CN1973715A - Shoulder strap clip and its making process - Google Patents
Shoulder strap clip and its making process Download PDFInfo
- Publication number
- CN1973715A CN1973715A CN 200610168046 CN200610168046A CN1973715A CN 1973715 A CN1973715 A CN 1973715A CN 200610168046 CN200610168046 CN 200610168046 CN 200610168046 A CN200610168046 A CN 200610168046A CN 1973715 A CN1973715 A CN 1973715A
- Authority
- CN
- China
- Prior art keywords
- film
- rete
- shoulder strap
- rectangle
- strap clip
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The shoulder strap clip is one splint including one upper film layer, one lower film layer, one glue layer and one protecting film layer successively arranged from the top to the bottom. The upper film layer has four small holes, whose connecting lines constitute one rectangle or one square, and is combined with the lower film layer through hot pressing except the rectangle or the square part. The rectangle or the square part of the upper film layer is provided with two arc section strings to separate the rectangle or the square part into four symmetrical parts. The shoulder strap clip is clamped onto the shoulder strap of corselet to increase the contact area between the shoulder strap and the shoulder, and this makes the corselet comfortable and less falling probability.
Description
Technical field
The present invention relates to a kind of shoulder strap clip and preparation method thereof.
Background technology
Usually, the chest measurement that the women wears is provided with shoulder belt mostly, to prevent coming off of chest measurement.But present shoulder belt is generally narrower, put on a period of time after because the flexible effect of shoulder belt, can form piggyback and rein in trace.It is attractive in appearance both to have influenced human body, has also caused discomfort.Simultaneously, the shoulder belt of present oblique shoulder brassiere is narrower, and skidproof effect piggyback is bad, and the shoulder that easily comes off has brought puzzlement to the women.
Summary of the invention
The technical problem to be solved in the present invention provides a kind of shoulder strap clip, and this shoulder strap clip can easily be clipped on the shoulder belt, has increased the contact area between shoulder belt and the shoulder, has alleviated the pressure of shoulder belt to shoulder, and discomfort greatly reduces, and does not also rein in trace in formation simultaneously; Solved the caducous problem of oblique shoulder brassiere simultaneously.
Another technical problem that the present invention will solve provides a kind of preparation method of shoulder strap clip.
For solving above-mentioned first technical problem, the present invention adopts following technical scheme: a kind of shoulder strap clip is a plate body, and this plate body comprises rete, following rete, glue layer and protective film from top to bottom successively; The described rete of going up is provided with four apertures, and the line between these four apertures is rectangle or square, and this rectangle or square part are separated with following rete, and the remainder of last rete is hot-forming integrative-structure with following rete; The rectangle of described four aperture lines formation or square part go up rete and are provided with two arc-shaped sections lines, and this section line is divided into upper and lower symmetry, four symmetrical parts of a left side and the right side with rectangle or the square rete of partly going up.
Described rete and the following rete ovalize gone up; This oval-shaped long diameter is 34～46 millimeters; Short diameter is 21～25 millimeters.
Four hole diameters on the described upper layer film are 1.8～2.2 millimeters.
The length of the rectangle separating part that four aperture lines on the described upper layer film form is 14～24 millimeters; Wide is 11～16 millimeters.
Institute's rete of saying and following rete are the thermoplastic polyurethane materials.
