportion, starch glycerite ester, modified starch are sent into kneading machine and were kneaded 15-20 minute;
The 5th step, the 4th step good raw material of kneading is sent in the high speed mixing roll, added dispersion agent, composite coupler, softening agent, oxidation inhibitor, fluorescent whitening agent, UV light absorber, weighting agent successively in proportion; Uniform mixing is made compound;
The 6th goes on foot, the 5th step compound is sent in the single screw extrusion machine, and temperature is controlled between 150-165 ℃, produces granular article and gets final product.
Described dispersion agent is polyethylene wax W1080; Described composite coupler is the mixture of silane and titanate coupling agent; Described white dyes is the special-purpose whitening agent of plastics; Described oxidation inhibitor is 1010 and auxiliary antioxidant PS802FL; Described UV light absorber is UV-9; Described weighting agent is the above pure wood powders of 1250 orders; Described softening agent is a Plasticizer Epoxidized Soybean Oil.
Claims (5)
1, a kind of complete biodegradable plastics, it is characterized in that: it is by the degraded resin 33-40% of weight percent, starch glycerite ester 10-14%, modified starch 35-42%, dispersion agent 3-5%, composite coupler 2-3%, softening agent 4-8%, oxidation inhibitor 2-5%, white dyes 1-3%, UV light absorber 0.5-2%, weighting agent 2.5-8% prepares according to following step:
The first step, the resin of will degrading in proportion, starch glycerite ester, modified starch are sent into kneading machine and were kneaded 15-20 minute;
Second goes on foot, the raw material that it is good that the first step is kneaded is sent in the high speed mixing roll, adds dispersion agent, composite coupler, softening agent, oxidation inhibitor, fluorescent whitening agent, UV light absorber, weighting agent successively; Uniform mixing is made compound;
The 3rd goes on foot, the second step compound is sent in the single screw extrusion machine, and temperature is controlled between 150-165 ℃, produces granular article and gets final product.
2, complete biodegradable plastics according to claim 1 is characterized in that: described degraded resin is 31% hydrochloric acid, sodium bicarbonate according to following weight parts proportioning and step preparation by polyvinyl alcohol, butyraldehyde-n, concentration:
A, proportioning:
50 parts of polyvinyl alcohol, 30 parts of butyraldehyde-ns, concentration are 31% 50 parts of hydrochloric acid, 0.4 part of sodium bicarbonate;
B, step:
Getting 600 parts of distilled water adds in the dissolution kettle, when being warming up to 70 ℃, under agitation slowly add polyvinyl alcohol, progressively be warmed up to 95 ℃, in dissolution kettle, constant temperature dissolving 4 hours, make polyvinyl alcohol become the aqueous solution fully, change over to after the filtration in the acetal still, add butyraldehyde-n after being cooled to 50 ℃, continue to be cooled to 18 ℃ ± 5 ℃, add hydrochloric acid, be incubated 1 hour then under 18-20 ℃ of temperature, insulation is 1.5 hours under 20-25 ℃ of temperature, and insulation is 0.5 hour under 25-30 ℃ of temperature, insulation is 0.5 hour under 30-35 ℃ of temperature, insulation is 0.5 hour under 35-40 ℃ of temperature, and insulation is 0.5 hour under 40-45 ℃ of temperature, and insulation is 0.5 hour under 45-50 ℃ of temperature; Insulation is cooled to 30 ℃ after finishing, and puts into the filter of washing still from the taking-up of acetal still and does, and with tap water material is washed to pH value 6-7 earlier, is washed with distilled water to no chlorion again, adds the sodium bicarbonate ambient stable again, 120 minutes steady time; Stable good liquid material is moved into drying plant, through atomizing, be drying to obtain described degraded resin powder.
3, complete biodegradable plastics according to claim 1 is characterized in that: the preparation method of described starch glycerite ester is:
Squeeze into saponification level glycerine in the enamel reaction still earlier, when being warming up to 50 ℃, the starch that under agitation adds the equivalent weight ratio gradually, keep the even temperature of glycerine and starch to separate, stop after in 60-80 minute, being warmed up to 150 ℃ heating up, constant temperature is 30 minutes under this temperature, is cooled to 40 ℃ then, and blowing is the starch glycerite ester.
4, complete biodegradable plastics according to claim 1 is characterized in that: the preparation method of described modified starch is:
Get starch 63%, saponification level glycerine 25%, urea 7%, the ethylene acrylic acid co polymer 5% of weight percent, knead by kneading machine, 140 ℃ of granulations promptly in single screw extrusion machine.
5, complete biodegradable plastics according to claim 1 is characterized in that: described dispersion agent is polyethylene wax W1080; Described composite coupler is the mixture of silane and titanate coupling agent; Described white dyes is the special-purpose whitening agent of plastics; Described oxidation inhibitor is 1010 and auxiliary antioxidant PS802FL; Described UV light absorber is UV-9; Described weighting agent is the above pure wood powders of 1250 orders; Described softening agent is a Plasticizer Epoxidized Soybean Oil.