For solving above-mentioned second technical problem, the preparation method of a kind of shoulder strap clip of the present invention comprises the steps:
1) gets the transparent membrane of 0.4～0.6 millimeters thick and the hot melt film of 0.15～0.25 millimeters thick and be placed on the sanction bed, open material, open the cut-parts that are cut into protection usefulness with the PE hyaline membrane and by dimensional requirement according to the size of afore mentioned rules;
2) the dull and stereotyped forming machine of heating, last film temperature is decided to be 145～155 ℃, and following film temperature is set at 125～135 ℃;
3) treat to get behind the temperature stabilization that rubber that a slice uses as concora crush is placed on and down on the dull and stereotyped centre position of film, get the hyaline membrane of a slice 0.4～0.6 millimeters thick, be coated with the one side that is sprinkled upon hyaline membrane uniformly with bronze, and then get a slice and do not have 0.4～0.6 millimeters thick hyaline membrane of bronze to be placed on above the hyaline membrane of bronze, bronze is placed on two-layer hyaline membrane above the rubber on the machine between two-layer hyaline membrane again, and then gets a slice rubber and be placed on the hyaline membrane, hot pressing 30～40 seconds makes upper layer film;
4) mould that the shoulder strap clip punching is used is contained on the punch press, and adjusts machine, and the upper layer film that hot pressing is good is placed on the punching film tool and locates, and four apertures are gone out in punching then on upper layer film, and the line between these four apertures is rectangle or square;
5) open the high frequency power supply, whether the inspection machine performance is good, and the mould that the shoulder strap clip impression is used is contained on the high frequency and adjusts; The high frequency temperature is made as about 130～140 ℃, and electric current is transferred to 60～80A, and the time during impression is 3～5 seconds;
6) upper layer film of hole punch is placed on carries out impression on the impression mould, contraposition is wanted accurately during impression, behind the impression four pore size distributions even, no off normal phenomenon; The effect of impression is location usefulness during for last trimming;
7) will open and cut out good PE diaphragm cut-parts and be placed on the rectangle or foursquare position that four holes of upper layer film form, this PE diaphragm cut-parts size is the same big with rectangle or the area that four hole lines form, place it in then on the rubber on the purl machine, above the hot melt film of getting a slice 0.18～0.22 millimeters thick again is placed on, begin hot pressing then; The last film temperature of hot pressing purl machine is made as 125～135 ℃, and following film temperature is made as 110～120 ℃, and the time was made as 25～35 seconds;
8) shoulder belt that hot pressing is the good one side that accompanies hot melt film upwards is placed on gluing with on the mould, is coated with on hot melt film evenly with glue then, and glue thickness is 1～2 millimeter; Glue can not be adhered to other place when noting gluing, keep the clean of shoulder strap clip;
9) oven temperature is made as 95～105 ℃, the time was made as 8～12 minutes, the shoulder strap clip that coats glue is put into baking box toast; The hot melt film in this glue layer and the 8th step forms down rete together;
10) mould that the shoulder strap clip trimming is used is contained on the punch press and adjusts, cover lastblock and shoulder belt PE film of the same size again in the baked one side that has glue, do not made dirty with protection glue, placed it in then on the trimming film tool, with punch press all the other positions, limit are washed out along high frequency impression position;
11) behind good limit, the one side that does not have cementing is handled clean with white spirit, tear the PE diaphragm of glue face then off and go up on the rete rectangle that four hole lines form or the PE diaphragm of square position, get one and shoulder strap clip finished product PE diaphragm of a size again and overlayed on the glue one side; Make finished product.
Advantage of the present invention is: can easily be clipped on the shoulder belt, increase the contact area between shoulder belt and the shoulder, alleviate the pressure of shoulder belt to shoulder, discomfort greatly reduces, and does not also rein in trace in formation simultaneously; Solved the caducous problem of oblique shoulder brassiere simultaneously.
Description of drawings
Fig. 1 is a shoulder strap clip structural representation of the present invention;
Fig. 2 is that Fig. 1 is along A-A face cutaway view;
Fig. 3 is the rectangular segment rollover states figure of rete in the present invention.
The specific embodiment
Shown in Fig. 1～3, a kind of shoulder strap clip of the present invention is a plate body, and it comprises rete 1, following rete 2, glue layer 3 and protective film 4 from top to bottom successively this plate body; The described rete 1 of going up is provided with four apertures 11, and the line between these four apertures 11 is rectangle 12, and these rectangle 12 parts are separated with following rete 2, and the remainder of last rete 1 is hot-forming integrative-structures with following rete 2; Rete is provided with two arc-shaped sections lines 13 on rectangle 12 parts that described four apertures 11 form, and this section line 13 is divided into upper and lower symmetry with rete on rectangle 12 parts, four parts of a left side and right symmetry.
Described rete 1 and following rete 2 ovalizes gone up; This oval-shaped long diameter is 45 millimeters; Short diameter is 24 millimeters.
Four aperture 11 diameters on the described upper layer film 1 are 2.0 millimeters.
The length of the rectangle separating part that four apertures 11 on the described upper layer film 1 form is 23 millimeters; Wide is 15 millimeters.
Institute's rete of saying 1 and following rete 2 are thermoplastic polyurethane materials.
The preparation method of a kind of shoulder strap clip of the present invention comprises the steps:
1) gets the transparent membrane of 0.5 millimeters thick and the hot melt film of 0.2 millimeters thick and be placed on the sanction bed, open material, open the cut-parts of cutting out protection usefulness with the PE hyaline membrane and by dimensional requirement according to the size of afore mentioned rules;
2) the dull and stereotyped forming machine of heating, last film temperature is decided to be 150 ℃, and following film temperature is set at 130 ℃;
3) treat to get behind the temperature stabilization that rubber that a slice uses as concora crush is placed on and down on the dull and stereotyped centre position of film, get the hyaline membrane of a slice 0.5 millimeters thick, be coated with the one side that is sprinkled upon hyaline membrane uniformly with bronze, and then get a slice and do not have 0.5 millimeters thick hyaline membrane of bronze to be placed on above the hyaline membrane of bronze, bronze is placed on two-layer hyaline membrane above the rubber on the machine between two-layer hyaline membrane again, and then gets a slice rubber and be placed on the hyaline membrane, hot pressing 35 seconds makes upper layer film;
4) mould that the shoulder strap clip punching is used is contained on the punch press, and adjusts machine, and the upper layer film that hot pressing is good is placed on the punching film tool and locates, and 4 apertures that are rectangle are gone out in punching then on upper layer film;
5) open the high frequency power supply, whether the inspection machine performance is good, and the mould that the shoulder strap clip impression is used is contained on the high frequency and adjusts; The high frequency temperature is made as 135 ℃, and electric current is transferred to 70A, and the time during impression is 4 seconds;
6) upper layer film of hole punch is placed on carries out impression on the impression mould, contraposition is wanted accurately during impression, behind the impression four pore size distributions even, no off normal phenomenon; The effect of impression is location usefulness during for last trimming;
7) will open and cut out good PE diaphragm cut-parts and be placed on the rectangle position that four holes of upper layer film form, this PE diaphragm cut-parts size is the same big with the rectangular area that four hole lines form, place it in then on the rubber on the purl machine, above the hot melt film of getting a slice 0.2 millimeters thick again is placed on, begin hot pressing then; The last film temperature of hot pressing purl machine is made as 130 ℃, and following film temperature is made as 115 ℃, and the time was made as 30 seconds;
8) shoulder belt that hot pressing is the good one side that accompanies hot melt film upwards is placed on gluing with on the mould, is coated with on hot melt film evenly with glue then, and glue thickness is 1.5 millimeters; Glue can not be adhered to other place when noting gluing, keep the clean of shoulder strap clip;
9) oven temperature is made as 100 ℃, the time was made as 10 minutes, the shoulder strap clip that coats glue is put into baking box toast; The hot melt film in this glue layer and the 8th step forms down rete together;
10) mould that the shoulder strap clip trimming is used is contained on the punch press and adjusts, cover lastblock and shoulder belt PE film of the same size again in the baked one side that has glue, do not made dirty with protection glue, placed it in then on the trimming film tool, with punch press all the other positions, limit are washed out along high frequency impression position;
11) behind good limit, the one side that does not have cementing is handled clean with white spirit, tear the PE diaphragm of glue face then off and go up on the rete PE diaphragm of the rectangle position that four hole lines form, get one and shoulder strap clip finished product PE diaphragm of a size again and overlayed on the glue one side; Make finished product.
Embodiment 2
Shown in Fig. 1～3, a kind of shoulder strap clip of the present invention is a plate body, and it comprises rete 1, following rete 2, glue layer 3 and protective film 4 from top to bottom successively this plate body; The described rete 1 of going up is provided with four apertures 11, and the line between these four apertures 11 is square 12, and these square 12 parts are separated with following rete 2, and the remainder of last rete 1 is hot-forming integrative-structures with following rete 2; Rete is provided with two arc-shaped sections lines 13 on square 12 parts that described four apertures 11 form, and this section line 13 is divided into upper and lower symmetry with rete on square 12 parts, four parts of a left side and right symmetry.
Described rete and the following rete ovalize gone up; This oval-shaped long diameter is 35 millimeters; Short diameter is 23 millimeters.
Four hole diameters on the described upper layer film are 1.8 millimeters.
The length of the square discrete part that four apertures on the described upper layer film form is 15 millimeters; Wide is 15 millimeters.
Institute's rete of saying and following rete are the thermoplastic polyurethane materials.
The preparation method of a kind of shoulder strap clip of the present invention comprises the steps:
1) gets the transparent membrane of 0.4 millimeters thick and the hot melt film of 0.15 millimeters thick and be placed on the sanction bed, open material, open the cut-parts of cutting out protection usefulness with the PE hyaline membrane and by dimensional requirement according to above-mentioned size;
2) the dull and stereotyped forming machine of heating, last film temperature is decided to be 145 ℃, and following film temperature is set at 125 ℃;
3) treat to get behind the temperature stabilization that rubber that a slice uses as concora crush is placed on and down on the dull and stereotyped centre position of film, get the hyaline membrane of a slice 0.4 millimeters thick, be coated with the one side that is sprinkled upon hyaline membrane uniformly with bronze, and then get a slice and do not have 0.4 millimeters thick hyaline membrane of bronze to be placed on above the hyaline membrane of bronze, bronze is placed on two-layer hyaline membrane above the rubber on the machine between two-layer hyaline membrane again, and then gets a slice rubber and be placed on the hyaline membrane, hot pressing 30 seconds makes upper layer film;
4) mould that the shoulder strap clip punching is used is contained on the punch press, and adjusts machine, and the upper layer film that hot pressing is good is placed on the punching film tool and locates, and four apertures are gone out in punching then on upper layer film, and the line between these four apertures is square;
5) open the high frequency power supply, whether the inspection machine performance is good, and the mould that the shoulder strap clip impression is used is contained on the high frequency and adjusts; The high frequency temperature is made as 130 ℃, and electric current is transferred to 60A, and the time during impression is 3 seconds;
6) upper layer film of hole punch is placed on carries out impression on the impression mould, contraposition is wanted accurately during impression, behind the impression four pore size distributions even, no off normal phenomenon; The effect of impression is location usefulness during for last trimming;
7) will open and cut out good PE diaphragm cut-parts and be placed on the square position that four holes of upper layer film form, this PE diaphragm cut-parts size is the same big with the area that four hole lines form, place it in then on the rubber on the purl machine, above the hot melt film of getting a slice 0.18 millimeters thick again is placed on, begin hot pressing then; The last film temperature of hot pressing purl machine is made as 125 ℃, and following film temperature is made as 110 ℃, and the time was made as 25 seconds;
8) shoulder belt that hot pressing is the good one side that accompanies hot melt film upwards is placed on gluing with on the mould, is coated with on hot melt film evenly with glue then, and glue thickness is 1 millimeter; Glue can not be adhered to other place when noting gluing, keep the clean of shoulder strap clip;
9) oven temperature is made as 95 ℃, the time was made as 8 minutes, the shoulder strap clip that coats glue is put into baking box toast; The hot melt film in this glue layer and the 8th step forms down rete together;
10) mould that the shoulder strap clip trimming is used is contained on the punch press and adjusts, cover lastblock and shoulder belt PE film of the same size again in the baked one side that has glue, do not made dirty with protection glue, placed it in then on the trimming film tool, with punch press all the other positions, limit are washed out along high frequency impression position;
11) behind good limit, the one side that does not have cementing is handled clean with white spirit, tear the PE diaphragm of glue face then off and go up on the rete PE diaphragm of the square position that four hole lines form, get one and shoulder strap clip finished product PE diaphragm of a size again and overlayed on the glue one side; Make finished product.
Embodiment 3
Shown in Fig. 1～3, a kind of shoulder strap clip of the present invention is a plate body, and it comprises rete 1, following rete 2, glue layer 3 and protective film 4 from top to bottom successively this plate body; The described rete 1 of going up is provided with four apertures 11, and the line between these four apertures 11 is rectangle 12, and these rectangle 12 parts are separated with following rete 2, and the remainder of last rete 1 is hot-forming integrative-structures with following rete 2; Rete is provided with two arc-shaped sections lines 13 on rectangle 12 parts that described four apertures 11 form, and this section line 13 is divided into upper and lower symmetry with rete on rectangle 12 parts, four parts of a left side and right symmetry.
Described rete and the following rete ovalize gone up; This oval-shaped long diameter is 42 millimeters; Short diameter is 22 millimeters.
Four hole diameters on the described upper layer film are 2.2 millimeters.
The length of the rectangle separating part that four apertures on the described upper layer film form is 23 millimeters; Wide is 12 millimeters.
Institute's rete of saying and following rete are the thermoplastic polyurethane materials.
The preparation method of a kind of shoulder strap clip of the present invention comprises the steps:
1) gets the transparent membrane of 0.6 millimeters thick and the hot melt film of 0.25 millimeters thick and be placed on the sanction bed, open material, open the cut-parts of cutting out protection usefulness with the PE hyaline membrane and by dimensional requirement according to the size of regulation;
2) the dull and stereotyped forming machine of heating, last film temperature is decided to be 155 ℃, and following film temperature is set at 135 ℃;
3) treat to get behind the temperature stabilization that rubber that a slice uses as concora crush is placed on and down on the dull and stereotyped centre position of film, get the hyaline membrane of a slice 0.6 millimeters thick, be coated with the one side that is sprinkled upon hyaline membrane uniformly with bronze, and then get a slice and do not have 0.6 millimeters thick hyaline membrane of bronze to be placed on above the hyaline membrane of bronze, bronze is placed on two-layer hyaline membrane above the rubber on the machine between two-layer hyaline membrane again, and then gets a slice rubber and be placed on the hyaline membrane, hot pressing 40 seconds makes upper layer film;
4) mould that the shoulder strap clip punching is used is contained on the punch press, and adjusts machine, and the upper layer film that hot pressing is good is placed on the punching film tool and locates, and four apertures are gone out in punching then on upper layer film, and the line between these four apertures is rectangle;
5) open the high frequency power supply, whether the inspection machine performance is good, and the mould that the shoulder strap clip impression is used is contained on the high frequency and adjusts; The high frequency temperature is made as 140 ℃, and electric current is transferred to 80A, and the time during impression is 5 seconds;
6) upper layer film of hole punch is placed on carries out impression on the impression mould, contraposition is wanted accurately during impression, behind the impression four pore size distributions even, no off normal phenomenon; The effect of impression is location usefulness during for last trimming;
7) will open and cut out good PE diaphragm cut-parts and be placed on the rectangle position that four holes of upper layer film form, this PE diaphragm cut-parts size is the same big with the rectangular area that four hole lines form, place it in then on the rubber on the purl machine, above the hot melt film of getting a slice 0.22 millimeters thick again is placed on, begin hot pressing then; The last film temperature of hot pressing purl machine is made as 135 ℃, and following film temperature is made as 120 ℃, and the time was made as 35 seconds;
8) shoulder belt that hot pressing is the good one side that accompanies hot melt film upwards is placed on gluing with on the mould, is coated with on hot melt film evenly with glue then, and glue thickness is 2 millimeters; Glue can not be adhered to other place when noting gluing, keep the clean of shoulder strap clip;
9) oven temperature is made as 105 ℃, the time was made as 12 minutes, the shoulder strap clip that coats glue is put into baking box toast; The hot melt film in this glue layer and the 8th step forms down rete together;
10) mould that the shoulder strap clip trimming is used is contained on the punch press and adjusts, cover lastblock and shoulder belt PE film of the same size again in the baked one side that has glue, do not made dirty with protection glue, placed it in then on the trimming film tool, with punch press all the other positions, limit are washed out along high frequency impression position;
11) behind good limit, the one side that does not have cementing is handled clean with white spirit, tear the PE diaphragm of glue face then off and go up on the rete PE diaphragm of the rectangle position that four hole lines form, get one and shoulder strap clip finished product PE diaphragm of a size again and overlayed on the glue one side; Make finished product.
Claims (6)
1, a kind of shoulder strap clip is characterized in that: this shoulder strap clip is a plate body, and this plate body comprises rete, following rete, glue layer and protective film from top to bottom successively; The described rete of going up is provided with four apertures, and the line between these four apertures is rectangle or square, and this rectangle or square part are separated with following rete, and the remainder of last rete is hot-forming integrative-structure with following rete; The rectangle of described four aperture lines formation or square part go up rete and are provided with two arc-shaped sections lines, and this section line is divided into upper and lower symmetry, four symmetrical parts of a left side and the right side with rectangle or the square rete of partly going up.
2, shoulder strap clip as claimed in claim 1 is characterized in that: described rete and the following rete ovalize gone up; This oval-shaped long diameter is 34～46 millimeters; Short diameter is 21～25 millimeters.
3, shoulder strap clip as claimed in claim 1 or 2 is characterized in that: four hole diameters on the described upper layer film are 1.8～2.2 millimeters.
4, shoulder strap clip as claimed in claim 3 is characterized in that: the rectangle that four apertures on the described upper layer film form or the length of positive square separating part are 14～24 millimeters; Wide is 11～16 millimeters.
5, shoulder strap clip as claimed in claim 4 is characterized in that: the described rete of going up is the thermoplastic polyurethane material with following rete.
6, a kind of preparation method of shoulder strap clip is characterized in that: comprise the steps:
1) gets the transparent membrane of 0.4～0.6 millimeters thick and the hot melt film of 0.15～0.25 millimeters thick and be placed on the sanction bed, open material, open the cut-parts that are cut into protection usefulness with the PE hyaline membrane and by dimensional requirement according to the size of afore mentioned rules;
2) the dull and stereotyped forming machine of heating, last film temperature is decided to be 145～155 ℃, and following film temperature is set at 125～135 ℃:
3) treat to get behind the temperature stabilization that rubber that a slice uses as concora crush is placed on and down on the dull and stereotyped centre position of film, get the hyaline membrane of a slice 0.4～0.6 millimeters thick, be coated with the one side that is sprinkled upon hyaline membrane uniformly with bronze, and then get a slice and do not have 0.4～0.6 millimeters thick hyaline membrane of bronze to be placed on above the hyaline membrane of bronze, bronze is placed on two-layer hyaline membrane above the rubber on the machine between two-layer hyaline membrane again, and then gets a slice rubber and be placed on the hyaline membrane, hot pressing 30～40 seconds makes upper layer film;
4) mould that the shoulder strap clip punching is used is contained on the punch press, and adjusts machine, and the upper layer film that hot pressing is good is placed on the punching film tool and locates, and four apertures are gone out in punching then on upper layer film, and the line between these four apertures is rectangle or square;
5) open the high frequency power supply, whether the inspection machine performance is good, and the mould that the shoulder strap clip impression is used is contained on the high frequency and adjusts; The high frequency temperature is made as about 130～140 ℃, and electric current is transferred to 60～80A, and the time during impression is 3～5 seconds;
6) upper layer film of hole punch is placed on carries out impression on the impression mould, contraposition is wanted accurately during impression, behind the impression four pore size distributions even, no off normal phenomenon; The effect of impression is location usefulness during for last trimming;
7) will open and cut out good PE diaphragm cut-parts and be placed on the rectangle or foursquare position that four holes of upper layer film form, this PE diaphragm cut-parts size is the same big with rectangle or the area that four hole lines form, place it in then on the rubber on the purl machine, above the hot melt film of getting a slice 0.18～0.22 millimeters thick again is placed on, begin hot pressing then; The last film temperature of hot pressing purl machine is made as 125～135 ℃, and following film temperature is made as 110～120 ℃, and the time was made as 25～35 seconds;
8) shoulder belt that hot pressing is the good one side that accompanies hot melt film upwards is placed on gluing with on the mould, is coated with on hot melt film evenly with glue then, and glue thickness is 1～2 millimeter; Glue can not be adhered to other place when noting gluing, keep the clean of shoulder strap clip;
9) oven temperature is made as 95～105 ℃, the time was made as 8～12 minutes, the shoulder strap clip that coats glue is put into baking box toast; The hot melt film in this glue layer and the 8th step forms down rete together;
10) mould that the shoulder strap clip trimming is used is contained on the punch press and adjusts, cover lastblock and shoulder belt PE film of the same size again in the baked one side that has glue, do not made dirty with protection glue, placed it in then on the trimming film tool, with punch press all the other positions, limit are washed out along high frequency impression position;
11) behind good limit, the one side that does not have cementing is handled clean with white spirit, tear the PE diaphragm of glue face then off and go up on the rete rectangle that four hole lines form or the PE diaphragm of square position, get one and shoulder strap clip finished product PE diaphragm of a size again and overlayed on the glue one side; Make finished product.